CN104452267A - Finishing process of knitted fabric - Google Patents

Abstract

The invention discloses a finishing process of a knitted fabric. The finishing process comprises the following steps: (1) putting 2.1 parts by mass of magnesium chloride hexahydrate, 1.2 parts by mass of potassium oxalate and 3.4 parts by mass of sodium hydroxide into 12.6 parts by mass of deionized water and stirring uniformly; (2) sequentially adding 1.7 parts by mass of solid nano titanium dioxide and 2.8 parts by mass of sodium tripolyphosphate and further stirring until the components are mixed uniformly so as to obtain finishing liquid; and (3) padding the fabric in the finishing liquid and drying at a constant temperature. According to the finishing process of the knitted fabric, the finished fabric is washable and has the excellent anti-wrinkle property and antibacterial property.

Description

The finishing technique of knit fabric

Technical field

The present invention relates to the finishing technique of knit fabric.

Background technology

The wash durability of existing fabric, wrinkle resistance and anti-microbial property all have much room for improvement.

Summary of the invention

The object of the present invention is to provide a kind of finishing technique of knit fabric, the fabric after its arrangement is water-fastness, and has excellent wrinkle resistance and anti-microbial property.

For achieving the above object, technical scheme of the present invention designs a kind of finishing technique of knit fabric, comprises the steps:

1) 2.1 parts by mass magnesium chloride hexahydrates, 1.2 parts by mass potassium oxalates, 3.4 parts by mass NaOH are dropped in 12.6 parts by mass deionized waters, stir;

2) add 1.7 parts by mass solid nano titanium dioxide, 2.8 parts by mass sodium phosphate trimers more successively, continue to stir, to fully mixing, obtained dressing liquid;

3) fabric is padded process in dressing liquid, constant temperature drying.

Advantage of the present invention and beneficial effect are: the finishing technique providing a kind of knit fabric, and the fabric after its arrangement is water-fastness, and has excellent wrinkle resistance and anti-microbial property.

Detailed description of the invention

Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.

The technical scheme that the present invention specifically implements is:

A finishing technique for knit fabric, comprises the steps:

1) 2.1 parts by mass magnesium chloride hexahydrates, 1.2 parts by mass potassium oxalates, 3.4 parts by mass NaOH are dropped in 12.6 parts by mass deionized waters, stir;

2) add 1.7 parts by mass solid nano titanium dioxide, 2.8 parts by mass sodium phosphate trimers more successively, continue to stir, to fully mixing, obtained dressing liquid;

3) fabric is padded process in dressing liquid, constant temperature drying.

The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.

Claims (1)

1. the finishing technique of knit fabric, is characterized in that, comprises the steps:

1) 2.1 parts by mass magnesium chloride hexahydrates, 1.2 parts by mass potassium oxalates, 3.4 parts by mass NaOH are dropped in 12.6 parts by mass deionized waters, stir;

2) add 1.7 parts by mass solid nano titanium dioxide, 2.8 parts by mass sodium phosphate trimers more successively, continue to stir, to fully mixing, obtained dressing liquid;

3) fabric is padded process in dressing liquid, constant temperature drying.