CN114561078A - 高耐候性抗菌塑料 - Google Patents
高耐候性抗菌塑料 Download PDFInfo
- Publication number
- CN114561078A CN114561078A CN202210184937.3A CN202210184937A CN114561078A CN 114561078 A CN114561078 A CN 114561078A CN 202210184937 A CN202210184937 A CN 202210184937A CN 114561078 A CN114561078 A CN 114561078A
- Authority
- CN
- China
- Prior art keywords
- parts
- weather
- antibacterial
- antibacterial plastic
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种高耐候性抗菌塑料，该高耐候性抗菌塑料包括如下质量份的各组分：ABS塑料母粒50份至70份、不饱和聚酯树脂5份至10份、阻燃填料15份至30份、聚乙烯2份至4份、聚丙烯2份至4份、分散剂0.2份至0.3份、硅烷偶联剂0.3份至0.4份、抗菌剂0.02份至0.04份、抗氧化剂0.2份至0.4份以及增韧剂0.3份至0.7份。上述高耐候性抗菌塑料中，ABS塑料母粒、不饱和聚酯树脂、阻燃填料、聚乙烯以及聚丙烯共同作为高耐候性抗菌塑料的基料，稳定性高，耐候性强，阻燃填料在构成基料的同时可以增加上述高耐候性抗菌塑料的耐高温和阻燃性能。抗菌剂增加了高耐候性抗菌塑料的抗菌性能，抗氧化剂增加了高耐候性抗菌塑料的抗氧化性能和耐候性能。
Description
技术领域
本发明涉及塑料生产领域，特别是涉及一种高耐候性抗菌塑料。
背景技术
塑料是以单体为原料，通过加聚或缩聚反应聚合而成的高分子化合物，塑料的抗形变能力中等，介于纤维和橡胶之间，由合成树脂及填料、增塑剂、稳定剂、润滑剂、色料等添加剂组成。塑料的主要成分是树脂。树脂是指尚未和各种添加剂混合的高分子化合物。树脂这一名词最初是由动植物分泌出的脂质而得名，如松香、虫胶等。树脂约占塑料总重量的40%～100%。塑料的基本性能主要决定于树脂的本性，但添加剂也起着重要作用。有些塑料基本上是由合成树脂所组成，不含或少含添加剂，如有机玻璃等。
塑料可区分为热固性与热塑性二类，前者无法重新塑造使用，后者可以再重复生产。热可塑性其物理延伸率较大，一般在50%~500%。在不同延伸率下力不完全成线性变化。塑料不同性能决定了其在生活在工业中的用途，随着技术的进步，对塑料改性一直没有停止过研究。希望不远的将来，塑料通过改性后的可以有更广泛的应用，甚至可代替钢铁等材料并对环境不再污染。但是传统的塑料抗菌效果差，耐候性差，满足不了市场上对塑料高耐候性和抗菌性的需求。
发明内容
基于此，有必要针对传统的塑料抗菌效果差，耐候性差，满足不了市场上对塑料高耐候性和抗菌性的需求提供一种高耐候性抗菌塑料。
一种高耐候性抗菌塑料，该高耐候性抗菌塑料包括如下质量份的各组分：ABS塑料母粒50份至70份、不饱和聚酯树脂5份至10份、阻燃填料15份至30份、聚乙烯2份至4份、聚丙烯2份至4份、分散剂0.2份至0.3份、硅烷偶联剂0.3份至0.4份、抗菌剂0.02份至0.04份、抗氧化剂0.2份至0.4份以及增韧剂0.3份至0.7份。
在其中一个实施例中，高耐候性抗菌塑料还包括质量份为1份至2份的玻璃纤维。
在其中一个实施例中，所述增韧剂包括如下质量份的各组分：高胶粉50份至70份和橡胶粉30份至50份。
在其中一个实施例中，所述抗氧化剂为亚磷酸酯。
在其中一个实施例中，所述无机填料粉包括如下质量份的各组分：氢氧化铝微粉50份至70份、碳酸钙粉20份至40份以及氢氧化钙10份至20份。
在其中一个实施例中，所述抗菌剂为纳米银粉。
在其中一个实施例中，所述分散剂包括如下质量份的各组分：硬脂酸单甘油酯50份至70份和三硬脂酸甘油酯30份至50份。
在其中一个实施例中，高耐候性抗菌塑料还包括质量份为0.2份至0.5份的增强剂。
在其中一个实施例中，所述增强剂为玻璃微珠。
在其中一个实施例中，高耐候性抗菌塑料还包括质量份为0.5份至0.8份的有机硅阻燃剂。
上述高耐候性抗菌塑料中，ABS塑料母粒、不饱和聚酯树脂、阻燃填料、聚乙烯以及聚丙烯共同作为高耐候性抗菌塑料的基料，稳定性高，耐候性强，阻燃填料在构成基料的同时可以增加上述高耐候性抗菌塑料的耐高温和阻燃性能。分散剂可以使得各组分能够均匀的混合开，硅烷偶联剂增加了各组分的结合稳定性。抗菌剂增加了高耐候性抗菌塑料的抗菌性能，抗氧化剂增加了高耐候性抗菌塑料的抗氧化性能和耐候性能。增韧剂增加了高耐候性抗菌塑料的结构强度、韧性和结构稳定性。上述高耐候性抗菌塑料在具有良好韧性的同时，抗菌性能优异，耐候性强，使用寿命长，适用范围广。
附图说明
图1为一个实施例中高耐候性抗菌塑料的组分图。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合附图及实施例，对本发明进行进一步详细说明。应当理解，此处描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
一种高耐候性抗菌塑料，该高耐候性抗菌塑料包括如下质量份的各组分：ABS塑料母粒50份至70份、不饱和聚酯树脂5份至10份、阻燃填料15份至30份、聚乙烯2份至4份、聚丙烯2份至4份、分散剂0.2份至0.3份、硅烷偶联剂0.3份至0.4份、抗菌剂0.02份至0.04份、抗氧化剂0.2份至0.4份以及增韧剂0.3份至0.7份。具体的，在本实施例中，所述抗氧化剂为亚磷酸酯。进一步地，在其中一个实施例中，该高耐候性抗菌塑料包括如下质量份的各组分：ABS塑料母粒55份至65份、不饱和聚酯树脂6份至8份、阻燃填料18份至24份、聚乙烯2.5份至3.5份、聚丙烯2.5份至3.5份、分散剂0.25份至0.28份、硅烷偶联剂0.32份至0.38份、抗菌剂0.025份至0.038份、抗氧化剂0.25份至0.36份以及增韧剂0.4份至0.6份。
为了进一步地增加高耐候性抗菌塑料的韧性和结构强度，在其中一个实施例中，所述增韧剂包括如下质量份的各组分：高胶粉50份至70份和橡胶粉30份至50份。进一步地，所述增韧剂包括如下质量份的各组分：高胶粉55份至65份和橡胶粉35份至45份。具体的，所述增韧剂包括如下质量份的各组分：高胶粉60份和橡胶粉40份。高胶粉和橡胶粉均具有一定的弹性和良好的韧性以及优良的耐腐蚀性能。在增加高耐候性抗菌塑料的韧性和结构强度的同时可以增加高耐候性抗菌塑料的耐候性。
为了增加高耐候性抗菌塑料的抗菌性能，在其中一个实施例中，所述抗菌剂为纳米银粉。纳米银粉具有良好的杀菌效果，并且可以进一步地增加高耐候性抗菌塑料的阻燃性能。如此，纳米银粉增加了高耐候性抗菌塑料的抗菌性能和阻燃性能。
为了增加高耐候性抗菌塑料的韧性和结构强度，在其中一个实施例中，高耐候性抗菌塑料还包括质量份为1份至2份的玻璃纤维。玻璃纤维具有良好的韧性和阻燃性能，玻璃纤维一方面可以增加高耐候性抗菌塑料的韧性和结构强度，并且玻璃纤维可以进一步地增加高耐候性抗菌塑料的阻燃性能。如此，玻璃纤维增加了高耐候性抗菌塑料的韧性、结构强度以及阻燃性能。
为了增加高耐候性抗菌塑料的阻燃性能，在其中一个实施例中，所述无机填料粉包括如下质量份的各组分：氢氧化铝微粉50份至70份、碳酸钙粉20份至40份以及氢氧化钙10份至20份。进一步地，所述无机填料粉包括如下质量份的各组分：氢氧化铝微粉55份至65份、碳酸钙粉25份至35份以及氢氧化钙12份至18份。具体的，所述无机填料粉包括如下质量份的各组分：氢氧化铝微粉56份、碳酸钙粉28份以及氢氧化钙16份。氢氧化铝微粉、碳酸钙粉、氢氧化钙均具有阻燃的性能，且具有一定的杀菌性能。在增加高耐候性抗菌塑料的阻燃性能的同时增加了高耐候性抗菌塑料的抗菌性能。
为了使得高耐候性抗菌塑料中的各组分进行均匀地混合，在其中一个实施例中，所述分散剂包括如下质量份的各组分：硬脂酸单甘油酯50份至70份和三硬脂酸甘油酯30份至50份。进一步地，所述分散剂包括如下质量份的各组分：硬脂酸单甘油酯55份至65份和三硬脂酸甘油酯35份至45份。具体的，所述分散剂包括如下质量份的各组分：硬脂酸单甘油酯60份和三硬脂酸甘油酯40份。硬脂酸单甘油酯和三硬脂酸甘油酯具有良好的润滑和分散性能，包括硬脂酸单甘油酯和三硬脂酸甘油酯的分散剂可以使得高耐候性抗菌塑料中的各组分进行均匀地混合。
为了进一步地增加高耐候性抗菌塑料的结构强度，在其中一个实施例中，高耐候性抗菌塑料还包括质量份为0.2份至0.5份的增强剂。具体的，在本实施例中，所述增强剂为玻璃微珠。玻璃微珠具有良好的结构强度和耐高温性能以及优良的耐候性能，在增加高耐候性抗菌塑料的结构强度的同时可以增加高耐候性抗菌塑料的阻燃性能。进一步地，在其中一个实施例中，高耐候性抗菌塑料还包括质量份为0.5份至0.8份的有机硅阻燃剂。有机硅阻燃剂进一步地增加高耐候性抗菌塑料的阻燃性能。
上述高耐候性抗菌塑料中，ABS塑料母粒、不饱和聚酯树脂、阻燃填料、聚乙烯以及聚丙烯共同作为高耐候性抗菌塑料的基料，稳定性高，耐候性强，阻燃填料在构成基料的同时可以增加上述高耐候性抗菌塑料的耐高温和阻燃性能。分散剂可以使得各组分能够均匀的混合开，硅烷偶联剂增加了各组分的结合稳定性。抗菌剂增加了高耐候性抗菌塑料的抗菌性能，抗氧化剂增加了高耐候性抗菌塑料的抗氧化性能和耐候性能。增韧剂增加了高耐候性抗菌塑料的结构强度、韧性和结构稳定性。上述高耐候性抗菌塑料在具有良好韧性的同时，抗菌性能优异，耐候性强，使用寿命长，适用范围广。
以上实施例的各技术特征可以进行任意的组合，为使描述简洁，未对上述实施例中的各个技术特征所有可能的组合都进行描述，然而，只要这些技术特征的组合不存在矛盾，都应当认为是本说明书记载的范围。
以上所述实施例仅表达了本发明的几种实施方式，其描述较为具体和详细，但并不能因此而理解为对发明专利范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。因此，本发明专利的保护范围应以所附权利要求为准。
Claims (10)
1.一种高耐候性抗菌塑料，其特征在于，包括如下质量份的各组分：ABS塑料母粒50份至70份、不饱和聚酯树脂5份至10份、阻燃填料15份至30份、聚乙烯2份至4份、聚丙烯2份至4份、分散剂0.2份至0.3份、硅烷偶联剂0.3份至0.4份、抗菌剂0.02份至0.04份、抗氧化剂0.2份至0.4份以及增韧剂0.3份至0.7份。
2.根据权利要求1所述的高耐候性抗菌塑料，其特征在于，还包括质量份为1份至2份的玻璃纤维。
3.根据权利要求1所述的高耐候性抗菌塑料，其特征在于，所述增韧剂包括如下质量份的各组分：高胶粉50份至70份和橡胶粉30份至50份。
4.根据权利要求1所述的高耐候性抗菌塑料，其特征在于，所述抗氧化剂为亚磷酸酯。
5.根据权利要求1所述的高耐候性抗菌塑料，其特征在于，所述无机填料粉包括如下质量份的各组分：氢氧化铝微粉50份至70份、碳酸钙粉20份至40份以及氢氧化钙10份至20份。
6.根据权利要求1所述的高耐候性抗菌塑料，其特征在于，所述抗菌剂为纳米银粉。
7.根据权利要求1所述的高耐候性抗菌塑料，其特征在于，所述分散剂包括如下质量份的各组分：硬脂酸单甘油酯50份至70份和三硬脂酸甘油酯30份至50份。
8.根据权利要求1所述的高耐候性抗菌塑料，其特征在于，还包括质量份为0.2份至0.5份的增强剂。
9.根据权利要求8所述的高耐候性抗菌塑料，其特征在于，所述增强剂为玻璃微珠。
10.根据权利要求1所述的高耐候性抗菌塑料，其特征在于，还包括质量份为0.5份至0.8份的有机硅阻燃剂。