CN106928629A - 一种abs塑料 - Google Patents

一种abs塑料 Download PDF

Info

Publication number
CN106928629A
CN106928629A CN201511012957.9A CN201511012957A CN106928629A CN 106928629 A CN106928629 A CN 106928629A CN 201511012957 A CN201511012957 A CN 201511012957A CN 106928629 A CN106928629 A CN 106928629A
Authority
CN
China
Prior art keywords
parts
abs plastic
plastic according
nano
weight ratio
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201511012957.9A
Other languages
English (en)
Inventor
不公告发明人
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Cixi Changhe Yuan Rubber Products Factory
Original Assignee
Cixi Changhe Yuan Rubber Products Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Cixi Changhe Yuan Rubber Products Factory filed Critical Cixi Changhe Yuan Rubber Products Factory
Priority to CN201511012957.9A priority Critical patent/CN106928629A/zh
Publication of CN106928629A publication Critical patent/CN106928629A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种ABS塑料，包括以下重量份组分：载体50份，硅烷偶联剂8份，增韧剂10份，分散剂1份，发泡剂2份，抗菌剂6份，阻燃剂2份，抗静电剂4份，抗紫外线剂2份，所述载体为丙烯腈-苯乙烯共聚物、苯乙烯-丁二烯共聚物、聚苯乙烯中的一种或几种。该ABS塑料在抗菌性、抗静电性、阻燃性以及抗紫外线性能等方面有了较大的提高。

Description

一种 ABS 塑料
技术领域
本发明涉及一种ABS塑料。
背景技术
ABS树脂是重要的通用合成树脂，主要是丙烯腈、丁二烯和苯乙烯的共混物或三元共聚物，是一种坚韧而有刚性的热塑料塑料，用途非常广泛，汽车工业常用于制造汽车零部件如仪表板、车身外板、内装饰板、方向盘等等，家电行业常用于制造如电冰箱、电视机、真空吸尘器等等，建筑行业常用语制造如卫生器具、游泳池衬里、管材和管件等，另外还用于制造安全帽、摩托车挡板、玩具、时钟、化妆品盒等等。
尽管ABS应用广泛，但由于ABS本身分子结构性能的特性，需要对ABS在抗菌性、抗静电性、阻燃性以及抗紫外线方面进行改进。
发明内容
为了解决上述现有技术的不足，本发明的目的是提供一种ABS塑料。
为了实现上述目的，本发明所设计的一种ABS塑料，包括以下重量份组分：载体 50份，硅烷偶联剂 8份，增韧剂 10份，分散剂 1份，发泡剂 2份，抗菌剂6份，阻燃剂2份，抗静电剂4份， 抗紫外线剂2份，所述载体为丙烯腈-苯乙烯共聚物、苯乙烯-丁二烯共聚物、聚苯乙烯中的一种或几种。
优选的，所述抗菌剂包括重量比为1：1的纳米银纤维与纳米锌纤维，所述纳米银纤维与纳米锌纤维的直径均为15~20um，长度均为1~3mm。
优选的，所述阻燃剂包括重量比为1：1的三氧化二锑与三聚磷酸铝。
优选的，所述抗静电剂包括重量比为1：1的石墨烯与二氧化钛。
优选的，所述抗紫外线剂为UV- P、UV-0、UV-531中的一种或多种。
优选的，所述硅烷偶联剂为γ-氨丙基三乙氧基硅烷、γ-缩水甘油醚氧丙基三甲氧基硅烷、γ-（甲基丙烯酰氧）丙基三甲氧基硅烷中的一种或几种。
优选的，所述增韧剂为甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物、甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物、氢化苯乙烯/丁二烯/苯乙烯嵌段共聚物中的一种或多种。
优选的，所述分散剂为硬脂酸单甘油脂、三硬脂酸甘油酯、乙撑双硬脂酰胺、低分子量离聚物、乙烯-丙烯酸共聚物中的一种或几种。
优选的，所述发泡剂为AC发泡剂。
本发明得到的一种ABS塑料，其技术效果是：该ABS塑料在抗菌性、抗静电性、阻燃性以及抗紫外线性能等方面有了较大的提高。
具体实施方式
下面结合实施例对本发明进一步说明。
本发明提供的一种ABS塑料，包括以下重量份组分：载体 50份，硅烷偶联剂 8份，增韧剂 10份，分散剂 1份，发泡剂 2份，抗菌剂6份，阻燃剂2份，抗静电剂4份， 抗紫外线剂2份，所述载体为丙烯腈-苯乙烯共聚物、苯乙烯-丁二烯共聚物、聚苯乙烯中的一种或几种。
所述抗菌剂包括重量比为1：1的纳米银纤维与纳米锌纤维，所述纳米银纤维与纳米锌纤维的直径均为15~20um，长度均为1~3mm。
所述阻燃剂包括重量比为1：1的三氧化二锑与三聚磷酸铝。
所述抗静电剂包括重量比为1：1的石墨烯与二氧化钛。
所述抗紫外线剂为UV- P、UV-0、UV-531中的一种或多种。
所述硅烷偶联剂为γ-氨丙基三乙氧基硅烷、γ-缩水甘油醚氧丙基三甲氧基硅烷、γ-（甲基丙烯酰氧）丙基三甲氧基硅烷中的一种或几种。
所述增韧剂为甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物、甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物、氢化苯乙烯/丁二烯/苯乙烯嵌段共聚物中的一种或多种。
所述分散剂为硬脂酸单甘油脂、三硬脂酸甘油酯、乙撑双硬脂酰胺、低分子量离聚物、乙烯-丙烯酸共聚物中的一种或几种。
所述发泡剂为AC发泡剂。
将上述重量份载体、硅烷偶联剂、增韧剂、分散剂、发泡剂、抗菌剂、阻燃剂、抗静电剂以及抗紫外线剂一起在高混机或密炼机内搅拌混合，混合均匀后加入双螺杆挤出机中，双螺杆挤出机的加工温度 ：一区温度180℃，二区温度185℃，三区温度190℃，四区温度195℃，五区温度210℃，六区温度215℃，七区温度230℃，八区温度240℃，九区温度245℃，挤出后冷却牵条、风干切粒制得本发明的ABS塑料。
该ABS塑料在抗菌性、阻燃性 、抗静电性以及抗紫外线等性能方面有了较明显的提高。

Claims (9)

1.一种ABS塑料，其特征在于，包括以下重量份组分：载体 50份，硅烷偶联剂 8份，增韧剂 10份，分散剂 1份，发泡剂 2份，抗菌剂6份，阻燃剂2份，抗静电剂4份， 抗紫外线剂2份，所述载体为丙烯腈-苯乙烯共聚物、苯乙烯-丁二烯共聚物、聚苯乙烯中的一种或几种。
2.根据权利要求1所述的ABS塑料，其特征在于：所述抗菌剂包括重量比为1：1的纳米银纤维与纳米锌纤维，所述纳米银纤维与纳米锌纤维的直径均为15~20um，长度均为1~3mm。
3.根据权利要求1所述的ABS塑料，其特征在于：所述阻燃剂包括重量比为1：1的三氧化二锑与三聚磷酸铝。
4.根据权利要求1所述的ABS塑料，其特征在于：所述抗静电剂包括重量比为1：1的石墨烯与二氧化钛。
5.根据权利要求1所述的ABS塑料，其特征在于：所述抗紫外线剂为UV- P、UV-0、UV-531中的一种或多种。
6.根据权利要求1所述的ABS塑料，其特征在于：所述硅烷偶联剂为γ-氨丙基三乙氧基硅烷、γ-缩水甘油醚氧丙基三甲氧基硅烷、γ-（甲基丙烯酰氧）丙基三甲氧基硅烷中的一种或几种。
7.根据权利要求1所述的ABS塑料，其特征在于：所述增韧剂为甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物、甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物、氢化苯乙烯/丁二烯/苯乙烯嵌段共聚物中的一种或多种。
8.根据权利要求1所述的ABS塑料，其特征在于：所述分散剂为硬脂酸单甘油脂、三硬脂酸甘油酯、乙撑双硬脂酰胺、低分子量离聚物、乙烯-丙烯酸共聚物中的一种或几种。
9.根据权利要求1所述的ABS塑料，其特征在于：所述发泡剂为AC发泡剂。
CN201511012957.9A 2015-12-31 2015-12-31 一种abs塑料 Pending CN106928629A (zh)