CN106675739A - 一种添加乳化二氧化钛光催化杀菌型微乳化切削液 - Google Patents
一种添加乳化二氧化钛光催化杀菌型微乳化切削液 Download PDFInfo
- Publication number
- CN106675739A CN106675739A CN201611157431.4A CN201611157431A CN106675739A CN 106675739 A CN106675739 A CN 106675739A CN 201611157431 A CN201611157431 A CN 201611157431A CN 106675739 A CN106675739 A CN 106675739A
- Authority
- CN
- China
- Prior art keywords
- solution
- added
- deionized water
- stirring
- cutting fluid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种添加乳化二氧化钛光催化杀菌型微乳化切削液,由以下原料制备制成:精制矿物油、十二烷基磷酸酯、油酸三乙醇胺、十二烷基甜菜碱、酸式磷酸月桂酯、苯并三氮唑、三乙醇胺、消泡剂、石油磺酸钠、氯化钠、丙三醇、硫化脂肪酸酯、钛酸丁酯、十六烷基三甲基溴化铵、乳化剂OP‑10、过硫酸钾、苯胺适量、环己醇适量、三乙胺适量、盐酸适量、无水乙醇适量、丙酮适量、去离子水适量;本发明制备的微乳化切削液不仅具有良好的防锈蚀和防霉变性能,并且具有良好的润滑性、耐极压和光催化杀菌性能,同时安全环保,对环境无污染。
Description
技术领域
本发明涉及微乳化切削液技术领域,尤其涉及一种添加乳化二氧化钛光催化杀菌型微乳化切削液。
背景技术
金属切削液是金属加工过程中重要的配套材料,其主要作用是冷却、润滑、清洗和防锈。按照介质状况分为两大类:油基型和水基型切削液,油基型切削液的主要成分通常是矿物油(也有植物油或其他合成材料),并加入油溶性防锈剂、油性剂和含活性元素的极压润滑剂调合而成,相比水基切削液,油基切削液的润滑性能和防锈性能较好,但却具有易产生油雾、易着火等缺点,水基切削液是用大量的水将浓缩液稀释后使用的,因而不具有产生油烟和引发火灾的缺点,水的比热容大,热导率高,汽化热大,是非常优良的冷却剂,切且成本低廉,另外加工后的脱脂清洗也比较简单。微乳液是一种介于乳化液和合成液之间并兼具乳化液润滑性和合成液清晰性的性能优异的切削液,成本较低,是未来加工液的主要发展方向。随着经济的快速发展,各种钢铁和铝合金的加工也飞速发展,目前国内在钢铁和铝合金的润滑方面金属切削液研究较少,主要以进口为主,我国在这方面的的研究工作起步较晚,而且主要集中在材料加工成型上,对切削加工中的润滑和防腐蚀方面的问题重视不够。近年来随着新型加工机械的不断出现,加工条件日趋苛刻,对金属切削液也提出了更高的要求。
付巧莲在《添加剂在微乳液中对铝/钢润滑性能影响的研究》一文中针对铝-钢摩擦副难于润滑的问题,以水性微乳化液为基础液,系统的研究了氯系、磷系、硫系、酯类以及聚醚类五大类润滑添加剂在微乳化液中对钢-钢摩擦副、铝-钢摩擦副的润滑特性。研究发现微乳液的最大无卡咬负荷与添加剂的种类和用量有关,其中对钢-钢摩擦副的润滑效果是多硫化物LZ5340L在水基微乳液中的响应值最好,加入量为5%时最大无卡咬负荷值为1118N,其次是氯化脂肪酸DA8527,硫化甘油三酸酯RC2411也有较好的润滑性能;在微乳化液中对铝-钢的摩擦副润滑结果为,硫系添加剂RC2411对铝-钢的摩擦副润滑效果最好,当其浓度为4%时,铝销的磨损量只有0.1mg,LZ5340L在加入量为4%时,铝销的磨损量也只有0.2mg。通过一系列试验后发现硫系添加剂对钢-钢摩擦副和铝-钢摩擦副具有较好的润滑性能,对其机理进行初步分析认为硫系添加剂能在金属表面形成一层致密的硫化膜,降低剪切应力,起到润滑作用。虽然作者系统的研究了在微乳化液中添加硫系润滑剂能够有效的提高切削液的润滑性能,但是随着加工器件日趋多元化,人们对微乳化切削液的要求越来越高,防锈蚀和使用寿命问题是切削液加工过程中不得不考虑的一个重要因素,因此对微乳化切削液必须进行改性以期获得的切削液能够提高加工效率和工件的表面质量,同时延长刀具和切削液本身的使用寿命,降低加工成本,获得最佳经济效益才是当前的研究热点。
发明内容
本发明目的就是为了弥补已有技术的缺陷,提供一种添加乳化二氧化钛光催化杀菌型微乳化切削液。
本发明是通过以下技术方案实现的:
一种添加乳化二氧化钛光催化杀菌型微乳化切削液,由以下重量份的原料制备制成:精制矿物油15-20、十二烷基磷酸酯13-15、油酸三乙醇胺5-6、十二烷基甜菜碱6-7、酸式磷酸月桂酯2.8-3、苯并三氮唑3-5、三乙醇胺3-4、消泡剂0.05-0.1、石油磺酸钠2-3、氯化钠2.3-2.5、丙三醇0.5-0.7、硫化脂肪酸酯4-5、钛酸丁酯10-12、十六烷基三甲基溴化铵5-6、乳化剂OP-10 30-35、过硫酸钾13-15、苯胺适量、环己醇适量、三乙胺适量、盐酸适量、无水乙醇适量、丙酮适量、去离子水适量。
所述一种添加乳化二氧化钛光催化杀菌型微乳化切削液,由下列具体步骤制备制成:
(1)将钛酸丁酯在搅拌条件下逐滴加到环己醇中搅拌混合得到浓度为0.2g/ml的透明溶液A,将十六烷基三甲基溴化铵用去离子水溶解形成浓度为1.08mol/L的均匀溶液B,将溶液B中加入2.5倍量去离子水体积的环己醇得到混合溶液C,以1000-1200r/min的速率搅拌溶液C,并将溶液A以1.5d/s的速率逐滴加到溶液C中,连续搅拌直至得到稳定的溶胶,再加入适量的三乙胺调节溶胶的pH值为8.5,继续搅拌2h后过滤,用丙酮洗涤数次后将滤饼置于烘箱中80℃下干燥得到改性二氧化钛粉末备用;
(2)将步骤(1)制备的产物加到去离子水中制成浓度为18g/L的分散液,再加入2mol/l的盐酸超声分散1-1.5h,其中2mol/L的盐酸与去离子水的体积比为1:10-11,将乳化剂OP-10用去离子水溶解搅拌形成质量浓度为1.5%的乳化剂溶液,再加入苯胺搅拌混合均匀,然后向上述悬浮液中加入该混合溶液,磁力搅拌0.5-0.7h,其中苯胺与步骤(1)制备的产物质量比为2-3:1,将5%的过硫酸铵溶液缓慢滴加到上述混合溶液中,确保2h内滴加完毕,继续搅拌反应10-12h,将得到的沉淀用盐酸、去离子水和无水乙醇多次滤洗,然后在60℃的真空干燥箱中烘干至恒重,粉碎后备用;
(3)在反应容器中加入精制矿物油,搅拌加热至60-65℃时依次加入石油磺酸钠、酸式磷酸月桂酯、油酸三乙醇胺、十二烷基磷酸酯、十二烷基甜菜碱,每加入一种物料搅拌均匀后即可加入下一种物料,而后加入苯并三氮唑,搅拌溶解均匀得油相体系;
(4)在容器中加入去离子水加热到70-80℃,在搅拌下缓慢加入氯化钠和丙三醇充分搅拌溶解,搅拌均匀后加入步骤(2)制备的产物超声分散均匀得水相体系;
(5)在保持60-70℃下将水相体系缓慢加到以200-300r/min转速搅拌的油相体系中,待水相体系滴加结束后控制反应温度为40-50℃,加入消泡剂得到基础浓缩液,向该浓缩液中加入其余剩余物料调成母液,用去离子水将其稀释成浓度为10%的微乳化切削液即可。
本发明的优点是:聚苯胺具有合成原料成本低廉、优异的抗划伤、抗点蚀能力等优点,能够在钢铁和铝合金的表面形成均匀致密的聚苯胺膜,起到良好的防腐防锈的作用,但是其在一般的有机溶剂中溶解性较差,因此需要对其进行掺杂改善其溶解性,聚苯胺具有优异的俘获纳米粒子的寄主能力,可以与一些活泼的无机纳米粒子共同掺杂有效的改善其溶解性及耐蚀能力,利用传统的方法生成的二氧化钛尺寸大、分布不均匀,容易在水基中聚集,本发明利用在油包水的体系环境下对二氧化钛溶胶改性,使其纳米粒子不容易发生团聚而使之形成良好的分散性与稳定性,并且利用乳化剂OP-10对聚苯胺进行掺杂,有利于分子链的离域和舒展,降低分子链间的相互作用力,起到接枝增溶的作用,有助于提高聚苯胺乳液的流动性和分散性,并且原位聚合成聚苯胺在改性二氧化钛表面,在水基中具有良好的分散性和稳定性,提高了微乳化切削液的防腐蚀、耐磨、减摩、催化杀菌等功能,本发明制备的微乳化切削液不仅具有良好的防锈蚀和防霉变性能,并且具有良好的润滑性、耐极压和光催化杀菌性能,同时安全环保,对环境无污染。
具体实施方式
一种添加乳化二氧化钛光催化杀菌型微乳化切削液,由以下重量份的原料制备制成:精制矿物油15、十二烷基磷酸酯13、油酸三乙醇胺5、十二烷基甜菜碱6、酸式磷酸月桂酯2.8、苯并三氮唑3、三乙醇胺3、消泡剂0.05、石油磺酸钠2、氯化钠2.3、丙三醇0.5、硫化脂肪酸酯4、钛酸丁酯10、十六烷基三甲基溴化铵5、乳化剂OP-10、过硫酸钾13、苯胺适量、环己醇适量、三乙胺适量、盐酸适量、无水乙醇适量、丙酮适量、去离子水适量。
所述一种添加乳化二氧化钛光催化杀菌型微乳化切削液,由下列具体步骤制备制成:
(1)将钛酸丁酯在搅拌条件下逐滴加到环己醇中搅拌混合得到浓度为0.2g/ml的透明溶液A,将十六烷基三甲基溴化铵用去离子水溶解形成浓度为1.08mol/L的均匀溶液B,将溶液B中加入2.5倍量去离子水体积的环己醇得到混合溶液C,以1000r/min的速率搅拌溶液C,并将溶液A以1.5d/s的速率逐滴加到溶液C中,连续搅拌直至得到稳定的溶胶,再加入适量的三乙胺调节溶胶的pH值为8.5,继续搅拌2h后过滤,用丙酮洗涤数次后将滤饼置于烘箱中80℃下干燥得到改性二氧化钛粉末备用;
(2)将步骤(1)制备的产物加到去离子水中制成浓度为18g/L的分散液,再加入2mol/l的盐酸超声分散1h,其中2mol/L的盐酸与去离子水的体积比为1:10,将乳化剂OP用去离子水溶解搅拌形成质量浓度为1.5%的乳化剂溶液,再加入苯胺搅拌混合均匀,然后向上述悬浮液中加入该混合溶液,磁力搅拌0.5h,其中苯胺与步骤(1)制备的产物质量比为2:1,将5%的过硫酸铵溶液缓慢滴加到上述混合溶液中,确保2h内滴加完毕,继续搅拌反应10h,将得到的沉淀用盐酸、去离子水和无水乙醇多次滤洗,然后在60℃的真空干燥箱中烘干至恒重,粉碎后备用;
(3)在反应容器中加入精制矿物油,搅拌加热至60℃时依次加入石油磺酸钠、酸式磷酸月桂酯、油酸三乙醇胺、十二烷基磷酸酯、十二烷基甜菜碱,每加入一种物料搅拌均匀后即可加入下一种物料,而后加入苯并三氮唑,搅拌溶解均匀得油相体系;
(4)在容器中加入去离子水加热到70℃,在搅拌下缓慢加入氯化钠和丙三醇充分搅拌溶解,搅拌均匀后加入步骤(2)制备的产物超声分散均匀得水相体系;
(5)在保持60℃下将水相体系缓慢加到以200r/min转速搅拌的油相体系中,待水相体系滴加结束后控制反应温度为40℃,加入消泡剂得到基础浓缩液,向该浓缩液中加入其余剩余物料调成母液,用去离子水将其稀释成浓度为10%的微乳化切削液即可。
对实施例制备的微乳化切削液进行性能测试,结果如下:
贮存安定性:无变色、无分层;消泡性(mL•10-1min-1):<2;腐蚀试验(55±2℃,铸铁/h):>48;腐蚀试验(55±2℃,铝/h):>12;防锈性试验(铸铁,h)>48;最大无卡咬负和(N):932;抗磨性(N):>59。
Claims (2)
1.一种添加乳化二氧化钛光催化杀菌型微乳化切削液,其特征在于,由以下重量份的原料制备制成:精制矿物油15-20、十二烷基磷酸酯13-15、油酸三乙醇胺5-6、十二烷基甜菜碱6-7、酸式磷酸月桂酯2.8-3、苯并三氮唑3-5、三乙醇胺3-4、消泡剂0.05-0.1、石油磺酸钠2-3、氯化钠2.3-2.5、丙三醇0.5-0.7、硫化脂肪酸酯4-5、钛酸丁酯10-12、十六烷基三甲基溴化铵5-6、乳化剂OP-1030-35、过硫酸钾13-15、苯胺适量、环己醇适量、三乙胺适量、盐酸适量、无水乙醇适量、丙酮适量、去离子水适量。
2.根据权利要求1所述一种添加乳化二氧化钛光催化杀菌型微乳化切削液,其特征在于,由下列具体步骤制备制成:
(1)将钛酸丁酯在搅拌条件下逐滴加到环己醇中搅拌混合得到浓度为0.2g/ml的透明溶液A,将十六烷基三甲基溴化铵用去离子水溶解形成浓度为1.08mol/L的均匀溶液B,将溶液B中加入2.5倍量去离子水体积的环己醇得到混合溶液C,以1000-1200r/min的速率搅拌溶液C,并将溶液A以1.5d/s的速率逐滴加到溶液C中,连续搅拌直至得到稳定的溶胶,再加入适量的三乙胺调节溶胶的pH值为8.5,继续搅拌2h后过滤,用丙酮洗涤数次后将滤饼置于烘箱中80℃下干燥得到改性二氧化钛粉末备用;
(2)将步骤(1)制备的产物加到去离子水中制成浓度为18g/L的分散液,再加入2mol/l的盐酸超声分散1-1.5h,其中2mol/L的盐酸与去离子水的体积比为1:10-11,将乳化剂OP-10用去离子水溶解搅拌形成质量浓度为1.5%的乳化剂溶液,再加入苯胺搅拌混合均匀,然后向上述悬浮液中加入该混合溶液,磁力搅拌0.5-0.7h,其中苯胺与步骤(1)制备的产物质量比为2-3:1,将5%的过硫酸铵溶液缓慢滴加到上述混合溶液中,确保2h内滴加完毕,继续搅拌反应10-12h,将得到的沉淀用盐酸、去离子水和无水乙醇多次滤洗,然后在60℃的真空干燥箱中烘干至恒重,粉碎后备用;
(3)在反应容器中加入精制矿物油,搅拌加热至60-65℃时依次加入石油磺酸钠、酸式磷酸月桂酯、油酸三乙醇胺、十二烷基磷酸酯、十二烷基甜菜碱,每加入一种物料搅拌均匀后即可加入下一种物料,而后加入苯并三氮唑,搅拌溶解均匀得油相体系;
(4)在容器中加入去离子水加热到70-80℃,在搅拌下缓慢加入氯化钠和丙三醇充分搅拌溶解,搅拌均匀后加入步骤(2)制备的产物超声分散均匀得水相体系;
(5)在保持60-70℃下将水相体系缓慢加到以200-300r/min转速搅拌的油相体系中,待水相体系滴加结束后控制反应温度为40-50℃,加入消泡剂得到基础浓缩液,向该浓缩液中加入其余剩余物料调成母液,用去离子水将其稀释成浓度为10%的微乳化切削液即可。