CN101722788A - Antique finished porcelain with twisted body and manufacturing method thereof - Google Patents
Antique finished porcelain with twisted body and manufacturing method thereof Download PDFInfo
- Publication number
- CN101722788A CN101722788A CN200810230408A CN200810230408A CN101722788A CN 101722788 A CN101722788 A CN 101722788A CN 200810230408 A CN200810230408 A CN 200810230408A CN 200810230408 A CN200810230408 A CN 200810230408A CN 101722788 A CN101722788 A CN 101722788A
- Authority
- CN
- China
- Prior art keywords
- texture
- mud
- porcelain
- twisted body
- pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an antique finished porcelain product with twisted body, which has at least two colors and determined texture and patterns which are exposed through the inside and outside of green body. The manufacturing method of the antique finished porcelain product with twisted body comprises the steps of raw material processing, molding, firing and the like. The manufactured antique finished porcelain product with twisted body has determined texture and patterns which are exposed through the inside and outside of green body, and reproduces all the characteristics of antique porcelain with twisted body. The invention adopts a handcrafted technique, porcelain clays of various colors are twisted mutually for molding, or porcelain pastes of two colors are twisted to make determined texture to be stuck and molded on a female die to determine the colors and patterns of the ware.
Description
Technical field
The invention belongs to ceramic, relate in particular to a kind of antique finished porcelain with twisted body, the invention still further relates to the preparation method of this antique finished porcelain with twisted body.
Background technology
Strand tire porcelain claims " stirring the tire porcelain " again, is to put or integrate with two or more look mud is alternate the ceramic that burns till through throwing moulding, glazing.Be interlinked to the outside in the various textures of made porcelain or identical, have the effect that is different from other porcelain.Strand tire porcelain comes across the Tang Dynasty, and is prosperous in the Song dynasty, and its kiln site is positioned at present Xiuwu County, Henan Province when positive valley one band, and quiet asking in health year because of chaos caused by war interrupted, and its production method has only a small amount of goods to deposit generation because of of the remote past lost.In recent years, the production method of genseng according to domestic ceramics arranged constantly, attempt recovering this tradition name porcelain, but fail to realize the preparation method that this is lost always.The patent No. is Chinese patent strand tire artistic porcelain and the production method thereof of 03126249.X, discloses a kind of strand tire artistic porcelain that utilizes grinding placenta process and modern art pottery skill and technique to combine and produce, and the production method of this strand tire artistic porcelain is provided.The strand tire porcelain that this invention is produced has only reappeared the inside and outside consistent feature of strand tire porcelain, but because the defective of manufacture craft, can not make to twist the tire porcelain in predetermined texture and pattern and ancient times bigger difference is arranged, and can not obtain experts and scholars' approval.For example, this method can not be copied out the feature of the featheriness texture of determining on Song's Dangyangyu kilns strand tire canister.
Summary of the invention
The object of the present invention is to provide a kind of antique finished porcelain with twisted body and preparation method thereof with definite texture and pattern.
To achieve these goals, the present invention by the following technical solutions: a kind of antique finished porcelain with twisted body includes at least two kinds of colors, and have through base substrate, in texture and the pattern determined that are interlinked to the outside.
The preparation method of described antique finished porcelain with twisted body comprises raw material processing, moulding, fires, and wherein forming step is:
A, pug through the manual white silk of rubbing, discharge the air in the pug, the pug of different colours is cut into the identical mud cake of size, the mud cake of different colours is overlapped on together, make the mud cake that thickness has texture uniformly;
B, the mud cake that processes is cut into uniform mud bar, again the mud bar is cut into the mud section;
C, with mud section upset, make facing up of exhibit textural, according to definite texture, pattern and model size, push, be spliced into the bulk mud cake;
D, the bulk mud cake is patted, repaired, then put into definite former, push with hand, and use the formpiston that is complementary with former to carry out punching press, and then finishing;
E, the former that will match carry out matched moulds structure envelope;
After f, the drying, from former, take out base substrate, treat the abundant drying of base substrate after, take off mill, the base substrate extexine is sloughed 0.3～0.7 millimeter, the endosexine is also sloughed 0.3～0.7 millimeter, washes base then, water respectively is washed till inside and outside top layer few 1 time;
G, etc. get final product glazing behind the body drying.
Described extruding is meant the mud section is squeezed into the mud section that has the alternate texture of color according to definite texture.
Described splicing is meant that the mud section splicing that will have texture becomes definite pattern.
Described definite texture is meant the featheriness texture, and seat is compiled texture.
Described definite pattern is meant birds pattern, bird pattern.
Take off in the mill process, the base substrate extexine is sloughed 0.5 millimeter, the endosexine is also sloughed 0.5 millimeter.
Firing temperature is 1280 ℃～1300 ℃, and the time is 8～10 hours.
The strand tire porcelain that adopts technique scheme to make, have see through base substrate, in texture and the pattern determined that are interlinked to the outside, all features of twisting the tire porcelain ancient times have been reappeared, what the present invention used is a kind of artisan craftsmanship gimmick, it is with the mutual stranded moulding of the tire soil phase of multiple color, or it is laminating on former to twist out definite texture with the tire mud of two kinds of colors, and the design and color of implements is all determined, decorative pattern has feather line, leaf line, wood grain, cloudlet line etc.Use this invention preparation method successfully to copy out Song's Dangyangyu kilns strand tire canister, and have a jar round mouth, short neck, the drum abdomen, flat.Neck is executed white glaze, and outer belly glaze colours is brown white dichromatism, and decorative pattern is the feather ring-type, and the ring ring superposes, and has reproduced all characteristics of Song's Dangyangyu kilns strand tire canister.Be subjected to expert and scholar's consistent favorable comment.
The specific embodiment
Embodiment 1
A kind of antique finished porcelain with twisted body includes brown, white two kinds of colors, and have through base substrate, in texture and the pattern determined that are interlinked to the outside.The preparation method of described antique finished porcelain with twisted body, step such as comprise raw material processing, moulding, fire, wherein forming step is:
A, the pug of brown and white through the manual white silk of rubbing, discharge the air in the pug, this pug of two kinds is cut into each 3 of the identical mud cakes of size respectively, the mud cake of different colours is overlapped on together, make the mud cake that thickness has brown white alternate texture uniformly;
B, the mud cake that processes is cut into wide 1 centimetre mud bar, again the mud bar is cut into 2 centimetres mud section;
C, with mud section upset, make to show facing up of brown white alternate texture, with mud section jack-up before the white side direction, be extruded into arc with finger tip, each arc mud section is stitched together by equidirectional, and extruding is closely made the bulk mud cake;
D, the bulk mud cake is patted, repaired, then put into definite former, push with hand, and use the formpiston that is complementary with former to carry out punching press, remove the outer unnecessary mud of former with pocket knife then;
E, two formers that match are carried out matched moulds structure envelope;
F, natural air drying after the drying, take out base substrate from former, treat the abundant drying of base substrate after, take off mill, the base substrate extexine is sloughed 0.5 millimeter, the endosexine is also sloughed 0.5 millimeter, water is respectively washed inside and outside top layer 1 time then;
G, etc. behind the body drying, last clear frit.
The control firing temperature is 1300 ℃, and the time is 9.5 hours.
It after firing successfully antique finished porcelain with twisted body with featheriness texture.
The strand tire canister that adopts technique scheme to make, have through base substrate, in texture and the pattern determined that are interlinked to the outside, all features of having reappeared Song's Dangyangyu kilns strand tire canister, jar young, rich shoulder, flat.Except that mouth was executed white glaze, entire body twisted out just like the featheriness decorative pattern with white, brown dichromatism mud, imposes clear frit again.Be subjected to expert and scholar's consistent favorable comment.
Embodiment 2
In step a, the manual white silk of rubbing of the pug process of blue and white, discharge the air in the pug, this pug of two kinds is cut into each 3 of the identical mud cakes of size respectively, the mud cake of different colours is overlapped on together, make the mud cake that thickness has blue white alternate texture uniformly, and reserve a part of white mud cake.Among the step c, arc mud section is spliced into the pattern of bird shape, fills up white mud section then in the gap.Other steps are with embodiment 1.
After firing successfully be have have through base substrate, in the antique finished porcelain with twisted body of bird pattern of the featheriness texture that is interlinked to the outside.
Embodiment 3
In step c, directly the mud section is staggeredly placed, make the texture of adjacent mud section perpendicular, and extruding is closely made the bulk mud cake.Other steps are with embodiment 1.
After firing successfully be have through base substrate, in the seat that is interlinked to the outside compile the antique finished porcelain with twisted body of texture.
Claims (8)
1. antique finished porcelain with twisted body is characterized in that: include at least two kinds of colors, and have through base substrate, in texture and the pattern determined that are interlinked to the outside.
2. the preparation method of antique finished porcelain with twisted body as claimed in claim 1 comprises raw material processing, moulding, fires, and it is characterized in that forming step is:
A, pug through the manual white silk of rubbing, discharge the air in the pug, the pug of different colours is cut into the identical mud cake of size, the mud cake of different colours is overlapped on together, make the mud cake that thickness has texture uniformly;
B, the mud cake that processes is cut into uniform mud bar, again the mud bar is cut into the mud section;
C, with mud section upset, make facing up of exhibit textural, according to definite texture, pattern and model size, push, be spliced into the bulk mud cake;
D, the bulk mud cake is patted, repaired, then put into definite former, push with hand, and use the formpiston that is complementary with former to carry out punching press, and then finishing;
E, the former that will match carry out matched moulds structure envelope;
After f, the drying, from former, take out base substrate, treat the abundant drying of base substrate after, take off mill, the base substrate extexine is sloughed 0.3～0.7 millimeter, the endosexine is also sloughed 0.3～0.7 millimeter, washes base then, water respectively is washed till inside and outside top layer few 1 time;
G, etc. get final product glazing behind the body drying.
3. according to the described antique finished porcelain with twisted body preparation method of claim 2, it is characterized in that: described extruding is meant the mud section is squeezed into the mud section that has the alternate texture of color according to definite texture.
4. according to the described antique finished porcelain with twisted body preparation method of claim 3, it is characterized in that: described splicing is meant that the mud section splicing that will have texture becomes definite pattern.
5. according to the described antique finished porcelain with twisted body preparation method of claim 4, it is characterized in that: described definite texture is meant the featheriness texture, and seat is compiled texture.
6. according to the described antique finished porcelain with twisted body preparation method of claim 5, it is characterized in that: described definite pattern is meant birds pattern, bird pattern.
7. according to the described antique finished porcelain with twisted body preparation method of claim 2, it is characterized in that: take off in the mill process, the base substrate extexine is sloughed 0.5 millimeter, the endosexine is also sloughed 0.5 millimeter.
8. according to the described antique finished porcelain with twisted body preparation method of claim 2, it is characterized in that: firing temperature is 1280 ℃～1300 ℃, and the time is 8～10 hours.