CN105297418A - Processing technique of plush fabric - Google Patents
Processing technique of plush fabric Download PDFInfo
- Publication number
- CN105297418A CN105297418A CN201510863227.3A CN201510863227A CN105297418A CN 105297418 A CN105297418 A CN 105297418A CN 201510863227 A CN201510863227 A CN 201510863227A CN 105297418 A CN105297418 A CN 105297418A
- Authority
- CN
- China
- Prior art keywords
- parts
- mass
- fabric
- stir
- finishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a processing technique of a plush fabric. The technique comprises a finishing process. The finishing process comprises the following steps: (1) adding 1-2 parts by mass of butyl acrylate, 1.8 parts by mass of octadecyl trimethyl ammonium chloride and 2.3 parts by mass of potassium oxalate into 15.6 parts by mass of deionized water, mixing, and stirring uniformly; (2) simultaneously and slowly adding 0.7 parts by mass of bock greenbrier rhizome extract and 1.6 parts by mass of cetyl stearyl alcohol, and continuously stirring till fully and uniformly mixing, thus preparing a finishing agent; (3) padding the fabric in the maceration extract containing the finishing agent, and drying at a constant temperature. According to the processing technique of the plush fabric, the finished fabric has excellent antibacterial performance, high antifouling property and high washing resistance.
Description
Technical field
The present invention relates to the processing technology of cashmere shell-fabric.
Background technology
The anti-microbial property of existing fabric, antifouling property and washing fastness all have much room for improvement.
Summary of the invention
The object of the present invention is to provide a kind of processing technology of cashmere shell-fabric, the fabric after its arrangement has excellent anti-microbial property, antifouling property, and washability is strong.
For achieving the above object, technical scheme of the present invention designs a kind of processing technology of cashmere shell-fabric, and comprise finishing technique, this finishing technique comprises the steps:
1) in 15.6 parts by mass deionized waters, drop into 1 ~ 2 parts by mass butyl acrylate, 1.8 parts by mass octadecyl trimethyl ammonium chloride, 2.3 parts by mass potassium oxalate mixing, stir;
2) slowly add 0.7 parts by mass diamond vine extract, 1.6 parts by mass cetyl stearyl alcohols more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Preferably, the processing technology of cashmere shell-fabric, comprises finishing technique, and this finishing technique comprises the steps:
1) in 15.6 parts by mass deionized waters, drop into 1 parts by mass butyl acrylate, 1.8 parts by mass octadecyl trimethyl ammonium chloride, 2.3 parts by mass potassium oxalate mixing, stir;
2) slowly add 0.7 parts by mass diamond vine extract, 1.6 parts by mass cetyl stearyl alcohols more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Preferably, the processing technology of cashmere shell-fabric, comprises finishing technique, and this finishing technique comprises the steps:
1) in 15.6 parts by mass deionized waters, drop into 2 parts by mass butyl acrylates, 1.8 parts by mass octadecyl trimethyl ammonium chloride, 2.3 parts by mass potassium oxalate mixing, stir;
2) slowly add 0.7 parts by mass diamond vine extract, 1.6 parts by mass cetyl stearyl alcohols more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Advantage of the present invention and beneficial effect are: the processing technology providing a kind of cashmere shell-fabric, and the fabric after its arrangement has excellent anti-microbial property, antifouling property, and washability is strong.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
A processing technology for cashmere shell-fabric, comprises finishing technique, and this finishing technique comprises the steps:
1) in 15.6 parts by mass deionized waters, drop into 1 ~ 2 parts by mass butyl acrylate, 1.8 parts by mass octadecyl trimethyl ammonium chloride, 2.3 parts by mass potassium oxalate mixing, stir;
2) slowly add 0.7 parts by mass diamond vine extract, 1.6 parts by mass cetyl stearyl alcohols more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Embodiment 2
The processing technology of cashmere shell-fabric, comprises finishing technique, and this finishing technique comprises the steps:
1) in 15.6 parts by mass deionized waters, drop into 1 parts by mass butyl acrylate, 1.8 parts by mass octadecyl trimethyl ammonium chloride, 2.3 parts by mass potassium oxalate mixing, stir;
2) slowly add 0.7 parts by mass diamond vine extract, 1.6 parts by mass cetyl stearyl alcohols more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.
Embodiment 3
The processing technology of cashmere shell-fabric, comprises finishing technique, and this finishing technique comprises the steps:
1) in 15.6 parts by mass deionized waters, drop into 2 parts by mass butyl acrylates, 1.8 parts by mass octadecyl trimethyl ammonium chloride, 2.3 parts by mass potassium oxalate mixing, stir;
2) slowly add 0.7 parts by mass diamond vine extract, 1.6 parts by mass cetyl stearyl alcohols more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. the processing technology of cashmere shell-fabric, is characterized in that, comprises finishing technique, and this finishing technique comprises the steps:
1) in 15.6 parts by mass deionized waters, drop into 1 ~ 2 parts by mass butyl acrylate, 1.8 parts by mass octadecyl trimethyl ammonium chloride, 2.3 parts by mass potassium oxalate mixing, stir;
2) slowly add 0.7 parts by mass diamond vine extract, 1.6 parts by mass cetyl stearyl alcohols more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.
2. the processing technology of cashmere shell-fabric according to claim 1, is characterized in that, comprises finishing technique, and this finishing technique comprises the steps:
1) in 15.6 parts by mass deionized waters, drop into 1 parts by mass butyl acrylate, 1.8 parts by mass octadecyl trimethyl ammonium chloride, 2.3 parts by mass potassium oxalate mixing, stir;
2) slowly add 0.7 parts by mass diamond vine extract, 1.6 parts by mass cetyl stearyl alcohols more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.
3. the processing technology of cashmere shell-fabric according to claim 1, is characterized in that, comprises finishing technique, and this finishing technique comprises the steps:
1) in 15.6 parts by mass deionized waters, drop into 2 parts by mass butyl acrylates, 1.8 parts by mass octadecyl trimethyl ammonium chloride, 2.3 parts by mass potassium oxalate mixing, stir;
2) slowly add 0.7 parts by mass diamond vine extract, 1.6 parts by mass cetyl stearyl alcohols more simultaneously, continue to stir, to fully mixing, obtained finishing agent;
3) fabric is padded process in containing the maceration extract of finishing agent, constant temperature drying.