CN107540295A - A kind of color quartz sand water-permeable brick - Google Patents
A kind of color quartz sand water-permeable brick Download PDFInfo
- Publication number
- CN107540295A CN107540295A CN201710901123.6A CN201710901123A CN107540295A CN 107540295 A CN107540295 A CN 107540295A CN 201710901123 A CN201710901123 A CN 201710901123A CN 107540295 A CN107540295 A CN 107540295A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- quartz sand
- permeable brick
- brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of color quartz sand water-permeable brick, the water-permeable brick by weight, including following component:30 50 parts of quartz sand, 30 50 parts of cement, 50 80 parts of water, 5 10 parts of colouring agent, 5 10 parts of magnalium cementing agent, 20 30 parts of basalt microlith, 10 15 parts of cenosphere, 35 parts of accelerator, 5 10 parts of stone flour.It the advantage is that:The present invention uses magnalium cementing agent, in the absence of organic cementing agent, present in heating process because of the heatproof low intensity caused by oxidation the problem of, makes water-permeable brick heat resistance good;The present invention solves brick body easy-weathering during traditional water-permeable brick use, and brick emaciated face falls, influence it is attractive in appearance, and due to the problem of brick body is layered, and permeability rate is low, and permeable effect is bad.
Description
Technical field
A kind of technical field of buildings of the present invention, and in particular to color quartz sand water-permeable brick.
Background technology
With the development of Process of Urbanization Construction, increasing hard ground is laid in city, its environment-friendly function is poor, displeasant
Occupy.For example, excess surface water and urban waterlogging, natural precipitation can not ooze caused by the tropical island effect of mattess, drainage difference
Saturating recharge of groundwater causes ground water circulation to go to pot.Existing concrete road pavement brick is a kind of typical hard ground, greatly
Mostly solid brick, coefficient of permeability is very low, does not possess pervious function substantially.
Sponge city is that city can adapt to environmental change and reply natural calamity etc. with good as sponge
Good " elasticity ", can be absorbed water when rainy, water storage, infiltration, water purification, it is necessary to during with water, the water energy " release " of storage is simultaneously used,
Urban ecological system can be lifted and reduce the generation of Urban Flood Waterlogging.
In the prior art, water-permeable brick has been the common construction material of in the market, but existing water-permeable brick is largely present
Brick body easy-weathering, brick emaciated face fall, and influence attractive in appearance, and many bricks cause permeability low, permeable effect is not due to lamination problem
It is good.
The content of the invention
In view of the above-mentioned deficiencies in the prior art, it is an object of the present invention to now provide, a kind of water permeability is good, anti-wear performance is good
Color quartz sand water-permeable brick.
In order to solve the above technical problems, the technical solution adopted by the present invention is:A kind of color quartz sand water-permeable brick, it is innovated
Point is:The water-permeable brick by weight, including following component:Quartz sand 30-50 parts, cement 30-50 parts, water 50-80 parts,
Colouring agent 5-10 parts, magnalium cementing agent 5-10 parts, basalt microlith 20-30 parts, cenosphere 10-15 parts, accelerator 3-5 parts,
Stone flour 5-10 parts.
Further, the quartz sand particle size is 100nm-1000nm.
Further, the basalt microlith particle diameter is 1mm-2mm.
Beneficial effects of the present invention are as follows:The present invention uses magnalium cementing agent, in the absence of organic cementing agent, in heating process
Present in because of the heatproof low intensity caused by oxidation the problem of, make water-permeable brick heat resistance good;It is permeable that the present invention solves tradition
Brick body easy-weathering during brick use, brick emaciated face fall, influence it is attractive in appearance, and due to brick body be layered, permeability rate is low, and permeable effect is not
The problem of good.
Embodiment
Embodiments of the present invention are illustrated by particular specific embodiment below, those skilled in the art can be by this explanation
Content disclosed by book understands other advantages and effect of the present invention easily.
Embodiment 1
A kind of color quartz sand water-permeable brick, water-permeable brick by weight, including following component:30 parts of quartz sand, 30 parts of cement, water
50 parts, 5 parts of colouring agent, 5 parts of magnalium cementing agent, 20 parts of basalt microlith, 10 parts of cenosphere, 3 parts of accelerator, 5 parts of stone flour.
Embodiment 2
A kind of color quartz sand water-permeable brick, water-permeable brick by weight, including following component:50 parts of quartz sand, 50 parts of cement, water
80 parts, 10 parts of colouring agent, 10 parts of magnalium cementing agent, 30 parts of basalt microlith, 15 parts of cenosphere, 5 parts of accelerator, stone flour 10
Part.
Embodiment 3
A kind of color quartz sand water-permeable brick, water-permeable brick by weight, including following component:40 parts of quartz sand, 40 parts of cement, water
65 parts, 7 parts of colouring agent, 7 parts of magnalium cementing agent, 25 parts of basalt microlith, 12 parts of cenosphere, 4 parts of accelerator, 7 parts of stone flour.
The present invention uses magnalium cementing agent, in the absence of organic cementing agent, present in heating process caused by oxidation
The problem of heatproof low intensity, make water-permeable brick heat resistance good;The present invention solves the easy wind of brick body during traditional water-permeable brick use
Change, the problem of brick emaciated face falls, and influences attractive in appearance, and because brick body is layered, permeability rate is low, and permeable effect is bad.
Above-described embodiment is presently preferred embodiments of the present invention, is not the limitation to technical solution of the present invention, as long as
The technical scheme that can be realized on the basis of above-described embodiment without creative work, it is regarded as falling into patent of the present invention
Rights protection scope in.
Claims (3)
- A kind of 1. color quartz sand water-permeable brick, it is characterised in that:The water-permeable brick by weight, including following component:Quartz Sand 30-50 parts, cement 30-50 parts, water 50-80 parts, colouring agent 5-10 parts, magnalium cementing agent 5-10 parts, basalt microlith 20-30 Part, cenosphere 10-15 parts, accelerator 3-5 parts, stone flour 5-10 parts.
- A kind of 2. color quartz sand water-permeable brick according to claim 1, it is characterised in that:The quartz sand particle size is 100nm-1000nm。
- A kind of 3. color quartz sand water-permeable brick according to claim 1, it is characterised in that:The basalt microlith particle diameter is 1mm-2mm。