CN106978080A - The floor paint and preparation method of a kind of novel environment friendly dry powder shape - Google Patents
The floor paint and preparation method of a kind of novel environment friendly dry powder shape Download PDFInfo
- Publication number
- CN106978080A CN106978080A CN201710135021.8A CN201710135021A CN106978080A CN 106978080 A CN106978080 A CN 106978080A CN 201710135021 A CN201710135021 A CN 201710135021A CN 106978080 A CN106978080 A CN 106978080A
- Authority
- CN
- China
- Prior art keywords
- floor paint
- groups
- preparation
- film
- environment friendly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to floor paint technical field, it is proposed that a kind of floor paint of novel environment friendly dry powder shape, by the material composition of following weight proportion：Latex powder 10 35, silica gel salt 8 12；Calcium carbonate 10 18；Titanium dioxide 8 25；Coarse whiting 5 10；Talcum powder 58；Wollastonite 12 30；Cellulose 18；Defoamer 0.2 0.8；Coloring pigment 0 25, film-forming agents 0 12；Forming agent 2 20.The invention also provides a kind of preparation method of floor paint.By above-mentioned technical proposal, the problem of solving the volatile noxious material of floor paint in the prior art and poor performance.
Description
Technical field
The invention belongs to floor paint technical field, it is related to the floor paint and preparation method of a kind of novel environment friendly dry powder shape.
Background technology
Floor paint is by a variety of different materials are blended, dissolving, many end production process such as scattered are manufactured and constituted.Floor paint
The features such as with beautiful, true, attractive in appearance, wear-resisting, waterproof, anti-corrosion.But use epoxy resin floor paint of the prior art more
, there is volatile noxious material, the problem of not possessing the feature of environmental protection in solvent floor paint, and hardness of paint film is low in use, resistance to
Ageing time is short, the problem of resistance to acids and bases is poor.
The content of the invention
The present invention proposes the floor paint and preparation method of a kind of novel environment friendly dry powder shape, solves terrace in the prior art
The problem of painting volatile noxious material and poor performance.
The technical proposal of the invention is realized in this way：
A kind of floor paint of novel environment friendly dry powder shape：
By the material composition of following weight proportion：Latex powder 10-35, silica gel salt 8-12；Calcium carbonate 10-18；Titanium dioxide 8-
25；Coarse whiting 5-10；Talcum powder 5-8；Wollastonite 12-30；Cellulose 1-8；Defoamer 0.2-0.8；Coloring pigment 0-25, film forming system
Agent 0-12；Forming agent 2-20.
Further, the film-forming agents are alcohol ester 12.
Further, the forming agent by following weight proportion material composition：Modified rosin resin 20-25；Paraffin oil 17-
20；Dibutyl phthalate 10-13；Lauric acid/dodecanoic acid acid amides 9-14.
A kind of preparation method of floor paint, comprises the following steps：
Step one, above-mentioned component is divided into A groups：Latex powder, silica gel salt, titanium dioxide, coarse whiting, talcum powder and silicon ash
Stone；
B groups：Cellulose, defoamer, coloring pigment, film-forming agents and forming agent；
Step 2：A groups material is weighed respectively according to above-mentioned quality proportioning and a is denoted as,
Step 2, B group materials are weighed be denoted as b according to above-mentioned quality proportioning, are (a+b) * 50% by B groups material and quality
Diluent it is well mixed after, stand 30min, then the A group materials mixed are gradually added into and stirred, finally by quality
Diluent for (a+b) * 30% is added and stirred.
Further, in step 2, after B groups material and diluent are well mixed, it is warming up to 35-40 DEG C of standing 30min.
Further, in step 2, A groups material is according to titanium dioxide, coarse whiting, talcum powder, wollastonite, silica gel salt and latex powder
Order is sequentially added into B groups material and the solution of diluent mixing.
Beneficial effects of the present invention are：
1st, the floor paint in the present invention is without poisonous, destructive stimulus the material of any volatilization, is real Diamond Search, zero formaldehyde,
The floor paint of zero lead mercury, and hardness of paint film is high, and the ageing-resistant time is long, and cracking resistance is good, and water resistance is strong, is that can replace biography
System epoxy resin solvent floor paint.A kind of new product of novel environment friendly dry powder floor paint, be widely used in factory, cell, school,
The places such as hospital.
A kind of environmental protection floor paint of floor paint in the present invention, meets environmentally friendly, free of contamination growth requirement, is to replace traditionally
The Novel terrace paint of level ground paint.
2nd, the floor paint made of floor paint preparation method in the present invention, can significantly improve the tensile strength, curved of floor paint
Qu Qiangdu and compression strength, and can have good wearability.
Embodiment
Below in conjunction with embodiments of the invention, the technical scheme in the embodiment of the present invention is clearly and completely retouched
State, it is clear that described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based on the present invention
In embodiment, the every other implementation that those of ordinary skill in the art are obtained under the premise of creative work is not made
Example, belongs to the scope of protection of the invention.
Embodiment 1
A kind of floor paint of novel environment friendly dry powder shape：
By the material composition of following weight proportion：Latex powder 10, silica gel salt 8；Calcium carbonate 10；Titanium dioxide 8；Coarse whiting 5；Talcum
Powder 5；Wollastonite 12；Cellulose 1；Defoamer 0.2；Film-forming agents 1；Forming agent 2.
Further, film-forming agents are alcohol ester 12.
Further, forming agent by following weight proportion material composition：Modified rosin resin 20-25；Paraffin oil 17-20；
Dibutyl phthalate 10-13；Lauric acid/dodecanoic acid acid amides 9-14.
The preparation method that floor paint is used in the present embodiment, comprises the following steps：
Step one, above-mentioned component is divided into A groups：Latex powder, silica gel salt, titanium dioxide, coarse whiting, talcum powder and silicon ash
Stone；
B groups：Cellulose, defoamer, coloring pigment, film-forming agents and forming agent；
Step 2：A groups material is weighed respectively according to above-mentioned quality proportioning and a is denoted as,
Step 2, B group materials are weighed be denoted as b according to above-mentioned quality proportioning, are (a+b) * 50% by B groups material and quality
Diluent it is well mixed after, stand 30min, then the A group materials mixed are gradually added into and stirred, finally by quality
Diluent for (a+b) * 30% is added and stirred.
Further, in step 2, after B groups material and diluent are well mixed, it is warming up to 35-40 DEG C of standing 30min.
Further, in step 2, A groups material is according to titanium dioxide, coarse whiting, talcum powder, wollastonite, silica gel salt and latex powder
Order is sequentially added into B groups material and the solution of diluent mixing.
Embodiment 2
A kind of floor paint of novel environment friendly dry powder shape：
By the material composition of following weight proportion：Latex powder 22.5, silica gel salt 10；Calcium carbonate 14；Titanium dioxide 16.5；Coarse whiting
7.5；Talcum powder 6.5；Wollastonite 21；Cellulose 4.5；Defoamer 0.5；Coloring pigment 12.5, film-forming agents 6；Forming agent 11.
Further, film-forming agents are alcohol ester 12.
Wherein, forming agent by following weight proportion material composition：Modified rosin resin 22.5；Paraffin oil 18.8；Adjacent benzene
Dibutyl carboxylic acid 11.7；Lauric acid/dodecanoic acid acid amides 11.6.
The preparation method that floor paint is used in the present embodiment, comprises the following steps：
Step one, above-mentioned component is divided into A groups：Latex powder, silica gel salt, titanium dioxide, coarse whiting, talcum powder and silicon ash
Stone；
B groups：Cellulose, defoamer, coloring pigment, film-forming agents and forming agent；
Step 2：A groups material is weighed respectively according to above-mentioned quality proportioning and a is denoted as,
Step 2, B group materials are weighed be denoted as b according to above-mentioned quality proportioning, are (a+b) * 50% by B groups material and quality
Diluent it is well mixed after, stand 30min, then the A group materials mixed are gradually added into and stirred, finally by quality
Diluent for (a+b) * 30% is added and stirred.
Further, in step 2, after B groups material and diluent are well mixed, it is warming up to 35-40 DEG C of standing 30min.
Further, in step 2, A groups material is according to titanium dioxide, coarse whiting, talcum powder, wollastonite, silica gel salt and latex powder
Order is sequentially added into B groups material and the solution of diluent mixing.
Embodiment 3
A kind of floor paint of novel environment friendly dry powder shape：
By the material composition of following weight proportion：Latex powder 35, silica gel salt 12；Calcium carbonate 18；Titanium dioxide 25；Coarse whiting 10；
Talcum powder 8；Wollastonite 30；Cellulose 8；Defoamer 0.8；Coloring pigment 25, film-forming agents 12；Forming agent 20.
Further, film-forming agents are alcohol ester 12.
Further, forming agent by following weight proportion material composition：Modified rosin resin 25；Paraffin oil 20；Adjacent benzene two
Formic acid dibutyl ester 13；Lauric acid/dodecanoic acid acid amides 14.
The preparation method that floor paint is used in the present embodiment, comprises the following steps：
Step one, above-mentioned component is divided into A groups：Latex powder, silica gel salt, titanium dioxide, coarse whiting, talcum powder and silicon ash
Stone；
B groups：Cellulose, defoamer, coloring pigment, film-forming agents and forming agent；
Step 2：A groups material is weighed respectively according to above-mentioned quality proportioning and a is denoted as,
Step 2, B group materials are weighed be denoted as b according to above-mentioned quality proportioning, are (a+b) * 50% by B groups material and quality
Diluent it is well mixed after, stand 30min, then the A group materials mixed are gradually added into and stirred, finally by quality
Diluent for (a+b) * 30% is added and stirred.
Further, in step 2, after B groups material and diluent are well mixed, it is warming up to 35-40 DEG C of standing 30min.
Further, in step 2, A groups material is according to titanium dioxide, coarse whiting, talcum powder, wollastonite, silica gel salt and latex powder
Order is sequentially added into B groups material and the solution of diluent mixing.
Embodiment 4
A kind of floor paint of novel environment friendly dry powder shape：
By the material composition of following weight proportion：Latex powder 22.5, silica gel salt 10；Calcium carbonate 14；Titanium dioxide 16.5；Coarse whiting
7.5；Talcum powder 6.5；Wollastonite 21；Cellulose 4.5；Defoamer 0.5；Coloring pigment 12.5, film-forming agents 6；Forming agent 11.
Further, film-forming agents are alcohol ester 12.
Wherein, forming agent by following weight proportion material composition：Modified rosin resin 22.5；Paraffin oil 18.8；Adjacent benzene
Dibutyl carboxylic acid 11.7；Lauric acid/dodecanoic acid acid amides 11.6.
The preparation method that floor paint is used in the present embodiment, comprises the following steps：
Step one, above-mentioned component is divided into A groups：Latex powder, silica gel salt, titanium dioxide, coarse whiting, talcum powder and silicon ash
Stone；
B groups：Cellulose, defoamer, coloring pigment, film-forming agents and forming agent；
Step 2：A groups material is weighed respectively according to above-mentioned quality proportioning and a is denoted as,
Step 2, B group materials are weighed be denoted as b according to above-mentioned quality proportioning, are (a+b) * 50% by B groups material and quality
Diluent it is well mixed after, stand 30min, then the A group materials mixed are gradually added into and stirred, finally by quality
Diluent for (a+b) * 30% is added and stirred.
Further, in step 2, after B groups material and diluent are well mixed, it is warming up to 35-40 DEG C of standing 30min.
Embodiment 5
A kind of floor paint of novel environment friendly dry powder shape：
By the material composition of following weight proportion：Latex powder 22.5, silica gel salt 10；Calcium carbonate 14；Titanium dioxide 16.5；Coarse whiting
7.5；Talcum powder 6.5；Wollastonite 21；Cellulose 4.5；Defoamer 0.5；Coloring pigment 12.5, film-forming agents 6；Forming agent 11.
Further, film-forming agents are alcohol ester 12.
Wherein, forming agent by following weight proportion material composition：Modified rosin resin 22.5；Paraffin oil 18.8；Adjacent benzene
Dibutyl carboxylic acid 11.7；Lauric acid/dodecanoic acid acid amides 11.6.
The preparation method that floor paint is used in the present embodiment, comprises the following steps：
Step one, above-mentioned component is divided into A groups：Latex powder, silica gel salt, titanium dioxide, coarse whiting, talcum powder and silicon ash
Stone；
B groups：Cellulose, defoamer, coloring pigment, film-forming agents and forming agent；
Step 2：A groups material is weighed respectively according to above-mentioned quality proportioning and a is denoted as,
Step 2, B group materials are weighed be denoted as b according to above-mentioned quality proportioning, are (a+b) * 50% by B groups material and quality
Diluent it is well mixed after, stand 30min, then the A group materials mixed are gradually added into and stirred, finally by quality
Diluent for (a+b) * 30% is added and stirred.
Further, in step 2, A groups material is according to titanium dioxide, coarse whiting, talcum powder, wollastonite, silica gel salt and latex powder
Order is sequentially added into B groups material and the solution of diluent mixing.
Embodiment 6
A kind of floor paint of novel environment friendly dry powder shape：
By the material composition of following weight proportion：Latex powder 22.5, silica gel salt 10；Calcium carbonate 14；Titanium dioxide 16.5；Coarse whiting
7.5；Talcum powder 6.5；Wollastonite 21；Cellulose 4.5；Defoamer 0.5；Coloring pigment 12.5, film-forming agents 6；Forming agent 11.
Further, film-forming agents are alcohol ester 12.
Wherein, forming agent by following weight proportion material composition：Modified rosin resin 22.5；Paraffin oil 18.8；Adjacent benzene
Dibutyl carboxylic acid 11.7；Lauric acid/dodecanoic acid acid amides 11.6.
The preparation method that floor paint is used in the present embodiment, comprises the following steps：
Step one, above-mentioned component is divided into A groups：Latex powder, silica gel salt, titanium dioxide, coarse whiting, talcum powder and silicon ash
Stone；
B groups：Cellulose, defoamer, coloring pigment, film-forming agents and forming agent；
Step 2：A groups material is weighed respectively according to above-mentioned quality proportioning and a is denoted as,
Step 2, B group materials are weighed be denoted as b according to above-mentioned quality proportioning, are (a+b) * 50% by B groups material and quality
Diluent it is well mixed after, stand 30min, then the A group materials mixed are gradually added into and stirred, finally by quality
Diluent for (a+b) * 30% is added and stirred.
Embodiment 7
By the material composition of following weight proportion：Latex powder 22.5, silica gel salt 10；Calcium carbonate 14；Titanium dioxide 16.5；Coarse whiting
7.5；Talcum powder 6.5；Wollastonite 21；Cellulose 4.5；Defoamer 0.5；Coloring pigment 12.5, film-forming agents 6；Forming agent 11.
Further, film-forming agents are alcohol ester 12.
Wherein, forming agent by following weight proportion material composition：Modified rosin resin 22.5；Paraffin oil 18.8；Adjacent benzene
Dibutyl carboxylic acid 11.7；Lauric acid/dodecanoic acid acid amides 11.6.
The preparation method that floor paint is used in the present embodiment, comprises the following steps：
Each material is weighed respectively according to the weight proportion in the present embodiment and a is denoted as, by these materials and weight
It is uniformly mixed for a*80% diluent.
Embodiment 8
A kind of floor paint, by the material composition of following weight proportion：
Hydroxy-containing resin 50, dispersant 0.2, defoamer 0.2, anti-settling agent 1, pigment 8, filler 35, active solvent 5.6.
In use, the component in the present embodiment is well mixed with curing agent.
The performance in above-described embodiment is detected using same method, as a result such as following table：
By upper table, the floor paint of embodiment 1- embodiments 7 is substantially better than the floor paint in embodiment 8, with more
Good hardness, wearability, fire resistance, resistance to acids and bases and resistance to ag(e)ing.
These are only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc. should be included in the scope of the protection.
Claims (6)
1. a kind of floor paint of novel environment friendly dry powder shape, it is characterised in that：By the material composition of following weight proportion：Latex powder
10-35, silica gel salt 8-12；Calcium carbonate 10-18；Titanium dioxide 8-25；Coarse whiting 5-10；Talcum powder 5-8；Wollastonite 12-30；Cellulose
1-8；Defoamer 0.2-0.8；Coloring pigment 0-25, film-forming agents 0-12；Forming agent 2-20.
2. a kind of floor paint of novel environment friendly dry powder shape according to claim 1, it is characterised in that：The film-forming agents
For alcohol ester 12.
3. a kind of floor paint of novel environment friendly dry powder shape according to claim 1, it is characterised in that：The forming agent by
The material composition of following weight proportion：Modified rosin resin 20-25；Paraffin oil 17-20；Dibutyl phthalate 10-13；Ten
Diacid amide 9-14.
4. a kind of preparation method according to any one of the claim 1-3 floor paints, it is characterised in that：Comprise the following steps：
Step one, above-mentioned component is divided into A groups：Latex powder, silica gel salt, titanium dioxide, coarse whiting, talcum powder and wollastonite；
B groups：Cellulose, defoamer, coloring pigment, film-forming agents and forming agent；
Step 2：A groups material is weighed respectively according to above-mentioned quality proportioning and a is denoted as,
Step 2, B group materials are weighed be denoted as b according to above-mentioned quality proportioning, are the dilute of (a+b) * 50% by B groups material and quality
Release agent it is well mixed after, stand 30min, then the A group materials mixed are gradually added into and stirred, is finally (a by quality
+ b) * 30% diluent adds and stirs.
5. a kind of preparation method of floor paint according to claim 4, it is characterised in that：In step 2, by B groups material and
After diluent is well mixed, 35-40 DEG C of standing 30min is warming up to.
6. a kind of preparation method of floor paint according to claim 4, it is characterised in that：In step 2, A groups material according to
Titanium dioxide, coarse whiting, talcum powder, wollastonite, the order of silica gel salt and latex powder are sequentially added to B groups material and diluent mixing
In solution.