CN106906656A - Terylene crease-resistant no-iron finishing agent - Google Patents

Terylene crease-resistant no-iron finishing agent Download PDF

Info

Publication number
CN106906656A
CN106906656A CN201610521141.7A CN201610521141A CN106906656A CN 106906656 A CN106906656 A CN 106906656A CN 201610521141 A CN201610521141 A CN 201610521141A CN 106906656 A CN106906656 A CN 106906656A
Authority
CN
China
Prior art keywords
parts
crease
finishing agent
terylene
resistant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610521141.7A
Other languages
Chinese (zh)
Inventor
陆海蓉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610521141.7A priority Critical patent/CN106906656A/en
Publication of CN106906656A publication Critical patent/CN106906656A/en
Pending legal-status Critical Current

Abstract

The invention discloses terylene crease-resistant no-iron finishing agent, including following weight portion component, 10~20 parts of polyurethane, 10~20 parts of acrylic acid, 10~20 parts of zinc nitrate, 6~12 parts of ammonium citrate, 20~30 parts of triethanolamine, 10~18 parts of magnesium chloride hexahydrate, 4~8 parts of rosin glycerin ester resin, 8~16 parts of poly divinyl acetylene, 10~18 parts of aphthenic acids, 2~8 parts of glacial acetic acid, 8~16 parts of acrylamide, 5~15 parts of vinyl chloride ethylene ester, 80~120 parts of deionized water.The terylene crease-resistant no-iron finishing agent that the present invention is provided, makes simple, and the raw materials for production selection of use is avirulent, the fabric processed with this finishing agent can crease and shrink resistance, fixed effect is good, exempts from flatiron, with it is well-pressed, plentiful, not dirty the features such as.

Description

Terylene crease-resistant no-iron finishing agent
Technical field
The present invention relates to a kind of finishing agent technical field, and in particular to a kind of terylene crease-resistant no-iron finishing agent.
Background technology
In recent years, with the improvement of people ' s living standards, under working environment with water repellent, refuse oil, soil-repellent finishing clothes need The amount of asking constantly increases, the fabric treated using finishing agent, can protect the user against splashing for water, oil, chemicals and pollutant Infringement is echoed, with protective, can be used for protective garments or work clothes etc. under the working environment of making high-quality, by people Attention and have a good application prospect；The finishing agent function of using at present is relatively simple, and using effect is poor, it is necessary to enter The improvement of one step, simple finishing agent can not meet the required of people.
The content of the invention
It is an object of the invention to provide terylene crease-resistant no-iron finishing agent, one in above-mentioned prior art problem or many is solved It is individual.
According to an aspect of the present invention, terylene crease-resistant no-iron finishing agent, including following weight portion component,
10~20 parts of polyurethane, 10~20 parts of acrylic acid, 10~20 parts of zinc nitrate, 6~12 parts of ammonium citrate, triethanolamine 20~30 parts, 10~18 parts of magnesium chloride hexahydrate, 4~8 parts of rosin glycerin ester resin, 8~16 parts of poly divinyl acetylene, aphthenic acids 10~ 18 parts, 2~8 parts of glacial acetic acid, 8~16 parts of acrylamide, 5~15 parts of vinyl chloride ethylene ester, 80~120 parts of deionized water.
The terylene crease-resistant no-iron finishing agent that the present invention is provided, makes simple, and the raw materials for production selection of use is avirulent, uses The fabric of this finishing agent treatment can crease and shrink resistance, fixed effect is good, exempts from flatiron, with Water-proof and oil-proof, well-pressed, plentiful, not dirty etc. Feature.
Specific embodiment
Embodiment 1
By 10 parts of polyurethane, 10 parts of acrylic acid, 10 parts of zinc nitrate, 6 parts of ammonium citrate, 20 parts of triethanolamine, six water chlorinations 10 parts of magnesium, 4 parts of rosin glycerin ester resin, 8 parts of poly divinyl acetylene, 10 parts of aphthenic acids, 2 parts of glacial acetic acid, 8 parts of acrylamide, chloroethene 5 parts of alkene vinyl acetate, 80 parts of deionized water is put into reactor, is stirred continuously, and 60 DEG C, after uniform stirring are heated to after mixing completely Obtain final product product.
Embodiment 2
By 15 parts of polyurethane, 15 parts of acrylic acid, 15 parts of zinc nitrate, 9 parts of ammonium citrate, 25 parts of triethanolamine, six water chlorinations 14 parts of magnesium, 6 parts of rosin glycerin ester resin, 12 parts of poly divinyl acetylene, 14 parts of aphthenic acids, 5 parts of glacial acetic acid, 12 parts of acrylamide, chlorine 10 parts of Ethylene Vinyl Ester, 100 parts of deionized water is put into reactor, is stirred continuously, and 60 DEG C are heated to after mixing completely, is uniformly stirred Product is obtained final product after mixing.
Embodiment 3
By 20 parts of polyurethane, 20 parts of acrylic acid, 20 parts of zinc nitrate, 12 parts of ammonium citrate, 30 parts of triethanolamine, six water chlorinations 18 parts of magnesium, 8 parts of rosin glycerin ester resin, 16 parts of poly divinyl acetylene, 18 parts of aphthenic acids, 8 parts of glacial acetic acid, 16 parts of acrylamide, chlorine 15 parts of Ethylene Vinyl Ester, 120 parts of deionized water is put into reactor, is stirred continuously, and 60 DEG C are heated to after mixing completely, is uniformly stirred Product is obtained final product after mixing.
The above is only preferred embodiment of the invention, it is noted that to those skilled in the art, not On the premise of departing from the invention design, some similar deformations and improvement can also be made, these also should be regarded as the present invention Protection domain within.

Claims (1)

1. terylene crease-resistant no-iron finishing agent, it is characterised in that：Component including following weight portion,
10~20 parts of polyurethane, 10~20 parts of acrylic acid, 10~20 parts of zinc nitrate, 6~12 parts of ammonium citrate, triethanolamine 20~ 30 parts, 10~18 parts of magnesium chloride hexahydrate, 4~8 parts of rosin glycerin ester resin, 8~16 parts of poly divinyl acetylene, aphthenic acids 10~18 Part, 2~8 parts of glacial acetic acid, 8~16 parts of acrylamide, 5~15 parts of vinyl chloride ethylene ester, 80~120 parts of deionized water.
CN201610521141.7A 2016-07-01 2016-07-01 Terylene crease-resistant no-iron finishing agent Pending CN106906656A (en)