CN106866046A - A kind of quartz sand water-permeable brick - Google Patents
A kind of quartz sand water-permeable brick Download PDFInfo
- Publication number
- CN106866046A CN106866046A CN201611231984.XA CN201611231984A CN106866046A CN 106866046 A CN106866046 A CN 106866046A CN 201611231984 A CN201611231984 A CN 201611231984A CN 106866046 A CN106866046 A CN 106866046A
- Authority
- CN
- China
- Prior art keywords
- parts
- quartz sand
- water
- permeable brick
- permeable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of quartz sand water-permeable brick, is related to building material field.A kind of quartz sand water-permeable brick, is made up of following raw materials by weight portion：1 20 parts of water, 10 95 parts of quartz sand, 10 30 parts of cement, 1 20 parts of stone flour, 0.01 10 parts of colouring agent.Inventive formulation is simple, and technological process is succinct, is easy to promote.Perfectly solve brick body easy-weathering during traditional water-permeable brick use, brick emaciated face falls, influence is attractive in appearance, and many water-permeable bricks cause permeability rate low due to lamination problem, influence the problem of permeable effect, and forming method of the invention takes extrusion forming, without firing, energy resource consumption, energy-saving and emission-reduction are reduced.
Description
Technical field
The present invention relates to building material field, a kind of especially quartz sand water-permeable brick.
Background technology
The concept in sponge city proposed that sponge city, i.e. city can adapt to ring as sponge in 2012 first
Border changes and reply natural calamity etc. aspect has good " elasticity ", water suction when rainy, retaining, infiltration, water purification, it is necessary to when by
The water " release " that stores simultaneously is used.The generation of lifting urban ecological system function and reduction Urban Flood Waterlogging.
One of most important measure of sponge urban construction is exactly the permeable pavement of urban ground, to reach natural precipitation
Urban inner is deposited in greatest extent, is easy to the purpose for recycling.And during the permeable pavement in city, water-permeable brick is most
One of important construction material.
In the prior art, water-permeable brick has been the common construction material of in the market, there is provided the enterprise of water-permeable brick also be unequal to piece
Lift.But, there is brick body easy-weathering in the existing water-permeable brick major part of in the market, brick emaciated face falls, and influence attractive in appearance, and many permeable
Brick causes permeability rate low due to lamination problem, influences permeable effect.Present inventor is by multiple research experiment, there is provided one
Quartz sand water-permeable brick is planted, can be solved the above problems well..
The content of the invention
In order to solve the above-mentioned technical problem, the present invention provides a kind of quartz sand water-permeable brick.
The technical solution adopted for the present invention to solve the technical problems is：
A kind of quartz sand water-permeable brick, is made up of following raw materials by weight portion：Water 1-20 parts, quartz sand 10-95 parts, cement 5-35
Part, stone flour 2-40 parts, colouring agent 0.01-10 parts.
Preferably, a kind of quartz sand water-permeable brick, is made up of following raw materials by weight portion：Water 5-18 parts, quartz sand 15-80
Part, cement 12-27 parts, stone flour 5-35 parts, colouring agent 1-8 parts.
Preferably, a kind of quartz sand water-permeable brick, is made up of following raw materials by weight portion：Water 7-16 parts, quartz sand 30-66
Part, cement 16-22 parts, stone flour 8-12 parts, colouring agent 3-7 parts.
Preferably, a kind of quartz sand water-permeable brick, is made up of following raw materials by weight portion：10 parts of water, 52 parts of quartz sand, water
20 parts of mud, 11 parts of stone flour, 2 parts of colouring agent.
A kind of quartz sand water-permeable brick, its production stage is：Prepare corresponding various raw materials according to formula ratio, it is full and uniform to stir
Mix, be well mixed, grind, particle diameter stands 30 minutes between 0.5-3mm, and the raw material after mixing is put into extruder
Interior extrusion forming, obtains final product adobe, and adobe is removed, and in 5-25 DEG C of temperature, in the environment of humidity 50%-90% constant temperature and humidities, places
Sizing 1-4 days, wraps up preservative film natural curing.
Beneficial effects of the present invention：Inventive formulation is simple, and technological process is succinct, is easy to promote.Perfectly solve biography
Brick body easy-weathering during system water-permeable brick use, brick emaciated face falls, and influences attractive in appearance, and many water-permeable bricks are led due to lamination problem
Cause permeability rate low, influence the problem of permeable effect, and forming method of the invention takes extrusion forming, without firing, reduces
Energy resource consumption, energy-saving and emission-reduction.
Specific embodiment
With reference to specific embodiment, the invention will be further described：
Embodiment one
A kind of quartz sand water-permeable brick, is made up of following raw materials by weight portion：3 parts of water, 50 parts of quartz sand, 15 parts of cement, stone flour
10 parts, 0.5 part of colouring agent.Prepare corresponding various raw materials according to formula ratio, full and uniform stirring is well mixed, grinds,
Particle diameter stands 30 minutes between 0.5-3mm, and the raw material after mixing is put into extrusion forming in extruder, obtains final product adobe, will
Adobe is removed, and in 10 DEG C of temperature, in the environment of the constant temperature and humidity of humidity 60%, places sizing 1-4 days, parcel preservative film natural curing
.
Embodiment two
A kind of quartz sand water-permeable brick, is made up of following raw materials by weight portion：10 parts of water, 92 parts of quartz sand, 25 parts of cement, stone flour
30 parts, 2 parts of colouring agent.Prepare corresponding various raw materials according to formula ratio, full and uniform stirring is well mixed, grinds, grain
Footpath stands 30 minutes between 0.5-3mm, and the raw material after mixing is put into extrusion forming in extruder, obtains final product adobe, by brick
Base is removed, and in 15 DEG C of temperature, in the environment of the constant temperature and humidity of humidity 70%, places sizing 1-4 days, and wrapping up preservative film natural curing is
Can.
Embodiment three
A kind of quartz sand water-permeable brick, is made up of following raw materials by weight portion：5 parts of water, 80 parts of quartz sand, 22 parts of cement, stone flour
20 parts, 1 part of colouring agent.Prepare corresponding various raw materials according to formula ratio, full and uniform stirring is well mixed, grinds, grain
Footpath stands 30 minutes between 0.5-3mm, and the raw material after mixing is put into extrusion forming in extruder, obtains final product adobe, by brick
Base is removed, and in 20 DEG C of temperature, in the environment of the constant temperature and humidity of humidity 80%, places sizing 1-4 days, and wrapping up preservative film natural curing is
Can.
Finally it should be noted that specific embodiment is unrestricted to of the invention further illustrating, to this area
For those of ordinary skill, can be done in the case where substance of the present invention is not departed from and further converted, and all these changes
Change the protection domain that should all belong to appended claims of the present invention.
Claims (5)
1. a kind of quartz sand water-permeable brick, it is characterised in that：It is made up of following raw materials by weight portion：Water 1-20 parts, quartz sand 10-
95 parts, cement 10-30 parts, stone flour 1-20 parts, colouring agent 0.01-10 parts.
2. a kind of quartz sand water-permeable brick according to claim 1, it is characterised in that：By following raw materials by weight portion group
Into：Water 5-10 parts, quartz sand 30-80 parts, cement 15-25 parts, stone flour 5-15 parts, colouring agent 1-8 parts.
3. a kind of quartz sand water-permeable brick according to claim 1, it is characterised in that：By following raw materials by weight portion group
Into：Water 6-8 parts, quartz sand 40-70 parts, cement 16-22 parts, stone flour 8-12 parts, colouring agent 3-7 parts.
4. a kind of quartz sand water-permeable brick according to claim 1, it is characterised in that：By following raw materials by weight portion group
Into：10 parts of water, 52 parts of quartz sand, 20 parts of cement, 11 parts of stone flour, 2 parts of colouring agent.
5. according to a kind of any described quartz sand water-permeable bricks of claim 1-4, it is characterised in that：The quartz sand water-permeable brick life
Producing step is：Prepare corresponding various raw materials according to formula ratio, full and uniform stirring is well mixed, grinds, and particle diameter exists
Between 0.5-3mm, 30 minutes are stood, the raw material after mixing is put into extrusion forming in extruder, obtains final product adobe, and adobe is taken
Under, in 5-25 DEG C of temperature, in the environment of humidity 50%-90% constant temperature and humidities, place sizing 1-4 days, parcel preservative film natural curing
.