CN104294587A - Crease-resist resin finishing agent for cotton cloth - Google Patents
Crease-resist resin finishing agent for cotton cloth Download PDFInfo
- Publication number
- CN104294587A CN104294587A CN201410552590.9A CN201410552590A CN104294587A CN 104294587 A CN104294587 A CN 104294587A CN 201410552590 A CN201410552590 A CN 201410552590A CN 104294587 A CN104294587 A CN 104294587A
- Authority
- CN
- China
- Prior art keywords
- parts
- finishing agent
- resin finishing
- resistant resin
- crease
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a crease-resistant resin finishing agent for cotton cloth. The crease-resistant resin finishing agent comprises the following components in parts by weight: 2-3 parts of block polyoxyethylene-polyoxypropylene, 4-5 parts of nonylphenol ethoxylate carboxylate, 5-6 parts of glycerin monostearate, 1-2 parts of thiourea, 4-5 parts of formic acid, 1-2 parts of potassium hydroxide, 2-3 parts of antimonous oxide, 3-4 parts of triethanolamine oleic soap, 2-3 parts of phosphate, 2-3 parts of sodium polyacrylate and 2-3 parts of a penetrating agent JFC. The crease-resistant resin finishing agent for the cotton cloth has minimal effect on the strength of fabrics, and the fabrics do not deform after being shaped.
Description
Technical field
The present invention relates to the wrinkle resistant resin finishing agent for cotton.
Background technology
For a long time, after the drying of plant lamp draining, form local deformation, have a strong impact on and block up, cause water stain spot etc. on the surface of fabric due to the difference of light reflection.
Summary of the invention
The object of the present invention is to provide a kind of wrinkle resistant resin finishing agent for cotton, it is minimum on fabric intensity impact, once sizing, can not reverse.
For achieving the above object, technical scheme of the present invention is a kind of wrinkle resistant resin finishing agent for cotton of design, consists of the following composition by weight:
2 ~ 3 parts of Block polyoxyethylene-polyethenoxy ethers,
4 ~ 5 parts of nonylphenol ethoxylate carboxylates,
5 ~ 6 parts of glycerin monostearates,
1 ~ 2 part of thiocarbamide,
4 ~ 5 parts of formic acid,
1 ~ 2 part of potassium hydroxide,
2 ~ 3 parts of antimonous oxides,
3 ~ 4 parts of trihydroxy ethylamine oleate soaps,
2 ~ 3 parts of phosphates,
2 ~ 3 parts of Sodium Polyacrylates,
2 ~ 3 parts of penetrating agent JFCs.
Preferably, for the wrinkle resistant resin finishing agent of cotton, consist of the following composition by weight:
3 parts of Block polyoxyethylene-polyethenoxy ethers,
5 parts of nonylphenol ethoxylate carboxylates,
6 parts of glycerin monostearates,
2 parts of thiocarbamides,
5 parts of formic acid,
2 parts of potassium hydroxide,
3 parts of antimonous oxides,
4 parts of trihydroxy ethylamine oleate soaps,
3 parts of phosphates,
3 parts of Sodium Polyacrylates,
3 parts of penetrating agent JFCs.
Preferably, for the wrinkle resistant resin finishing agent of cotton, consist of the following composition by weight:
2 parts of Block polyoxyethylene-polyethenoxy ethers,
4 parts of nonylphenol ethoxylate carboxylates,
5 parts of glycerin monostearates,
1 part of thiocarbamide,
4 parts of formic acid,
1 part of potassium hydroxide,
2 parts of antimonous oxides,
3 parts of trihydroxy ethylamine oleate soaps,
2 parts of phosphates,
2 parts of Sodium Polyacrylates,
2 parts of penetrating agent JFCs.
Preferably, for the wrinkle resistant resin finishing agent of cotton, consist of the following composition by weight:
2.3 parts of Block polyoxyethylene-polyethenoxy ethers,
4.5 parts of nonylphenol ethoxylate carboxylates,
5.6 parts of glycerin monostearates,
1.2 parts of thiocarbamides,
4.5 parts of formic acid,
1.2 parts of potassium hydroxide,
2.3 parts of antimonous oxides,
3.4 parts of trihydroxy ethylamine oleate soaps,
2.3 parts of phosphates,
2.3 parts of Sodium Polyacrylates,
2.3 parts of penetrating agent JFCs.
Advantage of the present invention and beneficial effect are: provide a kind of wrinkle resistant resin finishing agent for cotton, and it is minimum on fabric intensity impact, once sizing, can not reverse.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
For the wrinkle resistant resin finishing agent of cotton, consist of the following composition by weight:
3 parts of Block polyoxyethylene-polyethenoxy ethers,
5 parts of nonylphenol ethoxylate carboxylates,
6 parts of glycerin monostearates,
2 parts of thiocarbamides,
5 parts of formic acid,
2 parts of potassium hydroxide,
3 parts of antimonous oxides,
4 parts of trihydroxy ethylamine oleate soaps,
3 parts of phosphates,
3 parts of Sodium Polyacrylates,
3 parts of penetrating agent JFCs.
Embodiment 2
For the wrinkle resistant resin finishing agent of cotton, consist of the following composition by weight:
2 parts of Block polyoxyethylene-polyethenoxy ethers,
4 parts of nonylphenol ethoxylate carboxylates,
5 parts of glycerin monostearates,
1 part of thiocarbamide,
4 parts of formic acid,
1 part of potassium hydroxide,
2 parts of antimonous oxides,
3 parts of trihydroxy ethylamine oleate soaps,
2 parts of phosphates,
2 parts of Sodium Polyacrylates,
2 parts of penetrating agent JFCs.
Embodiment 3
For the wrinkle resistant resin finishing agent of cotton, consist of the following composition by weight:
2.3 parts of Block polyoxyethylene-polyethenoxy ethers,
4.5 parts of nonylphenol ethoxylate carboxylates,
5.6 parts of glycerin monostearates,
1.2 parts of thiocarbamides,
4.5 parts of formic acid,
1.2 parts of potassium hydroxide,
2.3 parts of antimonous oxides,
3.4 parts of trihydroxy ethylamine oleate soaps,
2.3 parts of phosphates,
2.3 parts of Sodium Polyacrylates,
2.3 parts of penetrating agent JFCs.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1., for the wrinkle resistant resin finishing agent of cotton, it is characterized in that, consist of the following composition by weight:
2 ~ 3 parts of Block polyoxyethylene-polyethenoxy ethers,
4 ~ 5 parts of nonylphenol ethoxylate carboxylates,
5 ~ 6 parts of glycerin monostearates,
1 ~ 2 part of thiocarbamide,
4 ~ 5 parts of formic acid,
1 ~ 2 part of potassium hydroxide,
2 ~ 3 parts of antimonous oxides,
3 ~ 4 parts of trihydroxy ethylamine oleate soaps,
2 ~ 3 parts of phosphates,
2 ~ 3 parts of Sodium Polyacrylates,
2 ~ 3 parts of penetrating agent JFCs.
2. the wrinkle resistant resin finishing agent for cotton according to claim 1, is characterized in that, consist of the following composition by weight:
3 parts of Block polyoxyethylene-polyethenoxy ethers,
5 parts of nonylphenol ethoxylate carboxylates,
6 parts of glycerin monostearates,
2 parts of thiocarbamides,
5 parts of formic acid,
2 parts of potassium hydroxide,
3 parts of antimonous oxides,
4 parts of trihydroxy ethylamine oleate soaps,
3 parts of phosphates,
3 parts of Sodium Polyacrylates,
3 parts of penetrating agent JFCs.
3. the wrinkle resistant resin finishing agent for cotton according to claim 1, is characterized in that, consist of the following composition by weight:
2 parts of Block polyoxyethylene-polyethenoxy ethers,
4 parts of nonylphenol ethoxylate carboxylates,
5 parts of glycerin monostearates,
1 part of thiocarbamide,
4 parts of formic acid,
1 part of potassium hydroxide,
2 parts of antimonous oxides,
3 parts of trihydroxy ethylamine oleate soaps,
2 parts of phosphates,
2 parts of Sodium Polyacrylates,
2 parts of penetrating agent JFCs.
4. the wrinkle resistant resin finishing agent for cotton according to claim 1, is characterized in that, consist of the following composition by weight:
2.3 parts of Block polyoxyethylene-polyethenoxy ethers,
4.5 parts of nonylphenol ethoxylate carboxylates,
5.6 parts of glycerin monostearates,
1.2 parts of thiocarbamides,
4.5 parts of formic acid,
1.2 parts of potassium hydroxide,
2.3 parts of antimonous oxides,
3.4 parts of trihydroxy ethylamine oleate soaps,
2.3 parts of phosphates,
2.3 parts of Sodium Polyacrylates,
2.3 parts of penetrating agent JFCs.