CN106750720A - 纳米改性高密度聚乙烯材料 - Google Patents

纳米改性高密度聚乙烯材料 Download PDF

Info

Publication number
CN106750720A
CN106750720A CN201510830163.7A CN201510830163A CN106750720A CN 106750720 A CN106750720 A CN 106750720A CN 201510830163 A CN201510830163 A CN 201510830163A CN 106750720 A CN106750720 A CN 106750720A
Authority
CN
China
Prior art keywords
density polyethylene
nano modification
antioxidant
dispersant
area
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510830163.7A
Other languages
English (en)
Inventor
黄亚楠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingdao Gerunde New Material Co Ltd
Original Assignee
Qingdao Gerunde New Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Gerunde New Material Co Ltd filed Critical Qingdao Gerunde New Material Co Ltd
Priority to CN201510830163.7A priority Critical patent/CN106750720A/zh
Publication of CN106750720A publication Critical patent/CN106750720A/zh
Pending legal-status Critical Current

Abstract

聚乙烯缺点是耐候性能和温度性能较差，通过纳米改性后，聚乙烯本身的物理性能将发生改变。本发明的目的是提供一种纳米改性高密度聚乙烯。纳米改性高密度聚乙烯材料由下列重量比的原料组成：高密度聚乙烯：70～80；纳米超细碳酸钙：10～30；偶联剂：0.5～1.5；PE蜡：1.0～2.0；抗氧剂：0.5～1.5；分散剂：0.5～1.5；交联剂：0.5～1.5。

Description

纳米改性高密度聚乙烯材料
技术领域
本发明属于纳米改性高密度聚乙烯材料材料生产技术领域，改善了纳米改性高密度聚乙烯材料的不足。
背景技术
聚乙烯简称PE，是五大合成树脂之一。聚乙烯-简聚乙烯主要分为线性低密度聚乙烯(LLDPE)、低密度聚乙烯(LDPE)、高密度聚乙烯(HDPE)三大类。HDPE通常用于强度高、韧性好的产品，如防弹材料。其缺点是耐候性能和温度性能较差，通过纳米改性后，聚乙烯本身的物理性能将发生改变。
发明内容
本发明的目的是提供一种纳米改性高密度聚乙烯。纳米改性高密度聚乙烯材料由下列重量比的原料组成：
高密度聚乙烯：70～80；
纳米超细碳酸钙：10～30；
偶联剂：0.5～1.5；
PE蜡：1.0～2.0；
抗氧剂：0.5～1.5；
分散剂：0.5～1.5；
交联剂：0.5～1.5。
本发明中所述分散剂为TAS-2A分散润滑剂，所述抗氧剂为乙烯-辛烯的共聚物，所述交联剂为过氧化二异丙苯，所述偶联剂为钛酸酯。
该纳米改性高密度聚乙烯材料的制备方法为：先将纳米超细碳酸钙进行表面处理，再将上述各种原料在高速混合器中干混3-5分钟，再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装成品即可；其中，双螺杆挤出机一区温度为80-900℃，二区为150-170℃，三区为180-190℃，四区为175-185℃；五区为175-185℃，停留时间为1-2分钟，压力为10-15Mpa。
具体实施方式
下面通过具体实施方式对发明做进一步说明，以下实施例是对本发明进行说明而非加以限定。
实施例1
(1)按重量比分别称取各原料如下：
高密度聚乙烯：70；
纳米超细碳酸钙：10；
偶联剂：0.5；
PE蜡：1.0；
抗氧剂：0.5；
分散剂：0.5；
交联剂：0.5。
(2)将先将纳米超细碳酸钙进行表面处理，再将上述各种原料在高速混合器中干混3-5分钟，再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装成品即可；其中，双螺杆挤出机一区温度为80-900℃，二区为150-170℃，三区为180-190℃，四区为175-185℃；五区为175-185℃，停留时间为1-2分钟，压力为10-15Mpa。
实验结果：
实施例2
(1)按重量比分别称取各原料如下：
高密度聚乙烯：75；
纳米超细碳酸钙：20；
偶联剂：1.0；
PE蜡：1.5；
抗氧剂：1.0；
分散剂：1.0；
交联剂：1.0。
(2)将先将纳米超细碳酸钙进行表面处理，再将上述各种原料在高速混合器中干混3-5分钟，再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装成品即可；其中，双螺杆挤出机一区温度为80-900℃，二区为150-170℃，三区为180-190℃，四区为175-185℃；五区为175-185℃，停留时间为1-2分钟，压力为10-15Mpa。
实验结果：
实施例3
(1)按重量比分别称取各原料如下：
高密度聚乙烯：80；
纳米超细碳酸钙：30；
偶联剂:1.5；
PE蜡：2.0；
抗氧剂：1.5；
分散剂：1.5；
交联剂：1.5。
(2)将先将纳米超细碳酸钙进行表面处理，再将上述各种原料在高速混合器中干混3-5分钟，再置于双螺杆挤出机中经熔融挤出、冷却、切粒、包装成品即可；其中，双螺杆挤出机一区温度为80-900℃，二区为150-170℃，三区为180-190℃，四区为175-185℃；五区为175-185℃，停留时间为1-2分钟，压力为10-15Mpa。
实验结果：

Claims (3)

1.纳米改性高密度聚乙烯材料，其特征在于，由下列重量比原料组成：
高密度聚乙烯：70～80；
纳米超细碳酸钙：10～30；
偶联剂：0.5～1.5；
PE蜡：1.0～2.0；
抗氧剂：0.5～1.5；
分散剂：0.5～1.5；
交联剂：0.5～1.5。
2.根据权利要求1所述的纳米改性高密度聚乙烯材料，其特征在于，最优重量比原料组成为：
高密度聚乙烯：75；
纳米超细碳酸钙：20；
偶联剂：1.0；
PE蜡：1.5；
抗氧剂：1.0；
分散剂：1.0；
交联剂：1.0。
3.根据权利要求1所述的纳米改性高密度聚乙烯材料，其特征在于，所述分散剂为TAS-2A分散润滑剂，所述抗氧剂为乙烯-辛烯的共聚物，所述交联剂为过氧化二异丙苯，所述偶联剂为钛酸酯。
CN201510830163.7A 2015-11-25 2015-11-25 纳米改性高密度聚乙烯材料 Pending CN106750720A (zh)