CN107021697A - For the preparation method of the material, artificial hillock and artificial hillock that make artificial hillock - Google Patents
For the preparation method of the material, artificial hillock and artificial hillock that make artificial hillock Download PDFInfo
- Publication number
- CN107021697A CN107021697A CN201710216321.9A CN201710216321A CN107021697A CN 107021697 A CN107021697 A CN 107021697A CN 201710216321 A CN201710216321 A CN 201710216321A CN 107021697 A CN107021697 A CN 107021697A
- Authority
- CN
- China
- Prior art keywords
- artificial hillock
- outer layer
- inorfil
- pigment
- make artificial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of material for being used to make artificial hillock, it can not use mould and can make artificial hillock.A kind of material for being used to make artificial hillock, it is characterised in that:Including inorfil, binding agent, pigment and auxiliary agent;Wherein inorfil is made up of the composition of following mass percent:Al203 15‑20%、CaO 20‑25%、MgO 7‑12%、Ti02 0.5‑2%、MnO 0.01‑0.5%、P205 0.01‑0.5%、Na20 0.1‑3%、K20 0.1‑3%、Si02 35‑55%。
Description
Technical field
The invention belongs to the technical field of artificial hillock.
Background technology
The A of publication number CN 105128591, the Chinese invention patent application in publication date on December 09th, 2015 disclose one kind
Raw rockwork is planted, including shell, osculum, planting hole, kind grass planting and filler, the shell is colored full lightweight aggregate fiber
Concrete casing, the filler is haydite foam water soil filler.The colored full lightweight aggregate fiber concrete component includes bone
Material, fiber, cement, steel wire and water reducer, the aggregate are bulk density 500kg/m3~1000kg/m3 haydite
And pottery sand, the fiber is high elastic modulus organic fiber or alkali-resistant glass fibre, and the cement is white cement, aluminium sulfate water
One kind in mud or Portland cement, the water reducer is the high efficiency water reducing agent of water-reducing rate more than 25%, the concrete
More than compression strength 30MPa.
However, the inner stuffing of the raw rockwork of the plant of this structure is not convenient using haydite foam water soil materials, and
And the rockwork shape is made by designing mold shape, so make also inconvenient.
The content of the invention
It is an object of the invention to provide a kind of material for being used to make artificial hillock, it can not use mould and can make vacation
Mountain.
In order to solve the above technical problems, the object of the present invention is achieved like this:
A kind of material for being used to make artificial hillock, it is characterised in that:Including inorfil, binding agent, pigment and auxiliary agent;It is wherein inorganic
Fiber is made up of the composition of following mass percent:Al203 15-20%、CaO 20-25%、MgO 7-12%、Ti02 0.5-2%、
MnO 0.01-0.5%、 P205 0.01-0.5%、Na20 0.1-3%、K20 0.1-3% 、Si02 35-55%。
On the basis of such scheme and it is used as the preferred scheme of such scheme:The average diameter of inorfil is 2 ~ 7 micro-
Rice;Inorfil average length is 0.2 ~ 40 millimeter.
On the basis of such scheme and it is used as the preferred scheme of such scheme:Binding agent includes rapid-curing cutback cement and silicate
Cement;Mass ratio between rapid-curing cutback cement and portland cement is 0-10:5.
On the basis of such scheme and it is used as the preferred scheme of such scheme:The pigment is selected from iron oxide red, oxidation
One or more in titanium, carbon black, iron oxide yellow and chrome green.
On the basis of such scheme and it is used as the preferred scheme of such scheme:The auxiliary agent includes early strength agent, water reducer,
And selected from Al (SO4)3•18H2O、Al2(SO4)3•K2SO4•24H2O、NaAlO3With the one or more in molysite crystal;Its
In, molysite crystal is selected from FeCl3•6H2O、FeSO4•6H2O and Fe2(SO4)3•2H2One or more in O.
On the basis of such scheme and it is used as the preferred scheme of such scheme:Between inorfil, binding agent and pigment
Mass ratio be 800-1000:30-400:0-10;The mass ratio of inorfil, the gross mass of binding agent and pigment and auxiliary agent is
1000:1-5.
On the basis of such scheme and it is used as the preferred scheme of such scheme::Also include being used to be coated in the material
The urea-formaldehyde glue on the surface after shaping.
The present invention, which also provides a kind of application, the artificial hillock of above-mentioned material, including foundation structure, it is characterised in that:The base
Plinth structure is made of foam block, soil, building waste, stone, concrete and/or steelframe, in the outer surface of the foundation structure
Outer layer is covered with, the outer layer is made after being mixed using described material with water.
The present invention also provides the preparation method that a kind of application has the artificial hillock of above-mentioned material, including foundation structure, including base
Plinth structure construction step, the initial shape of artificial hillock is constructed using foam block, soil, building waste, stone, concrete and/or steelframe
Shape;Outer layer coating step, described material mixed with water after after and its it is uncured before overlay on the surface of foundation structure, the material
Mass ratio with water is 100:70-150.
On the basis of such scheme and it is used as the preferred scheme of such scheme:Before outer layer is uncured, press to
The density of outer layer is controlled, a part of region of outer layer forms high-density region, and another part region of outer layer forms low density area
Domain.
The present invention is prominent and beneficial compared with prior art to be had the technical effect that:
The material for being used to make artificial hillock of the present invention so that there is good water-retaining property, water penetration after shaping.In addition, through reality
Checking is bright, the good slump is shown using the inorfil of this composition, advantage becomes apparent from terms of the plastotype of artificial hillock.By
There is the good slump in it so that need not can also produce the distinct corner angle of artificial hillock using mould in manufacturing process.
Brief description of the drawings
Fig. 1 is the cross-sectional view of the artificial hillock of the present invention.
Embodiment
To make the purpose, technical scheme and advantage of the application clearer, below in conjunction with the accompanying drawing in embodiment, to reality
The technical scheme applied in example is clearly and completely described, it is clear that described embodiment is only the application part implementation
Example, rather than whole embodiments.Based on the embodiment provided, those of ordinary skill in the art are not before creative work is made
The every other embodiment obtained is put, the scope of the application protection is belonged to.
In the description of the present application, it is to be understood that the orientation or position relationship of the instruction such as term " on ", " under " are base
In orientation shown in the drawings or position relationship, it is for only for ease of description the application and simplifies description, rather than indicate or imply
Signified device or element must have specific orientation, with specific azimuth configuration and operation, therefore it is not intended that to this
The limitation of application.
The invention discloses a kind of material for being used to make artificial hillock, including inorfil, binding agent, pigment and auxiliary agent.Make
Use this material, the greatly convenient making of artificial hillock especially shows that reduction is used for the choice requirement for making artificial hillock.So,
Make artificial hillock during, can gather materials on the spot, i.e., using foam block, soil, building waste, stone, concrete and/or steelframe come
Foundation structure is built, the general shape of artificial hillock is constructed, then its outer surface is attached to using the material of the present invention and is made
Type, and make artificial hillock that there are distinct corner angle, so as to invest the agile sense of artificial hillock and aesthetic feeling.The material for being used to make artificial hillock of the present invention
In specific application, it is mixed material in proportion with water, upon mixing for artificial hillock moulding, with fine and smooth the rib for showing artificial hillock
Angle.Binding agent is used to be solidified inorfil, makes it into intensity, rigidity.As a result of inorfil, make material
There is hole, with appropriate water penetration, water-retaining property, to utilize plant growth after solidification.Pigment is used for the color for enriching artificial hillock.
By using the slump can be reduced under the collective effect of auxiliary agent and inorfil composition, in order to the moulding of artificial hillock.
Generally, the mass ratio between inorfil, binding agent and pigment is 800-1000:30-400:0-10;Inorganic fibre
The mass ratio of dimension, the gross mass of binding agent and pigment and auxiliary agent is 1000:1-5.
It should be noted that pigment and auxiliary agent can be mixed in advance with inorfil, binding agent etc. or the later stage applies
Man-hour adds.
In the present embodiment, the average diameter of inorfil is 2 ~ 7 microns;Inorfil average length is 0.2 ~ 40 milli
Rice.Generally, the composition of inorfil is:Al203 15-20%、CaO 20-25%、MgO 7-12%、Ti02 0.5-2%、 MnO
0.01-0.5%、 P205 0.01-0.5%、Na20 0.1-3%、K20 0.1-3% 、Si02 35-55%.Using this inorfil,
There is hole after hardening so that there is good water-retaining property, water penetration after shaping.In addition, the experiment proved that, using this
The inorfil of composition shows the good slump, and advantage becomes apparent from terms of the plastotype of artificial hillock.
In the present embodiment, binding agent includes rapid-curing cutback cement and portland cement;Between rapid-curing cutback cement and portland cement
Mass ratio be 0-10:5.
Generally, binding agent is mixed and synthesized using rapid-curing cutback muddy water and portland cement.Using this two-component, you can so that nothing
Machine fiber obtains rapid curing, it is also ensured that the intensity after its solidification.Certainly, binding agent can also be only with silicate cement
Mud.
In the present embodiment, the pigment is in iron oxide red, titanium oxide, carbon black, iron oxide yellow and chrome green
One or more.The color of artificial hillock can be enriched using these pigment.
The auxiliary agent includes early strength agent, water reducer, and selected from Al (SO4)3•18H2O、Al2(SO4)3•K2SO4•24H2O、
NaAlO3With the one or more in molysite crystal;Wherein, molysite crystal is selected from FeCl3•6H2O、FeSO46H2O and Fe2
(SO4)3•2H2One or more in O.Above-mentioned aluminium salt crystal and molysite crystal, it is used as water purification precipitating reagent.
Mixing water amount can be reduced by being reduced by water reducer, accelerated hydrated cementitious speed by early strength agent, improved early stage
Intensity.It is understood that by adding water reducer and early strength agent in the mixture of inorfil and binding agent, passing through
Reduce water consumption and improve early strength, significantly reduce the slump., can be not under the collective effect of these compositions
The distinct corner of artificial hillock is easily moulded on the premise of mould using globality, that is, carries out moulding, and can also ensure that vacation
The shaping of mountain corner.Further, since employing inorfil in component, there is crack after shaping can be avoided.
It should be noted that the mould due to artificial hillock in forming process without using globality, that is, applying above-mentioned material
During do not use mould, so, during coming to artificial hillock moulding using above-mentioned material, in the different zones of artificial hillock
Density domination can be carried out by press degree of constructing.Its density of the region of compacting is pressed in work progress big, be relatively free of rammer
Real its density of region is small.Accordingly, the small porosity of density is small, and the small porosity of density is big.Used in the region without compacting
In cultivated plant.
Also include the urea-formaldehyde glue for being used to be coated in the surface after the material shaping.
The artificial hillock surface after construction and maintenance is coated in by urea-formaldehyde glue so that form rigid course on the surface of artificial hillock.
Generally, after construction and maintenance, in the closely knit place's spraying urea-formaldehyde glue of the pressing of artificial hillock, to form rigid course in this place.Need
Bright, urea-formaldehyde glue can not also be sprayed by pressing closely knit place, and the later stage can cultivate the lichens such as moss.In no pressing compacting
Region is used for cultivating plants.
There are the artificial hillock of above-mentioned material, including foundation structure 1 the invention also discloses a kind of application, its described foundation structure
It is made, is covered with the outer surface of the foundation structure outer of foam block, soil, building waste, stone, concrete and/or steelframe
Layer 2, the outer layer is made after being mixed using described material with water.
It should be noted that when making the outer layer of artificial hillock, after described material is mixed with water and its is uncured
Before be attached to the outer surface of foundation structure.Due to containing binding agent in the material, so that outer layer is securely attached to basis
The outer surface of structure.
It is pointed out that the outer surface of foundation structure refers to be exposed to earth's surface part above.
There are the method that above-mentioned material makes artificial hillock, including foundation structure, including basis knot invention additionally discloses a kind of application
Structure construction step, the original shape of artificial hillock is constructed using foam block, soil, building waste, stone, concrete and/or steelframe;Outside
Layer coating step, after described material is mixed with water and its it is uncured before overlay on the surface of foundation structure, the material and water
Mass ratio is 100:70-150.
Before outer layer is uncured, press to control the density of outer layer, a part of region of outer layer forms high density area
Domain, another part region of outer layer forms density regions.Specifically, outer layer a part of region carry out pressing compacting with
Form high-density region;Another part region then forms density regions.It should be noted that when making density regions,
It can slightly press or not press.
It is pointed out that
Artificial hillock after completing, postmenstruation maintenance, the lichens such as moss can be cultivated in the high-density region later stage.In low-density
Region is used for cultivating plants.Generally, it is provided with density regions in groove, groove and is implanted into plant.Because plant is positioned at low close
Region is spent, and foundation structure is also to be made up of foam block, soil, building waste, stone, concrete and/or steelframe, beneficial to plant
Root growth.
It should be noted that high-density region and density regions are relative concepts, i.e., shown in outer layer different
Density, the density in a part of region higher than another region density when, the relatively large region of density is defined as high density area
Domain, density regions are defined as by the relatively small region of density.
Above-described embodiment is only presently preferred embodiments of the present invention, is not limited the scope of the invention according to this, therefore:It is all according to
The equivalence changes that structure, shape, the principle of the present invention is done, all should be covered by within protection scope of the present invention.
Claims (10)
1. a kind of material for being used to make artificial hillock, it is characterised in that:Including inorfil, binding agent, pigment and auxiliary agent;Wherein without
Machine fiber is made up of the composition of following mass percent:Al203 15-20%、CaO 20-25%、MgO 7-12%、Ti02 0.5-
2%、 MnO 0.01-0.5%、 P205 0.01-0.5%、Na20 0.1-3%、K20 0.1-3% 、Si02 35-55%。
2. the material according to claim 1 for being used to make artificial hillock, it is characterised in that:The average diameter of inorfil be 2 ~
7 microns;Inorfil average length is 0.2 ~ 40 millimeter.
3. the material according to claim 1 for being used to make artificial hillock, it is characterised in that:Binding agent includes rapid-curing cutback cement and silicon
Acid salt cement;Mass ratio between rapid-curing cutback cement and portland cement is 0-10:5.
4. the material according to claim 1 for being used to make artificial hillock, it is characterised in that:The pigment be selected from iron oxide red,
One or more in titanium oxide, carbon black, iron oxide yellow and chrome green.
5. the material according to claim 1 for being used to make artificial hillock, it is characterised in that:The auxiliary agent includes early strength agent, subtracted
Aqua, and selected from Al (SO4)3•18H2O、Al2(SO4)3•K2SO4•24H2O、NaAlO3With one kind in molysite crystal or several
Kind;Wherein, molysite crystal is selected from FeCl3•6H2O、FeSO4•6H2O and Fe2(SO4)3•2H2One or more in O.
6. the material according to claim 1 for being used to make artificial hillock, it is characterised in that:Inorfil, binding agent and pigment
Between mass ratio be 800-1000:30-400:0-10;The quality of inorfil, the gross mass of binding agent and pigment and auxiliary agent
Than for 1000:1-5.
7. the material according to claim 1 for being used to make artificial hillock, it is characterised in that:Also include being used to be coated in the material
The urea-formaldehyde glue on the surface after material shaping.
The artificial hillock of the material described in requirement 1-7 8. a kind of application is had the right, including foundation structure, it is characterised in that:The basis
Structure is made of foam block, soil, building waste, stone, concrete and/or steelframe, is covered in the outer surface of the foundation structure
There are outer layer, the outer layer to be made after being mixed using described material with water.
The preparation method of the artificial hillock of the material described in requirement 1-7 9. a kind of application is had the right, including foundation structure, its feature exist
In:Including infrastructures built step, artificial hillock is constructed using foam block, soil, building waste, stone, concrete and/or steelframe
Original shape;Outer layer coating step, described material mixed with water after after and its it is uncured before overlay on the surface of foundation structure,
The mass ratio of the material and water is 100:70-150.
10. the preparation method of artificial hillock according to claim 9, it is characterised in that:Before outer layer is uncured, press to
The density of outer layer is controlled, a part of region of outer layer forms high-density region, and another part region of outer layer forms low density area
Domain.