CN106700191A - 用于粉末注射成形的粘结剂及注射成形方法 - Google Patents

用于粉末注射成形的粘结剂及注射成形方法 Download PDF

Info

Publication number
CN106700191A
CN106700191A CN201510783631.XA CN201510783631A CN106700191A CN 106700191 A CN106700191 A CN 106700191A CN 201510783631 A CN201510783631 A CN 201510783631A CN 106700191 A CN106700191 A CN 106700191A
Authority
CN
China
Prior art keywords
paraffin
component
binding agent
mass fraction
composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510783631.XA
Other languages
English (en)
Inventor
王林生
王全生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU MIMO METAL TECHNOLOGY Co Ltd
Original Assignee
SUZHOU MIMO METAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU MIMO METAL TECHNOLOGY Co Ltd filed Critical SUZHOU MIMO METAL TECHNOLOGY Co Ltd
Priority to CN201510783631.XA priority Critical patent/CN106700191A/zh
Publication of CN106700191A publication Critical patent/CN106700191A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种用于粉末注射成形的粘结剂，其包括20％～60％质量份数的组分A，其中该组分A选自由聚乙烯、高密度聚乙烯、聚丙烯、聚苯乙烯、聚酰胺、乙烯-醋酸乙烯共聚物和聚乙烯醇和其改性体组成的热塑性树脂组；6％～15％质量份数的组分B，其中该组分B选自由C5石油树脂和C9石油树脂组成的石油树脂组；和10％～20％质量份数的组分C，其中该组分C选自由C52石蜡、C54石蜡、C56石蜡、C58石蜡、C60石蜡、C62石蜡和C64石蜡组成的石蜡组。

Description

用于粉末注射成形的粘结剂及注射成形方法
技术领域
本发明涉及粉末注射成形技术领域，尤其涉及用于可烧结金属粉末，如铁粉或可烧结非金属，如陶瓷粉末注射成形的粘结剂。
背景技术
金属粉末注射成形(Metal Injection Molding，简称MIM)是一种将金属粉末(或可烧结非金属，如陶瓷粉末)与相应粘结剂的混合原料注射于模型中成形的冶金技术。在最近十几年，金属粉末注射成形技术发展迅速，其不仅具有常规冶金工艺的工序少、切削少等优点，还克服了传统冶金技术的制品密度低、材质不均、机械性能低、无法制造复杂形状结构制品等缺点。金属粉末注射成形技术特别适合大批量制造形状复杂的金属零件或部件。
金属粉末注射成形技术需要选取符合要求的金属粉末(或可烧结非金属，如陶瓷粉末)和粘结剂，然后在一定温度下，采用适当的方法将粉末和粘结剂混合制成混合原料，然后再对混合料进行制粒，随后将混合原料颗粒注射成形得到具有预期形状的成形坯，最后，成形坯经过脱脂和烧结处理，致密化成为最终成品。如果需要的话，后期还可能会对制成品进行二次机械加工和表面处理。在金属粉末注射成形技术中，粘结剂起着非常关键的作用。粘结剂的加入是在金属粉末注射成形成形加工工艺链的上游，去除则是在烧结之前，因此，一旦粘结剂导致成形坯出现缺陷，则此缺陷将难以在后续工艺中被去除。因此，粘结剂的加入和脱除直接影响到混合、注射成形、脱脂等工序，对注射成形坯的质量、脱脂及尺寸精度、合金成分等有很大的影响。粘结剂的脱除不完全会影响到产品的质量。粘结剂的脱除难度过高或脱除工艺过于复杂，会导致最终产品的生产成本上升。可以说，在金属粉末注射成形技术中，粘结剂的脱除最费时、最难控制，是MIM中最困难和最重要的环节，其一直是阻碍MIM技术发展的难题。
根据粘结剂的组成，现有的金属粉末注射成形粘结剂常被分为塑基体系和蜡基体系。蜡基体系粘结剂的组成成分主要是石蜡和聚烯烃等，其具有粘度低、成形坯强度高、注射范围宽、成本低、装载量高等优点。但蜡基体系粘结剂在混料时易发生挥发、易产生相分离、注射料性能不稳定、保形性差。塑基体系的组成成分主要是长链聚醛树脂等，其具有成形坯强度高、保形式性好等优点。但塑基体系粘结剂价格高昂、难以根据实际的工艺和制造产品对具体成份进行调整。此外，现有的金属粉末注射成形粘结剂还具有以下缺陷：首先，现有的金属粉末注射成形工艺多需用到硝酸或三氯乙烯，生产过程不够安全和环保；其次，混合喂料利用率低，工艺复杂和产品保型性差；最后，粘结剂原料价格相对较高，导致生产成本较高。
发明内容
本发明的主要目的在于其提供一种用于金属粉末，如铁粉或可烧结非金属，如陶瓷粉末注射成形粘结剂的组合物，其中使用该组合物的粘结剂比现有的粘结剂更加环境友好。
本发明的另一目的在于其提供一种用于金属粉末，如铁粉或可烧结非金属，如陶瓷粉末注射成形粘结剂的组合物，其中使用该组合物的粘结剂可有效提高混合喂料的利用率和生产效率。
本发明的另一目的在于其提供一种用于金属粉末，如铁粉或可烧结非金属，如陶瓷注射成形粘结剂的组合物，其中使用该组合物的粘结剂的组成成分的沸点或降解温度不同，以使粘结剂在脱脂过程中随着温度的升高被逐渐除去，从而尽可能使粘结剂在金属粉末或可烧结非金属，如陶瓷粉末注射成形过程中被去除完全。
本发明的另一目的在于其提供一种用于金属粉末，如铁粉或可烧结非金属，如陶瓷粉末注射成形粘结剂的粘结剂，其中该粘结剂比现有的粘结剂更加环境友好。
本发明的另一目的在于其提供一种用于金属粉末，如铁粉或可烧结非金属，如陶瓷粉末注射成形粘的粘结剂，其中该粘结剂可有效提高混合喂料的利用率和生产效率。
本发明的另一目的在于其提供一种用于金属粉末，如铁粉或可烧结非金属，如陶瓷粉末注射成形的粘结剂，其中该粘结剂的组成成分的沸点或降解温度不同，以使粘结剂在脱脂过程中随着温度的升高被逐渐除去，从而尽可能使粘结剂在金属粉末或可烧结非金属，如陶瓷粉末注射成形过程中被去除完全。
本发明的另一目的在于其提供一种用于金属粉末，如铁粉或可烧结非金属，如陶瓷粉末注射成形的粘结剂，其中该粘结剂的组成成分大多价格低廉和易于获得，从而使得采用本发明粘结剂的金属粉末或可烧结非金属，如陶瓷粉末注射成形技术具有更低的生产成本。
本发明的主要目的在于其提供一种新的用于制备金属(或可烧结非金属)模制品的组合物，其中该用于制备金属模制品的组合物可在加工产品的壁厚较小时，成形胚不需要萃取而直接进入烧结炉烧结，仍能除去粘结剂和制得理想产品。
本发明的主要目的在于其提供一种用于制备金属(或可烧结非金属)模制品的组合物，其中该用于制备金属模制品的组合物能够减小注射时，该组合物的组分分离，从而提高成形胚的均匀性和一致性。
本发明的主要目的在于其提供一种用于制备金属(或可烧结非金属)模制品的组合物，其中该用于制备金属模制品的组合物包括至少一种可烧结金属粉末，且该用于制备金属模制品的组合物比现有的用于制备金属模制品的组合物更加环境友好。
本发明的另一目的在于其提供一种用于制备金属(或可烧结非金属)模制品的组合物，其中该用于制备金属模制品的组合物可有效提高混合喂料的利用率和生产效率。
本发明的另一目的在于其提供一种用于制备金属(或可烧结非金属)模制品的组合物，其中该用于制备金属模制品的组合物的粘结剂的组成成分的沸点或降解温度不同，以使粘结剂在脱脂过程中随着温度的升高被逐渐除去，从而尽可能使粘结剂在金属粉末或可烧结非金属，如陶瓷粉末注射成形过程中被去除完全。
本发明的其它目的和特点通过下述的详细说明得以充分体现并可通过所附权利要求中特地指出的手段和装置的组合得以实现。
依本发明，能够实现前述目的和其他目的和优势的本发明用于制备粉末注射成形粘结剂的组合物，其包括:
20％～60％质量份数的组分A，其中该组分A选自由聚乙烯、高密度聚乙烯、聚丙烯、聚苯乙烯、聚酰胺、乙烯-醋酸乙烯共聚物和聚乙烯醇和其改性体组成的热塑性树脂组；
6％～15％质量份数的组分B，其中该组分B选自由C5石油树脂和C9石油树脂组成的石油树脂组；和
10％～20％质量份数的组分C，其中该组分C选自由C52石蜡、C54石蜡、C56石蜡、C58石蜡、C60石蜡、C62石蜡和C64石蜡组成的石蜡组。
进一步地，该粘结剂中，该组分A的质量分数为45％～50％。
进一步地，该粘结剂包括9％～27％质量份数的组分D，其中该组分D为液态石蜡。
进一步地，该粘结剂包括2％～8％质量份数的聚乙烯蜡和/或棕榈蜡。
进一步地，该粘结剂包括质量份数不大于5％的改性剂，其中该改性剂为表面改性剂、增塑剂、抗氧化剂、钝化剂和/或表面活性。
本发明进一步提供一种用于制备金属模制品的组合物，包括：
50％～65％体积份数的至少一种可烧结非金属粉末；和
35％～50％体积份数的粘结剂，其中该粘结剂包括：
20％～60％质量份数的组分A，其中该组分A选自由聚乙烯、高密度聚乙烯、聚丙烯、聚苯乙烯、聚酰胺、乙烯-醋酸乙烯共聚物和聚乙烯醇和其改性体组成的热塑性树脂组；
6％～15％质量份数的组分B，其中该组分B选自由C5石油树脂和C9石油树脂组成的石油树脂组；和
10％～20％质量份数的组分C，其中该组分C选自由C52石蜡、C54石蜡、C56石蜡、C58石蜡、C60石蜡、C62石蜡和C64石蜡组成的石蜡组。
本发明进一步提供一种用于制备非金属模制品的组合物，包括：
50％～65％体积份数的至少一种可烧结非金属粉末；和
35％～50％体积份数的粘结剂，其中该粘结剂包括：
20％～60％质量份数的组分A，其中该组分A选自由聚乙烯、高密度聚乙烯、聚丙烯、聚苯乙烯、聚酰胺、乙烯-醋酸乙烯共聚物和聚乙烯醇和其改性体组成的热塑性树脂组；
6％～15％质量份数的组分B，其中该组分B选自由C5石油树脂和C9石油树脂组成的石油树脂组；和
10％～20％质量份数的组分C，其中该组分C选自由C52石蜡、C54石蜡、C56石蜡、C58石蜡、C60石蜡、C62石蜡和C64石蜡组成的石蜡组。
本发明进一步提供一种用于制备粉末注射成形粘结剂的组合物，其含有C5石油树脂和/或C9石油树脂。
进一步地，该组合物含有液态石蜡。
进一步地，该组合物含有组分C，其中该组分C选自由C52石蜡、C54石蜡、C56石蜡、C58石蜡、C60石蜡、C62石蜡和C64石蜡组成的石蜡组。
进一步地，该组合物含有组分A，其中该组分A选自由聚乙烯、高密度聚乙烯、聚丙烯、聚苯乙烯、聚酰胺、乙烯-醋酸乙烯共聚物和聚乙烯醇和其改性体组成的热塑性树脂组。
本发明进一步提供一种用于制备粉末注射成形粘结剂的组合物，其含有液态石蜡。
通过对随后的描述和附图的理解，本发明进一步的目的和优势将得以充分体现。
本发明的这些和其它目的、特点和优势，通过下述的详细说明，附图和权利要求得以充分体现。
附图说明
图1为依本发明较佳实施例的粘结剂的TGA图谱。
图2为依本发明较佳实施例的金属粉末(或可烧结非金属粉末)注射成形方法的流程图。
图3为依本发明较佳实施例的另一种金属粉末(或可烧结非金属粉末)注射成形方法的流程图。
具体实施方式
下述描述被揭露以使本领域技术人员可制造和使用本发明。下述描述中提供的较佳实施例仅作为对本领域技术人员显而易见的示例和修改，其并不构成对本发明范围的限制。下述描述中所定义的一般原理可不背离本发明精神和发明范围地应用于其它实施例、可选替代、修改、等同实施和应用。
本发明的主要目的是提供一种组合物，其中该组合物可被用来制造金属粉末(或可烧结非金属粉末)注射成形粘结剂。换句话说，本发明提供一种可用作金属粉末(或可烧结非金属粉末)注射成形粘结剂功能组分的组合物。因此，本发明组合物可用于制造金属粉末(或可烧结非金属粉末)注射成形粘结剂，或替代现有金属粉末(或可烧结非金属粉末)注射成形粘结剂中的相应成分，以降低粘结剂的制造成本。
本领域技术人员能够理解，本文中的粉末注射成形优选指的是金属粉末，如不锈钢粉粉末、铁粉粉末、硬质合金粉末注射成形。可选地，本文中的粉末注射成形也可以是可烧结非金属粉末，如陶瓷粉末或铁氧粉体注射成形。
具体地，本发明用于制备粉末注射成形粘结剂的组合物含有C5石油树脂和/或C9石油树脂。当粉末注射成形粘结剂中存在C5石油树脂和C9石油树脂或其组合时，粘结剂的粘度和相容性可得到改善。本发明用于制备粉末注射成形粘结剂的组合物进一步含有液态石蜡。数据表明，液态石蜡可用于调节粉末注射成形粘结剂的粘度。此外，液态石蜡的挥发(或降解温度)一般低于粉末注射成形粘结剂的基体成分的挥发(或降解温度)，有利于粉末注射成形过程中，粘结剂的逐步去除。优选地，本发明用于制备粉末注射成形粘结剂的组合物中，C5石油树脂和/或C9石油树脂与液态石蜡的质量比为2:1至9:2。更优选地，本发明用于制备粉末注射成形粘结剂的组合物进一步包括含有组分C，其中该组分C选自由C52石蜡、C54石蜡、C56石蜡、C58石蜡、C60石蜡、C62石蜡和C64石蜡组成的石蜡组。更优选地，该组分C包括C52石蜡、C54石蜡、C56石蜡、C58石蜡、C60石蜡、C62石蜡和C64石蜡。本发明用于制备粉末注射成形粘结剂的组合物的组分C中含有的不同熔点的石蜡可在调节该粘结剂的同时，使该粘结剂的各个成分随粉末注射成形时，温度的升高而被逐渐去除，从而缩短粉末注射成形工艺时间和尽量使粘结剂的各个成分被去除完全。
进一步地，本发明用于制备粉末注射成形粘结剂的组合物还含有组分A，其中该组分A选自由聚乙烯(PE)、高密度聚乙烯(HDPE)、聚丙烯(PP)、聚苯乙烯(PS)、聚酰胺(PA)、乙烯-醋酸乙烯共聚物(EVA)和聚乙烯醇(PVA)和其改性体，和其类似物组成的热塑性树脂组。优选地，该组分A为聚乙烯(PE)、高密度聚乙烯(HDPE)、聚丙烯(PP)、聚苯乙烯(PS)、聚酰胺(PA)、乙烯-醋酸乙烯共聚物(EVA)和/或聚乙烯醇(PVA)的改性体。
进一步地，本发明用于制备粉末注射成形粘结剂的组合物包括改性剂，其中该改性剂为表面改性剂，如硬脂酸(SA)、增塑剂，如邻苯二甲酸二辛酯(DOP)、抗氧化剂，如2,6-二叔丁基-4-甲基苯酚(BHT)、钝化剂，如硫酸乙烯酯(DTD)和/或表面活性剂，如聚醚类表面活性剂。
可选地，本发明用于制备粉末注射成形粘结剂的组合物进一步包括聚乙烯蜡和/或棕榈蜡。
本领域技术人员能够理解，本文中的C5石油树脂指的是石油裂解所得到的碳五树脂副产品，其分子量介于300-3000，相对密度0.97～1.07，软化点70～140℃，其主要组成成分为甲乙酮、醋酸乙酯、三氯乙烷、环己烷、甲苯等。本文中的C9石油树脂指的是以石油裂解所得到的C9馏分为主要原料，在催化剂存在下聚合，或将其与醛类、芳烃、萜烯类化合物进行共聚合而制得的热塑性树脂，其分子质量一般不大于3000，软化点不大于150℃。本文中的C52石蜡指的是熔点在52摄氏温度左右的石蜡，C54石蜡指的是熔点在54摄氏温度左右的石蜡，C56石蜡指的是熔点在56摄氏温度左右的石蜡，C58石蜡指的是熔点在58摄氏温度左右的石蜡，C60石蜡指的是熔点在60摄氏温度左右的石蜡，C64石蜡指的是熔点在64摄氏温度左右的石蜡。
本发明进一步提供一种金属粉末(或可烧结非金属粉末)注射成形粘结剂，其包括20％～60％质量份数的组分A，其中该组分A选自由聚乙烯(PE)、高密度聚乙烯(HDPE)、聚丙烯(PP)、聚苯乙烯(PS)、聚酰胺(PA)、乙烯-醋酸乙烯共聚物(EVA)和聚乙烯醇(PVA)和其改性体，和其类似物组成的热塑性树脂组；6％～15％质量份数的组分B，其中该组分B选自C5石油树脂和/或C9石油树脂组成的石油树脂组；和10％～20％质量份数的组分C，其中该组分C选自由C52石蜡、C54石蜡、C56石蜡、C58石蜡、C60石蜡、C62石蜡和C64石蜡组成的石蜡组。本领域技术人员可以理解，本文中的热塑性树脂可以是聚合树脂或缩合树脂，或两者的组合。优选地，该粘结剂中，该组分A的质量分数为45％～50％。更优选地，该粘结剂进一步含有9％～27％质量份数的组分D，其中该组分D为液态石蜡。
进一步地，该粘结剂包括2％～8％质量份数的聚乙烯蜡和/或棕榈蜡。
进一步地，本发明金属粉末(或可烧结非金属，如陶瓷)注射成形粘结剂包括不大于5％质量份数的改性剂，该改性剂为表面改性剂、增塑剂、抗氧化剂、钝化剂和/或表面活性。优选地，该改性剂的质量分数不大于2％。
值得注意的是，本发明金属粉末(或可烧结非金属，如陶瓷)注射成形粘结剂的低温组分，如液态石蜡，在金属粉末(或可烧结非金属，如陶瓷)注射成形胚起始加热阶段具有渗透性和可挥发性，从而可在成形胚的内部形成初始孔隙或通道，以利于其它粘结剂组分的后续脱除。此外，C5石油树脂和C9石油树脂含有多种化合物，且这些化合物的挥发或降解温度分别为240℃～480℃。因此，随着温度的不断升高，粘结剂中的成分被逐渐逐步脱除，从而提高粘结剂的脱除效率和缩短金属粉末注射成技术的工艺时间。
进一步地，该金属粉末(或可烧结非金属，如陶瓷)注射成形粘结剂包括20％～60％质量份数的极性接枝化合物,如马来酸酐(MAH)、聚乙烯(PE)、聚丙烯(PP)和/或乙烯-醋酸乙烯共聚物(EVA)等，以减小注射时，该用于制备金属模制品的组合物的组分分离，从而提高成形胚的均匀性和一致性。
本领域技术人员可以理解，本发明进一步提供一种用于制备金属模制品的组合物，其含有：
50％～65％体积份数的至少一种可烧结金属粉末；和
35％～50％体积份数的粘结剂，其中该粘结剂包括：
20％～60％质量份数的组分A，其中该组分A选自由聚乙烯、高密度聚乙烯、聚丙烯、聚苯乙烯、聚酰胺、乙烯-醋酸乙烯共聚物和聚乙烯醇和其改性体组成的热塑性树脂组；
6％～15％质量份数的组分B，其中该组分B选自由C5石油树脂和C9石油树脂组成的石油树脂组；和
10％～20％质量份数的组分C，其中该组分C选自由C52石蜡、C54石蜡、C56石蜡、C58石蜡、C60石蜡、C62石蜡和C64石蜡组成的石蜡组。
优选地，在该粘结剂中，该组分A的质量分数为45％～50％。
进一步地，本发明用于制备金属模制品的组合物的粘结剂包括9％～27％粘结剂质量份数的组分D，其中该组分D为液态石蜡。
进一步地，本发明用于制备金属模制品的组合物的粘结剂进一步包括2％～8％粘结剂质量份数的聚乙烯蜡和/或棕榈蜡。
进一步地，本发明用于制备金属模制品的组合物的粘结剂进一步包括占粘结剂质量份数不大于5％的改性剂，其中该改性剂为表面改性剂、增塑剂、抗氧化剂、钝化剂和/或表面活性。优选地，该改性剂的质量分数不大于2％。本领域技术人员可以理解，本发明用于制备金属模制品的组合物指的是用于金属粉末注射成形以制得金属粉末注射成形胚或被烧结后制得金属粉末注射成形产品的原料，该原料一般包括可烧结金属粉末和粘结剂等。
具体地，本发明可烧结金属粉末可以是铝粉、铁粉或其它类似金属粉末，或其组合物等。本领域技术人员可以理解，本发明进一步提供一种用于制备非金属模制品的组合物，其含有：
50％～65％体积份数的至少一种可烧结非金属粉末；和
35％～50％体积份数的粘结剂，其中该粘结剂包括：
20％～60％质量份数的组分A，其中该组分A选自由聚乙烯、高密度聚乙烯、聚丙烯、聚苯乙烯、聚酰胺、乙烯-醋酸乙烯共聚物和聚乙烯醇和其改性体组成的热塑性树脂组；
6％～15％质量份数的组分B，其中该组分B选自由C5石油树脂和C9石油树脂组成的石油树脂组；和
10％～20％质量份数的组分C，其中该组分C选自由C52石蜡、C54石蜡、C56石蜡、C58石蜡、C60石蜡、C62石蜡和C64石蜡组成的石蜡组。
优选地，在该粘结剂中，该组分A的质量分数为45％～50％。
进一步地，本发明用于制备金属模制品的组合物的粘结剂包括9％～27％粘结剂质量份数的组分D，其中该组分D为液态石蜡。
进一步地，本发明用于制备金属模制品的组合物的粘结剂进一步包括2％～8％粘结剂质量份数的聚乙烯蜡和/或棕榈蜡。
进一步地，本发明用于制备金属模制品的组合物的粘结剂进一步包括占粘结剂质量份数不大于5％的改性剂，其中该改性剂为表面改性剂、增塑剂、抗氧化剂、钝化剂和/或表面活性。优选地，该改性剂的质量分数不大于2％。本领域技术人员可以理解，本发明用于制备非金属模制品的组合物指的是用于非金属粉末，如陶瓷粉末、铁氧体粉末注射成形以制得非金属粉末注射成形胚或被烧结后制得非金属粉末注射成形产品的原料，该原料一般包括可烧结非金属粉末和粘结剂等。
具体地，本发明可烧结非金属粉末可以是陶瓷粉末、铁氧体粉末或其它类似非金属粉末，或其组合物等。
如附图之图2，本发明进一步提供一种金属粉末(或可烧结非金属粉末)注射成形方法，其包括以下步骤：
A)混合粘结剂与金属粉末，以得到混合原料；
B)对混合原料进行造粒处理，以得到颗粒性注射喂料；
C)将注射喂料注射进入预制模具，以成形；
D)对成形胚进行加热，以逐渐脱除粘结剂；和
E)在烧结炉内对脱脂后的成形胚进行烧结。
如附图之图3，本发明进一步提供一种金属粉末(或可烧结非金属粉末)注射成形方法，其包括以下步骤：A)混合粘结剂与金属粉末，以得到混合原料；
B)对混合原料进行造粒处理，以得到颗粒性注射喂料；
C)将注射喂料注射进入预制模具，以成形；
D)向脱脂室加入溶剂并对成形胚进行加热，以逐渐脱除粘结剂；和
E)在烧结炉内对脱脂后的成形胚进行烧结。
本领域技术人员会明白附图中所示的和以上所描述的本发明实施例仅是对本发明的示例而不是限制。
由此可以看到本发明目的可被充分有效完成。用于解释本发明功能和结构原理的该实施例已被充分说明和描述，且本发明不受基于这些实施例原理基础上的改变的限制。因此，本发明包括涵盖在附属权利要求书要求范围和精神之内的所有修改。

Claims (20)

1.一种用于金属粉末或非金属粉末注射成形的粘结剂，其特征在于，包括：
20％～60％质量份数的组分A，其中该组分A选自由聚乙烯、高密度聚乙烯、聚丙烯、聚苯乙烯、聚酰胺、乙烯-醋酸乙烯共聚物和聚乙烯醇和其改性体组成的热塑性树脂组；
6％～15％质量份数的组分B，其中该组分B选自由C5石油树脂和C9石油树脂组成的石油树脂组；和
10％～20％质量份数的组分C，其中该组分C选自由C52石蜡、C54石蜡、C56石蜡、C58石蜡、C60石蜡、C62石蜡和C64石蜡组成的石蜡组。
2.根据权利要求1所述的粘结剂，其特征在于，该粘结剂中，该组分A的质量分数为45％～50％。
3.根据权利要求1所述的粘结剂，其特征在于，进一步包括9％～27％质量份数的组分D，其中该组分D为液态石蜡。
4.根据权利要求1所述的粘结剂，其特征在于，进一步包括2％～8％质量份数的聚乙烯蜡和/或棕榈蜡。
5.根据权利要求1所述的粘结剂，其特征在于，进一步包括质量份数不大于5％的改性剂，其中该改性剂为表面改性剂、增塑剂、抗氧化剂、钝化剂和/或表面活性。
6.一种用于制备粉末注射成形粘结剂的组合物，其特征在于，含有C5石油树脂和/或C9石油树脂。
7.根据权利要求6所述的组合物，其特征在于，进一步含有液态石蜡。
8.根据权利要求6所述的组合物，其特征在于，进一步含有组分C，其中该组分C选自由C52石蜡、C54石蜡、C56石蜡、C58石蜡、C60石蜡、C62石蜡和C64石蜡组成的石蜡组。
9.根据权利要求6所述的组合物，其特征在于，进一步含有组分A，其中该组分A选自由聚乙烯、高密度聚乙烯、聚丙烯、聚苯乙烯、聚酰胺、乙烯-醋酸乙烯共聚物和聚乙烯醇和其改性体组成的热塑性树脂组。
10.一种用于制备粉末注射成形粘结剂的组合物，其特征在于，含有液态石蜡。
11.一种用于制备金属模制品的组合物，其特征在于，含有：
50％～65％体积份数的至少一种可烧结金属粉末；和
35％～50％体积份数的粘结剂，其中该粘结剂包括：
20％～60％质量份数的组分A，其中该组分A选自由聚乙烯、高密度聚乙烯、聚丙烯、聚苯乙烯、聚酰胺、乙烯-醋酸乙烯共聚物和聚乙烯醇和其改性体组成的热塑性树脂组；
6％～15％质量份数的组分B，其中该组分B选自由C5石油树脂和C9石油树脂组成的石油树脂组；和
10％～20％质量份数的组分C，其中该组分C选自由C52石蜡、C54石蜡、C56石蜡、C58石蜡、C60石蜡、C62石蜡和C64石蜡组成的石蜡组。
12.根据权利要求11所述的组合物，其特征在于，该粘结剂中，该组分A的质量分数为45％～50％。
13.根据权利要求11所述的组合物，其特征在于，该粘结剂进一步包括9％～27％粘结剂质量份数的组分D，其中该组分D为液态石蜡。
14.根据权利要求11所述的组合物，其特征在于，该粘结剂进一步包括2％～8％粘结剂质量份数的聚乙烯蜡和/或棕榈蜡。
15.根据权利要求11所述的组合物，其特征在于，该粘结剂进一步包括占粘结剂质量份数不大于5％的改性剂，其中该改性剂为表面改性剂、增塑剂、抗氧化剂、钝化剂和/或表面活性。
16.一种用于制备金属模制品的组合物，其特征在于，含有：
50％～65％体积份数的至少一种可烧结非金属粉末；和
35％～50％体积份数的粘结剂，其中该粘结剂包括：
20％～60％质量份数的组分A，其中该组分A选自由聚乙烯、高密度聚乙烯、聚丙烯、聚苯乙烯、聚酰胺、乙烯-醋酸乙烯共聚物和聚乙烯醇和其改性体组成的热塑性树脂组；
6％～15％质量份数的组分B，其中该组分B选自由C5石油树脂和C9石油树脂组成的石油树脂组；和
10％～20％质量份数的组分C，其中该组分C选自由C52石蜡、C54石蜡、C56石蜡、C58石蜡、C60石蜡、C62石蜡和C64石蜡组成的石蜡组。
17.根据权利要求16所述的组合物，其特征在于，该粘结剂中，该组分A的质量分数为45％～50％。
18.根据权利要求16所述的组合物，其特征在于，该粘结剂进一步包括9％～27％粘结剂质量份数的组分D，其中该组分D为液态石蜡。
19.根据权利要求16所述的组合物，其特征在于，该粘结剂进一步包括2％～8％粘结剂质量份数的聚乙烯蜡和/或棕榈蜡。
20.根据权利要求16所述的组合物，其特征在于，该粘结剂进一步包括占粘结剂质量份数不大于5％的改性剂，其中该改性剂为表面改性剂、增塑剂、抗氧化剂、钝化剂和/或表面活性。
CN201510783631.XA 2015-11-16 2015-11-16 用于粉末注射成形的粘结剂及注射成形方法 Pending CN106700191A (zh)