CN106636722A - Alloy material and preparation method thereof - Google Patents
Alloy material and preparation method thereof Download PDFInfo
- Publication number
- CN106636722A CN106636722A CN201610888745.5A CN201610888745A CN106636722A CN 106636722 A CN106636722 A CN 106636722A CN 201610888745 A CN201610888745 A CN 201610888745A CN 106636722 A CN106636722 A CN 106636722A
- Authority
- CN
- China
- Prior art keywords
- platinum
- alloy material
- preparation
- container
- smelting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an alloy material and a preparation method thereof. The alloy material comprises the following raw materials: 95 percent of platinum and 5 percent of ruthenium powder. The preparation method comprises the steps: extracting a plurality of platinum to manufacture a cylindrical platinum container and enabling the residual platinum to wait for smelting; pouring the ruthenium powder into the platinum container and sealing the platinum container; and smelting: putting the closed platinum container and the residual platinum into a smelting machine, and completely melting after the temperature of a smelting furnace of the smelting machine is increased to 1920 DEG C to obtain the alloy material. The alloy material and the preparation method thereof have the beneficial effects that adornments, artware, jewelry and the like manufactured by the alloy material have high alloy hardness and higher inlaying fastening degree; and the shape, the appearance and the diversity of each product are not limited by hardness.
Description
Technical field
The invention belongs to a kind of alloy material and preparation method thereof, and in particular to one kind can make ornament, handicraft, head
Alloy materials such as decorations and preparation method thereof.
Background technology
Now with the continuous progress of economic market, consumer to demands such as ornament, handicraft, jewellery increasingly
It is high.The platinum palladium that traditional handicraft is used again in manufacturing process due to its own alloy the characteristics of, its hardness is not hard enough, causes platinum palladium
The ornaments of class cannot meet existing market requirement.
The content of the invention
In order to solve the above problems, the present invention provides alloy material and its systems such as a kind of making ornament, handicraft, jewellery
Preparation Method.
In order to achieve the above object, the technical solution adopted for the present invention to solve the technical problems is：
One kind makes the alloy materials such as ornament, handicraft, jewellery, composed of the following components by weight percentage：Platinum
95%th, ruthenium powder 5%；
Platinum, there is will never fade, the physical attribute ground and do not damage.Weight：Per cubic centimeter is 21.45 grams, fusing point：1772
DEG C, boiling point：3827℃.
Ruthenium powder, among being present in platinum ore, content is few, and making an addition to can increase the hardness and wear resistance of alloy in alloy, can
To make ornament.Matter is hard and crisp, not easy processing, but wearability is strong.12.30 grams/cc of density.2310 DEG C of fusing point, boiling point
3900℃.Chemical property is very stable.
A kind of alloy material and preparation method thereof, containing raw material：Platinum 95%, ruthenium powder 5%；Step is as follows：
1st, platinum container processed：Extract some platinums and manufacture a tubular platinum container, residue waits melting platinum；
2nd, wrap up and close opening：Ruthenium powder is poured in platinum container, and by platinum container closure；
3rd, melting：Platinum container after closing, remaining platinum are put into together in gold smelting apparatus, gold smelting apparatus smelting furnace interior temperature is treated
Degree rises to 1920 degree, all after fusing, obtains alloy material.
The invention has benefit that there is following positive effect：Alloy formula and preparation side using the present invention
Method, can make the alloy rigidities such as ornament, handicraft, the jewellery of making high, inlay and reinforce Du Genggao, shape of product, outward appearance, various
Property will not be restricted by hardness.
Specific embodiment
Present pre-ferred embodiments given below, to describe technical scheme in detail.
A kind of alloy material and preparation method thereof, containing raw material：Platinum 95%, ruthenium powder 5%；Step is as follows：
1st, platinum container processed：Extract some platinums and manufacture a tubular platinum container, residue waits melting platinum；
2nd, wrap up and close opening：Ruthenium powder is poured in platinum container, and by platinum container closure；
3rd, melting：Platinum container after closing, remaining platinum are put into together in gold smelting apparatus, gold smelting apparatus smelting furnace interior temperature is treated
Degree rises to 1920 degree, all after fusing, obtains alloy material.
The invention has benefit that there is following good effect：Using the alloy formula and preparation method of the present invention, can
Make the alloy rigidities such as ornament, handicraft, the jewellery of making high, inlay and reinforce Du Genggao, shape of product, outward appearance, diversity are not
Can be limited by hardness.
Below as described herein, only the preferred embodiment of the present invention is described, not to the present invention's
Scope is defined, on the premise of without departing from design aim of the present invention, technology of the those of ordinary skill in the art to the present invention
Various modifications and improvement that scheme is made, all should belong to present invention determine that protection domain in.
Claims (2)
1. a kind of alloy material and preparation method thereof, it is characterised in that contain：It is composed of the following components by weight percentage：Platinum
95%, ruthenium powder 5%.
2. according to claim 1：A kind of alloy material and preparation method thereof, its step is as follows：
1. platinum container processed：Extract some platinums and manufacture a tubular platinum container, residue waits melting platinum；
2. wrap up and close opening：Ruthenium powder is poured in platinum container, and by platinum container closure；
3. melting：Platinum container after closing, remaining platinum are put into together in gold smelting apparatus, the molten in-furnace temperature liter of gold smelting apparatus is treated
To 1920 degree, all after fusing, alloy material is obtained.