CN106883643A - 一种硅藻土墙面涂料的制备方法 - Google Patents

一种硅藻土墙面涂料的制备方法 Download PDF

Info

Publication number
CN106883643A
CN106883643A CN201710106118.6A CN201710106118A CN106883643A CN 106883643 A CN106883643 A CN 106883643A CN 201710106118 A CN201710106118 A CN 201710106118A CN 106883643 A CN106883643 A CN 106883643A
Authority
CN
China
Prior art keywords
diatomite
added
wall covering
solution
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710106118.6A
Other languages
English (en)
Inventor
郭双福
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUHAN JINZHONGHAI HIGH-TECH Co Ltd
Original Assignee
WUHAN JINZHONGHAI HIGH-TECH Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUHAN JINZHONGHAI HIGH-TECH Co Ltd filed Critical WUHAN JINZHONGHAI HIGH-TECH Co Ltd
Priority to CN201710106118.6A priority Critical patent/CN106883643A/zh
Publication of CN106883643A publication Critical patent/CN106883643A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种本发明提供了一种硅藻土墙面涂料的制备方法，具有良好的化学稳定性和吸收性，步骤包括将硅藻土加入到盐酸溶液中混合搅拌，将硫酸铵与四氯化钛在烧杯中混合将硫酸铵与四氯化钛混合溶液缓慢加入到硅藻土与盐酸溶液中搅拌，加入膨润土继续搅拌，在电子束下进行共聚，加入硝酸银直至溶液反应，高压反应釜中进行反应。

Description

一种硅藻土墙面涂料的制备方法
技术领域
本发明涉及涂料领域，具体为一种硅藻土墙面涂料的制备方法。
背景技术
硅藻土涂料添加剂产品，具有孔隙度大、吸收性强、化学性质稳定、耐磨、耐热等特点，能为涂料提供优异的表面性能，增容，增稠以及提高附着力。由于它具有较大的孔体积，能使涂膜缩短干燥时间。还可减少树脂的用量，降低成本。该产品被认为是一种具有良好性价比的高效涂料用消光粉产品。
发明内容
本发明提供了一种硅藻土墙面涂料的制备方法，具有良好的化学稳定性和吸收性。
本发明的技术方案在于包括以下步骤：
(1)将硅藻土加入到盐酸溶液中混合搅拌，将硫酸铵与四氯化钛在烧杯中混合；
(2)将硫酸铵与四氯化钛混合溶液缓慢加入到硅藻土与盐酸溶液中搅拌；
(3)在步骤(2)中加入膨润土继续搅拌；
(4)将步骤(3)所得混合物在电子束下进行共聚；
(5)将步骤(4)所得的溶液中加入硝酸银直至溶液反应，直至不再产生沉淀物，过滤，用去离子水反复洗涤；
(6)将步骤(5)所得的溶液转移到聚四氟乙烯衬垫的高压反应釜中进行反应；
(7)将产物经过过滤、洗涤、干燥后得到所述硅藻土墙面涂料。
进一步的，步骤(1)中搅拌时间为10-40min，步骤(2)中搅拌时间为10-30min，步骤(3)中搅拌时间为30-50min。
进一步的，步骤(7)中反应温度为150-200℃，反应时间为1-1.5h。
具体实施方式
以下详细描述本发明的实施例。
先将20g硅藻土加入到500ml盐酸溶液中混合搅拌20min，将100g硫酸铵与200g四氯化钛在烧杯中混合搅拌25min；
将硫酸铵与四氯化钛混合溶液缓慢加入到硅藻土与盐酸溶液中搅拌50min；
然后加入50g膨润土继续搅拌；
将所得混合物在电子束下进行共聚；
将所得的溶液中加入硝酸银直至溶液反应，直至不再产生沉淀物，过滤，用去离子水反复洗涤；
将所得的溶液转移到聚四氟乙烯衬垫的高压反应釜中进行反应，反应温度150℃，反应时间1h；
将产物经过过滤、洗涤、干燥后得到所述硅藻土墙面涂料。
上述制备过程简单环保，成本低，得到的涂料化学稳定性和黏附性好，易于吸收。
以上仅为本发明的优选实施例而已，并不用于限制本发明，对于本领域的技术人员来说，本发明可以有各种更改和变化。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (3)

1.一种硅藻土墙面涂料的制备方法，其特征在于包括以下步骤：
(1)将硅藻土加入到盐酸溶液中混合搅拌，将硫酸铵与四氯化钛在烧杯中混合；
(2)将硫酸铵与四氯化钛混合溶液缓慢加入到硅藻土与盐酸溶液中搅拌；
(3)在步骤(2)中加入膨润土继续搅拌；
(4)将步骤(3)所得混合物在电子束下进行共聚；
(5)将步骤(4)所得的溶液中加入硝酸银直至溶液反应，直至不再产生沉淀物，过滤，用去离子水反复洗涤；
(6)将步骤(5)所得的溶液转移到聚四氟乙烯衬垫的高压反应釜中进行反应；
(7)将产物经过过滤、洗涤、干燥后得到所述硅藻土墙面涂料。
2.根据权利要求1所述的墙面涂料的制备方法，其特征在于：步骤(1)中搅拌时间为10-40min，步骤(2)中搅拌时间为10-30min，步骤(3)中搅拌时间为30-50min。
3.根据权利要求2所述的墙面涂料的制备方法，其特征在于：步骤(7)中反应温度为150-200℃，反应时间为1-1.5h。
CN201710106118.6A 2017-02-27 2017-02-27 一种硅藻土墙面涂料的制备方法 Pending CN106883643A (zh)