CN106892620A - A kind of water-permeable brick and its production technology - Google Patents
A kind of water-permeable brick and its production technology Download PDFInfo
- Publication number
- CN106892620A CN106892620A CN201710180164.0A CN201710180164A CN106892620A CN 106892620 A CN106892620 A CN 106892620A CN 201710180164 A CN201710180164 A CN 201710180164A CN 106892620 A CN106892620 A CN 106892620A
- Authority
- CN
- China
- Prior art keywords
- water
- rubble
- permeable brick
- cement
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to building material technical field, and in particular to a kind of water-permeable brick and its production technology suitable for pavement.The water-permeable brick includes the raw material of following parts by weight：90 200 parts of 180 400 parts of cement, 100 240 parts of 950 2160 part, meter stone of rubble, 0.3 2 parts of rubber powder, 0.8 3 parts of pigment and water.The present invention is by preparing various materials, preparing basic unit, prepare surface layer, natural curing forming step the water-permeable brick is obtained.Permeable brick structure of the present invention is fine and close, and intensity is high, and permeable effect is good, can be applied to pavement.
Description
Technical field
The invention belongs to building material technical field, and in particular to a kind of water-permeable brick and its production work suitable for pavement
Skill.
Background technology
As country is to energy-saving and emission-reduction, the call of comprehensive utilization of resources, the research and development of product requirement higher set out above.
The timely Collection utilization of such as rainwater, can solve urban waterlogging, and draining problem not in time causes that the water resource drained can again
With secondary utilization.By long-term observation, it is found that rainy day, especially heavy rain, during the pedestrian of pavement, still occurs
Ponding, pedestrian is very inconvenient on foot.Splicing seams between its arterial drainage path or brick and brick, and only enter by splicing seams
Row draining, can not meet heavy rain weather, the requirement of draining at all.For areas such as the pavement on urban road, square, parking lots
Domain, water-permeable brick application is gradually extensive, but existing water-permeable brick permeability rate is extremely low.
Chinese patent application CN104909640A discloses a kind of water-permeable brick and preparation method thereof, according to mass percent,
It is prepared from the following components：It is quartz sand 25%-30%, black cement 8%-10%, iron oxide red 0.5%-1%, mine tailing 8%-10%, thin
Sand 15%-20%, rice stone 15%-20%, cement 15%-20%.Present invention also offers the preparation process of water-permeable brick.The present invention has
The water-permeable brick long service life of preparation, it is specious the advantages of.But, the water-permeable brick cement content very little, the structure of water-permeable brick
More open, by the bonding effect of cement, very little, bonding force is not enough, low intensity for amount for self-strength；Contain sand, and amount in raw material
The amount of cement is alreadyd exceed, permeable path is easily blocked, and sand has an effect on the parcel power of cement and stone, reduces cement
Cementation.
Chinese patent CN101445340B discloses a kind of white clean formula water-permeable brick, including fabric and base-material, the base-material with
Weight percent meter, including rubble or building waste particle or slag 68.4%-77.5%, cement 10%-25%, water 5.3%-12%,
The fabric is in terms of weight percent, including high intensity sand 66.7%-71.8%, the 8%-26.5% of cement 10., the 4%- of water 3.
10.4%, Nano titanium dioxide 0.1% -1.0%, the fabric and base-material it is compacted together constitute a water-permeable brick entirety.This hair
It is bright to also disclose a kind of preparation method of white clean formula water-permeable brick：1）Weigh base-material and fabric is premixed respectively, stirring is used as former
Material is stand-by；2）Shaping；3）Steam curing；4）Sprinkling liquid titanium.White clean formula water-permeable brick laying road surface of the invention can be reduced
Permeable pore plugging, surface contamination with attenuating pavement temperature and efficient sterilizing effect, and recovers natural soil air and water
The circulatory system, prevent soil pollution from improving ecological environment.But, the patent water-permeable brick cement content is too small, water-permeable brick
Structure is also more open, and, by the bonding effect of cement, very little, bonding force is not enough, low intensity for amount for self-strength；Late maintaining mode
It is steam curing, maintenance cost is high, the wasting of resources；Fabric is substantial amounts of high intensity sand, and permeable effect is poor；Raw material type is complicated,
It is difficult to stir.
The content of the invention
To overcome drawbacks described above, it is an object of the invention to provide a kind of water-permeable brick and its production technology.
To achieve the above object, the present invention is adopted the following technical scheme that：
A kind of water-permeable brick, including following parts by weight raw material：Cement 180-400 parts, rubble 950-2160 parts, rice stone 100-
240 parts, rubber powder 0.3-2 parts, pigment 0.8-3 parts and water 90-200 parts.
Preferably, described cement is PO32.5R, PO42.5, PO42.5R, PO52.5 or PO52.5R class g cement.
Preferably, described rubble be 5-12mm grades of rubble, 10-15mm grades of rubble, 12-20mm grades of rubble, 15-25mm grades
In rubble and 20-30mm grades of rubble any one or a few.
Preferably, the particle diameter of described meter Shi is 2-5mm.
Preferably, the rubber powder is a kind of or several in hydroxypropyl methyl cellulose, dispersibility latex powder and polyvinyl alcohol
Kind.
Preferably, the pigment is iron black or iron oxide red.
The production technology of above-mentioned water-permeable brick is comprised the following steps：
（1）Prepare various materials；
（2）Prepare basic unit：The 50-70% of rubble, the 50-70% of cement, the 20-25% of rubber powder and water is well mixed, mould is put into
In tool, compacting；
（3）Prepare surface layer：Meter Shi, remaining cement, remaining rubber powder, pigment and remaining water are well mixed, continue to put into above-mentioned
In mould, compacting；
（4）Natural curing is molded.
Positive beneficial effect of the invention：
1. the various raw materials of water-permeable brick of the present invention act synergistically, gained water-permeable brick water-permeable brick compression strength >=22MPa, anti-folding destruction
Load >=6005N, mill hole length≤25mm, water-retaining property >=0.7 g/cm2, coefficient of permeability >=0.11cm/s, compact structure, intensity
Height, permeable effect is good, can be applied to pavement.
2. rubble of the present invention is 5-12mm grades of rubble, 10-15mm grades of rubble, 12-20mm grades of rubble, 15-25mm
Level rubble and 20-30mm grades of rubble in any one or a few, basic unit is crushed stone material, is matched somebody with somebody by the level of reasonable arrangement stone,
While permeable effect being taken into account, the mutual insertion between big small particle stone, and the intensity of entirety can be improved, surface layer is rice
Stone material, permeable effect is good, and aesthetic quality is good, and surface strength is high, also with anti-skidding effect higher.
3. water-permeable brick production technology of the present invention first makes basic unit's material with capstock respectively, it is to avoid influence each other,
Then natural curing mode is used, is economized on resources, and raw material is simple, and mixing is easily uniform.
Specific embodiment
With reference to some specific embodiments, the present invention is further described.
Embodiment 1
A kind of water-permeable brick, including following weight raw material：
180kg, 10-15mm grade of rubble 950kg of PO42.5 class g cements, rice stone 100kg, dispersibility latex powder 0.3kg, pigment
Iron black 0.8kg and water 90kg.
The particle diameter of described meter Shi is 3mm.
The production technology of above-mentioned water-permeable brick is comprised the following steps：
（1）Prepare various materials；
（2）Prepare basic unit：Rubble, the 50% of cement, the 20% of rubber powder and water 50% are well mixed, are put into mould, pressed
It is real；
（3）Prepare surface layer：Meter Shi, remaining cement, remaining rubber powder, pigment and remaining water are well mixed, continue to put into above-mentioned
In mould, compacting；
（4）Natural curing is molded.
Embodiment 2
A kind of water-permeable brick, including following weight raw material：
PO32.5R class g cements 180kg, rubble 972kg, rice stone 108kg, hydroxypropyl methyl cellulose 0.3kg, pigment iron oxide red
0.8kg and water 90kg.
The rubble is by 5-12mm grades of rubble 252kg, 10-15mm grade broken 620kg, 12-20mm grades of rubble 100kg group
Into.
The particle diameter of described meter Shi is 5mm.
The production technology of above-mentioned water-permeable brick is comprised the following steps：
（1）Prepare various materials；
（2）Prepare basic unit：Rubble, the 55% of cement, the 22% of rubber powder and water 55% are well mixed, are put into mould, pressed
It is real；
（3）Prepare surface layer：Meter Shi, remaining cement, remaining rubber powder, pigment and remaining water are well mixed, continue to put into above-mentioned
In mould, compacting；
（4）Natural curing is molded.
Embodiment 3
A kind of water-permeable brick, including following weight raw material：
PO42.5 class g cements 200kg, rubble 1000kg, rice stone 120kg, dispersibility latex powder 0.5kg, pigment iron oxide black 1.0kg
With water 100kg.
The rubble is by 10-15mm grades of broken 500kg, 15-25mm grades of rubble 500kg composition.
The particle diameter of described meter Shi is 3mm.
The production technology of above-mentioned water-permeable brick is comprised the following steps：
（1）Prepare various materials；
（2）Prepare basic unit：Rubble, the 60% of cement, the 20% of rubber powder and water 55% are well mixed, are put into mould, pressed
It is real；
（3）Prepare surface layer：Meter Shi, remaining cement, remaining rubber powder, pigment and remaining water are well mixed, continue to put into above-mentioned
In mould, compacting；
（4）Natural curing is molded.
Embodiment 4
A kind of water-permeable brick, including following weight raw material：
PO42.5R class g cements 250kg, rubble 1350kg, rice stone 150kg, polyvinyl alcohol 0.8kg, pigment iron oxide red 1.6kg and water
120kg。
The rubble by 5-12mm grades of rubble 150kg, 10-15mm grade broken 500kg, 12-20mm grades of rubble 300kg and
15-25mm grades of rubble 400kg composition.
The particle diameter of described meter Shi is 2mm.
The production technology of above-mentioned water-permeable brick is comprised the following steps：
（1）Prepare various materials；
（2）Prepare basic unit：Rubble, the 65% of cement, the 23% of rubber powder and water 60% are well mixed, are put into mould, pressed
It is real；
（3）Prepare surface layer：Meter Shi, remaining cement, remaining rubber powder, pigment and remaining water are well mixed, continue to put into above-mentioned
In mould, compacting；
（4）Natural curing is molded.
Embodiment 5
A kind of water-permeable brick, including following weight raw material：
PO52.5 class g cements 300kg, rubble 1620kg, rice stone 180kg, hydroxypropyl methyl cellulose 1kg, pigment iron oxide red 2kg and
Water 150kg.
The rubble is by 5-12mm grades of rubble 320kg, 10-15mm grade broken 500kg, 12-20mm grades of rubble 800kg group
Into.
The particle diameter of described meter Shi is 2mm.
The production technology of above-mentioned water-permeable brick is comprised the following steps：
（1）Prepare various materials；
（2）Prepare basic unit：Rubble, the 60% of cement, the 23% of rubber powder and water 60% are well mixed, are put into mould, pressed
It is real；
（3）Prepare surface layer：Meter Shi, remaining cement, remaining rubber powder, pigment and remaining water are well mixed, continue to put into above-mentioned
In mould, compacting；
（4）Natural curing is molded.
Embodiment 6
A kind of water-permeable brick, including following weight raw material：
PO52.5 class g cements 200kg, haydite 120kg, rubble 1620kg, rice stone 180kg, hydroxypropyl methyl cellulose 1kg, face
Material iron oxide red 2kg and water 150kg.
The haydite particle diameter is 1-3mm.
The rubble is by 5-12mm grades of rubble 320kg, 10-15mm grade broken 500kg, 12-20mm grades of rubble 800kg group
Into.
The particle diameter of described meter Shi is 2mm.
The production technology of above-mentioned water-permeable brick is comprised the following steps：
（1）Prepare various materials；
（2）Prepare basic unit：Rubble, the 60% of cement, the 50% of haydite, the 23% of rubber powder and water 60% are well mixed, are put into
In mould, compacting；
（3）Prepare surface layer：Meter Shi, remaining cement, remaining haydite, remaining rubber powder, pigment and remaining water are well mixed, continue to put
Enter in above-mentioned mould, be compacted；
（4）Natural curing is molded.
The present embodiment adds haydite, and haydite density is low, cylindrical compress strength is high, porosity is high, and coefficient of softing is high, frost resistance is good
Good, alkali resistant aggregate reaction is excellent, haydite loose structure, improves the water penetration of water-permeable brick, and haydite specific surface area is big, with cement
Structural capacity it is strong, improve the intensity of water-permeable brick.
Embodiment 7
A kind of water-permeable brick, including following weight raw material：
PO52.5 class g cements 320kg, rubble 1800kg, rice stone 200kg, dispersibility latex powder 1.2kg, pigment iron oxide red
2.1kg and water 160kg.
The rubble is by 5-12mm grades of rubble 200kg, 10-15mm grade broken 400kg, 12-20mm grades of rubble 600kg, 15-
300kg and 20-30mm grade of rubble 300kg composition of 25mm grades of rubble.
The particle diameter of described meter Shi is 2mm.
The production technology of above-mentioned water-permeable brick is comprised the following steps：
（1）Prepare various materials；
（2）Prepare basic unit：Rubble, the 65% of cement, the 25% of rubber powder and water 65% are well mixed, are put into mould, pressed
It is real；
（3）Prepare surface layer：Meter Shi, remaining cement, remaining rubber powder, pigment and remaining water are mixed
Uniformly, continue to put into above-mentioned mould, be compacted；
（4）Natural curing is molded.
Embodiment 8
A kind of water-permeable brick, including following weight raw material：
PO42.5 class g cements 350kg, rubble 2000kg, rice stone 210kg, polyvinyl alcohol 1.5kg, pigment iron oxide black 2.5kg and water
180kg。
The rubble is by 5-12mm grades of rubble 300kg, 10-15mm grade broken 400kg, 12-20mm grades of rubble 600kg, 15-
400kg and 20-30mm grade of rubble 300kg composition of 25mm grades of rubble.
The particle diameter of described meter Shi is 2mm.
The production technology of above-mentioned water-permeable brick is comprised the following steps：
（1）Prepare various materials；
（2）Prepare basic unit：Rubble, the 70% of cement, the 22% of rubber powder and water 65% are well mixed, are put into mould, pressed
It is real；
（3）Prepare surface layer：Meter Shi, remaining cement, remaining rubber powder, pigment and remaining water are well mixed, continue to put into above-mentioned
In mould, compacting；
（4）Natural curing is molded.
Embodiment 9
A kind of water-permeable brick, including following weight raw material：
PO52.5R class g cements 360kg, rubble 2100kg, rice stone 230kg, hydroxypropyl methyl cellulose 0.9kg, dispersibility
Latex powder 0.9kg, pigment iron oxide red 2.7kg and water 190kg.
The rubble is by 5-12mm grades of rubble 400kg, 10-15mm grade broken 500kg, 12-20mm grades of rubble 500kg, 15-
500kg and 20-30mm grade of rubble 200kg composition of 25mm grades of rubble.
The particle diameter of described meter Shi is 3mm.
The production technology of above-mentioned water-permeable brick is comprised the following steps：
（1）Prepare various materials；
（2）Prepare basic unit：Rubble, the 70% of cement, the 25% of rubber powder and water 65% are well mixed, are put into mould, pressed
It is real；
（3）Prepare surface layer：Meter Shi, remaining cement, remaining rubber powder, pigment and remaining water are well mixed, continue to put into above-mentioned
In mould, compacting；
（4）Natural curing is molded.
Embodiment 10
A kind of water-permeable brick, including following weight raw material：
PO52.5 class g cements 400kg, rubble 2160kg, rice stone 240kg, polyvinyl alcohol 2kg, pigment iron oxide black 3kg and water
200kg。
The rubble is by 5-12mm grades of rubble 560kg, 10-15mm grade broken 600kg, 12-20mm grades of rubble 1000kg.
The particle diameter of described meter Shi is 4mm.
The production technology of above-mentioned water-permeable brick is comprised the following steps：
（1）Prepare various materials；
（2）Prepare basic unit：Rubble, the 65% of cement, the 25% of rubber powder and water 70% are well mixed, are put into mould, pressed
It is real；
（3）Prepare surface layer：Meter Shi, remaining cement, remaining rubber powder, pigment and remaining water are well mixed, continue to put into above-mentioned
In mould, compacting；
（4）Natural curing is molded.
Comparative example 1
With reference to Chinese patent application CN104909640A, water-permeable brick is prepared, processing step is as follows：
Step one：According to mass percent, 25% quartz sand, 10% black cement, 1% iron oxide red are added in mixer, add water stirring
Uniformly, so as to be prepared into fabric；
Step 2：According to mass percent, 10% mine tailing, 18% fine sand, 18% meter of stone, 18% cement are added in mixer,
Add water and stir, so as to be prepared into bed material；
Step 3：Fabric obtained in step one is produced into surface layer using surface layer processing machine；
Step 4：Bed material obtained in step 2 is produced into bottom using bottom processing machine；
Step 5：Bottom obtained in step 4 is put into the die cavity for making brick machine, then again put surface layer obtained in step 2
Put on the upper surface of bottom, then press-fit shaping using making brick machine；
Step 6：The water-permeable brick that shaping will be press-fited is transported to workshop maintenance, carries out natural air drying；
Step 7：After air-drying, rewater and conserved, 20 days.
According to standard《Water-permeable brick professional standard》（JC/T945-2005）, by embodiment of the present invention 1-10 and comparative example
1 water-permeable brick makes 200 × 40mm specifications, and testing result is shown in Table 1.
The embodiment of the present invention 1-10 of table 1 and the water-permeable brick performance parameter of comparative example 1
As shown in Table 1, comparative example, embodiment of the present invention 1-10 water-permeable bricks compression strength >=22MPa, pressure resistance are compared to
Degree is high, and anti-folding failing load >=6005N, anti-folding failing load is high, and mill hole length≤25mm, wearability is good, water-retaining property >=0.7
g/cm2, good water-retaining property, coefficient of permeability >=0.11cm/s, permeable effect is good.
Claims (7)
1. a kind of water-permeable brick, it is characterised in that the raw material including following parts by weight：Cement 180-400 parts, rubble 950-2160
Part, 100-240 parts, rubber powder 0.3-2 parts, pigment 0.8-3 parts and water 90-200 parts of rice stone.
2. water-permeable brick according to claim 1, it is characterised in that described cement be PO32.5R, PO42.5, PO42.5R,
PO52.5 or PO52.5R class g cements.
3. water-permeable brick according to claim 1, it is characterised in that described rubble be 5-12mm grades of rubble, 10-15mm grades it is broken
In stone, 12-20mm grade rubble, 15-25mm grades of rubble and 20-30mm grades of rubble any one or a few.
4. water-permeable brick according to claim 1, it is characterised in that the particle diameter of described meter Shi is 2-5mm.
5. water-permeable brick according to claim 1, it is characterised in that the rubber powder is hydroxypropyl methyl cellulose, dispersibility
In latex powder and polyvinyl alcohol one or more.
6. water-permeable brick according to claim 1, it is characterised in that the pigment is iron black or iron oxide red.
7. the production technology of water-permeable brick described in a kind of claim 1, it is characterised in that comprise the following steps：
（1）Prepare various materials；
（2）Prepare basic unit：The 50-70% of rubble, the 50-70% of cement, the 20-25% of rubber powder and water is well mixed, mould is put into
In tool, compacting；
（3）Prepare surface layer：Meter Shi, remaining cement, remaining rubber powder, pigment and remaining water are well mixed, continue to put into above-mentioned
In mould, compacting；
（4）Natural curing is molded.