CN106609109A - 一种木器漆用双组份改性的水性聚氨酯涂料 - Google Patents
一种木器漆用双组份改性的水性聚氨酯涂料 Download PDFInfo
- Publication number
- CN106609109A CN106609109A CN201510702479.8A CN201510702479A CN106609109A CN 106609109 A CN106609109 A CN 106609109A CN 201510702479 A CN201510702479 A CN 201510702479A CN 106609109 A CN106609109 A CN 106609109A
- Authority
- CN
- China
- Prior art keywords
- accounts
- modified
- curing agent
- mass content
- based polyurethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种木器漆用双组份改性的水性聚氨酯涂料,由改性的水性聚氨酯分散体和可低温固化的水性聚氨酯固化剂按照质量比为(7.5-9.9):(1-3)组成,其中所述改性的水性聚氨酯分散体分别包括质量为数为45-50%的聚醚多元醇330N、30-35%环氧树脂、5-10%异佛尔酮二异氰酸酯、5-10%亲水扩链剂、2-5%交联剂和5-15%丙烯酸酯,所述可低温固化的改性水性聚氨酯固化剂分别包括质量分数为75-85%聚氨酯固化剂、15-30%封端剂和0.1-1%消泡剂,所得涂料的漆膜具有较好的硬度及耐水、耐溶剂性,且漆膜表面无缩孔,无气泡,平整度、光泽度高,能够低温固化。
Description
技术领域
本发明涉及一种木器漆用双组份改性的水性聚氨酯涂料。
背景技术
目前用于室内家具涂装的木器涂料主要是溶剂型,包括硝基类、醇酸类、聚氨酯类等,其中聚氨酯类木器漆又分为单组份漆和双组份漆,双组份聚氨酯由于其硬度、坚韧性、耐水耐油性等性能比较好,应用较广泛。但是溶剂型涂料在生产及使用过程中会产生大量对人体有害的有机挥发物。水性木器漆以水为介质,取代原有的有机溶剂,具有无毒无害无气味,以及节省能源的优点。
市售的聚氨酯型水性木器漆多为单组份,但由于漆膜丰满度不高,力学性能上也有些不足,虽通过交联改性使得涂膜的性能有所改善,但程度有限。制备双组份水性聚氨酯木器漆涂料多采用多官能度的脂肪族或芳香族异氰酸酯自聚体或脂肪酸改性的交联型聚酯。这类涂料形成的漆膜不仅耐磨、耐化学腐蚀性强、干燥速度快,而且光亮丰满,还可以配制成哑光漆,多用于高档家具的涂装。
发明内容
本发明要解决的技术问题是提供一种木器漆用双组份改性的水性聚氨酯涂料。
为解决上述问题,本发明采用如下技术方案,由改性的水性聚氨酯分散体和可低温固化的水性聚氨酯固化剂组成,其中,所述改性的水性聚氨酯分散体和所述可低温固化的水性聚氨酯固化剂的质量比为(7.5-9.9):(1-3),所述改性的水性聚氨酯分散体包括聚醚多元醇330N、环氧树脂、异佛尔酮二异氰酸酯、亲水扩链剂、交联剂和丙烯酸酯,其中所述聚醚多元醇330N的质量含量占45-50%,所述环氧树脂的质量含量占30-35%,所述异佛尔酮二异氰酸酯的质量含量占5-10%,所述亲水扩链剂的质量含量占5-10%,所述交联剂的质量含量占2-5%,所述丙烯酸酯的质量含量占5-15%,所述可低温固化的改性水性聚氨酯固化剂包括聚氨酯固化剂、封端剂和消泡剂,其中所述聚氨酯固化剂的质量含量占75-85%,所述封端剂的质量含量占15-30%,所述消泡剂的质量含量占0.1-1%。
作为优选,所述亲水扩链剂为二羟甲基丙酸或1,4-丁二醇。
作为优选,所述交联剂为三羟甲基丙烷。
作为优选,所述封端剂为2-乙基-4-甲基咪唑。
作为优选,所述消泡剂为有机硅类消泡剂。
本发明的有益效果:
本发明所得涂料的漆膜具有较好的硬度及耐水、耐溶剂性,且漆膜表面无缩孔,无气泡,平整度、光泽度高,能够低温固化。
具体实施方式
实施例1
一种木器漆用双组份改性的水性聚氨酯涂料,主要由改性的水性聚氨酯分散体和可低温固化的水性聚氨酯固化剂组成,其中,所述改性的水性聚氨酯分散体和所述可低温固化的水性聚氨酯固化剂的质量比为7.5:2.5,所述改性的水性聚氨酯分散体包括聚醚多元醇330N、环氧树脂、异佛尔酮二异氰酸酯、亲水扩链剂、交联剂和丙烯酸酯,其中所述聚醚多元醇330N占45%,所述环氧树脂占35%,所述异佛尔酮二异氰酸酯占5%,所述亲水扩链剂占5%,所述交联剂占2%,所述丙烯酸酯占8%,所述可低温固化的改性水性聚氨酯固化剂包括聚氨酯固化剂、封端剂和消泡剂,其中所述聚氨酯固化剂占75%,所述封端剂的含量占24.9%,所述消泡剂占0.1%。
亲水扩链剂为二羟甲基丙酸。
交联剂为三羟甲基丙烷。
封端剂为2-乙基-4-甲基咪唑。
消泡剂为有机硅类消泡剂。
实施例2
一种木器漆用双组份改性的水性聚氨酯涂料,主要由改性的水性聚氨酯分散体和可低温固化的水性聚氨酯固化剂组成,其中,所述改性的水性聚氨酯分散体和所述可低温固化的水性聚氨酯固化剂的质量比为8:2,所述改性的水性聚氨酯分散体包括聚醚多元醇330N、环氧树脂、异佛尔酮二异氰酸酯、亲水扩链剂、交联剂和丙烯酸酯,其中所述聚醚多元醇330N占50%,所述环氧树脂占30%,所述异佛尔酮二异氰酸酯占5%,所述亲水扩链剂占5%,所述交联剂占5%,所述丙烯酸酯占5%,所述可低温固化的改性水性聚氨酯固化剂包括聚氨酯固化剂、封端剂和消泡剂,其中所述聚氨酯固化剂占82%,所述封端剂的含量占17.5%,所述消泡剂占0.5%。
亲水扩链剂为1,4-丁二醇。
交联剂为三羟甲基丙烷。
封端剂为2-乙基-4-甲基咪唑。
消泡剂为有机硅类消泡剂
实施例3
一种木器漆用双组份改性的水性聚氨酯涂料,主要由改性的水性聚氨酯分散体和可低温固化的水性聚氨酯固化剂组成,其中,所述改性的水性聚氨酯分散体和所述可低温固化的水性聚氨酯固化剂的质量比为9:1,所述改性的水性聚氨酯分散体包括聚醚多元醇330N、环氧树脂、异佛尔酮二异氰酸酯、亲水扩链剂、交联剂和丙烯酸酯,其中所述聚醚多元醇330N占48%,所述环氧树脂占33%,所述异佛尔酮二异氰酸酯占5%,所述亲水扩链剂占5%,所述交联剂占2%,所述丙烯酸酯占7%,所述可低温固化的改性水性聚氨酯固化剂包括聚氨酯固化剂、封端剂和消泡剂,其中所述聚氨酯固化剂占80%,所述封端剂的含量占19%,所述消泡剂占1%。
所述亲水扩链剂为二羟甲基丙酸和1,4-丁二醇按照质量比为1:1混合的混合物。
所述交联剂为三羟甲基丙烷。
所述封端剂为2-乙基-4-甲基咪唑。
所述消泡剂为有机硅类消泡剂。
以上所述,仅为本发明的具体实施方式,但本发明的保护范围并不局限于此,任何不经过创造性劳动想到的变化或替换,都应涵盖在本发明的保护范围之内。因此,本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (5)
1.一种木器漆用双组份改性的水性聚氨酯涂料,其特征在于:由改性的水性聚氨酯分散体和可低温固化的水性聚氨酯固化剂组成,其中,所述改性的水性聚氨酯分散体和所述可低温固化的水性聚氨酯固化剂的质量比为(7.5-9.9):(1-3),所述改性的水性聚氨酯分散体包括聚醚多元醇330N、环氧树脂、异佛尔酮二异氰酸酯、亲水扩链剂、交联剂和丙烯酸酯,其中所述聚醚多元醇330N的质量含量占45-50%,所述环氧树脂的质量含量占30-35%,所述异佛尔酮二异氰酸酯的质量含量占5-10%,所述亲水扩链剂的质量含量占5-10%,所述交联剂的质量含量占2-5%,所述丙烯酸酯的质量含量占5-15%,所述可低温固化的改性水性聚氨酯固化剂包括聚氨酯固化剂、封端剂和消泡剂,其中所述聚氨酯固化剂的质量含量占75-85%,所述封端剂的质量含量占15-30%,所述消泡剂的质量含量占0.1-1%。
2.根据权利要求1所述的一种木器漆用双组份改性的水性聚氨酯涂料,其特征在于:所述亲水扩链剂为二羟甲基丙酸或1,4-丁二醇。
3.根据权利要求1所述的一种木器漆用双组份改性的水性聚氨酯涂料,其特征在于:所述交联剂为三羟甲基丙烷。
4.根据权利要求1所述的一种木器漆用双组份改性的水性聚氨酯涂料,其特征在于:所述封端剂为2-乙基-4-甲基咪唑。
5.根据权利要求1所述的一种木器漆用双组份改性的水性聚氨酯涂料,其特征在于:所述消泡剂为有机硅类消泡剂。