CN106906659A - Waterproof is according to oily crease proofing agent - Google Patents
Waterproof is according to oily crease proofing agent Download PDFInfo
- Publication number
- CN106906659A CN106906659A CN201610514550.4A CN201610514550A CN106906659A CN 106906659 A CN106906659 A CN 106906659A CN 201610514550 A CN201610514550 A CN 201610514550A CN 106906659 A CN106906659 A CN 106906659A
- Authority
- CN
- China
- Prior art keywords
- parts
- oily
- waterproof
- proofing agent
- crease
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses waterproof according to oily crease proofing agent, including following weight portion component, 100~160 parts of dimethylol urea, 20~60 parts of sodium carbonate, 40~60 parts of poly- isobutyl ester, 20~40 parts of aluminium hydroxide, 12~24 parts of phosphotriester, 20~40 parts of aluminum sulfate, 20~40 parts of trimethylol melamine, 20~30 parts of lauryl methacrylate, 20~30 parts of zinc nitrate hexahydrate, 10~20 parts of benzoyl peroxide, 600~800 parts of deionized water.The waterproof that the present invention is provided makes simple according to oily crease proofing agent, and the raw materials for production selection of use is avirulent, the fabric processed with this finishing agent can crease and shrink resistance, fixed effect is good, exempts from flatiron, with it is well-pressed, plentiful, not dirty the features such as.
Description
Technical field
The present invention relates to a kind of finishing agent technical field, and in particular to a kind of waterproof is according to oily crease proofing agent.
Background technology
In recent years, with the improvement of people ' s living standards, under working environment with water repellent, refuse oil, soil-repellent finishing clothes need
The amount of asking constantly increases, the fabric treated using finishing agent, can protect the user against splashing for water, oil, chemicals and pollutant
Infringement is echoed, with protective, can be used for protective garments or work clothes etc. under the working environment of making high-quality, by people
Attention and have a good application prospect;The finishing agent function of using at present is relatively simple, and using effect is poor, it is necessary to enter
The improvement of one step, simple finishing agent can not meet the required of people.
The content of the invention
It is an object of the invention to provide waterproof according to oily crease proofing agent, one in above-mentioned prior art problem or many is solved
It is individual.
According to an aspect of the present invention, waterproof is according to oily crease proofing agent, including following weight portion component,
100~160 parts of dimethylol urea, 20~60 parts of sodium carbonate, 40~60 parts of poly- isobutyl ester, aluminium hydroxide 20~40
Part, 12~24 parts of phosphotriester, 20~40 parts of aluminum sulfate, 20~40 parts of trimethylol melamine, lauryl methacrylate
20~30 parts, 20~30 parts of zinc nitrate hexahydrate, 10~20 parts of benzoyl peroxide, 600~800 parts of deionized water.
The waterproof that the present invention is provided makes simple according to oily crease proofing agent, and the raw materials for production selection of use is avirulent, uses
The fabric of this finishing agent treatment can crease and shrink resistance, fixed effect is good, exempts from flatiron, with Water-proof and oil-proof, well-pressed, plentiful, not dirty etc.
Feature.
Specific embodiment
Embodiment 1
By 1000 parts of dimethylol urea, 20 parts of sodium carbonate, 40 parts of poly- isobutyl ester, 20 parts of aluminium hydroxide, 12 parts of phosphotriester,
20 parts of aluminum sulfate, 20 parts of trimethylol melamine, 20 parts of lauryl methacrylate, 20 parts of zinc nitrate hexahydrate, benzoyl peroxide
0 part of formyl chloride-1,600 parts of deionized water is put into reactor, is stirred continuously, and 60 DEG C are heated to after mixing completely, after uniform stirring i.e.
Obtain product.
Embodiment 2
By 130 parts of dimethylol urea, 40 parts of sodium carbonate, 50 parts of poly- isobutyl ester, 30 parts of aluminium hydroxide, 18 parts of phosphotriester,
30 parts of aluminum sulfate, 30 parts of trimethylol melamine, 25 parts of lauryl methacrylate, 25 parts of zinc nitrate hexahydrate, benzoyl peroxide
5 parts of formyl chloride-1,700 parts of deionized water is put into reactor, is stirred continuously, and 60 DEG C are heated to after mixing completely, after uniform stirring i.e.
Obtain product.
Embodiment 3
By 160 parts of dimethylol urea, 60 parts of sodium carbonate, 60 parts of poly- isobutyl ester, 40 parts of aluminium hydroxide, 24 parts of phosphotriester,
40 parts of aluminum sulfate, 40 parts of trimethylol melamine, 30 parts of lauryl methacrylate, 30 parts of zinc nitrate hexahydrate, benzoyl peroxide
20 parts of formyl, 800 parts of deionized water is put into reactor, is stirred continuously, and 60 DEG C are heated to after mixing completely, after uniform stirring i.e.
Obtain product.
The above is only preferred embodiment of the invention, it is noted that to those skilled in the art, not
On the premise of departing from the invention design, some similar deformations and improvement can also be made, these also should be regarded as the present invention
Protection domain within.
Claims (1)
1. waterproof is according to oily crease proofing agent, it is characterised in that:Component including following weight portion,
100~160 parts of dimethylol urea, 20~60 parts of sodium carbonate, 40~60 parts of poly- isobutyl ester, 20~40 parts of aluminium hydroxide, phosphorus
Sour 12~24 parts of three ester, 20~40 parts of aluminum sulfate, 20~40 parts of trimethylol melamine, lauryl methacrylate 20~30
Part, 20~30 parts of zinc nitrate hexahydrate, 10~20 parts of benzoyl peroxide, 600~800 parts of deionized water.