CN106906636A - Crease and shrink resistant finishing agent - Google Patents
Crease and shrink resistant finishing agent Download PDFInfo
- Publication number
- CN106906636A CN106906636A CN201610520664.XA CN201610520664A CN106906636A CN 106906636 A CN106906636 A CN 106906636A CN 201610520664 A CN201610520664 A CN 201610520664A CN 106906636 A CN106906636 A CN 106906636A
- Authority
- CN
- China
- Prior art keywords
- parts
- crease
- finishing agent
- resistant finishing
- shrink resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses crease and shrink resistant finishing agent, including following weight portion component, 80~100 parts of trimethylol melamine, 30~40 parts of methacrylic acid, 40~60 parts of methyl methacrylate, 20~30 parts of lauryl methacrylate, 20~30 parts of zinc nitrate hexahydrate, 40~60 parts of poly- isobutyl ester, 20~40 parts of aluminium hydroxide, 12~24 parts of phosphotriester, 12~18 parts of antimony oxide, 4~12 parts of benzoyl peroxide, 12~24 parts of isopropanol, 4~8 parts of isopropyl acrylate, 8~12 parts of butyl acetate.The crease and shrink resistant finishing agent that the present invention is provided, makes simple, and the raw materials for production selection of use is avirulent, the fabric processed with this finishing agent can crease and shrink resistance, fixed effect is good, exempts from flatiron, with it is well-pressed, plentiful, not dirty the features such as.
Description
Technical field
The present invention relates to a kind of finishing agent technical field, and in particular to a kind of crease and shrink resistant finishing agent.
Background technology
In recent years, with the improvement of people ' s living standards, under working environment with water repellent, refuse oil, soil-repellent finishing clothes need
The amount of asking constantly increases, the fabric treated using finishing agent, can protect the user against splashing for water, oil, chemicals and pollutant
Infringement is echoed, with protective, can be used for protective garments or work clothes etc. under the working environment of making high-quality, by people
Attention and have a good application prospect;The finishing agent function of using at present is relatively simple, and using effect is poor, it is necessary to enter
The improvement of one step, simple finishing agent can not meet the required of people.
The content of the invention
It is an object of the invention to provide crease and shrink resistant finishing agent, one or more in above-mentioned prior art problem is solved.
According to an aspect of the present invention, crease and shrink resistant finishing agent, including following weight portion component,
80~100 parts of trimethylol melamine, 30~40 parts of methacrylic acid, 40~60 parts of methyl methacrylate,
20~30 parts of lauryl methacrylate, 20~30 parts of zinc nitrate hexahydrate, 40~60 parts of poly- isobutyl ester, aluminium hydroxide 20~40
Part, 12~24 parts of phosphotriester, 12~18 parts of antimony oxide, 4~12 parts of benzoyl peroxide, 12~24 parts of isopropanol, third
4~8 parts of isopropyl gadoleate, 8~12 parts of butyl acetate.
The crease and shrink resistant finishing agent that the present invention is provided, makes simple, and the raw materials for production selection of use is avirulent, whole with this
The fabric of reason agent treatment can crease and shrink resistance, fixed effect is good, exempts from flatiron, with it is well-pressed, plentiful, not dirty the features such as.
Specific embodiment
Embodiment 1
By 80 parts of trimethylol melamine, 30 parts of methacrylic acid, 40 parts of methyl methacrylate, methacrylic acid month
20 parts of osmanthus ester, 20 parts of zinc nitrate hexahydrate, 40 parts of poly- isobutyl ester, 20 parts of aluminium hydroxide, 12 parts of phosphotriester, antimony oxide 12
Part, 4 parts of benzoyl peroxide, 12 parts of isopropanol, 4 parts of isopropyl acrylate, 8 parts of butyl acetate is put into reactor, constantly stirs
Mix, 40 DEG C are heated to after mixing completely, product is obtained final product after uniform stirring.
Embodiment 2
By 90 parts of trimethylol melamine, 35 parts of methacrylic acid, 50 parts of methyl methacrylate, methacrylic acid month
25 parts of osmanthus ester, 25 parts of zinc nitrate hexahydrate, 50 parts of poly- isobutyl ester, 30 parts of aluminium hydroxide, 18 parts of phosphotriester, antimony oxide 15
Part, 8 parts of benzoyl peroxide, 18 parts of isopropanol, 6 parts of isopropyl acrylate, 10 parts of butyl acetate is put into reactor, constantly stirs
Mix, 40 DEG C are heated to after mixing completely, product is obtained final product after uniform stirring.
Embodiment 3
By 100 parts of trimethylol melamine, 40 parts of methacrylic acid, 60 parts of methyl methacrylate, methacrylic acid
30 parts of lauryl, 30 parts of zinc nitrate hexahydrate, 60 parts of poly- isobutyl ester, 40 parts of aluminium hydroxide, 24 parts of phosphotriester, antimony oxide 18
Part, 12 parts of benzoyl peroxide, 12~24 parts of isopropanol, 8 parts of isopropyl acrylate, 12 parts of butyl acetate is put into reactor,
It is stirred continuously, 40 DEG C is heated to after mixing completely, product is obtained final product after uniform stirring.
The above is only preferred embodiment of the invention, it is noted that to those skilled in the art, not
On the premise of departing from the invention design, some similar deformations and improvement can also be made, these also should be regarded as the present invention
Protection domain within.
Claims (1)
1. crease and shrink resistant finishing agent, it is characterised in that:Component including following weight portion,
80~100 parts of trimethylol melamine, 30~40 parts of methacrylic acid, 40~60 parts of methyl methacrylate, methyl
20~30 parts of lauryl acrylate, 20~30 parts of zinc nitrate hexahydrate, 40~60 parts of poly- isobutyl ester, 20~40 parts of aluminium hydroxide, phosphorus
Sour 12~24 parts of three ester, 12~18 parts of antimony oxide, 4~12 parts of benzoyl peroxide, 12~24 parts of isopropanol, acrylic acid is different
4~8 parts of propyl ester, 8~12 parts of butyl acetate.