CN104893394A - 一种灰白色耐水内墙腻子 - Google Patents
一种灰白色耐水内墙腻子 Download PDFInfo
- Publication number
- CN104893394A CN104893394A CN201510352931.2A CN201510352931A CN104893394A CN 104893394 A CN104893394 A CN 104893394A CN 201510352931 A CN201510352931 A CN 201510352931A CN 104893394 A CN104893394 A CN 104893394A
- Authority
- CN
- China
- Prior art keywords
- water
- preparation
- cement
- wall putty
- canescence
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
提供一种灰白色耐水内墙腻子及其制备方法,其包括按照如下重量份数配比的原料:灰钙粉20-40;白水泥150-200重钙粉;500-700羟丙甲基纤维素;2-4可分散胶粉;3-6木质纤维;1-3水泥减水剂。所述内墙腻子具有提高的施工性能、水泥强度和/或耐水性。
Description
技术领域
本发明属于化工领域,涉及建筑用填充材料,特别涉及一种灰白色耐水内墙腻子。
背景技术
腻子是漆类施工前,对施工面进行预处理的一种表面填充材料,目的在于填充施工面的孔隙及矫正施工面的曲线偏差,为获得均匀、平滑的漆面打好基础,故应具备良好的粘结强度以及耐水性,以保证在空气中水蒸汽的长期侵蚀下不会出现空鼓、起皮、开裂等现象而仍然能够与基体紧密结合,起到良好的装饰与保护作用。
CN102875086A公开了一种内墙耐水腻子粉,其包括按照如下重量百分数配比的原料:高岭土粉20-30%、海泡石粉10-20%、硅酸盐水泥15-35%、羟丙基甲基纤维素0.5-3.5%、粳米凝胶粉3-10%、交联淀粉2-6%、麦饭石粉0.5-2%。
CN1916089公开了一种内墙干粉腻子,其特征在于:其原料按重量百分比计包括:水泥20~40%、可分散胶粉0.5~2%,碳酸钙35~65%、灰钙粉2~10%、木质纤维0.1~0.5、纤维素0~1%、淀粉0~0.1%。
CN 1228399C公开了一种耐水腻子粉,其由氢氧化钙、白水泥、重钙为原料按重量比例3∶2∶5调配而成,上述原料混配均匀后,每吨原料中再加入甲基纤维素4-6千克。其中公开了所述耐水腻子粉具有耐水性能好、附着力强、施 工简便、不起皮、延展性好、透气性强、无毒无味等性能,但是,该专利中同样没有公开所述白水泥的具体组成以及所述耐水腻子粉的具体性能值。
CN 101585684B公开了一种凹凸棒内墙腻子粉,是由提纯后的凹凸棒、活性凹凸棒石粘土、白色硅酸盐水泥、聚丙烯酰胺和锐钛型钛白粉组成,其生产方法是:配料、粉碎、磨粉、包装。将凹凸棒内墙腻子粉放入容器内,添加水浸润5-30分钟,凹凸棒内墙腻子粉与水的比例为1∶0.5-1∶4,经过充分搅拌均匀后,就可以进行刮涂施工。
上述腻子或腻子粉中都使用了白水泥或硅酸盐水泥作为其主要成分之一,都没有使用减水剂,因而在施工性能较差,且腻子强度有待改进。
发明内容
本发明目的在于针对现有技术的不足,提供一种含有水泥减水剂的腻子,尤其提供一种能够提高施工性能、水泥强度和/或耐水性的内墙腻子。
为达到上述目的,本发明采用如下技术方案:
一种灰白色耐水内墙腻子,其包括按照如下重量份数配比的原料:
优选地,所述白水泥含有如下重量份的主要成分:煅烧高岭土60-80、煅 烧石膏30-40、生石灰30-40、沸石20-30,也即由按重量份数计,6080份的煅烧高岭土、30-40份的煅烧石膏、30-40份的生石灰和20-30份的沸石混合制成。
所述可分散胶粉没有特别限制,可以使用本领域常用的任意种类胶粉,例如山西三维集团股份有限公司生成的可分散胶粉。
优选地,所述水泥减水剂包含下述重量份的原料:
更优选地,所述水泥减水剂还包含下述重量份的原料:
优选地,所述异戊二烯基聚乙二醇(也即,异戊二烯基聚氧乙烯醚)的分子量为500-10000,优选2000-5000;所述丙烯酰胺基(甲基)丙磺酸为2丙烯酰胺基-2-甲基丙磺酸;所述酸酐为不饱和羧酸酐,例如顺丁烯二酸酐;所述分子量调节剂为甲基丙烯磺酸钠、巯基丙酸或其组合;所述引发剂为过氧 化物或双氧水,更优选双氧水;所述还原剂为维生素C。
优选地,所述水泥减水剂由包括如下步骤的方法制备:
一、底料制备
将水、异戊二烯基聚乙二醇、酸酐、丙烯酰胺基(甲基)丙磺酸、磷酸钠、部分丙烯酸、丙烯酰胺、部分分子量调节剂(优选甲基丙烯磺酸钠)混合,并使得温度达到20-25℃,然后加入引发剂,制得底料;
二、滴加料A的制备
将余量的丙烯酸溶解于水中制备得到丙烯酸水溶液,也即滴加料A;
三、滴加料B的制备
将余量的分子量调节剂(优选巯基丙酸)和维生素C加入到水中,制得所述滴加料B;
四、减水剂成品制备
搅拌使得底料中各组分混合均匀,同时开始滴加料A和滴加料B,滴加完毕以后,加入经过粉碎处理的多胺基纤维粉末,继续搅拌,优选升高温度至35-45℃(优选40-42℃),恒温老化1-3小时,然后加入pH调节剂进行中和。
另外,本发明还提高一种灰白色耐水内墙腻子的制备方法,其包括将灰钙粉、白水泥、重钙粉、羟丙甲基纤维素、可分散胶粉、木质纤维以及水泥减水剂混合的步骤。
具体实施方式
为更好地说明本发明,便于理解本发明的技术方案,本发明的典型但非限制性的实施例如下:
制备实施例1
一、底料制备
将3800千克去离子水、6600千克异戊二烯基聚乙二醇(分子量2400)、1千克顺丁烯二酸酐、23千克2-丙烯酰胺基-2-甲基丙磺酸、1千克磷酸钠、250千克丙烯酸、30千克丙烯酰胺、70千克甲基丙烯磺酸钠混合,并使得温度达到22℃,然后加入50%的双氧水30千克,制得底料;
二、滴加料A的制备
将500千克丙烯酸溶解于1200千克去离子水中制备得到丙烯酸水溶液,也即滴加料A;
三、滴加料B的制备
将35千克甲基丙烯磺酸钠和维生素C加入到水中,制得所述滴加料B;
四、减水剂成品制备
搅拌使得底料中各组分混合均匀,同时开始滴加料A和滴加料B,滴加完毕以后,加入经过粉碎处理的多胺基纤维(水合肼和二乙烯三胺为原料制备,平均分子量10000)粉末1千克,继续搅拌,升高温度至40℃,恒温老化1-3小时,然后加入140千克浓度为50%的氢氧化钠溶液进行中和。
制备实施例2
其它步骤与制备实施例1相同,不同之处在于使用3千克多胺基纤维,而不是1千克。
制备实施例3
其它步骤与制备实施例1相同,不同之处在于底料的步骤中不加入250千克丙烯酸,而将这250千克丙烯酸与滴加料A中的500千克丙烯酸合并,共计750千克,制备得到滴加料A。
制备实施例4
其它步骤与制备实施例1相同,不同之处在于在滴加料B的制备过程中用10千克巯基丙酸代替实施例1中所述35千克甲基丙烯磺酸钠。
制备实施例5
其它步骤与制备实施例1相同,使用2千克多胺基纤维,而不是1千克。
制备实施例6
其它步骤与制备实施例1相同,不同之处在于在滴加料B的制备过程中用35千克巯基丙酸代替实施例1中所述35千克甲基丙烯磺酸钠。
应用实施例1
将下述原料按照如下重量份数混合,制得灰白色耐水内墙腻子:
且其中所述减水剂为实施例1制备得到的减水剂,所述白水泥由煅烧高岭土70重量份、煅烧石膏30重量份、生石灰40重量份、沸石30重量份组成。
应用实施例2
其他条件与应用实施例1相同,不同之处在于使用制备实施例2中得到的水泥减水剂。
应用实施例3
其他条件与应用实施例1相同,不同之处在于使用制备实施例3中得到的 水泥减水剂。
应用实施例4
其他条件与应用实施例1相同,不同之处在于使用制备实施例4中得到的水泥减水剂。
应用实施例5
其他条件与应用实施例1相同,不同之处在于使用制备实施例5中得到的水泥减水剂。
应用实施例6
其他条件与应用实施例1相同,不同之处在于使用制备实施例6中得到的水泥减水剂。
表1 应用实施例1-6的的性能测试结果
上述测试中采用标准:GB/T 9756;GB/T 1732;JG/T3049-1996。
Claims (6)
1.一种灰白色耐水内墙腻子,其包括按照如下重量份数配比的原料:
2.权利要求1所述的灰白色耐水内墙腻子,其中所述白水泥含有如下重量份的主要成分:煅烧高岭土60-80、煅烧石膏30-40、生石灰30-40、沸石20-30。
3.权利要求1所述的灰白色耐水内墙腻子,其中所述水泥减水剂包含下述重量份的原料:
。
4.权利要求3所述的灰白色耐水内墙腻子,其中所述水泥减水剂还包含下述重量份的原料:
。
5.权利要求1-5任一项所述灰白色耐水内墙腻子的制备方法,其包括将灰钙粉、白水泥、重钙粉、羟丙甲基纤维素、可分散胶粉、木质纤维以及水泥减水剂混合的步骤。
6.权利要求5所述灰白色耐水内墙腻子的制备方法,其中水泥减水剂由包括如下步骤的方法制备:
一、底料制备
将水、异戊二烯基聚乙二醇、酸酐、丙烯酰胺基(甲基)丙磺酸、磷酸钠、部分丙烯酸、丙烯酰胺、部分分子量调节剂(优选甲基丙烯磺酸钠)混合,并使得温度达到20-25℃,然后加入引发剂,制得底料;
二、滴加料A的制备
将余量的丙烯酸溶解于水中制备得到丙烯酸水溶液,也即滴加料A;
三、滴加料B的制备
将余量的分子量调节剂(优选巯基丙酸)和维生索C加入到水中,制得所述滴加料B;
四、减水剂成品制备
搅拌使得底料中各组分混合均匀,同时开始滴加料A和淌加料13,滴加完毕以后,加入经过粉碎处理的多胺基纤维粉末,继续搅拌,优选升高温度至35 -45℃(优选40-42℃),恒温老化1-3小时,然后加入pH调节剂进行中和。