CN105462303A - Inorganic dry powder coating - Google Patents
Inorganic dry powder coating Download PDFInfo
- Publication number
- CN105462303A CN105462303A CN201510984640.5A CN201510984640A CN105462303A CN 105462303 A CN105462303 A CN 105462303A CN 201510984640 A CN201510984640 A CN 201510984640A CN 105462303 A CN105462303 A CN 105462303A
- Authority
- CN
- China
- Prior art keywords
- parts
- dry powder
- inorganic dry
- powder coating
- calcium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses inorganic dry powder coating, which is prepared from the flowing components in parts by weight: 1 to 2 parts of N-methyl pyrrolidone, 2.8 parts of fumed silica, 1.8 parts of alkyl naphthalene sulfonate, 3.1 parts of vinyltriethoxysilane, 9.7 parts of calcined kaolin, 8.9 parts of latex powder, 6.7 parts of sepiolite, 16.8 parts of calcium carbonate and 72.3 parts of white cement. The inorganic dry powder coating disclosed by the invention has the characteristics of water seepage resistance, fire protection, temperature adjustment, humidifying, antibiosis, release of anions, adsorption and decomposition of formaldehyde and carbon dioxide absorption.
Description
Technical field
The present invention relates to inorganic dry powder painting.
Background technology
Current dry powder paint, its anti-seep water, fire prevention, conditioning, antibacterial, anion releasing, adsorption-decomposition function formaldehyde and absorbing carbon dioxide performance all have much room for improvement.
Summary of the invention
The object of the present invention is to provide a kind of inorganic dry powder painting, there is the performance of anti-seep water, fire prevention, conditioning, antibacterial, anion releasing, adsorption-decomposition function formaldehyde and absorbing carbon dioxide.
For achieving the above object, technical scheme of the present invention is a kind of inorganic dry powder painting of design, composed of the following components by weight:
1 ~ 2 part of N-Methyl pyrrolidone, 2.8 parts of gas-phase silicas, 1.8 parts of sulfonated alkyl naphathalenes, 3.1 parts of vinyltriethoxysilanes, 9.7 parts of calcined kaolins, 8.9 parts of latex powder, 6.7 parts of sea bubble soil, 16.8 parts of calcium carbonate, 72.3 parts of white cements.
Preferably, inorganic dry powder painting, composed of the following components by weight:
1 part of N-Methyl pyrrolidone, 2.8 parts of gas-phase silicas, 1.8 parts of sulfonated alkyl naphathalenes, 3.1 parts of vinyltriethoxysilanes, 9.7 parts of calcined kaolins, 8.9 parts of latex powder, 6.7 parts of sea bubble soil, 16.8 parts of calcium carbonate, 72.3 parts of white cements.
Preferably, inorganic dry powder painting, composed of the following components by weight:
2 parts of N-Methyl pyrrolidone, 2.8 parts of gas-phase silicas, 1.8 parts of sulfonated alkyl naphathalenes, 3.1 parts of vinyltriethoxysilanes, 9.7 parts of calcined kaolins, 8.9 parts of latex powder, 6.7 parts of sea bubble soil, 16.8 parts of calcium carbonate, 72.3 parts of white cements.
Advantage of the present invention and beneficial effect are: provide a kind of inorganic dry powder painting, have the performance of anti-seep water, fire prevention, conditioning, antibacterial, anion releasing, adsorption-decomposition function formaldehyde and absorbing carbon dioxide.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A kind of inorganic dry powder painting, composed of the following components by weight:
1 ~ 2 part of N-Methyl pyrrolidone, 2.8 parts of gas-phase silicas, 1.8 parts of sulfonated alkyl naphathalenes, 3.1 parts of vinyltriethoxysilanes, 9.7 parts of calcined kaolins, 8.9 parts of latex powder, 6.7 parts of sea bubble soil, 16.8 parts of calcium carbonate, 72.3 parts of white cements.
Embodiment 2
Inorganic dry powder painting, composed of the following components by weight:
1 part of N-Methyl pyrrolidone, 2.8 parts of gas-phase silicas, 1.8 parts of sulfonated alkyl naphathalenes, 3.1 parts of vinyltriethoxysilanes, 9.7 parts of calcined kaolins, 8.9 parts of latex powder, 6.7 parts of sea bubble soil, 16.8 parts of calcium carbonate, 72.3 parts of white cements.
Embodiment 3
Inorganic dry powder painting, composed of the following components by weight:
2 parts of N-Methyl pyrrolidone, 2.8 parts of gas-phase silicas, 1.8 parts of sulfonated alkyl naphathalenes, 3.1 parts of vinyltriethoxysilanes, 9.7 parts of calcined kaolins, 8.9 parts of latex powder, 6.7 parts of sea bubble soil, 16.8 parts of calcium carbonate, 72.3 parts of white cements.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. inorganic dry powder painting, is characterized in that, composed of the following components by weight:
1 ~ 2 part of N-Methyl pyrrolidone, 2.8 parts of gas-phase silicas, 1.8 parts of sulfonated alkyl naphathalenes, 3.1 parts of vinyltriethoxysilanes, 9.7 parts of calcined kaolins, 8.9 parts of latex powder, 6.7 parts of sea bubble soil, 16.8 parts of calcium carbonate, 72.3 parts of white cements.
2. inorganic dry powder painting according to claim 1, is characterized in that, composed of the following components by weight:
1 part of N-Methyl pyrrolidone, 2.8 parts of gas-phase silicas, 1.8 parts of sulfonated alkyl naphathalenes, 3.1 parts of vinyltriethoxysilanes, 9.7 parts of calcined kaolins, 8.9 parts of latex powder, 6.7 parts of sea bubble soil, 16.8 parts of calcium carbonate, 72.3 parts of white cements.
3. inorganic dry powder painting according to claim 1, is characterized in that, composed of the following components by weight:
2 parts of N-Methyl pyrrolidone, 2.8 parts of gas-phase silicas, 1.8 parts of sulfonated alkyl naphathalenes, 3.1 parts of vinyltriethoxysilanes, 9.7 parts of calcined kaolins, 8.9 parts of latex powder, 6.7 parts of sea bubble soil, 16.8 parts of calcium carbonate, 72.3 parts of white cements.