KR200324510Y1 - porous concrete block - Google Patents

porous concrete block Download PDF

Info

Publication number
KR200324510Y1
KR200324510Y1 KR20-2003-0009995U KR20030009995U KR200324510Y1 KR 200324510 Y1 KR200324510 Y1 KR 200324510Y1 KR 20030009995 U KR20030009995 U KR 20030009995U KR 200324510 Y1 KR200324510 Y1 KR 200324510Y1
Authority
KR
South Korea
Prior art keywords
concrete block
porous concrete
weight
present
mixture
Prior art date
Application number
KR20-2003-0009995U
Other languages
Korean (ko)
Inventor
김갑중
Original Assignee
김갑중
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to KR20030004876 priority Critical
Priority to KR2020030004876 priority
Application filed by 김갑중 filed Critical 김갑중
Application granted granted Critical
Publication of KR200324510Y1 publication Critical patent/KR200324510Y1/en

Abstract

본 고안은 옹벽이나, 제방, 하천의 호안, 도로의 사면 등을 안정시키기 위한 구조물을 구축하는데 사용하는 블록에 관한 것으로, 보다 상세하게는 식물의 정착 및 생육이 가능할 뿐 아니라 식물뿌리가 토양에 용이하게 활착할 수 있도록 공극과 홈이 구비되며 중량이 크고 잘 깨지지 않는 강도를 가져서 구조적인 안정성과 환경친화성을 더욱 높인 다공성 콘크리트 블록에 관한 것이다.The present invention relates to a block used to build a structure for stabilizing a retaining wall, a levee, a river shore, a road slope, and more specifically, it is possible not only to settle and grow plants but also to facilitate plant roots in soil. The present invention relates to a porous concrete block provided with voids and grooves so as to easily slide, and having a high weight and not easily broken strength, thereby increasing structural stability and environmental friendliness.

본 고안의 다공성 콘크리트 블록은 자갈, 모래 등의 골재와, 상기 골재의 13∼18중량%의 고로시멘트와, 상기 고로시멘트의 25∼35중량%의 AE감수제, 접착제 및 물로 이루어진 혼합물을 섞어서 된 모르타르혼합물에 그 부피를 기준으로 2∼3부피%의 보강제를 추가하여 혼합하고, 다각형의 블록 형틀에 넣어 일정높이의 두께를 가지는 다각형의 평면형상으로 상하좌우면에는 측면홈(12)이 형성되고 모서리에 돌출부(13)가 형성되는 몸통부(10)로 이루어지며 상기 몸통부(10)의 중앙에는 식물이 뿌리를 내려 정착하기 쉽도록 다수개의 중앙홈(11)이 구비되게 성형하고, 미세한 분말상의 숯 또는 황토를 뿌린 후 50∼60℃의 스팀을 30분∼2시간 공급하여 굳히는 스팀양생을 통하여 이루어진다.The porous concrete block of the present invention is a mortar obtained by mixing aggregates such as gravel, sand, 13-18 wt% blast furnace cement of the aggregate, and 25-35 wt% AE reducing agent, adhesive, and water of the blast furnace cement. 2 ~ 3% by volume of reinforcing agent is added to the mixture and mixed, and put into a polygonal block form, and the side surface 12 is formed on the top, bottom, left, and right sides in a polygonal planar shape having a certain height. Consists of a body portion 10 is formed with a protrusion 13 in the center of the body portion 10 is formed to be provided with a plurality of central grooves 11 so that the plant is easy to settle down the root, fine powdery After sprinkling charcoal or loess, steam is cured by supplying steam at 50 to 60 ℃ for 30 minutes to 2 hours.

Description

다공성 콘크리트 블록{porous concrete block}Porous concrete block

본 고안은 공원등의 옹벽이나, 제방, 하천의 호안, 도로의 사면 등을 안정시키기 위한 구조물을 구축하는데 사용하는 콘크리트 블록에 관한 것으로, 특히 식물의 정착 및 생육이 용이하도록 일정크기의 공극을 형성하고, 잘 깨지지 않는 물성을 가지며 중량이 큰 다공성 콘크리트 블록을 제공함으로써, 구조적인 안정성이 확보될 뿐만 아니라 자연 생태적인 안정성이 확보되어서 환경친화적인 토목구조물을 구현할 수 있도록 한 다공성 콘크리트 블록 및 그의 제조방법에 관한 것이다.The present invention relates to a concrete block used to build a structure for stabilizing a retaining wall such as a park, a levee, a river bank, a slope of a road, and the like, and particularly, to form a certain size of pores to facilitate plant settlement and growth. The porous concrete block and its manufacturing method which can realize the eco-friendly civil engineering structure by ensuring the structural stability as well as the natural ecological stability by providing a porous concrete block having a heavy weight and hardly broken properties It is about.

지금까지 공원등지의 옹벽이나, 제방, 하천의 호안, 도로의 사면 등을 공사함에 있어서, 토양안정과 경사면보호라는 측면을 최우선으로 중요시하여 콘크리트 옹벽이나, 콘크리트 블록에 의한 시공이 주류를 이루고 있다.Up to now, when constructing retaining walls such as parks, banks, banks of rivers, slopes of roads, etc., priority has been placed on the stability of the soil and the protection of the slopes.

이와 같은 콘크리트구조의 사면은 주변의 자연환경과 어울리지 않는 딱딱한 외관을 제공하여 도시경관을 해치고 있다. 이에 따라 최근에는 조형미를 갖춘 조형블록에 의한 시공이 늘어났다. 하지만 이와 같은 조형블록도 콘크리트로 이루어졌기 때문에 식물이 생존할 수 없어서 여전히 콘크리트가 주는 딱딱한 느낌을 벗어나지 못하며, 원래의 하천이나 도로변의 자연 생태계와는 이질적이어서 식물이나 미생물, 어류, 소동물등의 자연 생태환경을 악화시키는 요인이 되고 있다.The slope of the concrete structure is damaging the urban landscape by providing a rigid appearance that does not match the surrounding natural environment. As a result, the construction by molding blocks with molding beauty has increased recently. However, since the molding block is made of concrete, the plant cannot survive and still cannot escape the hard feeling of concrete, and it is heterogeneous with the natural ecosystem of the river or roadside, so it is natural ecology of plants, microorganisms, fish and small animals. It is a factor that makes the environment worse.

또한, 콘크리트블록 자체에 배수기능이 없어 자갈등으로 뒷채움공사를 실시하나, 배수가 원활히 이루어지지 못하여서 수압에 의해 붕괴될 위험성이 상존하는 등 구조적인 안정성을 확보하기가 어려웠다.In addition, although the concrete block itself does not have a drainage function, the backfill work is performed with gravel, but it is difficult to secure structural stability, such as the risk of collapse due to water pressure due to the lack of drainage.

한편, 일부에서는 블록을 이용하여 사면을 안정화시키는데 있어서, 사면의 중간부분을 군데군데 생략한 채로 블록을 구축하여, 생략된 부분으로 노출되는 토양에 식물이 정착되도록 하는 시도가 이루어지고 있다. 그러나, 이 방법도 토양이 노출된 부분으로 인한 사면의 안정에 문제가 발생할 소지가 다분하여서 적용범위가 극히 제한적일 수 밖에 없으며, 사면 전체의 식생과는 거리가 멀다. 따라서 이러한 방법도 자연 생태계를 안정화시키기에는 충분한 기능을 제공해 주지 못하는 실정이다.Meanwhile, in some cases, in stabilizing slopes using blocks, attempts have been made to construct plants in the soil exposed to the omitted portions by constructing blocks while omitting the middle portions of the slopes. However, this method also has a very limited scope of application due to various problems of slope stability due to the exposed part of the soil, and far from the vegetation of the entire slope. Therefore, these methods do not provide enough functions to stabilize the natural ecosystem.

또 한편으로는, 식생네트를 도입하여 사면의 녹화를 시도하고 있으나, 식생네트를 이용하여 사면을 녹화시키는 경우에도 구조적으로 견고한 안정성을 확보하기에는 무리가 있어 적용범위가 극히 제한적일 뿐만 아니라, 강우량이 집중될 경우 유실될 위험성이 상존하며, 시공후 지속적으로 보수해 주어야 하는 등 유지관리적인 측면에서 여러 문제점이 있었다.On the other hand, the vegetation net is being introduced to try to record the slope. However, even when recording the slope using the vegetation net, it is difficult to secure structurally stable stability, and the range of application is extremely limited, and rainfall is concentrated. If there is a risk of loss, there are several problems in terms of maintenance, such as the need for continuous maintenance after construction.

최근에는 상하로 맞뚫리는 홀이 구비된 블록을 사면에 구축하여, 뚫어진 홀을 통하여 식물이 토양에 정착하도록 하는 시도가 이루어지고 있다. 그러나, 이 방법도 홀 이외의 부분에는 식물이 정착할 수 없으며 홀을 통하여 노출된 토양이 소실됨으로 인해 사면의 안정성은 물론 자연 생태계의 안정화에도 충분한 기능을 제공해 주지 못했다.In recent years, an attempt has been made to build a block having a hole that is drilled up and down on a slope, so that plants can settle in the soil through the drilled hole. However, this method did not provide sufficient functions for stabilization of natural slopes as well as slope stability due to the loss of soil exposed through the holes and the loss of vegetation.

또한 기존의 콘크리트 블록은 내구성이 좋지 않아 잘 깨지는 문제점이 발생하였다. 콘크리트 블록의 내구성을 개선하는 방법으로서 고로 슬래그 등을 혼합하여 콘크리트 블록의 강도를 높일 수 있으나 이런 방법은 고로 슬래그 미분이 물리적으로 콘크리트 블록 내부의 공극을 충진하여 밀실한 조직을 만들기 때문에 콘크리트 블록을 통하여 식물의 뿌리가 땅으로 정착하기 어려운 문제점이 있었다.In addition, the existing concrete blocks have a problem of breaking well due to poor durability. As a method of improving the durability of the concrete block, the strength of the concrete block can be increased by mixing blast furnace slag, but this method uses the concrete block because the blast furnace slag fine powder physically fills the voids in the concrete block to create a tight structure. The roots of the plant were difficult to settle to the ground.

이에, 본 고안은 공원등의 옹벽이나, 제방, 하천의 호안, 도로의 사면 등을 안정시키기 위한 구조물을 구축하는데 있어 상기한 종래 기술들이 가지는 제반 문제점을 해결하고자 안출한 것으로, 식물의 정착 및 생육이 가능하도록 자리가 조성될 뿐 아니라 식물뿌리의 활착이 용이하도록 공극과 홈이 구비되고 블록의 내구성을 증대시켜 잘 깨지지 않는 강도를 가지며 중량이 큰 블록을 제공함으로써, 구조적인 안정성을 더욱 높이는 동시에 환경친화적인 토목구조물을 구현시켜 주기 위한 다공성 콘크리트 블록을 제공하는데 그 목적이 있다.Accordingly, the present invention has been made to solve all the problems of the prior art in constructing a structure for stabilizing a retaining wall, a levee, a river bank, a road slope, etc., such as a park, the settlement and growth of plants Not only are the seats constructed to allow this, but also the voids and grooves are provided to facilitate the rooting of the plant roots, and the durability of the block is increased to provide a block with high strength and heavy weight, thereby improving structural stability and environment. The purpose is to provide a porous concrete block for realizing a friendly civil structure.

도 1은 본 고안에 따른 다공성 콘크리트 블록의 일실시예를 나타내는 사시도,1 is a perspective view showing an embodiment of a porous concrete block according to the present invention,

도 2는 도 1의 A-A선 단면도,2 is a cross-sectional view taken along the line A-A of FIG.

도 3a는 본 고안에 따른 다공성 콘크리트 블록을 설치한 제1시공예의 정면도,3a is a front view of a first construction example in which a porous concrete block is installed according to the present invention;

도 3b는 본 고안에 따른 다공성 콘크리트 블록을 설치한 제2시공예의 정면도,3b is a front view of a second construction example with a porous concrete block according to the present invention,

도 4는 본 고안에 따른 다공성 콘크리트 블록을 이용한 시공예의 단면도,4 is a cross-sectional view of a construction example using a porous concrete block according to the present invention,

도 5는 도 4의 시공된 다공성 콘크리트 블록의 확대단면도.Figure 5 is an enlarged cross-sectional view of the constructed porous concrete block of FIG.

※도면의 주요부분에 대한 부호의 설명※※ Explanation of symbols about main part of drawing ※

10 : 몸통부 11 : 중앙홈10: body portion 11: the center groove

12 : 측면홈 13 : 돌출부12: side groove 13: protrusion

14 : 골재14: aggregate

이와 같은 목적을 달성하기 위해 본 고안의 다공성 콘크리트 블록은 자갈, 모래 등의 골재와, 상기 골재의 13∼18중량%의 고로시멘트와, 상기 고로시멘트의 25∼35중량%의 AE감수제, 접착제 및 물로 이루어진 혼합물을 섞어서 된 모르타르혼합물에 보강제를 추가하여 혼합하고, 다각형의 블록 형틀에 넣어 일정높이의 두께를 가지는 다각형의 평면형상으로 상하좌우면에는 측면홈이 형성되고 모서리에 돌출부가 형성되는 몸통부로 이루어지며 상기 몸통부의 중앙에는 식물이 뿌리를 내려 정착하기 쉽도록 다수개의 중앙홈이 구비되게 성형하고, 미세한 분말상의 숯 또는 황토를 뿌린 후 50∼60℃의 스팀을 30분∼2시간 공급하여 굳히는 스팀양생하여 이루어진다.In order to achieve the above object, the porous concrete block of the present invention includes aggregates such as gravel and sand, 13-18 wt% blast furnace cement of the aggregate, 25-35 wt% AE reducing agent, adhesive and Add the reinforcing agent to the mortar mixture by mixing the mixture made of water, and put it in the polygonal block shape in a polygonal planar shape having a certain height thickness. It is made in the center of the body portion is formed to have a plurality of central grooves so that the plant is easy to settle down roots, sprinkled with fine powder charcoal or ocher, and then supplied with steam of 50-60 ℃ for 30 minutes to 2 hours to harden It is made by steam curing.

본 고안에 따르면 상기 모르타르혼합물에 사용되는 혼합물은 물 84∼88중량%, AE감수제 3∼4중량%, 접착제 9∼12중량%로 이루어지는 것을 특징으로 한다.According to the present invention, the mixture used for the mortar mixture is characterized by consisting of 84 to 88% by weight of water, 3 to 4% by weight of AE reducing agent, and 9 to 12% by weight of adhesive.

또 상기 모르타르혼합물에 추가되는 보강제는 무기계 섬유, 유기계 섬유, 스크랩, 고탄력고무 중 어느 하나 또는 하나 이상 혼합한 혼합물이 될 수 있다.In addition, the reinforcing agent added to the mortar mixture may be a mixture of any one or more of inorganic fibers, organic fibers, scrap, high elastic rubber.

이하, 본 고안의 다공성 콘크리트 블록 및 그의 제조방법에 대한 기술구성을 첨부도면을 참조하여 상세히 설명한다.Hereinafter, the technical configuration of the porous concrete block and the manufacturing method of the present invention will be described in detail with reference to the accompanying drawings.

도 1은 본 고안에 따른 다공성 콘크리트 블록의 일실시예를 나타내는 사시도이고, 도 2는 본 고안에 따른 다공성 콘크리트 블록의 일측단면도로서 도 1의 A-A선 단면도이고, 도 3a는 본 고안에 따른 다공성 콘크리트 블록을 설치한 제1시공예의 정면도이고, 도 3b는 본 고안에 따른 다공성 콘크리트 블록을 설치한 제2시공예의 정면도이고, 도 4는 본 고안에 따른 다공성 콘크리트 블록을 이용한 시공예의 단면도이며, 도 5는 도 4의 시공된 다공성 콘크리트 블록의 확대단면도이다.1 is a perspective view showing an embodiment of a porous concrete block according to the present invention, Figure 2 is a cross-sectional view taken along line AA of Figure 1 as one side cross-sectional view of the porous concrete block according to the present invention, Figure 3a is a porous concrete according to the present invention 3B is a front view of a second construction example in which a porous concrete block is installed according to the present invention, and FIG. 4 is a sectional view of a construction example using a porous concrete block according to the present invention, and FIG. 5. Is an enlarged cross-sectional view of the constructed porous concrete block of FIG.

본 고안에 따른 다공성 콘크리트 블록을 제조하기 위하여 먼저 고강도제로 사용될 혼화제로서 물, AE감수제, 접착제를 혼합하는데, 시멘트와의 접착력을 강화시켜 압축강도를 증대시키도록 물 84∼88중량%, AE감수제 3∼4중량%, 접착제 9∼12중량%를 혼합한 혼합물을 준비한다.In order to prepare a porous concrete block according to the present invention, first, the admixture to be used as a high strength agent is mixed with water, an AE reducing agent, and an adhesive, and 84 to 88% by weight of water and an AE reducing agent to increase the compressive strength by enhancing adhesion with cement. The mixture which mixed -4 weight% and 9-12 weight% of adhesive agents is prepared.

자갈, 모래 등의 골재와 고로시멘트, 그리고 미리 준비된 AE감수제, 접착제 및 물로 된 혼합물을 섞어서 모르타르혼합물을 만든다. 이때 혼합량은 우선 골재 사용량을 설정한 다음, 고로시멘트는 상기 골재의 중량을 기준으로 13∼18중량%, AE감수제, 접착제와 물로 된 혼합물은 상기 고로시멘트의 중량을 기준으로 25∼35중량%를 혼합한다.The mortar mixture is made by mixing aggregates such as gravel, sand, blast furnace cement, and a mixture of pre-prepared AE reducing agent, adhesive and water. At this time, the mixing amount is first set the aggregate usage, then the blast furnace cement is 13-18% by weight based on the weight of the aggregate, the mixture of AE water reducing agent, adhesive and water is 25-35% by weight based on the weight of the blast furnace cement Mix.

본 고안의 다공성 콘크리트 블록 제조에 사용되는 골재는 13∼25㎜ 정도의크기를 사용하는 것이 가장 바람직하다. 골재의 크기를 이와 같이 한정하는 이유는 식물의 뿌리가 완성된 다공성 콘크리트 블록의 공극 사이를 통과하여 블록 하부의 토양속으로 용이하게 활착될 수 있도록 공극률을 유지할 수 있을 뿐만 아니라, 상기 다공성 콘크리트 블록이 하천의 호안 등 물가에 시공될 경우 폭우나 급류로 인하여 떠내려 가지 않게 일정한 중량을 유지할 수 있도록, 콘크리트 블록의 공극률, 중량, 압축감 등을 고려한 것이다.Aggregate used in the manufacture of the porous concrete block of the present invention is most preferably using a size of about 13-25mm. The reason for limiting the size of the aggregate in this way is not only to maintain the porosity so that the roots of the plant can easily pass through the pores of the finished porous concrete block into the soil beneath the block, the porous concrete block is When it is installed on the shore of a river, such as a lake shore, the porosity, weight, and feeling of compression of concrete blocks are considered to maintain a constant weight so that it does not float due to heavy rain or rapids.

본 고안의 다공성 콘크리트 블록 제조에 사용되는 고로시멘트(portland blast furnace cement)는 용광로에서 선철을 제조할 때 생기는 부산물인 슬래그(광재)에 포틀랜드 시멘트와 석고(石膏)를 혼합하여 만든 혼합 시멘트로, 보통의 포틀랜드 시멘트에 비하여 시멘트의 경화과정에서 발생되는 열인 수화열(水和熱)이 낮고, 내구성이 높으며, 화학저항성이 큰 한편, 투수(透水)가 적은 특징이 있다. 또 중량이 크고 강도가 세며 알칼리성이 낮아 중성에 가깝고 특히 양생 후 강도가 좋아진다.The blast furnace cement used in the manufacture of porous concrete blocks of the present invention is a mixed cement made by mixing portland cement and gypsum in slag (slag), a by-product of the production of pig iron in a blast furnace. Compared with Portland cement, the heat of hydration, which is the heat generated during the hardening of cement, is low, durable, has high chemical resistance, and has low water permeability. In addition, the weight is high, the strength is strong, the alkalinity is close to the neutral, especially after curing, the strength is good.

고로시멘트를 골재 중량을 기준으로 13중량%이하 혼합할 경우, 다공성 콘크리트 블록의 강도가 저하되며 18중량%이상 혼합할 경우, 강도는 높아지나 원가가 상승하는 문제점이 발생하므로 고로시멘트의 양은 13∼18중량%로 혼합하는 것이 바람직하다.When the blast furnace cement is mixed in an amount of 13% by weight or less based on the aggregate weight, the strength of the porous concrete block is lowered. When the blast furnace cement is mixed in an amount of 18% by weight or more, the strength increases but the cost increases. It is preferable to mix at 18 weight%.

상기 AE감수제, 접착제 및 물로 이루어지는 혼합물은 고강도제로 사용되는 혼화제이다. 특히 AE감수제는 발포성(發泡性)이 현저한 계면활성제로서 콘크리트 중에 미소한 독립된 기포(氣泡)를 고르게 발생시켜 콘크리트의 내동결융해성(耐凍結融解性), 내식성(耐蝕性) 등 내구성을 개선시키며 시멘트와 화학반응하여 공간을 최소화 시키는 특성이 있고, 접착제는 시멘트의 접착력에 의해 압축강도를 증대시켜 접착력을 강하게 하는 특성이 있다.The mixture consisting of the AE reducing agent, the adhesive and the water is a admixture used as a high strength agent. In particular, the AE reducing agent is a surfactant with remarkable foaming properties, which evenly generates minute independent bubbles in concrete to improve durability such as freeze-melting resistance and corrosion resistance. And it has the characteristics of minimizing space by chemical reaction with cement, and adhesive has the property of increasing the adhesive strength by the adhesive strength of cement to strengthen the adhesive strength.

그러나, 상기 AE감수제 및 접착제를 너무 많이 사용하면 비경제적일 뿐 아니라 압축강도의 감소 등 여러 가지 장애가 발생하므로 적정 사용량을 엄수하는 것이 중요하다. 따라서, 본 고안의 다공성 콘크리트 블록의 제조에서는 물, AE감수제 및 접착제의 혼합량을 100을 기준으로 하여 물 84∼88중량%, AE감수제 3∼4중량%, 접착제 9∼12중량%으로 한정하는 것이 가장 바람직하다.However, too much use of the AE reducing agent and adhesive is not only economical, but also causes various obstacles such as a decrease in compressive strength. Therefore, in the preparation of the porous concrete block according to the present invention, the mixing amount of water, the AE reducing agent and the adhesive is limited to 84 to 88% by weight of water, 3 to 4% by weight of the AE reducing agent, and 9 to 12% by weight of the adhesive based on 100. Most preferred.

상술한 바와 같이 모르타르혼합물을 준비한 후, 콘크리트블록의 압축강도, 휨강도, 수명의 단점을 보강하기 위하여 보강제를 넣어 혼합한다. 이때 혼합되는 보강제로는 무기계 섬유, 유기계 섬유, 스크랩, 고탄력고무 등 다양한 결합재가 사용될 수 있으며 그 혼합량은 모르타르혼합물의 부피를 기준으로 2∼3%가 적합하다.After preparing the mortar mixture as described above, to reinforce the disadvantages of the compressive strength, flexural strength, and service life of the concrete block is mixed by mixing. In this case, as the reinforcing agent to be mixed, various binders such as inorganic fibers, organic fibers, scraps, and high elastic rubber may be used, and the mixing amount thereof is preferably 2 to 3% based on the volume of the mortar mixture.

본 고안에 사용되는 상기 강도보강용 섬유로서 무기계 섬유의 종류로는 강섬유, 유리섬유, 탄소섬유 등이 있고 유기계 섬유의 종류로는 아라미드섬유, 폴리프로필렌섬유, 비닐론섬유, 나일론 등이 있다. 본 고안에 따른 콘크리트블록은 각종 보강용섬유를 임의 크기로 절단하거나 실 또는 망사형상으로 만든 섬유사를 사용하는 것이 바람직하다.The strength reinforcing fibers used in the present invention include inorganic fibers as steel fibers, glass fibers, carbon fibers, and the like, and organic fibers include aramid fibers, polypropylene fibers, vinylon fibers, nylon, and the like. Concrete block according to the present invention is preferably used to cut a variety of reinforcing fibers to any size or use a fiber yarn made of thread or mesh shape.

스크랩(scrap)은 철강 및 금속공업에서 중요한 원료로 쓰이는 쇠부스러기, 파쇠, 고철 등을 나타내는 것으로, 모르타르혼합물에 넣어 콘크리트블록의 강도를높일 수 있다. 특히 폐스크랩을 사용함으로써 폐물을 재활용할 수 있고 우수한 강도를 갖는 콘크리트블록을 생산할 수 있으며 생산비용이 절약되는 효과를 얻을 수 있다.Scrap refers to scrap, scrap, scrap, etc., which are used as important raw materials in the steel and metal industry, and can be added to mortar mixtures to increase the strength of concrete blocks. In particular, by using the waste scrap can be recycled waste, can produce a concrete block with excellent strength, and the production cost can be saved.

또 상기 모르타르혼합물에 탄성이 강한 고탄력고무를 넣어 제조되는 콘크리트블록은 외력이 작용했을 때 전단응력과 인장강도가 더욱 높아지는 효과를 나타낸다.In addition, the concrete block manufactured by putting high elastic rubber having high elasticity in the mortar mixture exhibits an effect of increasing shear stress and tensile strength when an external force is applied.

모르타르혼합물에 상기된 바와 같은 다양한 보강재를 추가혼합시킴으로써 모르타르혼합물 자체의 결합을 좋게 하며, 완성된 콘크리트블록의 외력에 의한 균열 발생시 결합재 자체의 강도에 의해 균열의 진행을 억제한다.By further mixing the various reinforcement materials as described above in the mortar mixture to improve the bonding of the mortar mixture itself, and inhibits the progress of the crack by the strength of the binder itself when the crack generated by the external force of the finished concrete block.

이상과 같이 상술된 비율로 혼합하여 만들어진 모르타르혼합물을 다각형의 블록 형틀에 넣어 성형한다. 이때 사용되는 상기 블록 형틀은 그 내에서 성형된 다공성 콘크리트 블록이, 도 1에 나타낸 바와 같이, 일정높이의 두께를 가지는 다각형의 평면형상으로 상하좌우면에 측면홈(12)이 형성되고 모서리에 돌출부(13)가 형성되는 몸통부(10)를 구성하도록 이루어진다. 특히, 몸통의 중앙에 다수개의 볼록부가 형성된 다각형의 블록 형틀을 사용하여 상기 몸통부(10)의 중앙에 다수개의 중앙홈(11)이 구비되는 형상으로 완성함으로써, 상기 중앙홈(11)의 저부로부터 토양까지의 거리를 좁혀서 중앙홈(11)에 식재되는 식물이 블록을 관통하여 그 하부의 토양으로 뿌리를 내려 정착하기 쉽도록 하는 것이 바람직하다.The mortar mixture made by mixing at the above-mentioned ratio is put into a polygonal block mold and molded. At this time, the block mold used is a porous concrete block formed therein, as shown in Figure 1, in the planar shape of a polygon having a thickness of a certain height side grooves 12 are formed on the top, bottom, left and right surfaces and protrusions at the corners. It is made to constitute the body portion 10 is formed (13). In particular, the bottom of the central groove 11 by completing a shape in which a plurality of central grooves 11 are provided in the center of the body portion 10 using a polygonal block form having a plurality of convex portions formed at the center of the body. It is preferable to narrow the distance from the soil to the soil so that the plant planted in the central groove 11 penetrates the block and is easy to settle down to the soil beneath it.

상기 모르타르혼합물의 성형단계 후, 그 위로 미세한 분말상의 숯 또는 황토를 뿌려 성형된 콘크리트 블록의 상부에 숯 또는 황토 분말을 위치시킨다. 이것은본 고안의 콘크리트 블록을 환경친화적인 제품으로 만들기 위한 것으로, 상부에 숯 또는 황토가 위치됨으로써 오염된 토양 또는 빗물 속에 함유된 중금속 등이 흡수되게 한다.After the molding step of the mortar mixture, the char or ocher powder is placed on top of the molded concrete block by sprinkling fine powdery char or ocher thereon. This is to make the concrete block of the present invention into an environmentally friendly product. The charcoal or loess is placed at the top to absorb heavy metals contained in contaminated soil or rainwater.

상기 형상으로 성형된 콘크리트 블록은 50∼60℃의 스팀을 30분∼2시간 동안 공급하여 양생시킨다. 일반적으로 시멘트는 방치시키면 발열되면서 굳어지는데, 완전히 양생되는 데 2∼3일 정도로 오랜 시간이 걸린다. 이와 같은 단점을 해결하기 위해, 본 고안의 다공성 콘크리트 블록은 양생 단계에서 증기를 공급하여 스팀 양생시킨다. 스팀 양생을 함으로써 발열과정에서 시멘트가 물을 흡수하면서 경화되어 콘크리트 블록의 강도가 좋아질 뿐 아니라 경화되는 시간도 하절기에는 30분, 동절기에는 2시간 정도로 매우 짧아져 생산성을 향상시킬 수 있다.The concrete block molded in the shape is cured by supplying steam at 50 to 60 ℃ for 30 minutes to 2 hours. In general, when cement is left unheated, it hardens as it heats up. It takes a long time to completely cure 2 to 3 days. In order to solve this disadvantage, the porous concrete block of the present invention is steam curing by supplying steam in the curing step. By curing the steam, the cement hardens as it absorbs water during the heating process, which improves the strength of the concrete block. The curing time is also shortened to about 30 minutes in the summer and 2 hours in the winter, thereby improving productivity.

이때, 상기 공급되는 스팀의 온도가 50℃이하이면 콘크리트 블록의 경화 속도가 빠르지 않으며 65℃이상이면 시멘트의 강도가 약해지므로 50∼60℃의 온도를 유지시키는 것이 중요하다.At this time, if the temperature of the supplied steam is less than 50 ℃ hardening speed of the concrete block is not fast, if the strength of the cement is more than 65 ℃ it is important to maintain a temperature of 50 ~ 60 ℃.

이와 같이 하여 완성되는 본 고안의 다공성 콘크리트 블록은 공극률이 25%이상 유지되고 사면안정에 필요한 구조적 강도를 충분히 가진다.The porous concrete block of the present invention, which is completed in this way, maintains porosity of 25% or more and has sufficient structural strength for slope stability.

상술된 방법으로 완성된 본 고안의 다공성 콘크리트 블록을 사면 등을 안정시키기 위하여 시공할 때에는, 도 3a와 도 3b에 도시된 바와 같이, 가로·세로방향으로 연속적으로 맞대어 설치한다.When constructing the porous concrete block of the present invention completed by the above-described method to stabilize the slope, etc., as shown in Figures 3a and 3b, it is installed in a continuous horizontal and vertical direction.

도 3a와 같이 설치할 경우, 상호 맞닿는 두 개의 몸통부(10) 사이에는 두 개의 측면홈(12)으로 인한 토양 노출부(E)가 생기는데 이를 최소화시키기 위하여, 도3b에 나타낸 바와 같이, 본 고안의 다공성 콘크리트 블록 시공시 상하 또는 좌우 중 어느 한 방향으로 하나의 다공성 콘크리트 블록 측면홈(12)에 다른 2개의 다공성 콘크리트 블록의 돌출부(13)들이 마주닿게 위치시켜 3개의 다공성 콘크리트 블록이 상호 정합되게 할 수 있다.When installed as shown in Figure 3a, between the two body parts 10 which are in contact with each other, the soil exposed portion (E) due to the two side grooves 12 occurs to minimize this, as shown in Figure 3b, of the present invention When the porous concrete block is constructed, the projections 13 of the two other porous concrete blocks face each other in one porous concrete block side groove 12 in either up, down, left, or right directions so that the three porous concrete blocks are aligned with each other. Can be.

〈실시예〉<Example>

물 86중량%, AE감수제 4중량%, 접착제 10중량%를 혼합하여 모르타르혼합물에 사용될 혼합물을 준비하였다.86 wt% of water, 4 wt% of the AE reducing agent, and 10 wt% of the adhesive were mixed to prepare a mixture to be used in the mortar mixture.

자갈로 된 골재 1000g과 고로시멘트 180g과 미리 준비된 상기 AE감수제, 접착제 및 물로 된 혼합물 63g을 혼합하여 모르타르혼합물을 준비하였다.A mortar mixture was prepared by mixing 1000 g of gravel aggregate, 180 g of blast furnace cement, and 63 g of the above-prepared mixture of AE reducing agent, adhesive, and water.

상기 모르타르혼합물에 보강제로서 유기계 섬유인 폴리프로필렌섬유를 넣어 균일하게 혼합하였다. 이때 혼합된 폴리프로필렌섬유의 양은 모르타르혼합물의 부피를 기준으로 3% 첨가하였다.Polypropylene fiber, which is an organic fiber, was added to the mortar mixture as a reinforcing agent and mixed uniformly. At this time, the amount of the mixed polypropylene fiber was added 3% based on the volume of the mortar mixture.

상기 혼합된 모르타르혼합물을 블록 형틀에 넣어 성형하였다. 이때 사용된 블록 형틀은 몸통부(10)의 중앙에 홈을 형성할 수 있는 볼록부를 구비한 다각형상으로, 그 내에서 성형된 콘크리트 블록은 몸통부(10)의 중앙에 다수개의 중앙홈(11)이 구비되며 일정한 두께를 가지는 다각형의 평면형상으로 상하좌우면에는 측면홈(12)이 형성되고 모서리에 돌출부(13)가 형성되는 몸통부(10)로 이루어졌다.The mixed mortar mixture was molded into a block mold. At this time, the block mold used is a polygonal shape having a convex portion capable of forming a groove in the center of the body portion 10, the concrete block formed therein a plurality of central grooves 11 in the center of the body portion (10) ) Is provided in a planar shape of a polygon having a predetermined thickness, the upper and lower left and right surfaces are formed with a body portion 10 is formed with a side groove 12 and a protrusion 13 is formed in the corner.

상기 형상으로 성형된 콘크리트 블록의 상부로 숯 분말을 뿌린 다음, 60℃의 스팀을 80분 동안 공급하여 양생시켰다.After spraying the charcoal powder to the upper portion of the concrete block molded in the shape, it was cured by supplying steam at 60 ℃ for 80 minutes.

이상과 같은 방법으로 완성된 본 고안의 다공성 콘크리트 블록을 하천의 호안에 설치하고 흙으로 블록의 홈 등을 충진한 다음 복토하였다.The porous concrete block of the present invention completed as described above was installed in the lake's lake and filled with the groove of the block with soil, and then covered.

2개월 후 하천의 호안에 설치된 본원의 다공성 콘크리트 블록 위로 식물들이 초기발아하기 시작하였으며 6개월 후 블록 전면에 걸쳐 식생 군락이 형성되어 하천생태계와 육상생태계가 자연스럽게 연결된 자연형 하천으로 변하였다.Two months later, plants began to germinate on the porous concrete block of the main building installed on the lake's shore, and after six months, vegetation colonies were formed over the entire surface of the block, transforming it into a natural stream naturally connected to the river ecosystem and terrestrial ecosystem.

상기 자연형 하천으로 변한 일부분에서 본 고안의 다공성 콘크리트 블록을 들어올려 보았더니, 식물의 뿌리가 콘크리트 블록을 통과하여 토양에 활착된 것을 확인할 수 있었다.When lifting up the porous concrete block of the present invention in a portion changed to the natural stream, it was confirmed that the roots of the plant is attached to the soil through the concrete block.

이상에서 살펴본 바와 같이, 본 고안에 따른 다공성 콘크리트 블록은 식물의 정착 및 생육이 가능하도록 자리가 조성될 뿐 아니라 식물뿌리가 토양에 용이하게 활착하도록 공극과 홈이 구비되고, 보강제를 사용하여 다공성블록의 압축강도, 휨강도 및 수명을 연장할 수 있으며, 큰 중량을 가지기 때문에 옹벽이나, 제방, 하천의 호안, 도로의 사면 등을 안정시키기 위한 구조적인 안정성을 더욱 높일 수 있을 뿐 아니라 블록 전면에 걸쳐 식생 군락이 형성되는 환경친화적인 다공성 콘크리트 블록을 제공할 수 있다.As described above, the porous concrete block according to the present invention is not only a seat is formed to allow the settlement and growth of the plant, but also provided with pores and grooves so that the plant roots easily adhere to the soil, and the porous block using a reinforcing agent Compressive strength, flexural strength and service life can be extended, and because of its large weight, it can increase the structural stability for stabilizing retaining walls, banks, river banks, road slopes, etc. It is possible to provide an environmentally friendly porous concrete block in which a colony is formed.

Claims (4)

자갈, 모래 등의 골재와, 상기 골재의 13∼18중량%의 고로시멘트와, 상기 고로시멘트의 25∼35중량%의 AE감수제, 접착제 및 물로 이루어진 혼합물을 섞어서 된 모르타르혼합물에 보강제를 추가하여 혼합하고, 다각형의 블록 형틀에 넣어 일정높이의 두께를 가지는 다각형의 평면형상으로 상하좌우면에는 측면홈(12)이 형성되고 모서리에 돌출부(13)가 형성되는 몸통부(10)로 이루어지며 상기 몸통부(10)의 중앙에는 식물이 뿌리를 내려 정착하기 쉽도록 다수개의 중앙홈(11)이 구비되게 성형하고, 미세한 분말상의 숯 또는 황토를 뿌린 후 50∼60℃의 스팀을 30분∼2시간 공급하여 굳히는 스팀양생하여 이루어지는 것을 특징으로 하는 다공성 콘크리트 블록.Add a reinforcing agent to the mortar mixture by mixing a mixture of aggregates such as gravel and sand, 13 to 18% by weight blast furnace cement of the aggregate, and 25 to 35% by weight AE water reducing agent, adhesive and water of the blast furnace cement. And, in the polygonal planar shape of a polygon having a predetermined height in the block shape of the upper and lower left and right surfaces are formed with a body portion 10 is formed with a side groove 12 and a protrusion 13 is formed in the corner and the body In the center of the part 10 is formed to have a plurality of central grooves 11 so that the plant is easy to settle down roots, sprinkled fine powder of charcoal or ocher, and then steamed at 50 to 60 ° C. for 30 minutes to 2 hours. Porous concrete block, characterized in that made by steam curing to harden by supply. 제 1항에 있어서, 상기 모르타르혼합물에 사용되는 혼합물이 물 84∼88중량%, AE감수제 3∼4중량%, 접착제 9∼12중량%로 이루어지는 것을 특징으로 하는 다공성 콘크리트 블록.The porous concrete block according to claim 1, wherein the mixture used in the mortar mixture is composed of 84 to 88% by weight of water, 3 to 4% by weight of AE reducing agent, and 9 to 12% by weight of adhesive. 제 1항에 있어서, 상기 모르타르혼합물에 추가되는 보강제가 무기계 섬유, 유기계 섬유, 스크랩, 고탄력고무 중 어느 하나인 것을 특징으로 하는 다공성 콘크리트 블록.The porous concrete block according to claim 1, wherein the reinforcing agent added to the mortar mixture is any one of an inorganic fiber, an organic fiber, a scrap, and a high elastic rubber. 제 1항에 있어서, 상기 모르타르혼합물에 추가되는 보강제가 무기계 섬유, 유기계 섬유, 스크랩, 고탄력고무를 하나 이상 혼합하여 된 것을 특징으로 하는 다공성 콘크리트 블록.The porous concrete block according to claim 1, wherein the reinforcing agent added to the mortar mixture is at least one of inorganic fibers, organic fibers, scraps, and high elastic rubber.
KR20-2003-0009995U 2003-02-19 2003-04-02 porous concrete block KR200324510Y1 (en)