CN106906655A - Blend fabric finishing agent - Google Patents

Blend fabric finishing agent Download PDF

Info

Publication number
CN106906655A
CN106906655A CN201610513875.0A CN201610513875A CN106906655A CN 106906655 A CN106906655 A CN 106906655A CN 201610513875 A CN201610513875 A CN 201610513875A CN 106906655 A CN106906655 A CN 106906655A
Authority
CN
China
Prior art keywords
parts
finishing agent
ammonium citrate
blend fabric
fabric finishing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610513875.0A
Other languages
Chinese (zh)
Inventor
陆海蓉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610513875.0A priority Critical patent/CN106906655A/en
Publication of CN106906655A publication Critical patent/CN106906655A/en
Pending legal-status Critical Current

Abstract

The invention discloses blend fabric finishing agent, including following weight portion component, 6~12 parts of ammonium citrate, 20~30 parts of triethanolamine, 10~20 parts of sodium hypophosphite, 20~40 parts of formaldehyde resin, 10~16 parts of formic acid, 10~18 parts of magnesium chloride hexahydrate, 4~8 parts of rosin glycerin ester resin, 8~16 parts of poly divinyl acetylene, 10~18 parts of aphthenic acids, 4~12 parts of ammonium citrate, 2~8 parts of glacial acetic acid, 8~16 parts of acrylamide, 5~15 parts of vinyl chloride ethylene ester, 80~120 parts of deionized water.The blend fabric finishing agent that the present invention is provided, makes simple, and the raw materials for production selection of use is avirulent, the fabric processed with this finishing agent can crease and shrink resistance, fixed effect is good, exempts from flatiron, with it is well-pressed, plentiful, not dirty the features such as.

Description

Blend fabric finishing agent
Technical field
The present invention relates to a kind of finishing agent technical field, and in particular to a kind of blend fabric finishing agent.
Background technology
In recent years, with the improvement of people ' s living standards, under working environment with water repellent, refuse oil, soil-repellent finishing clothes need The amount of asking constantly increases, the fabric treated using finishing agent, can protect the user against splashing for water, oil, chemicals and pollutant Infringement is echoed, with protective, can be used for protective garments or work clothes etc. under the working environment of making high-quality, by people Attention and have a good application prospect;The finishing agent function of using at present is relatively simple, and using effect is poor, it is necessary to enter The improvement of one step, simple finishing agent can not meet the required of people.
The content of the invention
It is an object of the invention to provide blend fabric finishing agent, one or more in above-mentioned prior art problem is solved.
According to an aspect of the present invention, blend fabric finishing agent, including following weight portion component,
6~12 parts of ammonium citrate, 20~30 parts of triethanolamine, 10~20 parts of sodium hypophosphite, 20~40 parts of formaldehyde resin, first 10~16 parts of acid, 10~18 parts of magnesium chloride hexahydrate, 4~8 parts of rosin glycerin ester resin, 8~16 parts of poly divinyl acetylene, aphthenic acids 10 ~18 parts, 4~12 parts of ammonium citrate, 2~8 parts of glacial acetic acid, 8~16 parts of acrylamide, 5~15 parts of vinyl chloride ethylene ester, go from 80~120 parts of sub- water.
The blend fabric finishing agent that the present invention is provided, makes simple, and the raw materials for production selection of use is avirulent, whole with this The fabric of reason agent treatment can crease and shrink resistance, fixed effect is good, exempts from flatiron, with the spy such as Water-proof and oil-proof, well-pressed, plentiful, not dirty Point.
Specific embodiment
Embodiment 1
By 6 parts of ammonium citrate, 20 parts of triethanolamine, 10 parts of sodium hypophosphite, 20 parts of formaldehyde resin, 10 parts of formic acid, six water chlorine Change 10 parts of magnesium, 4 parts of rosin glycerin ester resin, 8 parts of poly divinyl acetylene, 10 parts of aphthenic acids, 4 parts of ammonium citrate, 2 parts of glacial acetic acid, third 8 parts of acrylamide, 5 parts of vinyl chloride ethylene ester, 80 parts of deionized water is put into reactor, is stirred continuously, and is heated to after mixing completely 60 DEG C, product is obtained final product after uniform stirring.
Embodiment 2
By 9 parts of ammonium citrate, 25 parts of triethanolamine, 15 parts of sodium hypophosphite, 30 parts of formaldehyde resin, 13 parts of formic acid, six water chlorine Change 14 parts of magnesium, 6 parts of rosin glycerin ester resin, 12 parts of poly divinyl acetylene, 14 parts of aphthenic acids, 8 parts of ammonium citrate, 5 parts of glacial acetic acid, third 12 parts of acrylamide, 10 parts of vinyl chloride ethylene ester, 100 parts of deionized water is put into reactor, is stirred continuously, heating after mixing completely To 60 DEG C, product is obtained final product after uniform stirring.
Embodiment 3
By 12 parts of ammonium citrate, 30 parts of triethanolamine, 20 parts of sodium hypophosphite, 40 parts of formaldehyde resin, 16 parts of formic acid, six water chlorine 18 parts of magnesium of change, 8 parts of rosin glycerin ester resin, 16 parts of poly divinyl acetylene, 18 parts of aphthenic acids, 12 parts of ammonium citrate, 8 parts of glacial acetic acid, 16 parts of acrylamide, 15 parts of vinyl chloride ethylene ester, 120 parts of deionized water is put into reactor, is stirred continuously, and is added after mixing completely Heat obtains final product product to 60 DEG C after uniform stirring.
The above is only preferred embodiment of the invention, it is noted that to those skilled in the art, not On the premise of departing from the invention design, some similar deformations and improvement can also be made, these also should be regarded as the present invention Protection domain within.

Claims (1)

1. blend fabric finishing agent, it is characterised in that:Component including following weight portion,
6~12 parts of ammonium citrate, 20~30 parts of triethanolamine, 10~20 parts of sodium hypophosphite, 20~40 parts of formaldehyde resin, formic acid 10 ~16 parts, 10~18 parts of magnesium chloride hexahydrate, 4~8 parts of rosin glycerin ester resin, 8~16 parts of poly divinyl acetylene, aphthenic acids 10~18 Part, 4~12 parts of ammonium citrate, 2~8 parts of glacial acetic acid, 8~16 parts of acrylamide, 5~15 parts of vinyl chloride ethylene ester, deionized water 80~120 parts.
CN201610513875.0A 2016-07-01 2016-07-01 Blend fabric finishing agent Pending CN106906655A (en)