CN106830885A - A kind of production method of pseudo-classic potter's clay flowerpot - Google Patents
A kind of production method of pseudo-classic potter's clay flowerpot Download PDFInfo
- Publication number
- CN106830885A CN106830885A CN201710016343.0A CN201710016343A CN106830885A CN 106830885 A CN106830885 A CN 106830885A CN 201710016343 A CN201710016343 A CN 201710016343A CN 106830885 A CN106830885 A CN 106830885A
- Authority
- CN
- China
- Prior art keywords
- flowerpot
- potter
- clay
- raw material
- idiosome
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention is a kind of production method of pseudo-classic potter's clay flowerpot, by the ripe mud of potter's clay, polished waste material and at least two pigment are well mixed, it is exhausted through homogenizer and is processed as strip material embryo, material embryo uses mould compressing in being sequentially placed into forming machine, flowerpot idiosome after compressing is together with mould one dried process, the demoulding is carried out to dried flowerpot idiosome, flowerpot idiosome feeding kiln after the demoulding is fired and obtains finished product flowerpot, potter's clay has the color of soil itself, the color of potter's clay can be changed after mixing with pigment, because being that the raw material before firing is mixed, therefore the color of potter's clay script is changed, after the mixing of at least two coloured pigments, color is usually dark, after adding potter's clay raw material, potter's clay raw material color is set to be primitive color, the form of potter's clay script is remained simultaneously, obtain pseudo-classic potter's clay flowerpot.
Description
Technical field
The present invention relates to flowerpot production technical field, more particularly to a kind of production method of pseudo-classic potter's clay flowerpot.
Background technology
Flowerpot is kind an a kind of vessel for flower, is the small inverted round stage in the big bottom of mouth or terrace edge shape, the flower of plantation flowers
Basin is various informative, not of uniform size, can select flowerpot according to the characteristics of the characteristic of flower plant and needs and flowerpot, more typically
Be potter's clay flowerpot or jardiniere.
Potter's clay flowerpot is to be fired to form with clay, there is kind of a natural affinity to soil, and with corrosion-resistant, permeability
Strong the characteristics of.Jardiniere is because draining, aeration are poor, many people when flowers are planted in order to the flower-pot cover that is treated as attractive in appearance is used,
Even directly appreciated as ornament.For the effect for taking into account plantation and appreciate, occur many ornamental potter's clay now
Flowerpot, more typically pseudo-classic potter's clay flowerpot, pseudo-classic flowerpot has the color and form of years vestige and taste and standby due to it
Liked by people, but how to realize that the quantization production of pseudo-classic flowerpot never has suitable method.
The content of the invention
It is an object of the invention to be directed to above technical problem, there is provided a kind of production method of pseudo-classic potter's clay flowerpot.
The ripe mud of potter's clay, polished waste material and at least two pigment are mixed equal by a kind of production method of pseudo-classic potter's clay flowerpot
It is even, it is exhausted through homogenizer and is processed as strip material embryo, material embryo uses mould compressing in being sequentially placed into forming machine, is pressed into
Flowerpot idiosome after type carries out the demoulding, the flowerpot embryo after the demoulding together with mould one dried process to dried flowerpot idiosome
Body feeding kiln fire 20-24 hours after again natural cooling 13-17 hours in kiln, obtain finished product flowerpot.
Wherein in one embodiment, the production process of the ripe mud is as follows：Weigh 1000kg laterite, 30-50kg kaolinites
Soil, 2-5kg baths of glass enter ball mill, add 300-400kg water to enter ball mill and raw material is pulverized and mixed uniformly as mud is delivered to
In raw material hole；Mud is entered in cooked flake wrapping machine by compression pump, the excessive moisture in mud is removed during cake of press, while to raw material
Further crushed, cooked flake wrapping machine pie raw material out enters in homogenizer, and homogenizer is exhausted treatment, in removing raw material
Gas reach the purpose of homogeneous, while moisture unnecessary in further removing raw material, raw material is out bar from homogenizer
The ripe mud of shape.
Kiln is delivered to wherein in one embodiment, after the flowerpot idiosome demoulding through polishing to fire.
Wherein in one embodiment, the polished waste material is from flowerpot idiosome in flowerpot idiosome polishing process after the demoulding
The upper waste material for cutting.
Wherein in one embodiment, the pigment is flowerpot surface coloring pigment, the use of pigment is at least two colors
Pigment is mixed.
In sum, a kind of production method of pseudo-classic potter's clay flowerpot, by the ripe mud of potter's clay, polished waste material and at least two face
Material is well mixed, is exhausted through homogenizer and is processed as strip material embryo, and material embryo is pressed into being sequentially placed into forming machine using mould
Type, it is compressing after flowerpot idiosome together with mould one dried process, the demoulding is carried out to dried flowerpot idiosome, after the demoulding
Flowerpot idiosome feeding kiln fire and obtain finished product flowerpot, potter's clay has the color of soil itself, and pottery can be changed after mixing with pigment
The color of soil, because being that the raw material before firing is mixed, therefore changes the color of potter's clay script, at least two color face
After material mixing, color is usually dark, after adding potter's clay raw material, makes potter's clay raw material color for primitive color, while remaining potter's clay
The form of script, therefore the last flowerpot produced according to flowerpot production technology has pseudo-classic color, so as to generate pseudo-classic
Flowerpot, and subsequent technique is identical with common potter's clay flowerpot technique, can realize high-volume production.
Specific embodiment
With reference to implementation method, the present invention is further detailed explanation.
The ripe mud of potter's clay, polished waste material and at least two pigment are mixed equal by a kind of production method of pseudo-classic potter's clay flowerpot
It is even, it is exhausted through homogenizer and is processed as strip material embryo, material embryo uses mould compressing in being sequentially placed into forming machine, is pressed into
Flowerpot idiosome after type carries out the demoulding, the flowerpot embryo after the demoulding together with mould one dried process to dried flowerpot idiosome
Body feeding kiln fire 20-24 hours after again natural cooling 13-17 hours in kiln, obtain finished product flowerpot.
The key problem of pseudo-classic flowerpot batch large-scale production is the proportioning of raw material, and raw material needs mixing such as primitive color,
Unify potter's clay raw material integral color, the product colour for finally obtaining could be unified, and primitive color is usually black system color, and
It is a kind of color close to soil and neither one is clearly defined, therefore is realized using various pigment hybrid energy multiple to difference
The modulation of patina, at the same can to production during assorted waste material carry out mixing match, therefore, it is possible to be given up to production process
Material is rationally utilized.
Wherein in one embodiment, the production process of the ripe mud is as follows：Weigh 1000kg laterite, 30-50kg kaolinites
Soil, 2-5kg baths of glass enter ball mill, add 300-400kg water to enter ball mill and raw material is pulverized and mixed uniformly as mud is delivered to
In raw material hole；Mud is entered in cooked flake wrapping machine by compression pump, the excessive moisture in mud is removed during cake of press, while to raw material
Further crushed, cooked flake wrapping machine pie raw material out enters in homogenizer, and homogenizer is exhausted treatment, in removing raw material
Gas reach the purpose of homogeneous, while moisture unnecessary in further removing raw material, raw material is out bar from homogenizer
The ripe mud of shape.Bath of glass is, by high-temperature digestion into clinker, then to form a kind of half with high-temperature high pressure water by sodium carbonate with quartz
Transparent solution, plays electrolyte effect in ceramic raw material forming process.Bath of glass is added in raw slurry the inside and can play dilute
The effect released, can improve the mobile performance of mud, and not influence the intensity of mud.
Kiln is delivered to wherein in one embodiment, after the flowerpot idiosome demoulding through polishing to fire.Flowerpot idiosome
The smoothness on flowerpot edge and surface can be increased after polishing, in order to the pseudo-classic sense for increasing pseudo-classic flowerpot can be to flowerpot embryo
Body is not processed by shot blasting, retains flowerpot and produce initial form.
Wherein in one embodiment, the polished waste material is from flowerpot idiosome in flowerpot idiosome polishing process after the demoulding
The upper waste material for cutting.Give up the corner that potter's clay flowerpot is substantially carried out being cut in physical change, therefore polishing process before the firing
Material can be collected the raw material as pseudo-classic flowerpot.
Wherein in one embodiment, the pigment is flowerpot surface coloring pigment, the use of pigment is at least two colors
Pigment is mixed.In order to embody pseudo-classic color effects, reconciled using multiple color and be preferred.
Embodiment 1
A kind of production method of pseudo-classic potter's clay flowerpot：Weigh 1000kg laterite, 30kg kaolin, 2kg baths of glass and enter ball mill, plus
Enter 300kg water and enter ball mill and be pulverized and mixed raw material uniform for mud to deliver to raw material hole；Mud is entered by compression pump presses
Remove the excessive moisture in mud in cake machine, during cake of press, while further being crushed to raw material, cooked flake wrapping machine cake out
Shape raw material enters in homogenizer, and homogenizer is exhausted treatment, removes the purpose that the gas in raw material reaches homogeneous, while can enter
One step removes unnecessary moisture in raw material, and raw material is out the ripe mud of strip from homogenizer, by ripe mud, the polished waste material of potter's clay
It is well mixed with red, two kinds of pigment of yellow, is exhausted through homogenizer and is processed as strip material embryo, material embryo is sequentially placed into forming machine
Middle use mould is compressing, it is compressing after flowerpot idiosome together with mould one dried process, to dried flowerpot embryo
Body carries out the demoulding, flowerpot idiosome after demoulding feeding kiln fire 20 hours after natural cooling 13 hours in kiln again, obtain into
Product flowerpot.
Embodiment 2
A kind of production method of pseudo-classic potter's clay flowerpot：Weigh 1000kg laterite, 40kg kaolin, 3kg baths of glass and enter ball mill, plus
Enter 350kg water and enter ball mill and be pulverized and mixed raw material uniform for mud to deliver to raw material hole；Mud is entered by compression pump presses
Remove the excessive moisture in mud in cake machine, during cake of press, while further being crushed to raw material, cooked flake wrapping machine cake out
Shape raw material enters in homogenizer, and homogenizer is exhausted treatment, removes the purpose that the gas in raw material reaches homogeneous, while can enter
One step removes unnecessary moisture in raw material, and raw material is out the ripe mud of strip from homogenizer, by ripe mud, the polished waste material of potter's clay
It is well mixed with white, blue, violet pigment, is exhausted through homogenizer and is processed as strip material embryo, material embryo is sequentially placed into shaping
In machine using mould it is compressing, it is compressing after flowerpot idiosome together with mould one dried process, to dried flowerpot
Idiosome carries out the demoulding, flowerpot idiosome after demoulding feeding kiln fire 22 hours after natural cooling 15 hours in kiln again, obtain
Finished product flowerpot.
Embodiment 3
A kind of production method of pseudo-classic potter's clay flowerpot：Weigh 1000kg laterite, 50kg kaolin, 5kg baths of glass and enter ball mill, plus
Enter 400kg water and enter ball mill and be pulverized and mixed raw material uniform for mud to deliver to raw material hole；Mud is entered by compression pump presses
Remove the excessive moisture in mud in cake machine, during cake of press, while further being crushed to raw material, cooked flake wrapping machine cake out
Shape raw material enters in homogenizer, and homogenizer is exhausted treatment, removes the purpose that the gas in raw material reaches homogeneous, while can enter
One step removes unnecessary moisture in raw material, and raw material is out the ripe mud of strip from homogenizer, by ripe mud, the polished waste material of potter's clay
It is well mixed with blueness, green, brown, red pigment, is exhausted through homogenizer and is processed as strip material embryo, material embryo is sequentially placed into
In forming machine using mould it is compressing, it is compressing after flowerpot idiosome together with mould one dried process, to dried
Flowerpot idiosome carries out the demoulding, flowerpot idiosome after demoulding feeding kiln fire 24 hours after natural cooling 17 hours in kiln again,
Obtain finished product flowerpot.
The above implementation method is only the preferred embodiment of the present invention, it is noted that for the art
Those of ordinary skill, under the premise without departing from the principles of the invention, can also make improvement and deform, these improve and deform
Also should be regarded as not departing from protection scope of the present invention.
Claims (5)
1. a kind of production method of pseudo-classic potter's clay flowerpot, it is characterised in that：By the ripe mud of potter's clay, polished waste material and at least two face
Material is well mixed, is exhausted through homogenizer and is processed as strip material embryo, and material embryo is pressed into being sequentially placed into forming machine using mould
Type, it is compressing after flowerpot idiosome together with mould one dried process, the demoulding is carried out to dried flowerpot idiosome, after the demoulding
Flowerpot idiosome feeding kiln fire 20-24 hours after again natural cooling 13-17 hours in kiln, obtain finished product flowerpot.
2. a kind of production method of pseudo-classic potter's clay flowerpot according to claim 1, it is characterised in that：The production of the ripe mud
Journey is as follows：Weigh 1000kg laterite, 30-50kg kaolin, 2-5kg baths of glass and enter ball mill, add 300-400kg water to enter ball milling
Machine simultaneously is pulverized and mixed raw material uniform for mud to deliver to raw material hole；Mud is entered in cooked flake wrapping machine by compression pump, cake of press process
In remove excessive moisture in mud, while further being crushed to raw material, cooked flake wrapping machine pie raw material out enters homogeneous
In machine, homogenizer is exhausted treatment, removes the purpose that the gas in raw material reaches homogeneous, while in further removing raw material
Unnecessary moisture, raw material is out the ripe mud of strip from homogenizer.
3. a kind of production method of pseudo-classic potter's clay flowerpot according to claim 1, it is characterised in that：The flowerpot idiosome demoulding
Kiln is delivered to by polishing to fire.
4. a kind of production method of pseudo-classic potter's clay flowerpot according to claim 1, it is characterised in that：The polished waste material is de-
The waste material for getting off is cut from flowerpot idiosome in flowerpot idiosome polishing process after mould.
5. a kind of production method of pseudo-classic potter's clay flowerpot according to claim 1, it is characterised in that：The pigment is flowerpot table
Face colouring pigment, using pigment at least two coloured pigments are mixed.