CN106906650A - Blend fabric wash and wear finisher - Google Patents
Blend fabric wash and wear finisher Download PDFInfo
- Publication number
- CN106906650A CN106906650A CN201610516267.5A CN201610516267A CN106906650A CN 106906650 A CN106906650 A CN 106906650A CN 201610516267 A CN201610516267 A CN 201610516267A CN 106906650 A CN106906650 A CN 106906650A
- Authority
- CN
- China
- Prior art keywords
- parts
- ammonium citrate
- blend fabric
- wear finisher
- fabric wash
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses blend fabric wash and wear finisher, component including following weight portion, 30~50 parts of dihydroxymethyl dihydroxy oxazoline ketone, 10~20 parts of acrylic acid, 6~12 parts of ammonium citrate, 20~30 parts of triethanolamine, 10~20 parts of sodium hypophosphite, 10~18 parts of magnesium chloride hexahydrate, 4~8 parts of rosin glycerin ester resin, 8~16 parts of poly divinyl acetylene, 10~18 parts of aphthenic acids, 4~12 parts of ammonium citrate, 2~8 parts of glacial acetic acid, 8~16 parts of acrylamide, 5~15 parts of vinyl chloride ethylene ester, 80~120 parts of deionized water.The blend fabric wash and wear finisher that the present invention is provided, makes simple, and the raw materials for production selection of use is avirulent, the fabric processed with this finishing agent can crease and shrink resistance, fixed effect is good, exempts from flatiron, with it is well-pressed, plentiful, not dirty the features such as.
Description
Technical field
The present invention relates to a kind of finishing agent technical field, and in particular to a kind of blend fabric wash and wear finisher.
Background technology
In recent years, with the improvement of people ' s living standards, under working environment with water repellent, refuse oil, soil-repellent finishing clothes need
The amount of asking constantly increases, the fabric treated using finishing agent, can protect the user against splashing for water, oil, chemicals and pollutant
Infringement is echoed, with protective, can be used for protective garments or work clothes etc. under the working environment of making high-quality, by people
Attention and have a good application prospect;The finishing agent function of using at present is relatively simple, and using effect is poor, it is necessary to enter
The improvement of one step, simple finishing agent can not meet the required of people.
The content of the invention
It is an object of the invention to provide blend fabric wash and wear finisher, one in above-mentioned prior art problem or many is solved
It is individual.
According to an aspect of the present invention, blend fabric wash and wear finisher, including following weight portion component,
30~50 parts of dihydroxymethyl dihydroxy oxazoline ketone, 10~20 parts of acrylic acid, 6~12 parts of ammonium citrate, triethanolamine
20~30 parts, 10~20 parts of sodium hypophosphite, 10~18 parts of magnesium chloride hexahydrate, 4~8 parts of rosin glycerin ester resin, poly divinyl acetylene 8
~16 parts, 10~18 parts of aphthenic acids, 4~12 parts of ammonium citrate, 2~8 parts of glacial acetic acid, 8~16 parts of acrylamide, vinyl chloride ethylene
5~15 parts of ester, 80~120 parts of deionized water.
The blend fabric wash and wear finisher that the present invention is provided, makes simple, and the raw materials for production selection of use is avirulent, uses
The fabric of this finishing agent treatment can crease and shrink resistance, fixed effect is good, exempts from flatiron, with Water-proof and oil-proof, well-pressed, plentiful, not dirty etc.
Feature.
Specific embodiment
Embodiment 1
By 30 parts of dihydroxymethyl dihydroxy oxazoline ketone, 10 parts of acrylic acid, 6 parts of ammonium citrate, 20 parts of triethanolamine, hypophosphorous acid
10 parts of sodium, 10 parts of magnesium chloride hexahydrate, 4 parts of rosin glycerin ester resin, 8 parts of poly divinyl acetylene, 10 parts of aphthenic acids, 4 parts of ammonium citrate,
2 parts of glacial acetic acid, 8 parts of acrylamide, 5 parts of vinyl chloride ethylene ester, 80 parts of deionized water is put into reactor, is stirred continuously, mixing
60 DEG C are heated to after completely, product is obtained final product after uniform stirring.
Embodiment 2
By 40 parts of dihydroxymethyl dihydroxy oxazoline ketone, 15 parts of acrylic acid, 9 parts of ammonium citrate, 25 parts of triethanolamine, hypophosphorous acid
15 parts of sodium, 14 parts of magnesium chloride hexahydrate, 6 parts of rosin glycerin ester resin, 12 parts of poly divinyl acetylene, 14 parts of aphthenic acids, ammonium citrate 8
Part, 5 parts of glacial acetic acid, 12 parts of acrylamide, 10 parts of vinyl chloride ethylene ester, 100 parts of deionized water is put into reactor, constantly stirs
Mix, 60 DEG C are heated to after mixing completely, product is obtained final product after uniform stirring.
Embodiment 3
By 50 parts of dihydroxymethyl dihydroxy oxazoline ketone, 20 parts of acrylic acid, 12 parts of ammonium citrate, 30 parts of triethanolamine, secondary phosphorus
20 parts of sour sodium, 18 parts of magnesium chloride hexahydrate, 8 parts of rosin glycerin ester resin, 16 parts of poly divinyl acetylene, 18 parts of aphthenic acids, ammonium citrate
12 parts, 8 parts of glacial acetic acid, 16 parts of acrylamide, 15 parts of vinyl chloride ethylene ester, 120 parts of deionized water is put into reactor, is constantly stirred
Mix, 60 DEG C are heated to after mixing completely, product is obtained final product after uniform stirring.
The above is only preferred embodiment of the invention, it is noted that to those skilled in the art, not
On the premise of departing from the invention design, some similar deformations and improvement can also be made, these also should be regarded as the present invention
Protection domain within.
Claims (1)
1. blend fabric wash and wear finisher, it is characterised in that:Component including following weight portion,
30~50 parts of dihydroxymethyl dihydroxy oxazoline ketone, 10~20 parts of acrylic acid, 6~12 parts of ammonium citrate, triethanolamine 20~
30 parts, 10~20 parts of sodium hypophosphite, 10~18 parts of magnesium chloride hexahydrate, 4~8 parts of rosin glycerin ester resin, poly divinyl acetylene 8~16
Part, 10~18 parts of aphthenic acids, 4~12 parts of ammonium citrate, 2~8 parts of glacial acetic acid, 8~16 parts of acrylamide, vinyl chloride ethylene ester 5
~15 parts, 80~120 parts of deionized water.