CN105801052A - Concrete water permeable brick and preparation method thereof - Google Patents
Concrete water permeable brick and preparation method thereof Download PDFInfo
- Publication number
- CN105801052A CN105801052A CN201610133849.5A CN201610133849A CN105801052A CN 105801052 A CN105801052 A CN 105801052A CN 201610133849 A CN201610133849 A CN 201610133849A CN 105801052 A CN105801052 A CN 105801052A
- Authority
- CN
- China
- Prior art keywords
- cement
- permeable brick
- granularity
- concrete
- top layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a concrete water permeable brick which comprises a surface layer, a middle layer and a lower layer, wherein the surface layer consists of the following components in percentage by weight: 38-42% of cement, 55-57% of fine sand with granularity of less than or equal to 0.5mm and 3-5% of pigment; the middle layer consists of the following components in percentage by weight: 40-45% of cement and 55-60% of coarse sand with granularity of less than or equal to 0.5-3mm; and the lower layer consists of the following components in percentage by weight: 45-50% of cement, stone powder with granularity of 5-8mm and 5-10% of talc powder. The invention also discloses a preparation method of the concrete water permeable brick. In the concrete water permeable brick and preparation method thereof, three-layer material distribution is implemented, and the materials are mixed according to respective proportions on the layers; and the concrete water permeable brick has the advantages of good water permeability, high coagulability, high compressive strength, environmental friendliness and low cost.
Description
Technical field
The invention belongs to cement or similar cementing material building block making technical field, specifically a kind of concrete permeable brick and preparation method thereof.
Background technology
Current water-permeable brick many employings monolayer or double-layer cloth on the market, because formula reason occurs that water-permeable brick water permeability is poor, coagulability is poor, does pressure low, water-permeable brick tomography situation even occurs.
Summary of the invention
In view of this, it is an object of the invention to provide a kind of concrete permeable brick and preparation method thereof, this water-permeable brick carries out three layers cloth, and each layer mixes in respective ratio, and water permeability is good, and coagulability is strong, does pressure height, environmental protection and with low cost.
In order to achieve the above object, one concrete permeable brick of the present invention, including top layer, middle level and lower floor, described top layer is made up of by weight following component: cement: 38～42%；The fine sand of granularity≤0.5m: 55～57%；Pigment: 3～5%；Described middle level is made up of by weight following component: cement: 40～45%；Granularity is the rough sand of 0.5mm～3mm: 55～60%；Described lower floor is made up of by weight following component: cement: 45～50%；Granularity is the stone powder of 5mm～8mm: 40～45%；Pulvis Talci 5～10%.
Further, the concrete mass ratio of the composition on described top layer is: cement: 40%；The fine sand of granularity≤0.5m: 56%；Pigment: 4%.
Further, the cement in described top layer is set to white cement, and the cement in described middle level and lower floor is set to standard cement.
Further, the thickness proportion of described top layer, middle level and lower floor is 2: 4: 1.
The invention also discloses a kind of preparation method preparing concrete permeable brick, its step is divided into:
(1) constituent of each layer adds suitable quantity of water respectively in proportion to stir in blender, after stirring；
(2) concrete transportation after being stirred by each layer according to the order cloth successively on lower floor, middle level and top layer, is then pressed to water-permeable brick machine；
(3) after molding, water-permeable brick waters a small amount of water curing 25 days in the open.The beneficial effects of the present invention is:
Concrete permeable brick of the present invention and preparation method thereof carries out three layers cloth, and each layer mixes in respective ratio, and water permeability is good, and coagulability is strong, does pressure height, environmental protection and with low cost.
Detailed description of the invention
One concrete permeable brick of the present invention, including top layer, middle level and lower floor, described top layer is made up of by weight following component: cement: 38～42%；The fine sand of granularity≤0.5m: 55～57%；Pigment: 3～5%；Described middle level is made up of by weight following component: cement: 40～45%；Granularity is the rough sand of 0.5mm～3mm: 55～60%；Described lower floor is made up of by weight following component: cement: 45～50%；Granularity is the stone powder of 5mm～8mm: 40～45%；Pulvis Talci 5～10%.
Further, it is preferred that the concrete mass ratio of composition on described top layer is: cement: 40%；The fine sand of granularity≤0.5m: 56%；Pigment: 4%.
The concrete mass ratio of composition in preferred described middle level is: cement: 40%；Granularity is the rough sand of 0.5mm～3mm: 60%.
The concrete mass ratio of composition of preferred described lower floor is: cement: 50%；Granularity is the stone powder of 5mm～8mm: 45%；Pulvis Talci 5%.
Further, it is preferred that the cement in described top layer is set to white cement, and the cement in described middle level and lower floor is set to standard cement.
Further, the thickness proportion of described top layer, middle level and lower floor is 2: 4: 1.
The invention also discloses a kind of preparation method preparing concrete permeable brick, its step is divided into:
(1) constituent of each layer adds suitable quantity of water respectively in proportion to stir in blender, after stirring；
(2) concrete transportation after being stirred by each layer according to the order cloth successively on lower floor, middle level and top layer, is then pressed to water-permeable brick machine；
(3) after molding, water-permeable brick waters a small amount of water curing 25 days in the open.The beneficial effects of the present invention is:
What finally illustrate is, preferred embodiment above is only in order to illustrate technical scheme and unrestricted, although the present invention being described in detail by above preferred embodiment, but skilled artisan would appreciate that, in the form and details it can be made various change, without departing from claims of the present invention limited range.
Claims (5)
1. a concrete permeable brick, it is characterised in that: including top layer, middle level and lower floor, described top layer is made up of by weight following component: cement: 38～42%；The fine sand of granularity≤0.5m: 55～57%；Pigment: 3～5%；Described middle level is made up of by weight following component: cement: 40～45%；Granularity is the rough sand of 0.5mm～3mm: 55～60%；Described lower floor is made up of by weight following component: cement: 45～50%；Granularity is the stone powder of 5mm～8mm: 40～45%；Pulvis Talci 5～10%.
2. concrete permeable brick according to claim 1, it is characterised in that: the concrete mass ratio of composition on described top layer is: cement: 40%；The fine sand of granularity≤0.5m: 56%；Pigment: 4%.
3. concrete permeable brick according to claim 2, it is characterised in that: the cement in described top layer is set to white cement, and the cement in described middle level and lower floor is set to standard cement.
4. concrete permeable brick according to claim 1, it is characterised in that: the thickness proportion of described top layer, middle level and lower floor is 2: 4: 1.
5. the preparation method of the concrete permeable brick prepared described in any one of Claims 1 to 4, it is characterised in that: the steps include:
(1) constituent of each layer adds suitable quantity of water respectively in proportion to stir in blender, after stirring；
(2) concrete transportation after being stirred by each layer according to the order cloth successively on lower floor, middle level and top layer, is then pressed to water-permeable brick machine；
(3) after molding, water-permeable brick waters a small amount of water curing 25 days in the open.