CN107558195A - Cotton noniron finish liquid - Google Patents
Cotton noniron finish liquid Download PDFInfo
- Publication number
- CN107558195A CN107558195A CN201610521123.9A CN201610521123A CN107558195A CN 107558195 A CN107558195 A CN 107558195A CN 201610521123 A CN201610521123 A CN 201610521123A CN 107558195 A CN107558195 A CN 107558195A
- Authority
- CN
- China
- Prior art keywords
- parts
- cotton
- finish liquid
- noniron finish
- lauryl methacrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses cotton noniron finish liquid, include the component of following parts by weight, 16~32 parts of ethylene glycol, 10~20 parts of melamine, 10~14 parts of formaldehyde resin, 6~12 parts of 2-hydroxyethyl methacry-late, 6~8 parts of methyl methacrylate, 4~6 parts of lauryl methacrylate, 2~6 parts of magnesium chloride, 2~4 parts of rosin glycerin ester resin, 10~20 parts of phosphotriester, 20~30 parts of lauryl methacrylate, 20~30 parts of zinc nitrate hexahydrate, 10~20 parts of benzoyl peroxide, 20~30 parts of poly divinyl acetylene, 10~16 parts of aphthenic acids, 200~300 parts of deionized water.Cotton noniron finish liquid provided by the invention, makes simple, and the raw materials for production selection of use is avirulent, the fabric handled with this finishing agent can crease and shrink resistance, fixed effect is good, exempts to press, and has the characteristics that well-pressed, plentiful, not dirty.
Description
Technical field
The present invention relates to a kind of finishing agent technical field, and in particular to a kind of cotton noniron finish liquid.
Background technology
In recent years, as the improvement of people's living standards, under working environment with water repellent, refuse oil, soil-repellent finishing clothes need
The amount of asking constantly increases, and the fabric treated using finishing agent, can protect the user against splashing for water, oil, chemicals and pollutant
Infringement is echoed, there is protective, available for protective garments or work clothes etc. under the working environment for making high-quality, by people
Attention and have a good application prospect；The finishing agent function of using at present is relatively simple, and using effect is poor, it is necessary to enter
The improvement of one step, simple finishing agent can not meet that people's is required.
The content of the invention
It is an object of the invention to provide cotton noniron finish liquid, solve one or more in above-mentioned prior art problem.
According to an aspect of the present invention, cotton noniron finish liquid, the component of following parts by weight is included,
16~32 parts of ethylene glycol, 10~20 parts of melamine, 10~14 parts of formaldehyde resin, 2-hydroxyethyl methacry-late 6
~12 parts, 6~8 parts of methyl methacrylate, 4~6 parts of lauryl methacrylate, 2~6 parts of magnesium chloride, rosin glycerin ester resin 2
~4 parts, 10~20 parts of phosphotriester, 20~30 parts of lauryl methacrylate, 20~30 parts of zinc nitrate hexahydrate, benzoyl peroxide first
10~20 parts of acyl, 20~30 parts of poly divinyl acetylene, 10~16 parts of aphthenic acids, 200~300 parts of deionized water.
Cotton noniron finish liquid provided by the invention, make simply, the raw materials for production selection of use is avirulent, whole of this
Manage agent processing fabric can crease and shrink resistance, fixed effect is good, exempts to press, and has Water-proof and oil-proof, the spy such as well-pressed, plentiful, not dirty
Point.
Embodiment
Embodiment 1
By 16 parts of ethylene glycol, 10 parts of melamine, 10 parts of formaldehyde resin, 6 parts of 2-hydroxyethyl methacry-late, methyl-prop
6 parts of e pioic acid methyl ester, 4 parts of lauryl methacrylate, 2 parts of magnesium chloride, 2 parts of rosin glycerin ester resin, 10 parts of phosphotriester, methyl-prop
20 parts of olefin(e) acid lauryl, 20 parts of zinc nitrate hexahydrate, 10 parts of benzoyl peroxide, 20 parts of poly divinyl acetylene, 10 parts of aphthenic acids, go
200 parts of ionized water is put into reactor, is stirred continuously, and is heated to 60 DEG C after mixing completely, product is produced after uniform stirring.
Embodiment 2
By 24 parts of ethylene glycol, 15 parts of melamine, 12 parts of formaldehyde resin, 9 parts of 2-hydroxyethyl methacry-late, methyl-prop
7 parts of e pioic acid methyl ester, 5 parts of lauryl methacrylate, 4 parts of magnesium chloride, 3 parts of rosin glycerin ester resin, 15 parts of phosphotriester, methyl-prop
25 parts of olefin(e) acid lauryl, 25 parts of zinc nitrate hexahydrate, 15 parts of benzoyl peroxide, 25 parts of poly divinyl acetylene, 13 parts of aphthenic acids, go
250 parts of ionized water is put into reactor, is stirred continuously, and is heated to 60 DEG C after mixing completely, product is produced after uniform stirring.
Embodiment 3
By 32 parts of ethylene glycol, 20 parts of melamine, 14 parts of formaldehyde resin, 12 parts of 2-hydroxyethyl methacry-late, methyl-prop
8 parts of e pioic acid methyl ester, 6 parts of lauryl methacrylate, 6 parts of magnesium chloride, 4 parts of rosin glycerin ester resin, 20 parts of phosphotriester, methyl-prop
30 parts of olefin(e) acid lauryl, 30 parts of zinc nitrate hexahydrate, 20 parts of benzoyl peroxide, 30 parts of poly divinyl acetylene, 16 parts of aphthenic acids, go
300 parts of ionized water is put into reactor, is stirred continuously, and is heated to 60 DEG C after mixing completely, product is produced after uniform stirring.
Described above is only the preferred embodiment of the present invention, it is noted that to those skilled in the art, not
On the premise of departing from the invention design, some similar modification and improvement can also be made, these also should be regarded as the present invention
Protection domain within.
Claims (1)
1. cotton noniron finish liquid, it is characterised in that：Include the component of following parts by weight,
16~32 parts of ethylene glycol, 10~20 parts of melamine, 10~14 parts of formaldehyde resin, 2-hydroxyethyl methacry-late 6~12
Part, 6~8 parts of methyl methacrylate, 4~6 parts of lauryl methacrylate, 2~6 parts of magnesium chloride, rosin glycerin ester resin 2~4
Part, 10~20 parts of phosphotriester, 20~30 parts of lauryl methacrylate, 20~30 parts of zinc nitrate hexahydrate, benzoyl peroxide
10~20 parts, 20~30 parts of poly divinyl acetylene, 10~16 parts of aphthenic acids, 200~300 parts of deionized water.