CN106751836A - 一种石墨烯复合吸波聚硫密封剂 - Google Patents
一种石墨烯复合吸波聚硫密封剂 Download PDFInfo
- Publication number
- CN106751836A CN106751836A CN201611025282.6A CN201611025282A CN106751836A CN 106751836 A CN106751836 A CN 106751836A CN 201611025282 A CN201611025282 A CN 201611025282A CN 106751836 A CN106751836 A CN 106751836A
- Authority
- CN
- China
- Prior art keywords
- cream
- absorbing
- sealant
- graphene
- composite wave
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明是一种石墨烯复合吸波聚硫密封剂,它是由基膏和硫化膏两个组分构成。其中基膏包含液体聚硫橡胶、石墨烯、羰基铁粉、环氧树脂;硫化膏包含二氧化锰、邻苯二甲酸二丁酯、促进剂DPG、硬脂酸。通过将石墨烯超声处理分散在基膏中制备的复合吸波聚硫密封剂在1GHz‑18GHz吸收雷达波性能良好,是一种良好的雷达吸波密封剂。
Description
技术领域
本发明一种石墨烯复合吸波聚硫密封剂,属于高分子材料及其生产技术领域,该密封剂具备良好的低频吸波性能,主要用于飞机或地面军事目标的隐身密封。
背景技术
目前雷达仍然是探测目标最主要、最可靠的设备,且不断向宽频化方向发展,主要的工作频段在0.5GHz-18GHz范围内。这就要求目标在宽频范围内具有优良的吸波性能,达到干扰雷达探测的目的。
目前对于飞机或电子设备的金属壳体可以通过使用涂层材料或贴片来达到吸收雷达波等电磁波的目的,但目前的研究主要集中在2GHz-18GHz范围内,对于2GHz以下的低频吸收性能研究较少。
《材料科学与工程学报》2007,Vol.25,No.1:99-101上公开的有机硅吸波密封胶的研究,以羰基铁粉为吸收剂、107硅橡胶(PDMS)为基体,配合硫化剂制备了吸波密封剂,研究其力学性能。
《材料科学与工程学报》2006,Vol.24,No.5:718-721上公开的羰基铁粉/硅橡胶复合体系的物理性能研究,以微米级羰基铁粉为填充剂,硅橡胶为基体,制备了单组分室温硫化的复合橡胶,研究了基铁粉添加量对复合橡胶机械性能、热空气老化性能和耐热稳定性的影响。
上述吸波材料研究仅仅研究了吸波材料的力学性能、耐热空气老化性能等,对于吸波材料的吸波能力研究未涉及,尚处于初步探索试验研究阶段,其实际吸波能力距离实际应用还有较大差距。
发明内容
本发明的目的正是针对现有研究的不足和实际应用的需求,而设计提供了一种一种石墨烯复合吸波聚硫密封剂,该吸波密封剂借助石墨烯配合羰基铁粉制备的密封剂在1GHz~18GHz范围内具备良好的吸波能力,可以用于干扰雷达探测的目标表面处理,实现隐身目的。
本发明的目的是通过以下技术方案来实现的:
该种石墨烯复合吸波聚硫密封剂,其特征在于:该密封剂是由基膏和硫化膏两个组分混合而成,基膏的组分及其质量份数为:
所述的液体聚硫橡胶是采用巯基封端的,其数均分子量在1000~6000之间,巯基摩尔百分比含量为0.5%~2%;
所述的石墨烯是将Hmmers法配合超声处理制备的氧化石墨烯,采用水合肼还原得到的;
所述的羰基铁粉的微观形态是球状或片状;
所述的环氧树脂牌号为E-44;
硫化膏的组分及其质量份数为:
本发明技术方案的特点是采用液体聚硫橡胶为基胶,以石墨烯复合羰基铁粉为吸波填料,以环氧树脂作为增粘剂、以二氧化锰为硫化剂制备的聚硫密封剂,制备出一种低频吸波的密封剂,该密封剂可以广泛应用在需要吸收电磁波尤其是雷达波部位的密封。
本发明技术方案中的基膏和硫化膏可以采用相同的方法炼制:将配方中的各组分按比例称量,将称取的物料混合均匀,采用三辊研磨剂混合3~5遍形成均匀的膏状物,然后将基膏和硫化膏按质量份数进行配比,混合均匀即可使用,密封剂在室温下即可固化。
本发明所述密封剂与现有技术相比具有如下优点:
1、采用石墨烯复合羰基铁粉提高了低频吸波性能,2GHz垂直反射率可以达到不高于-1.5dB,1GHz垂直反射率可以达到不高于-1.0dB
2、采用石墨烯复合羰基铁粉降低了密封剂的密度,密度由3.5g/cm3降低到了3.0g/cm3以下。
具体实施方式
以下将结合实施例对本发明技术方案作进一步地详述:
本发明技术方案实施中密封剂的各组分及其用量如表1所示。表1中每一个序号代表一种密封剂的实施例,其中序号6#为对比实施例。实施例的性能测试值如表2所示。以表1中序号1#的实施为例,密封剂的制备方法的步骤如下:
(1)基膏的制备:称取100份液体聚硫橡胶、0.1份石墨烯、150份羰基铁粉、3.0份环氧树脂E-44手混均匀后,用三辊研磨机混炼5遍混合均匀;
(2)硫化膏的制备:称取100份二氧化锰、120份邻苯二甲酸二丁酯、1.0份促进剂DPG、2.0份硬脂酸手混均匀后,用三辊研磨机混炼5遍混合均匀;
(3)密封剂的制备:按100∶4称取基膏和硫化膏,手工预混合,然后用三辊研磨机混炼3遍混合均匀,然后按照相应标准制备测试试片。
其中石墨烯复合吸波密封剂的密度按GB/T533-2008测试,垂直反射率按GJB2038A-2011测试,测试结果见表2。
从表2可以看出,本发明的石墨烯复合吸波密封剂采用石墨烯与羰基铁粉复合后,与未使用羰基铁粉的密封剂性能相比,1GHz和2GHz的垂直反射率显著降低,分别从-0.3dB和-0.5dB降低到-1.0dB和-1.5dB;密封剂的密度也从3.6g/cm3降低到2.6g/cm3。
表1石墨烯复合吸波聚硫密封剂配方中各组分的组合及用量
表2石墨烯复合吸波聚硫密封剂硫化后性能
Claims (1)
1.一种石墨烯复合吸波聚硫密封剂,其特征在于:该密封剂是由基膏和硫化膏两个组分混合而成,基膏的组分及其质量份数为:
所述的液体聚硫橡胶是采用巯基封端的,其数均分子量在1000~6000之间,巯基摩尔百分比含量为0.5%~2%;
所述的石墨烯是将Hmmers法配合超声处理制备的氧化石墨烯,采用水合肼还原得到的;
所述的羰基铁粉的微观形态是球状或片状;
所述的环氧树脂牌号为E-44;
硫化膏的组分及其质量份数为:
基膏和硫化膏的质量份数比为100∶(3~5)。