CN106906648A - Cotton fabric anticrease finishing liquid - Google Patents
Cotton fabric anticrease finishing liquid Download PDFInfo
- Publication number
- CN106906648A CN106906648A CN201610517764.7A CN201610517764A CN106906648A CN 106906648 A CN106906648 A CN 106906648A CN 201610517764 A CN201610517764 A CN 201610517764A CN 106906648 A CN106906648 A CN 106906648A
- Authority
- CN
- China
- Prior art keywords
- parts
- cotton fabric
- finishing liquid
- anticrease
- glyoxal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses cotton fabric anticrease finishing liquid, component including following weight portion, 100~200 parts of glyoxal, 100~160 parts of aluminum sulfate, 80~100 parts of trimethylol melamine, 20~30 parts of lauryl methacrylate, 20~30 parts of zinc nitrate hexahydrate, 40~60 parts of poly- isobutyl ester, 20~40 parts of aluminium hydroxide, 12~24 parts of phosphotriester, 12~18 parts of antimony oxide, 10~20 parts of benzoyl peroxide.The cotton fabric anticrease finishing liquid that the present invention is provided, makes simple, and the raw materials for production selection of use is avirulent, the fabric processed with this finishing agent can crease and shrink resistance, fixed effect is good, exempts from flatiron, with it is well-pressed, plentiful, not dirty the features such as.
Description
Technical field
The present invention relates to a kind of finishing agent technical field, and in particular to a kind of cotton fabric anticrease finishing liquid.
Background technology
In recent years, with the improvement of people ' s living standards, under working environment with water repellent, refuse oil, soil-repellent finishing clothes need
The amount of asking constantly increases, the fabric treated using finishing agent, can protect the user against splashing for water, oil, chemicals and pollutant
Infringement is echoed, with protective, can be used for protective garments or work clothes etc. under the working environment of making high-quality, by people
Attention and have a good application prospect；The finishing agent function of using at present is relatively simple, and using effect is poor, it is necessary to enter
The improvement of one step, simple finishing agent can not meet the required of people.
The content of the invention
It is an object of the invention to provide cotton fabric anticrease finishing liquid, one in above-mentioned prior art problem or many is solved
It is individual.
According to an aspect of the present invention, cotton fabric anticrease finishing liquid, including following weight portion component,
100~200 parts of glyoxal, 100~160 parts of aluminum sulfate, 80~100 parts of trimethylol melamine, metering system
20~30 parts of sour lauryl, 20~30 parts of zinc nitrate hexahydrate, 40~60 parts of poly- isobutyl ester, 20~40 parts of aluminium hydroxide, tricresyl phosphate
12~24 parts of ester, 12~18 parts of antimony oxide, 10~20 parts of benzoyl peroxide.
The cotton fabric anticrease finishing liquid that the present invention is provided, makes simple, and the raw materials for production selection of use is avirulent, with this
The fabric of finishing agent treatment can crease and shrink resistance, fixed effect is good, exempts from flatiron, with it is well-pressed, plentiful, not dirty the features such as.
Specific embodiment
Embodiment 1
By 100 parts of glyoxal, 100 parts of aluminum sulfate, 80 parts of trimethylol melamine, 20 parts of lauryl methacrylate,
20 parts of zinc nitrate hexahydrate, 40 parts of poly- isobutyl ester, 20 parts of aluminium hydroxide, 12 parts of phosphotriester, 12 parts of antimony oxide, benzoyl peroxide
0 part of formyl chloride-1 is put into reactor, is stirred continuously, and 60 DEG C are heated to after mixing completely, adds 300 parts of deionized waters, is uniformly stirred
Product is obtained final product after mixing.
Embodiment 2
By 150 parts of glyoxal, 130 parts of aluminum sulfate, 90 parts of trimethylol melamine, 25 parts of lauryl methacrylate,
25 parts of zinc nitrate hexahydrate, 50 parts of poly- isobutyl ester, 30 parts of aluminium hydroxide, 18 parts of phosphotriester, 15 parts of antimony oxide, benzoyl peroxide
5 parts of formyl chloride-1 is put into reactor, is stirred continuously, and 60 DEG C are heated to after mixing completely, adds 300 parts of deionized waters, is uniformly stirred
Product is obtained final product after mixing.
Embodiment 3
By 200 parts of glyoxal, 160 parts of aluminum sulfate, 100 parts of trimethylol melamine, 30 parts of lauryl methacrylate,
30 parts of zinc nitrate hexahydrate, 60 parts of poly- isobutyl ester, 40 parts of aluminium hydroxide, 24 parts of phosphotriester, 18 parts of antimony oxide, benzoyl peroxide
20 parts of formyl is put into reactor, is stirred continuously, and 60 DEG C are heated to after mixing completely, adds 300 parts of deionized waters, is uniformly stirred
Product is obtained final product after mixing.
The above is only preferred embodiment of the invention, it is noted that to those skilled in the art, not
On the premise of departing from the invention design, some similar deformations and improvement can also be made, these also should be regarded as the present invention
Protection domain within.
Claims (1)
1. cotton fabric anticrease finishing liquid, it is characterised in that：Component including following weight portion,
100~200 parts of glyoxal, 100~160 parts of aluminum sulfate, 80~100 parts of trimethylol melamine, methacrylic acid month
20~30 parts of osmanthus ester, 20~30 parts of zinc nitrate hexahydrate, 40~60 parts of poly- isobutyl ester, 20~40 parts of aluminium hydroxide, phosphotriester 12
~24 parts, 12~18 parts of antimony oxide, 10~20 parts of benzoyl peroxide.