CN107417215A - A kind of novel water permeable brick - Google Patents
A kind of novel water permeable brick Download PDFInfo
- Publication number
- CN107417215A CN107417215A CN201710869927.2A CN201710869927A CN107417215A CN 107417215 A CN107417215 A CN 107417215A CN 201710869927 A CN201710869927 A CN 201710869927A CN 107417215 A CN107417215 A CN 107417215A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- permeable brick
- water
- microlith
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of novel water permeable brick, fraction proportioning by weight is made up of following components：230 337 parts of quartz sand, 8 10 parts of black cement, 73 94 parts of silicate cement, 25 parts of iron oxide red, 32 36 parts of water, 15 20 parts of fine sand, 6 14 parts of mortar coagulator, 8 10 parts of mine tailing, 15 20 parts of 55 70 part, meter stone of air entraining agent, 11 13 parts of cementing agent, 1.5 2.1 parts of additive, 340 531 parts of microlith aggregate, 14 parts of pigment, 9 13 parts of cement intensifier, 12 14 parts of accelerator.The advantage of the invention is that：Water-permeable brick surface layer of the present invention is prepared by quartz sand, black cement, iron oxide red, and bottom is relatively good by mine tailing, fine sand, rice stone and cement production systD, quality, it is hardly damaged, service life is also just long, and due to containing iron oxide red in surface layer, therefore the appearance of water-permeable brick then better appearance.
Description
Technical field
The present invention relates to field of new materials, more particularly to a kind of novel water permeable brick.
Background technology
With the development of Process of Urbanization Construction, increasing hard ground is laid in city, its environment-friendly function is poor, displeasant
Occupy.For example, excess surface water and urban waterlogging, natural precipitation can not ooze caused by the tropical island effect of mattess, drainage difference
Saturating recharge of groundwater causes ground water circulation to go to pot.Existing concrete road pavement brick is a kind of typical hard ground, greatly
Mostly solid brick, coefficient of permeability is very low, does not possess pervious function substantially.
Because of the demand in " sponge city ", all kinds of seepy materials are widely used to municipal afforestation project.Water-permeable brick is as one
The material that kind has been widely used and technology maturation, construction is simple, cost are cheap is the fields such as pavement, community parking position, square
The main selection that ground is mated formation.
Existing all kinds of water-permeable bricks cause itself or water permeability poor because of its selection factor, or rough surface influence it is attractive in appearance, or into
Produce a series of problems, such as cost is high.
The content of the invention
Good the technical problem to be solved in the present invention is to provide a kind of water permeability, intensity is high, the cheap novel water permeable of cost
Brick.
In order to solve the above technical problems, the technical scheme is that：A kind of novel water permeable brick, its innovative point are：Press
Weight fraction proportioning is made up of following components：
Quartz sand 230-337 parts, black cement 8-10 parts, silicate cement 73-94 parts, iron oxide red 2-5 parts, water 32-36 parts, fine sand
15-20 parts, mortar coagulator 6-14 parts, mine tailing 8-10 parts, air entraining agent 55-70 parts, rice stone 15-20 parts, cementing agent 11-13
Part, additive 1.5-2.1 parts, microlith aggregate 340-531 parts, pigment 1-4 parts, cement intensifier 9-13 parts, accelerator 12-14
Part.
Further, the particle diameter of the quartz sand is 2-3mm, and the particle diameter of microlith aggregate is 3-5mm.
Further, the microlith aggregate is basalt microlith, and cementing agent is magnalium cementing agent, and cement intensifier is hollow
Microballon.
The advantage of the invention is that：Water-permeable brick surface layer of the present invention is prepared by quartz sand, black cement, iron oxide red, bottom by
Mine tailing, fine sand, rice stone and cement production systD, quality is relatively good, is hardly damaged, and service life is also just long, and due to
Contain iron oxide red in surface layer, therefore the appearance of water-permeable brick then better appearance.
For novel water permeable brick in the present invention from evengranular quartz sand as surface material, surface layer is uniformly attractive in appearance and protects
Tiny slit is stayed, from evengranular high-strength basalt as base material, ensures to leave while foundation base intension tiny
Slit.This product surface layer is uniformly attractive in appearance, and wearability is strong, and water permeability is good, and intensity is high, and cost is cheap.
Magnalium cementing agent is used in the present invention, and the particle diameter of magnalium cementing agent is nanoscale, is existed in the absence of organic cementing agent
Present in heating process because of the heatproof low intensity caused by oxidation the problem of, make novel water permeable brick heat resistance good.
Embodiment
The following examples can make professional and technical personnel that the present invention be more fully understood, but therefore not send out this
It is bright to be limited among described scope of embodiments.
Embodiment 1
The novel water permeable brick of present invention fraction proportioning by weight is made up of following components：
Fraction proportioning by weight is made up of following components：
230 parts of quartz sand, 8 parts of black cement, 73 parts of silicate cement, 2 parts of iron oxide red, 32 parts of water, 15 parts of fine sand, mortar coagulator 6
Part, 8 parts of mine tailing, 15 parts of 55 part, meter stone of air entraining agent, 11 parts of cementing agent, 1.5 parts of additive, 340 parts of microlith aggregate, pigment 1
Part, 9 parts of cement intensifier, 12 parts of accelerator.
In above-mentioned formula, the particle diameter of quartz sand is 2-3mm, and the particle diameter of microlith aggregate is 3-5mm, and microlith aggregate is the Black Warrior
Rock microlith, cementing agent are magnalium cementing agent, and cement intensifier is cenosphere.
Embodiment 2
The novel water permeable brick of present invention fraction proportioning by weight is made up of following components：
Fraction proportioning by weight is made up of following components：
337 parts of quartz sand, 10 parts of black cement, 94 parts of silicate cement, 5 parts of iron oxide red, 36 parts of water, 20 parts of fine sand, mortar coagulator
14 parts, 10 parts of mine tailing, 20 parts of 70 part, meter stone of air entraining agent, 13 parts of cementing agent, 2.1 parts of additive, 531 parts of microlith aggregate, pigment
4 parts, 13 parts of cement intensifier, 14 parts of accelerator.
In above-mentioned formula, the particle diameter of quartz sand is 2-3mm, and the particle diameter of microlith aggregate is 3-5mm, and microlith aggregate is the Black Warrior
Rock microlith, cementing agent are magnalium cementing agent, and cement intensifier is cenosphere.
Embodiment 3
The novel water permeable brick of present invention fraction proportioning by weight is made up of following components：
Fraction proportioning by weight is made up of following components：
287 parts of quartz sand, 9 parts of black cement, 84 parts of silicate cement, 3 parts of iron oxide red, 34 parts of water, 17 parts of fine sand, mortar coagulator 10
Part, 9 parts of mine tailing, 17 parts of 63 part, meter stone of air entraining agent, 12 parts of cementing agent, 1.8 parts of additive, 436 parts of microlith aggregate, pigment 2
Part, 11 parts of cement intensifier, 13 parts of accelerator.
In above-mentioned formula, the particle diameter of quartz sand is 2-3mm, and the particle diameter of microlith aggregate is 3-5mm, and microlith aggregate is the Black Warrior
Rock microlith, cementing agent are magnalium cementing agent, and cement intensifier is cenosphere.
Water-permeable brick surface layer of the present invention is prepared by quartz sand, black cement, iron oxide red, bottom by mine tailing, fine sand, meter Shi with
And cement production systD, quality is relatively good, is hardly damaged, and service life is also just long, and due to containing iron oxide red in surface layer, therefore
The appearance of water-permeable brick then better appearance.
For novel water permeable brick in the present invention from evengranular quartz sand as surface material, surface layer is uniformly attractive in appearance and protects
Tiny slit is stayed, from evengranular high-strength basalt as base material, ensures to leave while foundation base intension tiny
Slit.This product surface layer is uniformly attractive in appearance, and wearability is strong, and water permeability is good, and intensity is high, and cost is cheap.
Magnalium cementing agent is used in the present invention, and the particle diameter of magnalium cementing agent is nanoscale, is existed in the absence of organic cementing agent
Present in heating process because of the heatproof low intensity caused by oxidation the problem of, make novel water permeable brick heat resistance good.
It should be understood by those skilled in the art that the present invention is not limited to the above embodiments, above-described embodiment and explanation
Merely illustrating the principles of the invention described in book, without departing from the spirit and scope of the present invention, the present invention also have
Various changes and modifications, these changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention
By appended claims and its equivalent thereof.
Claims (3)
- A kind of 1. novel water permeable brick, it is characterised in that：Fraction proportioning by weight is made up of following components：Quartz sand 230-337 parts, black cement 8-10 parts, silicate cement 73-94 parts, iron oxide red 2-5 parts, water 32-36 parts, fine sand 15-20 parts, mortar coagulator 6-14 parts, mine tailing 8-10 parts, air entraining agent 55-70 parts, rice stone 15-20 parts, cementing agent 11-13 Part, additive 1.5-2.1 parts, microlith aggregate 340-531 parts, pigment 1-4 parts, cement intensifier 9-13 parts, accelerator 12-14 Part.
- 2. novel water permeable brick according to claim 1, it is characterised in that：The particle diameter of the quartz sand is 2-3mm, microlith bone The particle diameter of material is 3-5mm.
- 3. novel water permeable brick according to claim 1, it is characterised in that：The microlith aggregate is basalt microlith, cementing Agent is magnalium cementing agent.