CN106906666A - Terylene crease proofing agent - Google Patents

Terylene crease proofing agent Download PDF

Info

Publication number
CN106906666A
CN106906666A CN201610520970.3A CN201610520970A CN106906666A CN 106906666 A CN106906666 A CN 106906666A CN 201610520970 A CN201610520970 A CN 201610520970A CN 106906666 A CN106906666 A CN 106906666A
Authority
CN
China
Prior art keywords
parts
terylene
proofing agent
crease
crease proofing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610520970.3A
Other languages
Chinese (zh)
Inventor
陶洪燕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610520970.3A priority Critical patent/CN106906666A/en
Publication of CN106906666A publication Critical patent/CN106906666A/en
Pending legal-status Critical Current

Abstract

The invention discloses terylene crease proofing agent, component including following weight portion, 60~80 parts of dihydroxymethyl carbamide resin, 10~20 parts of polyurethane, 10~30 parts of stearic acid, ethylene glycol presses 8~12 parts, 10~20 parts of zinc nitrate, 6~12 parts of ammonium citrate, 20~30 parts of triethanolamine, 10~18 parts of magnesium chloride hexahydrate, 4~8 parts of rosin glycerin ester resin, 8~16 parts of poly divinyl acetylene, 10~18 parts of aphthenic acids, 2~8 parts of glacial acetic acid, 8~16 parts of acrylamide, 5~15 parts of vinyl chloride ethylene ester, 80~120 parts of deionized water.The terylene crease proofing agent that the present invention is provided, makes simple, and the raw materials for production selection of use is avirulent, the fabric processed with this finishing agent can crease and shrink resistance, fixed effect is good, exempts from flatiron, with it is well-pressed, plentiful, not dirty the features such as.

Description

Terylene crease proofing agent
Technical field
The present invention relates to a kind of finishing agent technical field, and in particular to a kind of terylene crease proofing agent.
Background technology
In recent years, with the improvement of people ' s living standards, under working environment with water repellent, refuse oil, soil-repellent finishing clothes need The amount of asking constantly increases, the fabric treated using finishing agent, can protect the user against splashing for water, oil, chemicals and pollutant Infringement is echoed, with protective, can be used for protective garments or work clothes etc. under the working environment of making high-quality, by people Attention and have a good application prospect；The finishing agent function of using at present is relatively simple, and using effect is poor, it is necessary to enter The improvement of one step, simple finishing agent can not meet the required of people.
The content of the invention
It is an object of the invention to provide terylene crease proofing agent, one or more in above-mentioned prior art problem is solved.
According to an aspect of the present invention, terylene crease proofing agent, including following weight portion component,
60~80 parts of dihydroxymethyl carbamide resin, 10~20 parts of polyurethane, 10~30 parts of stearic acid, ethylene glycol presses 8~12 parts, 10~20 parts of zinc nitrate, 6~12 parts of ammonium citrate, 20~30 parts of triethanolamine, 10~18 parts of magnesium chloride hexahydrate, rosin glycerin ester tree 4~8 parts of fat, 8~16 parts of poly divinyl acetylene, 10~18 parts of aphthenic acids, 2~8 parts of glacial acetic acid, 8~16 parts of acrylamide, chloroethene 5~15 parts of alkene vinyl acetate, 80~120 parts of deionized water.
The terylene crease proofing agent that the present invention is provided, makes simple, and the raw materials for production selection of use is avirulent, whole with this The fabric of reason agent treatment can crease and shrink resistance, fixed effect is good, exempts from flatiron, with the spy such as Water-proof and oil-proof, well-pressed, plentiful, not dirty Point.
Specific embodiment
Embodiment 1
60 parts of dihydroxymethyl carbamide resin, 10 parts of polyurethane, 10 parts of stearic acid, ethylene glycol are pressed into 8 parts, 10 parts of zinc nitrate, lemon Lemon 6 parts of ammonium of acid, 20 parts of triethanolamine, 10 parts of magnesium chloride hexahydrate, 4 parts of rosin glycerin ester resin, 8 parts of poly divinyl acetylene, aphthenic acids 10 parts, 2 parts of glacial acetic acid, 8 parts of acrylamide, 5 parts of vinyl chloride ethylene ester, 80 parts of deionized water is put into reactor, is stirred continuously, 60 DEG C are heated to after mixing completely, product is obtained final product after uniform stirring.
Embodiment 2
70 parts of dihydroxymethyl carbamide resin, 15 parts of polyurethane, 20 parts of stearic acid, ethylene glycol are pressed into 10 parts, 15 parts of zinc nitrate, lemon Lemon 9 parts of ammonium of acid, 25 parts of triethanolamine, 14 parts of magnesium chloride hexahydrate, 6 parts of rosin glycerin ester resin, 12 parts of poly divinyl acetylene, aphthenic acids 14 parts, 5 parts of glacial acetic acid, 12 parts of acrylamide, 10 parts of vinyl chloride ethylene ester, 100 parts of deionized water is put into reactor, is constantly stirred Mix, 60 DEG C are heated to after mixing completely, product is obtained final product after uniform stirring.
Embodiment 3
80 parts of dihydroxymethyl carbamide resin, 20 parts of polyurethane, 30 parts of stearic acid, ethylene glycol are pressed into 12 parts, 20 parts of zinc nitrate, lemon Lemon 12 parts of ammonium of acid, 30 parts of triethanolamine, 18 parts of magnesium chloride hexahydrate, 8 parts of rosin glycerin ester resin, 16 parts of poly divinyl acetylene, cycloalkanes 18 parts of acid, 8 parts of glacial acetic acid, 16 parts of acrylamide, 15 parts of vinyl chloride ethylene ester, 120 parts of deionized water is put into reactor, constantly Stirring, 60 DEG C are heated to after mixing completely, and product is obtained final product after uniform stirring.
The above is only preferred embodiment of the invention, it is noted that to those skilled in the art, not On the premise of departing from the invention design, some similar deformations and improvement can also be made, these also should be regarded as the present invention Protection domain within.

Claims (1)

1. terylene crease proofing agent, it is characterised in that：Component including following weight portion,
60~80 parts of dihydroxymethyl carbamide resin, 10~20 parts of polyurethane, 10~30 parts of stearic acid, ethylene glycol presses 8~12 parts, nitric acid 10~20 parts of zinc, 6~12 parts of ammonium citrate, 20~30 parts of triethanolamine, 10~18 parts of magnesium chloride hexahydrate, rosin glycerin ester resin 4 ~8 parts, 8~16 parts of poly divinyl acetylene, 10~18 parts of aphthenic acids, 2~8 parts of glacial acetic acid, 8~16 parts of acrylamide, vinyl chloride 5~15 parts of vinyl acetate, 80~120 parts of deionized water.
CN201610520970.3A 2016-07-01 2016-07-01 Terylene crease proofing agent Pending CN106906666A (en)