CN106906660A - Corduroy crease proofing agent - Google Patents
Corduroy crease proofing agent Download PDFInfo
- Publication number
- CN106906660A CN106906660A CN201610521710.8A CN201610521710A CN106906660A CN 106906660 A CN106906660 A CN 106906660A CN 201610521710 A CN201610521710 A CN 201610521710A CN 106906660 A CN106906660 A CN 106906660A
- Authority
- CN
- China
- Prior art keywords
- parts
- corduroy
- proofing agent
- crease
- crease proofing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses corduroy crease proofing agent, component including following weight portion, 16~48 parts of coconut oil fat acyl diethanol amine, 20~40 parts of rosin glycerin ester resin, 10~20 parts of ethyl acetate, 10~30 parts of butyl acetate, 100~160 parts of dimethylol urea, 20~60 parts of sodium carbonate, 40~60 parts of poly- isobutyl ester, 12~24 parts of phosphotriester, 20~40 parts of aluminum sulfate, 20~40 parts of trimethylol melamine, 20~30 parts of lauryl methacrylate, 20~30 parts of zinc nitrate hexahydrate, 10~20 parts of benzoyl peroxide, 600~800 parts of deionized water.The corduroy crease proofing agent that the present invention is provided, makes simple, and the raw materials for production selection of use is avirulent, the fabric processed with this finishing agent can crease and shrink resistance, fixed effect is good, exempts from flatiron, with it is well-pressed, plentiful, not dirty the features such as.
Description
Technical field
The present invention relates to a kind of finishing agent technical field, and in particular to a kind of corduroy crease proofing agent.
Background technology
In recent years, with the improvement of people ' s living standards, under working environment with water repellent, refuse oil, refuse dirty whole
The clothes demand of reason constantly increases, using finishing agent treat fabric, can protect the user against water,
Oil, chemicals and splashing for pollutant echo infringement, with protective, can be used to make the work of high-quality
Protective garments or work clothes etc. under environment, are valued by people and have a good application prospect;Mesh
The preceding finishing agent function of using is relatively simple, and using effect is poor, it is necessary to further improve, letter
Single finishing agent can not meet the required of people.
The content of the invention
It is an object of the invention to provide corduroy crease proofing agent, in above-mentioned prior art problem is solved
Or it is multiple.
According to an aspect of the present invention, corduroy crease proofing agent, including following weight portion component,
16~48 parts of coconut oil fat acyl diethanol amine, 20~40 parts of rosin glycerin ester resin, ethyl acetate
10~20 parts, 10~30 parts of butyl acetate, 100~160 parts of dimethylol urea, 20~60 parts of sodium carbonate,
40~60 parts of poly- isobutyl ester, 12~24 parts of phosphotriester, 20~40 parts of aluminum sulfate, trihydroxy methyl melamine
20~40 parts of amine, 20~30 parts of lauryl methacrylate, 20~30 parts of zinc nitrate hexahydrate, benzoyl peroxide
0~20 part of formyl chloride-1,600~800 parts of deionized water.
The corduroy crease proofing agent that the present invention is provided, makes simple, and the raw materials for production selection of use is nontoxic
Property, the fabric processed with this finishing agent can crease and shrink resistance, fixed effect is good, exempts from flatiron, with waterproof,
Grease proofing, well-pressed, plentiful, not dirty the features such as.
Specific embodiment
Embodiment 1
By 16 parts of coconut oil fat acyl diethanol amine, 20 parts of rosin glycerin ester resin, 10 parts of ethyl acetate,
10 parts of butyl acetate, 100 parts of dimethylol urea, 20 parts of sodium carbonate, 40 parts of poly- isobutyl ester, phosphoric acid
Three 12 parts of esters, 20 parts of aluminum sulfate, 20 parts of trimethylol melamine, lauryl methacrylate 20
Part, 20 parts of zinc nitrate hexahydrate, 10 parts of benzoyl peroxide, 600 parts of deionized water is put into reactor,
It is stirred continuously, 60 DEG C is heated to after mixing completely, product is obtained final product after uniform stirring.
Embodiment 2
By 32 parts of coconut oil fat acyl diethanol amine, 30 parts of rosin glycerin ester resin, 15 parts of ethyl acetate,
20 parts of butyl acetate, 130 parts of dimethylol urea, 40 parts of sodium carbonate, 50 parts of poly- isobutyl ester, phosphoric acid
Three 18 parts of esters, 30 parts of aluminum sulfate, 30 parts of trimethylol melamine, lauryl methacrylate 25
Part, 25 parts of zinc nitrate hexahydrate, 15 parts of benzoyl peroxide, 700 parts of deionized water is put into reactor,
It is stirred continuously, 60 DEG C is heated to after mixing completely, product is obtained final product after uniform stirring.
Embodiment 3
By 48 parts of coconut oil fat acyl diethanol amine, 40 parts of rosin glycerin ester resin, 20 parts of ethyl acetate,
30 parts of butyl acetate, 160 parts of dimethylol urea, 60 parts of sodium carbonate, 60 parts of poly- isobutyl ester, phosphoric acid
Three 24 parts of esters, 40 parts of aluminum sulfate, 40 parts of trimethylol melamine, lauryl methacrylate 30
Part, 30 parts of zinc nitrate hexahydrate, 20 parts of benzoyl peroxide, 800 parts of deionized water is put into reactor,
It is stirred continuously, 60 DEG C is heated to after mixing completely, product is obtained final product after uniform stirring.
The above is only preferred embodiment of the invention, it is noted that for those of ordinary skill in the art
For, without departing from the concept of the premise of the invention, some similar deformations can also be made and changed
Enter, these also should be regarded as within protection scope of the present invention.
Claims (1)
1. corduroy crease proofing agent, it is characterised in that:Component including following weight portion,
16~48 parts of coconut oil fat acyl diethanol amine, 20~40 parts of rosin glycerin ester resin, ethyl acetate
10~20 parts, 10~30 parts of butyl acetate, 100~160 parts of dimethylol urea, 20~60 parts of sodium carbonate,
40~60 parts of poly- isobutyl ester, 12~24 parts of phosphotriester, 20~40 parts of aluminum sulfate, trihydroxy methyl melamine
20~40 parts of amine, 20~30 parts of lauryl methacrylate, 20~30 parts of zinc nitrate hexahydrate, benzoyl peroxide
0~20 part of formyl chloride-1,600~800 parts of deionized water.