CN105647265A - 柔性耐水腻子及其制备方法 - Google Patents
柔性耐水腻子及其制备方法 Download PDFInfo
- Publication number
- CN105647265A CN105647265A CN201610200173.7A CN201610200173A CN105647265A CN 105647265 A CN105647265 A CN 105647265A CN 201610200173 A CN201610200173 A CN 201610200173A CN 105647265 A CN105647265 A CN 105647265A
- Authority
- CN
- China
- Prior art keywords
- flexible waterproof
- waterproof putty
- parts
- fibre
- minute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种柔性耐水腻子,该柔性耐水腻子按重量份包括以下组分:水泥45-60份、白云石粉10-15份、灰钙粉6-9份、钠基膨润土0.32-0.75份、可再分散乳胶粉20-24份、木质纤维4-7份、聚丙烯纤维3-5份、聚乙烯醇0.8-2.5份、憎水剂0.6-1.8份、保水剂1.5-2.3份和增稠剂1.3-1.7份。本发明的柔性耐水腻子具有优异的抗裂性能,粘结力强,对墙体和涂料具有双向亲和性。同时,该柔性耐水腻子的施工性良好,且无毒,无异味。
Description
技术领域
本发明涉及建筑材料领域,具体涉及一种柔性耐水腻子及其制备方法。
背景技术
柔性耐水腻子又称抗裂柔性耐水腻子,是由弹性乳液、助剂和粉料等制成的具有一定柔韧性和耐水性的腻子,适用于保温体系涂料施工前抗裂层表面的刮抹找平。
近年来,随着现代经济水平和生活水平的提高,人们对居住环境、办公环境的舒适性、美观性等要求越来越高。然而,现有的柔性耐水腻子存在很多问题,如易开裂、粉化,黏结强度低,耐水性差等。
发明内容
有鉴于此,本发明的目的是提供一种柔性耐水腻子。该柔性耐水腻子具有优异的抗裂性能,粘结强度高,耐水性好。
为实现上述目的,本发明采用的技术方案如下:
一种柔性耐水腻子,按重量份包括以下组分:水泥45-60份、白云石粉10-15份、灰钙粉6-9份、钠基膨润土0.32-0.75份、可再分散乳胶粉20-24份、木质纤维4-7份、聚丙烯纤维3-5份、聚乙烯醇0.8-2.5份、憎水剂0.6-1.8份、保水剂1.5-2.3份和增稠剂1.3-1.7份。
所述白云石粉为白色或浅灰白色粉末,系碳酸钙与碳酸镁的天然复盐,用作生产高级玻璃器皿、医药用瓶、光学玻璃、涂料的原料。
所述灰钙粉是以CaCO3为主要成分的天然优质石灰石,经高温煅烧后成为生石灰(CaO)后,再经精选,部分消化,主要成分是Ca(OH)2。然后再通过高速风选锤式粉碎机粉碎而成的。其表观洁白细腻,在工业、农业、建筑及制造及食品业中都有广泛应用,具体的应用行业有腻子粉、乳胶漆、保温砂浆、建筑涂料、电线电缆、塑钢门窗,还用于烟气脱硫、污水处理等。
所述钠基膨润土为碱性系数大于或等于1的膨润土。膨润土是一种具有多种用途的矿产,其质量和应用领域主要取决于其中蒙脱石含量和属性类型及其晶体化学特性。因而,其开发利用必须因矿而异,因作用而异。如生产活性白土,钙基转钠基,供石油钻探用的钻井注浆,代替淀粉用于纺纱、印染的浆料,建材上用内外墙涂料,制备有机膨润土、用膨润土合成4A沸石、生产白炭黑等。
所述聚乙烯醇是重要的化工原料,用于制造聚乙烯醇缩醛、耐汽油管道和维尼纶合成纤维、织物处理剂、乳化剂、纸张涂层、粘合剂、胶水等。
所述可再分散乳胶粉是聚合物乳液经喷雾干燥后形成的粉体,也称干粉胶。这种粉体在与水接触后能够迅速还原成乳液,并保持与初始乳液相同的性质,即水分蒸发后,这种膜具有高柔韧性、高耐候性和对各种基材的高粘结性。
进一步,所述水泥为普通硅酸盐水泥。所述普通硅酸盐水泥是由硅酸盐水泥熟料、5%-20%的混合材料及适量石膏磨细制成的水硬性胶凝材料,具有强度高、水化热大、抗冻性好、干缩小等特性。
进一步,所述木质纤维的纤维长度为2.1-2.8mm。所述木质纤维是天然可再生木材经过化学处理、机械法加工得到的有机絮状纤维物质,广泛用于混凝土砂浆、石膏制品、木浆海棉、沥青道路等领域,对防止涂层开裂、提高保水性、提高生产的稳定性和施工的和易性、增加强度、增强对表面的附着力等有良好的效果。
进一步,所述聚丙烯纤维的纤维长度为7.3-8.4mm。所述聚丙烯纤维是以丙烯聚合得到的等规聚丙烯为原料纺制而成的合成纤维。
进一步,所述憎水剂为有机硅憎水剂或硬脂酸钙憎水剂。所述憎水剂主要用于瓷砖外墙防水(喷涂)、卫生间、厨房、阳台等瓷砖缝防水,混凝土墙面、瓷砖、石材、木材、水泥面和路面防水,尤其是古建筑修缮(寺庙、教堂、国家保护的古文化遗址)。
进一步,所述保水剂为甲基纤维素醚。所述保水剂使用的是高吸水性树脂,它是一种吸水能力特别强的功能高分子材料。无毒无害,反复释水、吸水,因此农业上人们把它比喻为"微型水库"。同时,它还能吸收肥料、农药、并缓慢释放,增加肥效、药效。高吸水性树脂广泛用于农业、林业、园艺、建筑材料;在工业方面可广泛应用于石油化工、电缆、造纸、传感器、灭火器具、纤维制品、化妆品、食品保鲜、膨胀玩具等。
进一步,所述增稠剂为淀粉醚。
本发明的目的之二在于提供所述柔性耐水腻子的制备方法,其具体步骤为:
A.将上述质量份的水泥、白云石粉、灰钙粉和钠基膨润土放入混合机中搅拌10-15分钟;
B.将上述质量份的可再分散乳胶粉加入步骤A所述混合物中搅拌1-2分钟;
C.将上述质量份的木质纤维和聚丙烯纤维加入步骤B所得混合物中搅拌6-9分钟后研磨2-3分钟;
D.将上述质量份的聚乙烯醇、憎水剂、保水剂和增稠剂加入研磨后的混合物中搅拌3-5分钟,即得所述柔性耐水腻子。
本发明的目的还在于保护所述柔性耐水腻子在保温体系涂料施工前抗裂层表面的刮抹找平中的应用。
本发明的有益效果是:
本发明的柔性耐水腻子具有优异的抗裂性能,粘结力强,对墙体和涂料具有双向亲和性。同时,该柔性耐水腻子的施工性良好,且无毒,无异味。
具体实施方式
实施例1
一种柔性耐水腻子,其组成为:325R普通硅酸盐水泥60kg、白云石粉10kg、灰钙粉9kg、钠基膨润土0.32kg、可再分散乳胶粉24kg、纤维长度为2.1mm的木质纤维7kg、纤维长度为8.4mm的聚丙烯纤维3kg、聚乙烯醇2.5kg、有机硅憎水剂0.6kg、甲基纤维素醚2.3kg和淀粉醚1.3kg。
所述柔性耐水腻子的制备方法骤为:
A.将325R普通硅酸盐水泥、白云石粉、灰钙粉和钠基膨润土放入混合机中搅拌10分钟;
B.将可再分散乳胶粉加入步骤A所述混合物中搅拌2分钟;
C.将木质纤维和聚丙烯纤维加入步骤B所得混合物中搅拌9分钟后研磨2分钟;
D.将聚乙烯醇、有机硅憎水剂、甲基纤维素醚和淀粉醚加入研磨后的混合物中搅拌5分钟,即得所述柔性耐水腻子。
实施例2
一种柔性耐水腻子,其组成为:425R普通硅酸盐水泥45kg、白云石粉15kg、灰钙粉6kg、钠基膨润土0.75kg、可再分散乳胶粉20kg、纤维长度为2.8mm的木质纤维4kg、纤维长度为7.3mm的聚丙烯纤维5kg、聚乙烯醇0.8kg、硬脂酸钙憎水剂1.8kg、甲基纤维素醚1.5kg和淀粉醚1.7kg。
所述柔性耐水腻子的制备方法骤为:
A.将425R普通硅酸盐水泥、白云石粉、灰钙粉和钠基膨润土放入混合机中搅拌15分钟;
B.将可再分散乳胶粉加入步骤A所述混合物中搅拌1分钟;
C.将木质纤维和聚丙烯纤维加入步骤B所得混合物中搅拌6分钟后研磨3分钟;
D.将聚乙烯醇、硬脂酸钙憎水剂、甲基纤维素醚和淀粉醚加入研磨后的混合物中搅拌3分钟,即得所述柔性耐水腻子。
实施例3
一种柔性耐水腻子,其组成为:525R普通硅酸盐水泥54kg、白云石粉13kg、灰钙粉7kg、钠基膨润土0.56kg、可再分散乳胶粉22kg、纤维长度为2.5mm的木质纤维6kg、纤维长度为7.8mm的聚丙烯纤维4kg、聚乙烯醇1.7kg、有机硅憎水剂1.4kg、甲基纤维素醚1.9kg和淀粉醚1.5kg。
所述柔性耐水腻子的制备方法骤为:
A.将525R普通硅酸盐水泥、白云石粉、灰钙粉和钠基膨润土放入混合机中搅拌12分钟;
B.将可再分散乳胶粉加入步骤A所述混合物中搅拌2分钟;
C.将木质纤维和聚丙烯纤维加入步骤B所得混合物中搅拌8分钟后研磨2分钟;
D.将聚乙烯醇、有机硅憎水剂、甲基纤维素醚和淀粉醚加入研磨后的混合物中搅拌4分钟,即得所述柔性耐水腻子。
对比例1
一种柔性耐水腻子,其组成为:325普通硅酸盐水泥48kg、白云石粉11kg、灰钙粉7kg、钠基膨润土0.63kg、可再分散乳胶粉23kg、纤维长度为2.7mm的木质纤维5kg、纤维长度为7.5mm的聚丙烯纤维3kg、聚乙烯醇1.2kg、硬脂酸钙憎水剂0.9kg和淀粉醚1.4kg。
所述柔性耐水腻子的制备方法骤为:
A.将325普通硅酸盐水泥、白云石粉、灰钙粉和钠基膨润土放入混合机中搅拌11分钟;
B.将可再分散乳胶粉加入步骤A所述混合物中搅拌1分钟;
C.将木质纤维和聚丙烯纤维加入步骤B所得混合物中搅拌7分钟后研磨2分钟;
D.将聚乙烯醇、硬脂酸钙憎水剂和淀粉醚加入研磨后的混合物中搅拌3分钟,即得所述柔性耐水腻子。
对比例2
一种柔性耐水腻子,其组成为:425普通硅酸盐水泥57kg、白云石粉14kg、灰钙粉9kg、钠基膨润土0.68kg、可再分散乳胶粉20kg、纤维长度为2.3mm的木质纤维7kg、纤维长度为7.7mm的聚丙烯纤5kg、聚乙烯醇2.3kg、有机硅憎水剂1.1kg、甲基纤维素醚2.1kg和淀粉醚1.6kg。
所述柔性耐水腻子的制备方法骤为:
A.将425普通硅酸盐水泥、白云石粉、灰钙粉、钠基膨润土和木质纤维放入混合机中搅拌13分钟;
B.将可再分散乳胶粉加入步骤A所述混合物中搅拌1分钟;
C.将聚丙烯纤维加入步骤B所得混合物中搅拌7分钟后研磨3分钟;
D.将的聚乙烯醇、有机硅憎水剂、甲基纤维素醚和淀粉醚加入研磨后的混合物中搅拌3分钟,即得所述柔性耐水腻子。
对比例3
以公开号为CN102295848A的发明专利申请实施例所述配方及方法进行柔性腻子制备。具体为,按照重量配比通过搅拌机高速分散搅拌均匀制成:30份水泥,20份聚马来酸酐,15份石英砂,25份滑石粉,15份重钙粉,1份丙纤,2-2.5份聚乙烯醇,2份纳基膨润土,20份沉淀硫酸钡,1份丙二醇。
柔性腻子性能测试
对实施例1-3(分别为实验组1-3)及对比例1-3(分别为对照组1-3)制备得到的柔性腻子进行性能检测,检测结果如下表所示:
由此证明,本发明的柔性耐水腻子具有优异的抗裂性能,粘结力强,对墙体和涂料具有双向亲和性。同时,该柔性耐水腻子的施工性良好。
最后说明的是,以上实施例仅用以说明本发明的技术方案而非限制,尽管参照较佳实施例对本发明进行了详细说明,本领域的普通技术人员应当理解,可以对本发明的技术方案进行修改或者等同替换,而不脱离本发明技术方案的宗旨和范围,其均应涵盖在本发明的权利要求范围当中。
Claims (9)
1.一种柔性耐水腻子,其特征在于,按重量份包括以下组分:水泥45-60份、白云石粉10-15份、灰钙粉6-9份、钠基膨润土0.32-0.75份、可再分散乳胶粉20-24份、木质纤维4-7份、聚丙烯纤维3-5份、聚乙烯醇0.8-2.5份、憎水剂0.6-1.8份、保水剂1.5-2.3份和增稠剂1.3-1.7份。
2.根据权利要求1所述的一种柔性耐水腻子,其特征在于,所述水泥为普通硅酸盐水泥。
3.根据权利要求1所述的一种柔性耐水腻子,其特征在于,所述木质纤维的纤维长度为2.1-2.8mm。
4.根据权利要求1所述的一种柔性耐水腻子,其特征在于,所述聚丙烯纤维的纤维长度为7.3-8.4mm。
5.根据权利要求1所述的一种柔性耐水腻子,其特征在于,所述憎水剂为有机硅憎水剂或硬脂酸钙憎水剂。
6.根据权利要求1所述的一种柔性耐水腻子,其特征在于,所述保水剂为甲基纤维素醚。
7.根据权利要求1所述的一种柔性耐水腻子,其特征在于,所述增稠剂为淀粉醚。
8.权利要求1所述的柔性耐水腻子的制备方法,其特征在于,具体步骤为:
A.将上述质量份的水泥、白云石粉、灰钙粉和钠基膨润土放入混合机中搅拌10-15分钟;
B.将上述质量份的可再分散乳胶粉加入步骤A所述混合物中搅拌1-2分钟;
C.将上述质量份的木质纤维和聚丙烯纤维加入步骤B所得混合物中搅拌6-9分钟后研磨2-3分钟;
D.将上述质量份的聚乙烯醇、憎水剂、保水剂和增稠剂加入研磨后的混合物中搅拌3-5分钟,即得所述柔性耐水腻子。
9.权利要求1-7任一项所述的柔性耐水腻子在保温体系涂料施工前抗裂层表面的刮抹找平中的应用。