CN103193422A - Solid waste color baking-free brick and preparation method thereof - Google Patents
Solid waste color baking-free brick and preparation method thereof Download PDFInfo
- Publication number
- CN103193422A CN103193422A CN2013100800074A CN201310080007A CN103193422A CN 103193422 A CN103193422 A CN 103193422A CN 2013100800074 A CN2013100800074 A CN 2013100800074A CN 201310080007 A CN201310080007 A CN 201310080007A CN 103193422 A CN103193422 A CN 103193422A
- Authority
- CN
- China
- Prior art keywords
- brick
- bricks
- solid
- solidifying agent
- solid mixture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the fields of building materials and environmental protection, and particularly relates to a color baking-free brick made of solid waste and a preparation method thereof. The raw material comprises a solid mixing material and a curing agent mixing liquor, wherein the weight ratio of the solid mixing material and the curing agent mixing liquor is 10:0.7-1.5, the solid mixing material comprises solid waste, cement, a color material, a granular material, and the curing agent mixing liquor comprises water and a curing agent. Solid waste is used for making bricks and the waste is changed into treasure, so the invention has the advantages of energy conservation and environmental protection. The color of the brick is added and changed. The quality of the brick is in line with national standards. The brick is high in water resistance, high in heat preservation and compression resistance, and good in toughness, can be installed directly with expansion screws and powder mortar, sticked with ceramic tiles, and hung with stone slabs and advertising boards, and can be made into environmental-friendly bricks of different specifications, such as hollow bricks, porous bricks, solid bricks, road edge bricks, outside wall bricks, lawn bricks, wharf bricks, and weight-bearing and non-weight-bearing bricks.
Description
Technical field
The present invention relates to material of construction and field of environment protection, be specifically related to useless admittedly make colored non-burning brick and preparation method thereof of a kind of usefulness.
Background technology
The earth vitrified brick is still application Wall body material very widely now in the history of the existing more than one thousand years of China.But because the increase of population, the enlarging in city, per capita cultivated land and long-pendingly more and more reduce has been begun forbidding as traditional earth brick braised in soy sauce, has occurred non-burning brickly, and the non-clay brick that replaces with construction waste or other materials substitutes clay brick, will be trend of the times.Country has also given the support on the policy.A large amount of giving up admittedly in the production process of reality society, as: assorted soil, stone flour, ore deposit quarrel, construction waste etc., if solid giving up made brick, can turn waste into wealth, and can effectively protect environment, the very big minimizing pollutes.
Summary of the invention
The objective of the invention is to overcome above-mentioned deficiency of the prior art, provide a kind of usefulness useless admittedly make colored non-burning brick and preparation method thereof.
For achieving the above object, the present invention adopts following technical scheme: Gu useless colored non-burning brick, comprise: solid mixture and solidifying agent mixed solution, described solid mixture and solidifying agent mixed solution weight ratio are 10:0.7-1.5, described solid mixture comprises: Gu useless, cement, color material, particulate material, described solidifying agent mixed solution comprises water and solidifying agent.
Further, described solid mixture by weight percentage, its feed composition comprises: Gu useless be 55-80%, cement 7-16%, color material 5-10%, particulate material 7-20%, the volume ratio of described water and solidifying agent is 10000:3-8.
Described particulate material is handstone, coarse sand, particulate solid waste etc., and the water ratio of described solid mixture is 5-12%.
The present invention also further discloses above-mentioned solid useless colored non-burning brick preparation method, comprises the steps:
By weight percentage, take by weighing each material, to give up admittedly and further pulverize, again with particulate material, cement, color material mixing and stirring, get solid mixture, water and solidifying agent and stir by the mixed of 3-10:10000, the solidifying agent mixed solution, and stir solids compound limit, back spray to add mixing liquid, but pinches when agglomerating when the solid mixture hand, stop to spray mixing liquid, then the solid mixture that stirs is transported to brick pressing machine and suppresses, get the moulding fragment of brick, wrap the moulding fragment of brick with plastics film and prevent moisture evaporation, place open-air natural curing to exempt from water spray in 10 days, get finished product.
The present invention is owing to use useless admittedly brickmaking, turn waste into wealth, so have environmental protection, advantage such as energy-conservation, and can increase the color that changes brick, quality meets national standard, and water-repellancy is strong, insulation, crushing resistance are strong, good toughness, can directly install setscrew, flour sand slurry, paste ceramic tile, hanging stone plate material, billboard etc. and can produce the environmental protection brick of various different sizes.As hollow brick, perforated brick, solid brick, curb brick, exterior wall tile, lawn brick, harbour brick, load capacity and non-bearing weight brick etc.
Embodiment
Further set forth the present invention below in conjunction with embodiment.
Embodiment 1
By weight percentage, take by weighing solid mixture: Gu the useless 55-80% of being, cement 7-16%, color material 5-10%, particulate material 7-20%, weight ratio by solid mixture and solidifying agent mixed solution takes by weighing the solidifying agent mixed solution, to give up admittedly and further pulverize, again with particulate material, cement, color material mixing and stirring, get solid mixture, water and solidifying agent and stir by the mixed of 3-10:10000, get the solidifying agent mixed solution, and the adding mixing liquid is sprayed on stir solids compound limit, back, but pinch when agglomerating when the solid mixture hand, stop to spray mixing liquid, then the solid mixture that stirs is transported to brick pressing machine and suppresses, get the moulding fragment of brick, wrap the moulding fragment of brick with plastics film and prevent moisture evaporation, place open-air natural curing to exempt from water spray in 10 days, get finished product.
Embodiment 2
By weight percentage, take by weighing solid mixture: Gu useless be 60% kilogram, cement 13%, color material 7%, particulate material 20%, weight ratio by solid mixture and solidifying agent mixed solution takes by weighing the solidifying agent mixed solution, to give up admittedly and further pulverize, again with particulate material, cement, color material mixing and stirring, get solid mixture, water and solidifying agent and stir by the mixed of 3-10:10000, get the solidifying agent mixed solution, and the adding mixing liquid is sprayed on stir solids compound limit, back, but pinch when agglomerating when the solid mixture hand, stop to spray mixing liquid, then the solid mixture that stirs is transported to brick pressing machine and suppresses, get the moulding fragment of brick, wrap the moulding fragment of brick with plastics film and prevent moisture evaporation, place open-air natural curing to exempt from water spray in 10 days, get finished product.After testing, the result is ultimate compression strength mean value 13.6, and minimum value is 11.3, and hole ratio is 32.8, and impermeability is not more than 10, and dryness factor is 0.041.
Embodiment 3
By weight percentage, take by weighing solid mixture: Gu useless be 8400 kilograms, 1820 kilograms of cement, 980 kilograms in color material, 2800 kilograms of particulate material, weight ratio by solid mixture and solidifying agent mixed solution takes by weighing 1400 kilograms of solidifying agent mixed solutions, to give up admittedly and further pulverize, again with particulate material, cement, color material mixing and stirring, get solid mixture, water and solidifying agent and stir by the mixed of 3-10:10000, get the solidifying agent mixed solution, and the adding mixing liquid is sprayed on stir solids compound limit, back, when but the solid mixture hand is pinched when agglomerating, stop to spray mixing liquid, then the solid mixture that stirs being transported to brick pressing machine suppresses, get the moulding fragment of brick, wrap the moulding fragment of brick with plastics film and prevent moisture evaporation, place open-air natural curing to exempt from water spray in 10 days, getting specification is 240 * 115 * 53mm, weight is 1.4 kilograms 10000 of finished product standard bricks.
Claims (4)
1. solid useless colored non-burning brick, it is characterized in that: comprising: solid mixture and solidifying agent mixed solution, described solid mixture and solidifying agent mixed solution weight ratio are 10:0.7-1.5, described solid mixture comprises: Gu useless, cement, color material, particulate material, described solidifying agent mixed solution comprises water and solidifying agent.
2. according to claim 1 solid useless colored non-burning brick, it is characterized in that: described solid mixture by weight percentage, its feed composition comprises: be 55-80%, cement 7-16%, color material 5-10%, particulate material 7-20% Gu give up, the volume ratio of described water and solidifying agent is 10000:3-8.
3. according to claim 1 solid useless colored non-burning brick, it is characterized in that: described particulate material is handstone, coarse sand, particulate solid waste etc., and the water ratio of described solid mixture is 5-12%.
4. according to claim 1 solid useless colored non-burning brick, it is characterized in that: its preparation method, comprise the steps: by weight percentage, take by weighing each material, to give up admittedly and further pulverize, again with particulate material, cement, color material mixing and stirring, get solid mixture, water and solidifying agent and stir by the mixed of 3-10:10000, the solidifying agent mixed solution, and stir solids compound limit, back spray to add mixing liquid, but pinches when agglomerating when the solid mixture hand, stop to spray mixing liquid, then the solid mixture that stirs is transported to brick pressing machine and suppresses, get the moulding fragment of brick, wrap the moulding fragment of brick with plastics film and prevent moisture evaporation, place open-air natural curing to exempt from water spray in 10 days, get finished product.