CN106590131A - 生态矿物涂料 - Google Patents
生态矿物涂料 Download PDFInfo
- Publication number
- CN106590131A CN106590131A CN201611161814.9A CN201611161814A CN106590131A CN 106590131 A CN106590131 A CN 106590131A CN 201611161814 A CN201611161814 A CN 201611161814A CN 106590131 A CN106590131 A CN 106590131A
- Authority
- CN
- China
- Prior art keywords
- fineness
- mesh
- powder
- parts
- ecological
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种生态矿物涂料,包括重质碳酸钙粉、氢氧化钙粉、生态树脂型可分散胶粉、高岭土、轻质碳酸钙粉;按重量份数计:重质碳酸钙粉、600‑700份,细度400目;氢氧化钙粉、200‑300份,细度400目;生态树脂型可分散胶粉、15‑25份,细度80目;高岭土、40‑60份,细度800目;轻质碳酸钙粉、40‑60份,细度400目。采用本技术方案后,解决了传统内墙腻子粉强度过低,防潮防水性能不好,遇潮湿会很快霉变和降解,容易起皮,开裂,粉化,空鼓,脱落等质量通病。
Description
技术领域
本发明属于建筑材料技术领域,更具体是涉及一种生态矿物涂料。
背景技术
腻子粉是建筑装饰材料中经常用到的一种产品,其主要成分是滑石粉和胶水,腻子粉作为墙面修补找平的一种基材,为下一步刷油漆或贴壁纸打下良好的基础。授权公告号:CN102875086B,授权公告日2014.12.17的中国发明专利公开了一种内墙耐水腻子粉,其包括按照如下重量百分数配比的原料:高岭土粉20-30%、海泡石粉10-20%、硅酸盐水泥15-35%、羟丙基甲基纤维素0.5-3.5%、粳米凝胶粉3-10%、交联淀粉2-6%、麦饭石粉0.5-2%;其中,所述粳米凝胶粉按照如下方法制备:以粳米作为原料,加入其3-8倍重量的水,蒸煮至浆状,过滤除去非浆状物,再经冷却、干燥、磨碎成细度≤140目的粳米凝胶粉。
上述内墙耐水腻子粉在使用中发现,主要存在如下缺陷:1、粘附力小,水溶慢抗裂性差,低温稳定性差,保质期限短,涂层表面平滑度不好,装饰效果差质量难以稳定,装饰效果不耐久等。2、二次装修时还得将腻子底层、涂料面层全部铲除干净,而铲除下来的废弃物难以再利用,不仅浪费资源,还会对土壤和环境造成污染。
发明内容
为了解决现有技术存在的问题,本发明提供一种无毒、环保、耐水性、装饰性好的生态矿物涂料。
为了实现上述目的,本发明的采用的技术方案是:一种生态矿物涂料,包括重质碳酸钙粉、氢氧化钙粉、生态树脂型可分散胶粉、高岭土、轻质碳酸钙粉;按重量份数计:重质碳酸钙粉、600-700份,细度400目;氢氧化钙粉、200-300份,细度400目;生态树脂型可分散胶粉、15-25份,细度80目;高岭土、40-60份,细度800目;轻质碳酸钙粉、40-60份,细度400目。
采用本发明的技术方案后:生态树脂型可分散胶粉具有如有优点:1、增粘、增强、增稠、保湿、防裂、能与涂料中的合成树脂乳液中的极性基团发生胶联共聚反应,共聚成膜,可减少乳液用量30-80%,降低内外墙成本涂料30-50%,并使涂料性能符合或优于相关标准,添加量约1-4%。2、生态环保无污染,在产品的制造、运输、使用过程中和使用后,对人体和环境不仅无毒害,还对人居环境、环境保护、生态环境的良性循环大有益处,属低碳或无碳产品。3、粘稠度好,可改善砂浆的批刮容易性、打磨容易性,有效提高砂浆的初粘力、后期强度、使用寿命及稳定性。4、不会改变材料的基本特性,有效控制和降低水泥砂浆的干缩性,防止产生龟裂纹。5、生态多功能树脂型可分散胶粉产生的网状膜,分布在材料的空隙中,既起粘结作用,又起防水、防渗漏作用,当遇水、遇湿时,该胶粉与矿物材料产生的凝胶体或结晶体,就会吸湿膨胀,迅速堵塞和封闭微孔,微孔就不会渗漏水。6、生态多功能树脂型可分散胶粉具有增粘、增强、增稠、增塑、保湿、调湿、防裂、防温变形等功能,不需另加乳胶粉、木纤维、聚丙烯短纤维、甲酸钙、氢氧化钙、重质碳酸钙等,可节约产品的材料成本,提升生产企业产品的利润空间和市场竟争力。在矿物材料中引入生态多功能树脂型可分散胶粉进行化学改性,激发材料中的活性物质,产生新的凝胶物质,利用天然矿物材料中的一些特性,这种凝胶质量具有透气、调湿,净化功能和防火、防水、防渗滴能力,其粘附力较强,工作性好,干缩性小,表面强度高,不易粉化,使用成本低等特点,属于资源节约型产品。
具体实施方式
下面对本发明的技术方案做进一步的说明:
实施方式一
一种生态矿物涂料,包括重质碳酸钙粉、氢氧化钙粉、生态树脂型可分散胶粉、高岭土、轻质碳酸钙粉;按重量份数计:重质碳酸钙粉、650份,细度400目;氢氧化钙粉、250份,细度400目;生态树脂型可分散胶粉、20份,细度80目;高岭土、50份,细度800目;轻质碳酸钙粉、50份,细度400目。所述重质碳酸钙粉采用方解石粉。
实施方式二
一种生态矿物涂料,包括重质碳酸钙粉、氢氧化钙粉、生态树脂型可分散胶粉、高岭土、轻质碳酸钙粉;按重量份数计:方解石粉、600份,细度400目;氢氧化钙粉、200份,细度400目;生态树脂型可分散胶粉、15份,细度80目;高岭土、40份,细度800目;轻质碳酸钙粉、40份,细度400目。
实施方式三
一种生态矿物涂料,包括重质碳酸钙粉、氢氧化钙粉、生态树脂型可分散胶粉、高岭土、轻质碳酸钙粉;按重量份数计:方解石粉、700份,细度400目;氢氧化钙粉、300份,细度400目;生态树脂型可分散胶粉、25份,细度80目;高岭土、60份,细度800目;轻质碳酸钙粉、60份,细度400目。
上述三种配方制得的生态矿物涂料的监测数据如下:
(1)安全健康环保指标:测试项目标准值(一等品)实测值;游离甲醛(mg/kg)≤100未检出;VOC(mg/kg)≤15未检出;苯系物总和(mg/kg)≤300未检出;铅、镉、铬、汞(mg/kg)≤285未检出;放射性(GB6566-2001)中A类指标未检出;抗细菌、霉菌性能(HG/T3950——2007)0级。
(2)防火性能:燃烧性能级别(GB8624-2006)B1级;燃烧毒理性无滴落物、不产生浮尘和剧毒浓烟。
(3)技术指标:产品外观,白色粉末状;粘度(23±2℃),pa.s℃≥1.00≥1.1-4.3;180°剥离强度N/25mm≥10≥12-33;粘结强度MPa≥0.5≥0.8-1.1;低温稳定性(0℃24h)呈流动状态。
通过监测数据不难看出本方案制得的生态矿物涂料具有无毒、环保、耐水性、装饰性好的特点。
本发明不局限于上述最佳实施方式,任何人在本发明的启示下都可得出其他各种形式的产品,但不论在其形状或结构上作任何变化,凡是具有与本申请相同或相近似的技术方案,均落在本发明的保护范围之内。
Claims (3)
1.一种生态矿物涂料,其特征在于:包括重质碳酸钙粉、氢氧化钙粉、生态树脂型可分散胶粉、高岭土、轻质碳酸钙粉;按重量份数计:重质碳酸钙粉、600-700份,细度400目;氢氧化钙粉、200-300份,细度400目;生态树脂型可分散胶粉、15-25份,细度80目;高岭土、40-60份,细度800目;轻质碳酸钙粉、40-60份,细度400目。
2.根据权利要求1所述的生态矿物涂料,其特征在于:按重量份数计:重质碳酸钙粉、650份,细度400目;氢氧化钙粉、250份,细度400目;生态树脂型可分散胶粉、20份,细度80目;高岭土、50份,细度800目;轻质碳酸钙粉、50份,细度400目。
3.根据权利要求1所述的生态矿物涂料,其特征在于:所述重质碳酸钙粉采用方解石粉。