CN105421072A - Dyeing and finishing process of polar fleece - Google Patents
Dyeing and finishing process of polar fleece Download PDFInfo
- Publication number
- CN105421072A CN105421072A CN201510966052.9A CN201510966052A CN105421072A CN 105421072 A CN105421072 A CN 105421072A CN 201510966052 A CN201510966052 A CN 201510966052A CN 105421072 A CN105421072 A CN 105421072A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- weight
- parts
- dyeing
- finishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a dyeing and finishing process of polar fleece, comprising the following steps: (1) pretreating; (2) dyeing; (3) finishing: putting 1-2 parts by weight of block polyoxyethylene-polyoxyethylene ether, 1.1 parts by weight of sodium hexametaphosphate, 0.4 part by weight of calcium propionate and 0.2 part by weight of zeolite powder into 19.2 parts by mass of deionized water in sequence, and stirring evenly; then simultaneously putting 0.7 part by weight of plifenate, 0.7 part by weight of zinc acetate, 0.3 part by weight of N,N-nickel dibutyl dithiocarbamate and 1.4 parts by weight of 1,3-propane diamine, and continuously stirring until mixing sufficiently evenly, thus obtaining finishing liquid; then padding cloth in the finishing liquid, taking out, and drying at constant temperature. By adopting the dyeing and finishing process of the polar fleece, the cloth subjected to dyeing and finishing has excellent mould proof, mothproof, antibacterial, antiflaming and antistatic properties, and is strong in washability and soft in handfeel.
Description
Technical field
The present invention relates to the dyeing and finishing technology of polar fleece.
Background technology
The mildew-resistant of existing cloth, mothproof, antibacterial, fire-retardant, antistatic, washing fastness all have much room for improvement, and feel is soft not.
Summary of the invention
The object of the present invention is to provide a kind of dyeing and finishing technology of polar fleece, the cloth after its dyeing and finishing has excellent mildew-resistant, mothproof, antibacterial, fire-retardant, antistatic property, and washability is strong, soft.
For achieving the above object, technical scheme of the present invention designs a kind of dyeing and finishing technology of polar fleece, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 ~ 2 weight parts of block polyoxyethylene polyoxypropylene ether, 1.1 weight portion calgons, 0.4 weight portion calcium propionate, 0.2 weight portion zeolite powder are dropped in 19.2 parts by mass deionized waters successively, stirs; Drop into 0.7 weight portion benzethazet acetofenate, 0.7 weight portion zinc acetate, 0.3 weight portion N again, N-second, n-butyl dithiocarbamate nickel, 1.4 weight portions 1,3-the third two, continue to stir simultaneously, to fully mixing, and obtained dressing liquid; Again cloth is padded process in dressing liquid, constant temperature drying after taking out.
Preferably, the dyeing and finishing technology of polar fleece, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 weight parts of block polyoxyethylene polyoxypropylene ether, 1.1 weight portion calgons, 0.4 weight portion calcium propionate, 0.2 weight portion zeolite powder are dropped in 19.2 parts by mass deionized waters successively, stirs; Drop into 0.7 weight portion benzethazet acetofenate, 0.7 weight portion zinc acetate, 0.3 weight portion N again, N-second, n-butyl dithiocarbamate nickel, 1.4 weight portions 1,3-the third two, continue to stir simultaneously, to fully mixing, and obtained dressing liquid; Again cloth is padded process in dressing liquid, constant temperature drying after taking out.
Preferably, the dyeing and finishing technology of polar fleece, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 2 weight parts of block polyoxyethylene polyoxypropylene ethers, 1.1 weight portion calgons, 0.4 weight portion calcium propionate, 0.2 weight portion zeolite powder are dropped in 19.2 parts by mass deionized waters successively, stirs; Drop into 0.7 weight portion benzethazet acetofenate, 0.7 weight portion zinc acetate, 0.3 weight portion N again, N-second, n-butyl dithiocarbamate nickel, 1.4 weight portions 1,3-the third two, continue to stir simultaneously, to fully mixing, and obtained dressing liquid; Again cloth is padded process in dressing liquid, constant temperature drying after taking out.
Advantage of the present invention and beneficial effect are: the dyeing and finishing technology providing a kind of polar fleece, and the cloth after its dyeing and finishing has excellent mildew-resistant, mothproof, antibacterial, fire-retardant, antistatic property, and washability is strong, soft.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A dyeing and finishing technology for polar fleece, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 ~ 2 weight parts of block polyoxyethylene polyoxypropylene ether, 1.1 weight portion calgons, 0.4 weight portion calcium propionate, 0.2 weight portion zeolite powder are dropped in 19.2 parts by mass deionized waters successively, stirs; Drop into 0.7 weight portion benzethazet acetofenate, 0.7 weight portion zinc acetate, 0.3 weight portion N again, N-second, n-butyl dithiocarbamate nickel, 1.4 weight portions 1,3-the third two, continue to stir simultaneously, to fully mixing, and obtained dressing liquid; Again cloth is padded process in dressing liquid, constant temperature drying after taking out.
Embodiment 2
The dyeing and finishing technology of polar fleece, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 weight parts of block polyoxyethylene polyoxypropylene ether, 1.1 weight portion calgons, 0.4 weight portion calcium propionate, 0.2 weight portion zeolite powder are dropped in 19.2 parts by mass deionized waters successively, stirs; Drop into 0.7 weight portion benzethazet acetofenate, 0.7 weight portion zinc acetate, 0.3 weight portion N again, N-second, n-butyl dithiocarbamate nickel, 1.4 weight portions 1,3-the third two, continue to stir simultaneously, to fully mixing, and obtained dressing liquid; Again cloth is padded process in dressing liquid, constant temperature drying after taking out.
Embodiment 3
The dyeing and finishing technology of polar fleece, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 2 weight parts of block polyoxyethylene polyoxypropylene ethers, 1.1 weight portion calgons, 0.4 weight portion calcium propionate, 0.2 weight portion zeolite powder are dropped in 19.2 parts by mass deionized waters successively, stirs; Drop into 0.7 weight portion benzethazet acetofenate, 0.7 weight portion zinc acetate, 0.3 weight portion N again, N-second, n-butyl dithiocarbamate nickel, 1.4 weight portions 1,3-the third two, continue to stir simultaneously, to fully mixing, and obtained dressing liquid; Again cloth is padded process in dressing liquid, constant temperature drying after taking out.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. the dyeing and finishing technology of polar fleece, is characterized in that, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 ~ 2 weight parts of block polyoxyethylene polyoxypropylene ether, 1.1 weight portion calgons, 0.4 weight portion calcium propionate, 0.2 weight portion zeolite powder are dropped in 19.2 parts by mass deionized waters successively, stirs; Drop into 0.7 weight portion benzethazet acetofenate, 0.7 weight portion zinc acetate, 0.3 weight portion N again, N-second, n-butyl dithiocarbamate nickel, 1.4 weight portions 1,3-the third two, continue to stir simultaneously, to fully mixing, and obtained dressing liquid; Again cloth is padded process in dressing liquid, constant temperature drying after taking out.
2. the dyeing and finishing technology of polar fleece according to claim 1, is characterized in that, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 1 weight parts of block polyoxyethylene polyoxypropylene ether, 1.1 weight portion calgons, 0.4 weight portion calcium propionate, 0.2 weight portion zeolite powder are dropped in 19.2 parts by mass deionized waters successively, stirs; Drop into 0.7 weight portion benzethazet acetofenate, 0.7 weight portion zinc acetate, 0.3 weight portion N again, N-second, n-butyl dithiocarbamate nickel, 1.4 weight portions 1,3-the third two, continue to stir simultaneously, to fully mixing, and obtained dressing liquid; Again cloth is padded process in dressing liquid, constant temperature drying after taking out.
3. the dyeing and finishing technology of polar fleece according to claim 1, is characterized in that, comprises the steps:
1) preliminary treatment;
2) dye;
3) arrange: 2 weight parts of block polyoxyethylene polyoxypropylene ethers, 1.1 weight portion calgons, 0.4 weight portion calcium propionate, 0.2 weight portion zeolite powder are dropped in 19.2 parts by mass deionized waters successively, stirs; Drop into 0.7 weight portion benzethazet acetofenate, 0.7 weight portion zinc acetate, 0.3 weight portion N again, N-second, n-butyl dithiocarbamate nickel, 1.4 weight portions 1,3-the third two, continue to stir simultaneously, to fully mixing, and obtained dressing liquid; Again cloth is padded process in dressing liquid, constant temperature drying after taking out.