CN203947037U - A kind of epoxy resin luminous ground - Google Patents
A kind of epoxy resin luminous ground Download PDFInfo
- Publication number
- CN203947037U CN203947037U CN201420276875.XU CN201420276875U CN203947037U CN 203947037 U CN203947037 U CN 203947037U CN 201420276875 U CN201420276875 U CN 201420276875U CN 203947037 U CN203947037 U CN 203947037U
- Authority
- CN
- China
- Prior art keywords
- epoxy
- epoxy resin
- utility
- model
- bottom coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model relates to luminous ground technical field, it discloses a kind of epoxy resin luminous ground, comprise ortho-water mud layer, described ortho-water mud layer upper berth is provided with one deck epoxy bottom coating, on described epoxy bottom coating, be equipped with one deck epoxy floating coat, on described epoxy floating coat, be equipped with the epoxy finishing coat that one deck contains rare earth aluminate fluorescent material.The utility model adopts the light-accumulation fluorescent powder Rare earth doped aluminates with steady persistence, and this material, after the irradiation of daylight and light, can continue luminous 6-10 hours, can meet people's in evening lighting demand; There is high acidproof, antiseptic property; The sustainable luminous of the utility model, economical environment-protective, beautifies the environment, durable in use, can be used in the environment such as urban road, park, square and lounge.
Description
Technical field
The utility model relates to luminous ground technical field, refers more particularly to a kind of epoxy resin luminous ground.
Background technology
Road surface in urban road, park, square and lounge is generally single cement products or stone product at present, for anti-skidding and attractive in appearance, on these road surfaces, often can be provided with protruding decorative pattern or pattern, but there are many weak points on these road surfaces.If at night, pedestrian walks laying on the humanoid road on this kind of road surface or other road surfaces, can not accurately take one's bearings, and while having obstacle on Qie Dang road, also easily causes danger.Urban road, park and square all adopt street lamp to throw light on night at present, but street lamp can not shine all corners completely, and light is more dim.
Utility model content
The defects such as technical problem to be solved in the utility model is to provide a kind of epoxy resin luminous ground, short to overcome existing luminous ground fluorescent lifetime, and the luminescent material shelf time is short.
For solving the problems of the technologies described above, the utility model by the following technical solutions:
A kind of epoxy resin luminous ground, comprise ortho-water mud layer, it is characterized in that, described ortho-water mud layer upper berth is provided with one deck epoxy bottom coating, on described epoxy bottom coating, be equipped with one deck epoxy floating coat, on described epoxy floating coat, be equipped with the epoxy finishing coat that one deck contains rare earth aluminate fluorescent material.
Preferably, by weight, described epoxy bottom coating is, after 0.01-0.02 part of 0.8-1.2 parts of 1.8-2.2 parts of epoxy resin, polyamide curing agent and coupling agent is mixed, to be layered on described ortho-water mud layer, and ambient cure forms.
Preferably, by weight, described epoxy floating coat is, after 1 part, 4-5 parts, epoxy resin material, modified amine curing agent mixed, to be layered on described epoxy bottom coating, and ambient cure forms.
Preferably, by weight, described epoxy finishing coat is, after 0.1-1 part of 40-50 parts of 100 parts of weathe resistance epoxy resins, 1-5 parts, rare earth aluminate fluorescent material, UV resistant solidifying agent and auxiliary agent is mixed, to be layered on described epoxy floating coat, and ambient cure forms.
Preferably, described epoxy resin material comprises the raw material of following weight percent: epoxy resin 30-60%, reactive thinner 2-10%, silica powder 20-50%, pigment 1-10% and auxiliary agent 0.1-5%.
Preferably, the thickness of described epoxy bottom coating is 0.05-0.2mm.
Preferably, the thickness of described epoxy floating coat is 0.1-0.5mm.
Preferably, the thickness of described epoxy finishing coat is 0.2-0.5mm.
The utility model compared with prior art, have the following advantages: (1) the utility model adopts the light-accumulation fluorescent powder Rare earth doped aluminates with steady persistence, this material, after the irradiation of daylight and light, can continue luminous 6-10 hours, can meet people's in evening lighting demand; (2) the utility model not only has the attractive in appearance of epoxide terrace, also has high acidproof, antiseptic property; (3) the sustainable luminous of the utility model, economical environment-protective, beautifies the environment, durable in use, can be used in the environment such as urban road, park, square and lounge.
Accompanying drawing explanation
Below in conjunction with accompanying drawing, the technical solution of the utility model is further described in detail.
Fig. 1 is the utility model structural representation;
In figure, 1-ortho-water mud layer, 2-epoxy bottom coating, 3-epoxy floating coat, 4-epoxy finishing coat.
Embodiment
Below in conjunction with the drawings and specific embodiments, the technical solution of the utility model is further described in detail.
Epoxy resin luminous ground as shown in Figure 1, comprise ortho-water mud layer 1, on ortho-water mud layer 1, be equipped with the epoxy bottom coating 2 that one deck is made by epoxy resin, polyamide curing agent and coupling agent mixing material, on epoxy bottom coating 2, be equipped with the epoxy floating coat 3 that one deck is made by epoxy resin, modified amine curing agent, silica powder and quartz sand mixing material, on epoxy floating coat 3, be equipped with the epoxy finishing coat 4 that one deck is made by weathe resistance epoxy resin, rare earth aluminate fluorescent material, UV resistant solidifying agent and auxiliary agent mixing material.
For further illustrating the utility model, describe embodiment of the present utility model below in detail.
Embodiment mono-:
(1) by weight percentage, by epoxy resin 60%, reactive thinner 10%, silica powder 20%, pigment 5%, auxiliary agent 5% mixes, and is mixed with epoxy resin material;
(2) by weight, after 0.01 part of 2 parts of epoxy resin, 1 part of polyamide curing agent and coupling agent is mixed, be layered on the ortho-water mud layer basal plane of dried flat, form epoxy bottom coating after ambient cure, its thickness is 0.2mm;
(3) by weight, after 1 part, 4 parts, epoxy resin material, modified amine curing agent mixed, be layered on epoxy bottom coating, form epoxy floating coat after ambient cure, its thickness is 0.1mm;
(4) by weight, after 1 part of 100 parts of weathe resistance epoxy resins, 5 parts, rare earth aluminate fluorescent material, 50 parts, UV resistant solidifying agent and auxiliary agent is mixed, be layered on epoxy floating coat, form epoxy finishing coat, its thickness is 0.5mm;
(5) treat epoxy finishing coat complete drying.
Embodiment bis-:
(1) by weight percentage, by epoxy resin 30%, reactive thinner 8%, quartzy pulvis 50%, pigment 10%, auxiliary agent 2% mixes, and is mixed with epoxy resin material;
(2) by weight, after 0.02 part of 2.2 parts of epoxy resin, 1.2 parts of polyamide curing agents and coupling agent is mixed, be layered on the ortho-water mud layer basal plane of dried flat, form epoxy bottom coating after ambient cure, its thickness is 0.05mm;
(3) by weight, after 1 part, 4 parts, epoxy resin material, modified amine curing agent mixed, be layered on epoxy bottom coating, form epoxy floating coat after ambient cure, its thickness is 0.5mm;
(4) by weight, after 0.1 part of 100 parts of weathe resistance epoxy resins, 1 part, rare earth aluminate fluorescent material, 40 parts, UV resistant solidifying agent and auxiliary agent is mixed, be layered on epoxy floating coat, form epoxy finishing coat, its thickness is 0.2mm;
(5) treat epoxy finishing coat complete drying.
Embodiment tri-:
(1) by weight percentage, by epoxy resin 40%, reactive thinner 5%, quartzy pulvis 45%, pigment 7%, auxiliary agent 3% mixes, and is mixed with epoxy resin material;
(2) by weight, after 0.01 part of 1.8 parts of epoxy resin, 0.8 part of polyamide curing agent and coupling agent is mixed, be layered on the ortho-water mud layer basal plane of dried flat, form epoxy bottom coating after ambient cure, its thickness is 0.15mm;
(3) by weight, after 1 part, 5 parts, epoxy resin material, modified amine curing agent mixed, be layered on epoxy bottom coating, form epoxy floating coat after ambient cure, its thickness is 0.3mm;
(4) by weight, after 0.5 part of 100 parts of weathe resistance epoxy resins, 3 parts, rare earth aluminate fluorescent material, 45 parts, UV resistant solidifying agent and auxiliary agent is mixed, be layered on epoxy floating coat, form epoxy finishing coat, its thickness is 0.4mm;
(5) treat epoxy finishing coat complete drying.
Embodiment tetra-:
(1) by weight percentage, by epoxy resin 50%, reactive thinner 2%, quartzy pulvis 39.9%, pigment 8%, auxiliary agent 0.1% mixes, and is mixed with epoxy resin material;
(2) by weight, after 0.01 part of 1.9 parts of epoxy resin, 0.9 part of polyamide curing agent and coupling agent is mixed, be layered on the ortho-water mud layer basal plane of dried flat, form epoxy bottom coating after ambient cure, its thickness is 0.1mm;
(3) by weight, after 1 part, 5 parts, epoxy resin material, modified amine curing agent mixed, be layered on epoxy bottom coating, form epoxy floating coat after ambient cure, its thickness is 0.2mm;
(4) by weight, after 0.2 part of 100 parts of weathe resistance epoxy resins, 2 parts, rare earth aluminate fluorescent material, 42 parts, UV resistant solidifying agent and auxiliary agent is mixed, be layered on epoxy floating coat, form epoxy finishing coat, its thickness is 0.3mm;
(5) treat epoxy finishing coat complete drying.
Embodiment five:
(1) by weight percentage, by epoxy resin 55%, reactive thinner 7%, quartzy pulvis 35%, pigment 2%, auxiliary agent 1% mixes, and is mixed with epoxy resin material;
(2) by weight, after 0.02 part of 2.1 parts of epoxy resin, 1.1 parts of polyamide curing agents and coupling agent is mixed, be layered on the ortho-water mud layer basal plane of dried flat, form epoxy bottom coating after ambient cure, its thickness is 0.18mm;
(3) by weight, after 1 part, 4 parts, epoxy resin material, modified amine curing agent mixed, be layered on epoxy bottom coating, form epoxy floating coat after ambient cure, its thickness is 0.4mm;
(4) by weight, after 0.8 part of 100 parts of weathe resistance epoxy resins, 4 parts, rare earth aluminate fluorescent material, 48 parts, UV resistant solidifying agent and auxiliary agent is mixed, be layered on epoxy floating coat, form epoxy finishing coat, its thickness is 0.45mm;
(5) treat epoxy finishing coat complete drying.
The utility model compared with prior art, have the following advantages: (1) the utility model adopts the light-accumulation fluorescent powder Rare earth doped aluminates with steady persistence, this material, after the irradiation of daylight and light, can continue luminous 6-10 hours, can meet people's in evening lighting demand; (2) the utility model not only has the attractive in appearance of epoxide terrace, also has high acidproof, antiseptic property; (3) the sustainable luminous of the utility model, economical environment-protective, beautifies the environment, durable in use, can be used in the environment such as urban road, park, square and lounge.
It should be noted last that, above embodiment is only unrestricted in order to the technical solution of the utility model to be described, although the utility model is had been described in detail with reference to preferred embodiment, those of ordinary skill in the art is to be understood that, can modify or be equal to replacement the technical solution of the utility model, and not departing from the spirit and scope of technical solutions of the utility model, it all should be encompassed in the middle of claim scope of the present utility model.
Claims (4)
1. an epoxy resin luminous ground, comprise ortho-water mud layer, it is characterized in that, described ortho-water mud layer upper berth is provided with one deck epoxy bottom coating, on described epoxy bottom coating, be equipped with one deck epoxy floating coat, on described epoxy floating coat, be equipped with the epoxy finishing coat that one deck contains rare earth aluminate fluorescent material.
2. epoxy resin luminous according to claim 1 ground, is characterized in that, the thickness of described epoxy bottom coating is 0.05-0.2mm.
3. epoxy resin luminous according to claim 1 ground, is characterized in that, the thickness of described epoxy floating coat is 0.1-0.5mm.
4. epoxy resin luminous according to claim 1 ground, is characterized in that, the thickness of described epoxy finishing coat is 0.2-0.5mm.