CN106588084A - Lightweight multifunctional assembling type interior wall material and preparation method thereof - Google Patents
Lightweight multifunctional assembling type interior wall material and preparation method thereof Download PDFInfo
- Publication number
- CN106588084A CN106588084A CN201611199472.XA CN201611199472A CN106588084A CN 106588084 A CN106588084 A CN 106588084A CN 201611199472 A CN201611199472 A CN 201611199472A CN 106588084 A CN106588084 A CN 106588084A
- Authority
- CN
- China
- Prior art keywords
- parts
- interior wall
- wall material
- water
- light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a lightweight multifunctional assembling type interior wall material and a preparation method thereof. The lightweight multifunctional assembling type interior wall material comprises the following components in parts by weight: 65-85 parts of modified phosphorus-based building gypsum, 6-10 parts of cement, 13-17 parts of sand, 1-2 parts of fibers, 0.1-0.2 part of a modified SC type retarder, 0.05-0.1 part of a water retaining agent, 0.4-0.7 part of a water reducing agent, 1-2 parts of a foaming agent aluminum powder and 0.5-1 part of polystyrene particles. The preparation method of the material comprises the following steps: putting the components into a stirrer according to a ratio and uniformly stirring; then adding 40-60 parts of water at 40 DEG C-50 DEG C and continually stirring; adding the aluminum powder in a stirring process; after rapidly stirring for 25s-35s, taking calcium silicate boards as vertical molds of front and rear molds and molding; and compacting, maintaining, pre-molding and trimming to obtain the material. According to the lightweight multifunctional assembling type interior wall material, the phosphorus gypsum is used as a main raw material and resource utilization of solid wastes is facilitated; the product is convenient to load, unload and hoist and the requirement on the performance of rapidly assembly can be met; and meanwhile, the lightweight multifunctional assembling type interior wall material has functions of light weight, heat preservation and heat insulation, sound isolation, flame resistance and the like, and can be widely applied to assembling type civil buildings.
Description
Technical field
The invention belongs to building material field, and in particular to a kind of light multifunction assembled interior wall material and its preparation side
Method.
Background technology
Green building and building industrialization are that national " 13 " give priority to problem, and wherein assembled architecture is building work
The important implementation of industryization.Assembled architecture refer to will the part of building, component, material it is prefabricated in the factory, transport to applying
Work scene is installed, and by way of slurry anchor or rear pouring concrete the building products to be formed is connected.It has improves engineering matter
The advantages of amount, reduction of erection time, energy saving, reduction energy consumption, clean manufacturing.The 2.3- of inner wall of building area about position construction area
2.6 times, the construction of interior wall in building occupies larger ratio, the research tool of Green energy-saving buildings interior wall material in whole engineering
It is of great importance.At present, in assembled architecture interior wall based on the solid slab or cored slab of armored concrete, due to room
Diversity, diversified interior wall prefabricated board occupies a large amount of construction sites, and the lifting loaded down with trivial details, activity of installation is poor, solid slab more heavy, heap
The problems such as product is complicated.
Ardealite is the solid waste of phosphorous chemical industry production phosphoric acid discharge, about 70,000,000 tons of China ardealite annual emissions,
Accumulative accumulation is more than 300,000,000 tons.Less than 10%, the ardealite of bulk deposition does not only take up a large amount of ploughing to the average utilization of ardealite
Ground soil, occupancy ample resources and fund, while its soluble detrimental impurity, heavy metal, residual acid are leached with rainwater, produce big
Amount acid waste water, to soil, water system severe contamination is caused.It is sustainable that a large amount of waste phosphogypsums have become serious restriction phosphorous chemical industry
Development and the world-famous puzzle of environmental protection.
The green construction material that gypsum material is a kind of low energy consumption, be can be recycled, prefabricated gypsum plate is with gypsum as original
Material, by component design and maintaining process the material with cutting function for preparing is adjusted, and gypsum wallboard is used as novel wall material
The Typical Representative of material, it is excellent with fire prevention, insulation, sound-proof sound-absorbing, light weight, regulation indoor humidity, quick construction convenience etc.
Characteristic, extensively apply under construction.
At present, the research with regard to light cellular partition board has been reported.Such as:Patent《Ecological light weight partition wall board》
(CN200910059203.7) disclose a kind of ecological light weight partition wall board, including the trade waste building waste by weight ratio,
Agricultural wastes are that main materials and auxiliary materials and curing agent component are made, its trade waste 20-70 be major ingredient, its agricultural wastes 21-50
For auxiliary material, its curing agent is 14-39, and product meets national construction sector's partition plate standard and requires;Patent《Light cellular partition board》
(CN201320574299.2) a kind of light cellular partition board, has enhancing calcium silicates panel, lightweight in the both sides of light cellular partition board main body
Partition plate main body is blended together and is formed by flyash, crushed crude pearlite, cement and additive mixing core, granular polystyrene, in light partition wall
Plate lower body part has splicing mouth;Patent《A kind of method that utilization sulfur-fixing coal ash produces light cellular partition board》
(CN201310064276.1) a kind of method that utilization sulfur-fixing coal ash produces light cellular partition board is disclosed:It is divided into three steps A:
Sulfur-fixing coal ash is cleared up, B:Foam cement core, C are prepared using sulfur-fixing coal ash, cement etc.:By light partition wall board core material,
Wall material and reinforcing material shaping are poured into a mould, tear film, maintenance open.At present partition plate is based on cement-based material, such as patent《Light partition wall
Plate》Product sound insulation, humidity are poor, can not meet interior wall functionalization demand;Building industrialization will be China's future architecture
One of direction of development, patent《Ecological light weight partition wall board》And《A kind of method that utilization sulfur-fixing coal ash produces light cellular partition board》
The material preparation technology of offer is poor with assembled architecture matching, it is impossible to meet assembled architecture inner wall section construction demand.
Therefore invent it is a kind of have concurrently the functions such as lightweight, insulation, sound insulation, damping and can the interior wall material of quick assembling there is important meaning
Justice and actual demand.
The content of the invention
The technical problem to be solved is:For the deficiency that above-mentioned prior art is present, there is provided a kind of lightweight is more
Functional assembly formula interior wall material and preparation method thereof, according to the invention of assembled architecture feature it is a kind of have lightweight, insulation, every
The functions such as sound, damping can quick assembling Partition board material, with phosphorous chemical industry solid waste as raw material, ardealite can be promoted to provide
Sourceization is utilized, it is adaptable to assembled civil buildings.
The present invention solves its technical problem and adopts following technical scheme:
The light multifunction assembled interior wall material that the present invention is provided, by weight, its component is included:Modified phosphorus capital construction
Build gypsum 65-85 parts, cement 6-10 parts, sand 13-17 parts, fiber 1-2 parts, modified SC type retarder 0.1-0.2 parts, water-loss reducer
0.05-0.1 parts, water reducer 0.4-0.7 parts, foaming agent aluminium powder 1-2 parts, granules of polystyrene 0.5-1 parts.
By such scheme, described modified phosphorus base plaster of Paris, it is made up of following methods:By ardealite and carbide slag, powder
Coal ash and grinding aid in mass ratio 100:(6-10):(11-16):(0.4-0.7) it is placed in mixer and uniformly mixes, by ball processed
Machine raw material is made it is spherical, 145-160 DEG C calcine 2-3h, grinding, the modified phosphorus base plaster of Paris for obtaining.
By such scheme, described ardealite, its pH value is 5-6, its CaSO4·1/2H2O percentage composition >=90%.
By such scheme, described grinding aid be the one kind in diethylene glycol, polyalcohol amine, triethanolamine or ethylene glycol or
Several mixtures.
By such scheme, described fiber, be polypropylene fibre, Fypro, polyester fiber, polyacrylonitrile fibre,
One or more mixtures in vinal, fibre length is 5-12mm.
It is by the formaldehyde of SC type retarder Jing 18-24wt% concentration by such scheme, described modified SC types retarder
Obtain after solution immersion, dried process.
It is carboxylic propyl methocel ether, TYLOSE 30000, starch ether, hydroxyl by such scheme, described water-loss reducer
One kind in cellulose ether, methyl cellulose ether, or several mixtures.
By such scheme, described water reducer is melamine system water reducer, polycarboxylate based water reducer, naphthalene water reducer
In one or more mixture.
By such scheme, described granules of polystyrene, its density is 17-21Kg/m3, diameter≤4mm.
By such scheme, described calcium silicate board is thermal-insulating type, and thickness is 4mm or 6mm, commercially available.
By such scheme, the cement is one or more of Portland cement, slag cements, sulphate aluminium cement
By the mixture of any proportioning;
By such scheme, described sand is fine sand, a diameter of 0.1-0.25mm;
The above-mentioned light multifunction assembled interior wall material that the present invention is provided, its preparation method is:By weight ratio, will
Modified phosphorus base plaster of Paris, cement, sand, fiber, modified SC type retarder, water-loss reducer and water reducer are placed in mixer and stir equal
It is even, 40-60 part water is then added under the conditions of 40-50 DEG C, continue to stir, aluminium powder is added in whipping process, quickly stir 25-
Using calcium silicate board with microporous as the perpendicular mold forming of forward and backward face mould tool after 35 seconds, then Jing after jolt ramming, maintenance, the demoulding and deburring, obtain many work(of lightweight
Can assembled interior wall material.
The present invention has compared with prior art following main beneficial effect:
First, combine two kinds of lighting technologies of foaming agent foam and light aggregate, using ardealite solid waste as
Major gelled material, is designed by material component, and product has lightweight (120mm body of wall surface densities 68-72Kg/m2), thermal insulation separation
(120mm wall heat transfer coefficients can reach as 0.39-0.42B/W/m heat2K) the features such as, while having easy processing, sound insulation, tune
The function such as wet, effectively improves the deficiency of existing partition plate single function;
Second, according to assembled architecture feature, by material component design, with calcium silicate board as panel disposal molding etc.
Means, solve the problems, such as that gypsum surface layer intensity is relatively low, are not easy to load and unload handling, can apply in assembled architecture;
3rd, raw material is effectively promoted the utilization of phosphorous chemical industry solid waste resource recovery, with great based on ardealite
Environment protection significance.
Light multifunction assembled interior wall material that the present invention is provided and preparation method thereof is green construction material in building
Application in industrialization, significant and actual demand can extensively be applied in assembled architecture.
Specific embodiment
The invention of the application is further illustrated with reference to embodiment, but embodiment is not construed as the limit to right of the present invention
It is fixed.
The ardealite adopted in following embodiments is Yi Hua Group Co., Ltd of Hubei Province, cement, sand, fiber, retarder,
Water-loss reducer, water reducer, calcium silicate board with microporous, polystyrene are commercially available material, and aluminium powder meets GB2084 for commercially available《Get angry aluminium powder》Band
The dry aluminium powder of fat, sand is fine sand, a diameter of 0.1-0.25mm.
Embodiment 1:
A kind of light multifunction assembled interior wall material is prepared according to technical scheme, in parts by weight, it
Component be 70 parts of phosphorus base plaster of Paris, 8 parts of Portland cement, 15 parts of sand, 1.5 parts of polypropylene fibre, be modified SC slow settings
0.15 part of agent, 0.08 part of carboxylic propyl methocel ether water-loss reducer, 0.5 part of melamine system water reducer, 1.5 parts of aluminium powder, polyphenyl
0.6 part of ethene particle, silico-calcium plate thickness selects 6mm.
Said components are placed in mixer and stir 5-10min to stirring, under the conditions of 40-50 DEG C, add 46 parts
Water, adds aluminium powder during low rate mixing, quickly stir 30s, using calcium silicate board with microporous as front-back mould and reserved handling hole, erects mould
Shaping, jolt ramming strikes off, and conserves, the demoulding, deburring, and light multifunction assembled lining is obtained.According to《Building partition lightweight
Batten》(JG/T169-2005) standard requires sheet material measurement performance, the results are shown in Table 1.
Embodiment 2:
A kind of light multifunction assembled interior wall material is prepared according to technical scheme, in parts by weight, it
Component be 65 parts of phosphorus base plaster of Paris, 10 parts of slag cements, 15 parts of sand, 2.0 parts of Fypro, be modified SC retarder 0.11
Part, 0.07 part of TYLOSE 30000 water-loss reducer, 0.7 part of polycarboxylate based water reducer, 2.0 parts of aluminium powder, granules of polystyrene 0.5
Part, silico-calcium plate thickness selects 4mm.
Above-mentioned modified ardealite, cement, sand, fiber, retarder, water reducer, water-loss reducer are placed in mixer and stir 5-
10min under the conditions of 40-50 DEG C, adds 45 parts of water to stirring, and aluminium powder is added during low rate mixing, quick stirring
30s, using calcium silicate board with microporous as front-back mould and reserved handling hole, erects mold forming, and jolt ramming strikes off, and conserves, the demoulding, deburring, is obtained
Light multifunction assembled lining.According to《Light lath for building partition wall》(JG/T169-2005) standard requires sheet material measurement
Performance, the results are shown in Table 2.
Embodiment 3:
A kind of light multifunction assembled interior wall material is prepared according to technical scheme, in parts by weight, it
Component be 85 parts of phosphorus base plaster of Paris, 6 parts of sulphate aluminium cement, 13 parts of sand, 1.0 parts of polyester fiber, be modified SC retarder
0.20 part, 0.10 part of starch ether water-loss reducer, 0.7 part of naphthalene water reducer, 1.0 parts of aluminium powder, 0.7 part of granules of polystyrene, calcium silicate board with microporous
Thickness selects 6mm.
Above-mentioned modified ardealite, cement, sand, fiber, retarder, water reducer, water-loss reducer are placed in mixer and stir 5-
10min under the conditions of 40-50 DEG C, adds 60 parts of water to stirring, and aluminium powder is added during low rate mixing, quick stirring
30s, using calcium silicate board with microporous as front-back mould and reserved handling hole, erects mold forming, and jolt ramming strikes off, and conserves, the demoulding, deburring, is obtained
Light multifunction assembled lining.According to《Light lath for building partition wall》(JG/T169-2005) standard requires sheet material measurement
Performance, the results are shown in Table 3.
Embodiment 4:
A kind of light multifunction assembled interior wall material is prepared according to technical scheme, in parts by weight, it
Component be 10 parts of 66 parts of phosphorus base plaster of Paris, Portland cement and slag cements, 16 parts of sand, polyacrylonitrile fibre and poly-
1.5 parts of alcohol fibers, be modified 0.11 part of SC retarder, 0.08 part of hydroxyethyl ether cellulose water-loss reducer, melamine series and naphthalene
0.5 part of based water reducer, 1.0 parts of aluminium powder, 1.0 parts of granules of polystyrene, silico-calcium plate thickness selects 6mm.
Above-mentioned modified ardealite, cement, sand, fiber, retarder, water reducer, water-loss reducer are placed in mixer and stir 5-
10min under the conditions of 40-50 DEG C, adds 45 parts of water to stirring, and aluminium powder is added during low rate mixing, quick stirring
30s, using calcium silicate board with microporous as front-back mould and reserved handling hole, erects mold forming, and jolt ramming strikes off, and conserves, the demoulding, deburring, is obtained
Light multifunction assembled lining.According to《Light lath for building partition wall》(JG/T169-2005) standard requires sheet material measurement
Performance, the results are shown in Table 4.
Embodiment 5:
A kind of light multifunction assembled interior wall material is prepared according to technical scheme, in parts by weight, it
Component be 9 parts of 80 parts of phosphorus base plaster of Paris, Portland cement and sulphate aluminium cement, 15 parts of sand, vinal
1.5 parts, be modified 0.18 part of SC retarder, 0.10 part of methyl cellulose ether water-loss reducer, polycarboxylate water-reducer and naphthalene water reducer 0.7
Part, 1.2 parts of aluminium powder, 0.9 part of granules of polystyrene, silico-calcium plate thickness selects 4mm.
Above-mentioned modified ardealite, cement, sand, fiber, retarder, water reducer, water-loss reducer are placed in mixer and stir 5-
10min under the conditions of 40-50 DEG C, adds 55 parts of water to stirring, and aluminium powder is added during low rate mixing, quick stirring
30s, using calcium silicate board with microporous as front-back mould and reserved handling hole, erects mold forming, and jolt ramming strikes off, and conserves, the demoulding, deburring, is obtained
Light multifunction assembled lining.According to《Light lath for building partition wall》(JG/T169-2005) standard requires sheet material measurement
Performance, the results are shown in Table 5.
Embodiment 6:
A kind of light multifunction assembled interior wall material is prepared according to technical scheme, in parts by weight, it
Component be 75 parts of phosphorus base plaster of Paris, Portland cement, slag cements, 8 parts of sulphate aluminium cement, 14 parts of sand, poly- third
Alkene fiber, Fypro, polyester fiber, polyacrylonitrile fibre, 1.5 parts of vinal, be modified 0.16 part of SC retarder,
Carboxylic propyl methocel ether, TYLOSE 30000, starch ether, hydroxyethyl ether cellulose or methylcellulose ether mixture are protected
0.09 part of aqua, 0.6 part of melamine system water reducer, polyurethane water reducer, 1.3 parts of aluminium powder, 0.8 part of granules of polystyrene, silicon
Calcium plate thickness selects 4mm.
Above-mentioned modified ardealite, cement, sand, fiber, retarder, water reducer, water-loss reducer are placed in mixer and stir 5-
10min under the conditions of 40-50 DEG C, adds 50 parts of water to stirring, and aluminium powder is added during low rate mixing, quick stirring
30s, using calcium silicate board with microporous as front-back mould and reserved handling hole, erects mold forming, and jolt ramming strikes off, and conserves, the demoulding, deburring, is obtained
Light multifunction assembled lining.According to《Light lath for building partition wall》(JG/T169-2005) standard requires sheet material measurement
Performance, the results are shown in Table 6.
In above-described embodiment, the cement for being adopted is in Portland cement, slag cements, sulphate aluminium cement
Plant or several mixtures by any proportioning;The sand for being adopted for fine sand, a diameter of 0.1-0.25mm;The calcium silicate board for being adopted
For thermal-insulating type, thickness is 4mm or 6mm, commercially available.
Each raw material cited by the present invention, and bound, the interval value of each raw material of the invention, and technological parameter
Bound, interval value can realize the present invention, embodiment numerous to list herein.
The product of 1 embodiment of table 1 according to《Light lath for building partition wall》Standard requires sheet material measurement performance
Other performance is satisfied by《Light lath for building partition wall》(JG/T169-2005) standard is required.
The product of 2 embodiment of table 2 according to《Light lath for building partition wall》Standard requires sheet material measurement performance
Other performance is satisfied by《Light lath for building partition wall》(JG/T169-2005) standard is required.
The product of 3 embodiment of table 3 according to《Light lath for building partition wall》Standard requires sheet material measurement performance
Other performance is satisfied by《Light lath for building partition wall》(JG/T169-2005) standard is required.
The product of 4 embodiment of table 4 according to《Light lath for building partition wall》Standard requires sheet material measurement performance
Other performance is satisfied by《Light lath for building partition wall》(JG/T169-2005) standard is required.
The product of 5 embodiment of table 5 according to《Light lath for building partition wall》Standard requires sheet material measurement performance
Other performance is satisfied by《Light lath for building partition wall》(JG/T169-2005) standard is required.
The product of 6 embodiment of table 6 according to《Light lath for building partition wall》Standard requires sheet material measurement performance
Other performance is satisfied by《Light lath for building partition wall》(JG/T169-2005) standard is required.
Claims (10)
1. a kind of light multifunction assembled interior wall material, it is characterised in that by weight, its component is included:Modified phosphorus capital construction
Build gypsum 65-85 parts, cement 6-10 parts, sand 13-17 parts, fiber 1-2 parts, modified SC type retarder 0.1-0.2 parts, water-loss reducer
0.05-0.1 parts, water reducer 0.4-0.7 parts, foaming agent aluminium powder 1-2 parts, granules of polystyrene 0.5-1 parts.
2. light multifunction assembled interior wall material as claimed in claim 1, it is characterised in that described modified phosphorus capital construction is built
Gypsum, is made up of following methods:By ardealite and carbide slag, flyash and grinding aid in mass ratio 100:(6-10):(11-
16):(0.4-0.7) be placed in mixer and uniformly mix, raw material is made by marble forming machine it is spherical, 145-160 DEG C calcine 2-
3h, grinding, the modified phosphorus base plaster of Paris for obtaining.
3. light multifunction assembled interior wall material as claimed in claim 2, it is characterised in that described ardealite, its pH value
For 5-6, its CaSO4·1/2H2O percentage composition >=90%.
4. light multifunction assembled interior wall material as claimed in claim 2, it is characterised in that described grinding aid is diethyl
One or more mixtures in glycol, polyalcohol amine, triethanolamine or ethylene glycol.
5. light multifunction assembled interior wall material as claimed in claim 1, it is characterised in that described fiber, is polypropylene
One or more mixtures in fiber, Fypro, polyester fiber, polyacrylonitrile fibre, vinal, fiber is long
Spend for 5-12mm.
6. light multifunction assembled interior wall material as claimed in claim 1, it is characterised in that described modified SC types slow setting
Agent, is obtained Jing after formalin immersion, the dried process of 18-24wt% concentration by SC types retarder.
7. light multifunction assembled interior wall material as claimed in claim 1, it is characterised in that described water-loss reducer, is carboxylic third
One kind in ylmethyl cellulose ether, TYLOSE 30000, starch ether, hydroxyethyl ether cellulose, methyl cellulose ether, or it is several
Plant mixture.
8. light multifunction assembled interior wall material as claimed in claim 1, it is characterised in that described water reducer is trimerization
One or more mixture in cyanamide based water reducer, polycarboxylate based water reducer, naphthalene water reducer.
9. light multifunction assembled interior wall material as claimed in claim 1, it is characterised in that described granules of polystyrene,
Its density is 17-21Kg/m3, diameter≤4mm.
10. in a kind of claim 1 to 9 arbitrary light multifunction assembled interior wall material preparation method, it is characterized in that
By proportioning, modified phosphorus base plaster of Paris, cement, sand, fiber, modified SC type retarder, water-loss reducer and water reducer are placed in into stirring
Stir in machine, 40-60 part water then added under the conditions of 40-50 DEG C, continue to stir, aluminium powder is added in whipping process,
Using calcium silicate board with microporous as the perpendicular mold forming of forward and backward face mould tool after the quick stirring 25-35 seconds, then Jing after jolt ramming, maintenance, the demoulding and deburring,
Obtain light multifunction assembled interior wall material.