CN106747486A - 一种涂料 - Google Patents
一种涂料 Download PDFInfo
- Publication number
- CN106747486A CN106747486A CN201510803664.6A CN201510803664A CN106747486A CN 106747486 A CN106747486 A CN 106747486A CN 201510803664 A CN201510803664 A CN 201510803664A CN 106747486 A CN106747486 A CN 106747486A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- weight
- hot
- metal bottle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种涂料,其特征在于涂料的组成为:Al2O3:45—65份(以重量计),SiO2:8—20份(重量),SiC:5—12份(重量),C:8—15份(重量)。本发明由于采用Al2O3-SiC-C系涂料,能减低金属熔液和熔渣对铁水罐衬侵蚀和渗透,可以提高铁水罐的使用寿命,使铁水罐不“粘包”,减少其因铁水“粘包”产生的损失,并且除罐衬和冷铁容易。
Description
技术领域
本发明属于涂料领域,特别涉及一种用于铁水罐内衬的涂料。
背景技术
冶金工业中,常用铁水罐盛装铁水,因此铁水罐内衬的作用是用于搞高温金属溶液和熔渣对铁水罐的侵蚀。由于铁水罐在倒铁水时,随着铁水的温度下降,使铁水在罐衬上形成冷铁而产生粘滞现象(冶金行业称“粘包”),并且越积越厚,使铁水罐的有效体积大大减少,同时在清除罐中炉渣和冷铁时,容易损坏铁水罐衬,降低铁水罐的使用寿命。
本发明的目的,是提供一种涂料,它能减少金属熔液和熔渣对铁水罐的侵蚀、渗透、减少铁水“粘包”,清除罐衬和冷铁容易,并且能提高铁水罐的使用寿命的特点。为达上述目的,本发明的特征在于涂料的组成为:
Al2O345-65份(以重量计)、SiO2:8—20份(重量)SiC:5—12份(重量),C:8—15份(重量)
Al2O3的含量为25—60%
SiO2的含量为20—40%
SiC的含量为5—20%
C的含量为5—15%
本涂料上述组成可以采用耐火粘土粉为骨料,配加矾土熟料粉,碳化硅粉、碗粉、石墨粉、硅微粉组成基质并添加三聚磷酸钠。其中三聚磷酸钠和硅微粉对本涂料中的粉料有分散作用,使其混合均匀,三聚磷酸钠是一种减水剂,在本涂料加水混料时可以提高其塑性,使其与罐衬形成牢固的保护层。耐火粘土粉、矾土熟料粉和碗粉在铁水的高温作用下,形成部分莫来石相,能提高本涂料的对熔渣的耐腐蚀性,碳化硅粉和石墨粉可以防止熔渣对罐衬的渗透并且耐剥落性好。
具体实施方式:
本发明由于采用AI2O3—SiC—C系涂料,能减低金属熔液和熔渣对铁水罐衬侵蚀和渗透,因此可以提高铁水罐的使用寿命。同时可以降低铁水罐的“粘包”,并且有除罐衬和冷铁容易的特点。采用本涂料,铁水罐的使用寿命大大提高,由原来的每个铁水罐平均使用35次提高到平均使用300次。
下面通过实施例对本发明做进一步的说明,但本发明不仅限于这些例子,
实施例1(以下计量为重量份)
取60%的AI2O345份,加入20%的SiO28份,10%的SiC5份,10%的C8份,混匀后加入总重量6%的水,用常规的方法进行喷涂;
实例2(以下计量为重量份)
取45%的AI2O350份,加入30%的SiO212份,15%的SiC7份,10%的C10份,混匀后加入总重量6%的水,用常规的方法进行喷涂;
实例3(以下计量为重量份)
取45%的AI2O355份,加入30%的SiO215份,15%的SiC10份,10%的C12份,混匀后加入总重量6%的水,用常规的方法进行喷涂;
实例4(以下计量为重量份)
取25%的AI2O365份,加入40%的SiO220份,20%的SiC12份,15%的C15份,混匀后加入总重量6%的水,用常规的方法进行喷涂。
Claims (4)
1. 一种涂料,其特征在于涂料的组成为:
Al2O345-65份(以重量计)、SiO2:8—20份(重量)SiC:5—12份(重量),C:8—15份(重量)。
2.根据权利要求1所述的一种涂料,其特征在于Al2O3的含量为25—60%。
3.根据权利要求1所述的一种涂料,其特征在于SiO2的含量为20—40%。
4.根据权利要求1所述的一种涂料,其特征在于C的含量为5—15%。