CN107083049A - 具有颜色的聚氨酯泡沫填缝剂及其制备方法和用途 - Google Patents
具有颜色的聚氨酯泡沫填缝剂及其制备方法和用途 Download PDFInfo
- Publication number
- CN107083049A CN107083049A CN201710340924.XA CN201710340924A CN107083049A CN 107083049 A CN107083049 A CN 107083049A CN 201710340924 A CN201710340924 A CN 201710340924A CN 107083049 A CN107083049 A CN 107083049A
- Authority
- CN
- China
- Prior art keywords
- polyurethane foam
- coloured
- cranny filler
- pigment
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于聚氨酯泡沫填缝剂领域,具体涉及一种具有颜色的聚氨酯泡沫填缝剂及其制备方法和用途。其组分按质量分数包括:30%~40%石蜡、10%~30%聚醚多元醇、20~40%多亚甲基多苯基异氰酸酯(MDI)、2%~5%稳定剂、2%~5%催化剂、2%~5%溶剂以及5%~10%颜料。其制备方法是在20~50℃环境中将上述组分混合后搅拌至完全溶解,再将其与溶剂按一定比例并在充入二甲醚气体的条件下加入到耐压容器中并充分摇振,既得成品。有益之处在于:将其用于制作装饰领域和水族造景领域中的假山、人造石及人造沉木,通过对颜料的调配,使其颜色与真实的造景非常一致,生动形象,使用安全可靠,可塑性强,从而降低了水族造景的成本。
Description
技术领域
本发明属于聚氨酯泡沫填缝剂领域,具体涉及一种具有颜色的聚氨酯泡沫填缝剂及其制备方法和用途。
背景技术
聚氨酯发泡剂全称单组分聚氨酯泡沫填缝剂,俗称发泡剂、发泡胶、PU填缝剂,是气雾技术和聚氨酯泡沫技术交叉结合的产物。它是一种将聚氨酯预聚物、发泡剂、催化剂等组分装填于耐压气雾罐中的特殊聚氨酯产品。当物料从气雾罐中喷出时,泡沫状的聚氨酯物料会迅速膨胀并与空气或接触到的基体中的水分发生固化反应形成泡沫。固化后的聚氨酯泡沫填缝剂泡沫具有填缝、粘结、密封、隔热、吸音等多种效果,是一种环保节能、使用方便的建筑材料,可适用于密封堵漏、填空补缝、固定粘结、保温隔音,尤其适用于塑钢或铝合金门窗和墙体间的密封堵漏及防水。
目前,在水族领域中也经常使用聚氨酯泡沫填缝剂,主要应用于对缝隙的填充、固定沉木或假山等,影响其扩大使用范围的原因在于其自身颜色不能与水草和假山融为一体,颜色暗沉不自然,而且其只能保持聚氨酯泡沫填缝剂本色(白色或淡黄色),无法进行颜色的改变,目前要改变其颜色一般是在其固化后进行涂色,如此一来不仅耗费时间,增加使用成本,而且颜色不均匀,导致造景不够美观。
因此,发明一种应用于水族造景领域中的颜色逼真、使用方便,对水体无污染的聚氨酯泡沫填缝剂显得尤为重要。
发明内容
为了解决上述技术缺陷,本发明提供了一种具有颜色的聚氨酯泡沫填缝剂及其制备方法和用途,其具体技术方案如下:
一种具有颜色的聚氨酯泡沫填缝剂,其组分按质量分数包括:30%~40%石蜡、10%~30%聚醚多元醇、20~40%多亚甲基多苯基异氰酸酯(MDI)、2%~5%稳定剂、2%~5%催化剂、2%~5%溶剂以及5%~10%颜料。
作为本发明的一种优选技术方案,其组分按质量分数包括:33%石蜡、22%聚醚多元醇、29%多亚甲基多苯基异氰酸酯(MDI)、3%稳定剂、3%催化剂、3%溶剂以及7%颜料。
作为本发明的一种优选技术方案,所述颜料由质量份数为4~5份的黄色、4~5份的红色和1~2份的黑色颜料组成。
作为本发明的一种优选技术方案,所述颜料由质量份数为4~6份的黄色、4~6份的黑色颜料组成。
作为本发明的一种优选技术方案,所述颜料为青岛宝芝塑胶材料有限公司生产的YE-3659、RE-3645以及BL-3544或济南新星化工有限公司生产的黄色1#、红色9#以及黑色21#。
作为本发明的一种优选技术方案,所述石蜡为氯化石蜡42#和氯化石蜡52#的混合物,按重量份比,氯化石蜡42#∶氯化石蜡52#=16~30∶10~20。
作为本发明的一种优选技术方案,所述聚醚多元醇是羟值为180~260mgKOH/g,官能度为2~3的聚醚多元醇。
作为本发明的一种优选技术方案,所述稳定剂为硅油,所述溶剂为丙丁烷,所述催化剂为双吗啉基二乙基醚(DEDEE)、辛酸亚锡、二月硅酸二丁基锡中的至少一种。
本发明中进一步提供了一种制备上述一种具有颜色的聚氨酯泡沫填缝剂的方法,其具体方法是,按上述重量份配比,在20~50℃环境中将所述石蜡、聚醚多元醇、多亚甲基多苯基异氰酸酯(MDI)、稳定剂、催化剂和颜料混合后搅拌至完全溶解,再将其与溶剂按一定比例并在充入推进剂二甲醚气体的条件下加入到耐压容器中并充分摇振,既得成品。
此外,本发明还提供了一种上述的一种具有颜色的聚氨酯泡沫填缝剂的用途,即是用于制作装饰领域和水族造景领域中的假山、人造石及人造沉木。
本发明与现有技术相比,有益之处在于:
1、本发明属于单组份聚氨酯泡沫填缝剂,使用安全方便。
2、本发明的聚氨酯泡沫填缝剂由于加入了颜料,该颜料为硅性颜料或油性颜料,不仅性能稳定,不溶于水也不与水进行反应,因此不会污染水体,并且不退色,而且由于颜料加入改变了聚氨酯泡沫填缝剂的物理结构,进一步提高了发泡率,使得其固化后孔隙较多,利于形成水草的固定基,因此非常适合作为水族造景中的假山或人造沉木。
3、在本发明的具体创造过程中,发明人发现了在本聚氨酯泡沫填缝剂中最佳的颜料配比,该配比得出的聚氨酯泡沫填缝剂在固化后形成的假山或者人造沉木的颜色相比于现有技术中利用其他方法制成的水族造景相比较更加自然生动,几乎达到与真实的青龙石、火山石以及沉木不能分辨的程度,并且由于本发明的聚氨酯泡沫填缝剂可塑性是自然材料不能比拟的。
4、将本发明的聚氨酯泡沫填缝剂应用于水族造景领域中代替自然材料,不仅可塑性强,而且其化学物理性质稳定,长期置于水中不会发生变化,并且不会像自然材质的青龙石、火山石以及沉木容易被藻类附着。而且聚氨酯泡沫填缝剂的材质更轻,大大降低了水族缸的受力。
5、本发明的聚氨酯泡沫填缝剂由于加入了硅性颜料或油性颜料,固化后该颜料颗粒均匀分布于聚氨酯泡沫分子之间,不仅改变了聚氨酯泡沫填缝剂的范德瓦尔斯力,大大减少了固化时间,而且呈色均匀,此外,由于颜料颗粒大小不均,打破了现有技术的聚氨酯泡沫的微观结构,造成聚氨酯泡沫的发泡不均匀,孔隙不统一,从而产生更自然的效果。
综上所述,本发明的聚氨酯泡沫填缝剂由于创造性的加入了硅性颜料或油性颜料,并且进一步优化选择了各色颜料的配比,固化后即可形成颜色逼真的假山、沉木等造景,使用非常方便,性能稳定,不污染水质,特别适合水族造景领域。
具体实施方式
以下结合具体实施例对本发明的技术方案作进一步公开。
一种具有颜色的聚氨酯泡沫填缝剂,其组分按质量分数包括:石蜡、聚醚多元醇、多亚甲基多苯基异氰酸酯(MDI)、稳定剂、催化剂、溶剂以及颜料。所述颜料为青岛宝芝塑胶材料有限公司生产的YE-3659、RE-3645以及BL-3544或济南新星化工有限公司生产的黄色1#、红色9#以及黑色21#。所述石蜡为氯化石蜡42#和氯化石蜡52#的混合物,按重量份比,氯化石蜡42#∶氯化石蜡52#=16~30∶10~20。所述聚醚多元醇是羟值为180~260mgKOH/g,官能度为2~3的聚醚多元醇。所述稳定剂为硅油,所述溶剂为丙丁烷,所述催化剂为双吗啉基二乙基醚(DEDEE)、辛酸亚锡、二月硅酸二丁基锡中的至少一种。
本发明中进一步提供了一种制备上述一种具有颜色的聚氨酯泡沫填缝剂的方法,其具体方法是,按上述重量份配比,在20~50℃环境中将所述石蜡、聚醚多元醇、多亚甲基多苯基异氰酸酯(MDI)、稳定剂、催化剂和颜料混合后搅拌至完全溶解,再将其与溶剂按一定比例并在充入推进剂二甲醚气体的条件下加入到耐压容器中并充分摇振,既得成品。
此外,本发明还提供了一种上述的一种具有颜色的聚氨酯泡沫填缝剂的用途,即是用于制作装饰领域和水族造景领域中的假山、人造石及人造沉木。
下面通过表格来详细说明本发明的实施例(按质量分数计)
组分 | 实施例1 | 实施例2 | 实施例3 | 实施例4 |
石蜡 | 30% | 33% | 40% | 33 |
聚醚多元醇 | 30% | 22% | 10% | 15% |
多亚甲基多苯基异氰酸酯 | 20% | 29% | 30% | 40% |
稳定剂(硅油) | 5% | 3% | 2% | 2% |
催化剂 | 5% | 3% | 4% | 2% |
溶剂(丙丁烷) | 5% | 3% | 4% | 2% |
颜料 | 5% | 7% | 10% | 6% |
在上述实施例中,催化剂以及颜料的具体选择为:
对上述实施例1至4,以及以目前市面上常见的普通单组份聚氨酯泡沫填缝剂为对照例进行具体性能进行测试:
1、密度的测试:按照标准GB/T 6343单组份聚氨酯泡沫填缝剂的规定进行测定;
2、发泡倍数的测试:由于本发明的产品主要用于水族造景,因此只需进行常温测试:在20~30℃,相对湿度为50%,按照标准JC936-2004中7.8的规定进行测定。
3、完全固化时间:在温度25℃,相对湿度50%的环境中,喷出固定量(50g)的填缝剂后开始计时,至其完全成为泡沫固体时计时结束,计算泡沫完全固化所耗费的时间。
4、孔隙率:将完全固化后的泡沫固体进行测试孔隙率,采用固化后的泡沫固体体积与泡沫固体在密实状态的体积的差再与固化后的泡沫固体体积作商得出。
5、颜色观察,通过10人的肉眼观察与真实的青龙石和沉木进行颜色的比较,并以优良及格的评分标准进行计分。
以下是测试的结果:
通过上述性能测试,本发明的实施例与现有技术的对照例相比,很显然更适合作为水族造景领域,本发明的一种具有颜色的聚氨酯泡沫填缝剂在水中性能稳定,可保证5年不会发生变性和分解或褪色,并具有良好的粘结力和隔热性,固化后还可由人工进行外形的雕琢,使用方便安全,进一步降低了水族造景的成本。
上述具体实施方式仅是本发明的具体个案,本发明的专利保护范围包括但不限于上述具体实施方式的产品形态和式样,任何符合本发明权利要求书且任何所属技术领域的普通技术人员对其所做的适当变化或修饰,皆应落入本发明的专利保护范围。
Claims (10)
1.一种具有颜色的聚氨酯泡沫填缝剂,其特征在于,其组分按质量分数包括:30%~40%石蜡、10%~30%聚醚多元醇、20~40%多亚甲基多苯基异氰酸酯(MDI)、2%~5%稳定剂、2%~5%催化剂、2%~5%溶剂以及5%~10%颜料。
2.根据权利要求1所述的一种具有颜色的聚氨酯泡沫填缝剂,其特征在于,其组分按质量分数包括:33%石蜡、22%聚醚多元醇、29%多亚甲基多苯基异氰酸酯(MDI)、3%稳定剂、3%催化剂、3%溶剂以及7%颜料。
3.根据权利要求1所述的一种具有颜色的聚氨酯泡沫填缝剂,其特征在于,所述颜料由质量份数为4~5份的黄色、4~5份的红色和1~2份的黑色颜料组成。
4.根据权利要求1所述的一种具有颜色的聚氨酯泡沫填缝剂,其特征在于,所述颜料由质量份数为4~6份的黄色、4~6份的黑色颜料组成。
5.根据权利要求3或4所述的一种具有颜色的聚氨酯泡沫填缝剂,其特征在于,所述颜料为青岛宝芝塑胶材料有限公司生产的YE-3659、RE-3645以及BL-3544或济南新星化工有限公司生产的黄色1#、红色9#以及黑色21#。
6.根据权利要求1或2所述的一种具有颜色的聚氨酯泡沫填缝剂,其特征在于,所述石蜡为氯化石蜡42#和氯化石蜡52#的混合物,按重量份比,氯化石蜡42#∶氯化石蜡52#=16~30∶10~20。
7.根据权利要求1或2所述的一种具有颜色的聚氨酯泡沫填缝剂,其特征在于,所述聚醚多元醇是羟值为180~260mgKOH/g,官能度为2~3的聚醚多元醇。
8.根据权利要求1或2所述的一种具有颜色的聚氨酯泡沫填缝剂,其特征在于,所述稳定剂为硅油,所述溶剂为丙丁烷,所述催化剂为双吗啉基二乙基醚(DEDEE)、辛酸亚锡、二月硅酸二丁基锡中的至少一种。
9.一种制备权利要求1所述的一种具有颜色的聚氨酯泡沫填缝剂的方法,其特征在于,按上述重量份配比,在20~50℃环境中将所述石蜡、聚醚多元醇、多亚甲基多苯基异氰酸酯(MDI)、稳定剂、催化剂和颜料混合后搅拌至完全溶解,再将其与溶剂按一定比例并在充入推进剂二甲醚气体的条件下加入到耐压容器中并充分摇振,既得成品。
10.一种权利要求1所述的一种具有颜色的聚氨酯泡沫填缝剂的用途,其特征是,用于制作装饰领域和水族造景领域中的假山、人造石及人造沉木。