CN106565898A - 一种三防整理剂及其制备方法和应用 - Google Patents
一种三防整理剂及其制备方法和应用 Download PDFInfo
- Publication number
- CN106565898A CN106565898A CN201611034196.1A CN201611034196A CN106565898A CN 106565898 A CN106565898 A CN 106565898A CN 201611034196 A CN201611034196 A CN 201611034196A CN 106565898 A CN106565898 A CN 106565898A
- Authority
- CN
- China
- Prior art keywords
- acrylate
- mass
- finishing agent
- initiator
- proofing finishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种三防整理剂，用于织物的三防整理。所述三防整理剂为有效成分包含高分子聚合物A的水包油型乳液，其中所述高分子聚合物A由（甲基）丙烯酸全氟烷基丙烯酸酯M1、丙烯酸烷基酯M2和阳离子单体M3在引发剂D引发的条件下聚合而成。在本发明所述的三防整理剂中，添加了阳离子单体M3。通过调整所述阳离子单体M3的具体种类和用量，可以调整本发明所述三防整理剂的电性及电量，达到增大所述三防整理剂在织物表面的吸附量的目的，使得在同用量的条件下使用时有良好的三防效果，降低使用成本。
Description
技术领域
本发明涉及纺织品功能整理剂领域，特别涉及一种三防整理剂及其制备方法和应用。
背景技术
随着社会发展，对纺织品的功能整理需求越来越大。通过三防整理可以大大降低织物的表面张力，从而使织物可以具有拒水拒油防污功能。目前，高支高密涤纶等轻薄面料在三防整理过程中由于带液率偏低，经过三防整理剂整理之后往往效果不是很理想。
因此，我们需要一种新的三防整理剂，以解决目前存在的技术问题。
发明内容
本发明的目的在于提供一种三防整理剂，在配方中加入了阳离子单体M3，通过调整阳离子单体M3的具体种类和用量，调整三防整理剂的电性及电量。这样，由于高支高密涤纶面料本身带有负电荷，使得本发明所述的三防整理剂可以增强整理剂与面料之间的吸附量，在同用量的前提下提高三防整理效果，降低使用成本。
为了获得上述目的，本发明首先提供一种三防整理剂，所述三防整理剂为有效成分包含高分子聚合物A的水包油型乳液；其中，所述高分子聚合物A由（甲基）丙烯酸全氟烷基丙烯酸酯M1、丙烯酸烷基酯M2和阳离子单体M3在引发剂D引发的条件下聚合而成；并且，所述（甲基）丙烯酸全氟烷基丙烯酸酯M1的质量占所述高分子聚合物A的质量的15~70%；丙烯酸烷基酯M2的质量占所述高分子聚合物A的质量的30~80%；阳离子单体M3的质量占所述高分子聚合物A的质量的0.5~5%；并且，所述阳离子单体M3选自烯丙基胺、二烯丙基胺、三烯丙基胺、二甲基二烯丙基氯化铵、四烯丙基氯化铵、丙烯酸二甲氨基乙酯、丙烯酰氧乙基三甲基氯化铵、丙烯酰氧乙基二甲基苄基氯化铵、甲基丙烯酸二甲氨基乙酯、甲基丙烯酰氧乙基三甲基氯化铵、甲基丙烯酰氧乙基二甲基苄基氯化铵、二甲氨基丙基甲基丙烯酰胺、甲基丙烯酰丙基三甲基氯化铵、二甲氨基丙基丙烯酰胺、丙烯酰丙基三甲基氯化铵、N-羟甲基丙烯酰胺和二甲基丙烯酰胺中的一种或几种混合。
所述（甲基）丙烯酸全氟烷基丙烯酸酯M1选自含有4～14个全氟烷基碳的全氟丙烯酸酯单体中的一种或几种混合。
所述丙烯酸烷基酯M2选自1,6-己二醇二丙烯酸酯、丙烯酸-2-乙基己酯、丙烯酸丁酯、丙烯酸异辛酯、丙烯酸-2-乙氧基乙酯、丙烯酸十二酯、丙烯酸十六酯、丙烯酸十八酯、丙烯酸环己酯、甲基丙烯酸十八酯、丙烯酸甲酯、甲基丙基酸甲酯、丙烯酸-2-羟基乙酯、丙烯酸-2氰基乙酯、丙烯酸异冰片酯和甲基丙烯酸异冰片酯中的一种或几种混合。
所述引发剂D的质量为所述高分子聚合物A的质量的0. 1~5%。并且，所述引发剂D选自水溶性引发剂V50，过硫酸铵和过硫酸钾等中的一种。
所述三防整理剂还包含复合表面活性剂B、有机溶液C和去离子水；其中，所述复合表面活性剂B的质量为所述高分子聚合物A的质量的1~10%；所述有机溶液C的质量为所述高分子聚合物A的质量的30~60%；所述去离子水的质量为所述高分子聚合物A的质量的2~4倍。
所述表面活性剂B由阳离子表面活性剂和非离子表面活性剂组成；其中，所述阳离子表面活性剂与所述非离子表面活性剂的质量比为1 : (0.2~2)。所述阳离子表面活性剂选自十八烷基三甲基氯化铵、十六烷基三甲基氯化铵、十六烷基溴化吡啶、十六烷基三甲基季溴化铵、十八烷基二甲基苄基季氯化铵或双十八烷基二甲基氯化铵中的一种或几种混合；所述非离子表面活性剂选自脂肪醇聚氧乙烯醚、烷基酚聚氧乙烯醚、脂肪酸聚氧乙烯酯、脂肪胺聚氧乙烯醚、烷基醇酰胺聚氧乙烯醚、嵌段聚氧乙烯-聚氧丙烯醚、失水山梨醇脂肪酸酯和聚氧乙烯失水山梨醇脂肪酸酯中的一种或几种混合。
所述有机溶液C选自丙二醇单丁基醚、乙二醇丙醚、丙二醇单丙基醚、丙二醇乙醚、二乙二醇乙醚乙酸酯和二异丁基甲酮中的一种或几种混合。
所述引发剂D选自水溶性引发剂V50，过硫酸铵和过硫酸钾等中的一种。
本发明还提供上述三防整理剂的制备方法。所述方法是：将（甲基）丙烯酸全氟烷基丙烯酸酯M1、丙烯酸烷基酯M2、阳离子单体M3、、复合表面活性剂B、有机溶液C和去离子水在40~80℃下剪切分散形成预乳液；取部分所述预乳液后加入部分质量分数为5~20%的引发剂水溶液，65~90℃下保温半小时，获得种子乳液；最后，向所述种子乳液中加入剩下的预乳液及剩下的质量分数为5~20%的引发剂D水溶液，在65~90℃下保温4~5小时，获得所述三防整理剂；其中，所述（甲基）丙烯酸全氟烷基丙烯酸酯M1的质量占所述高分子聚合物A的质量的15~70%；丙烯酸烷基酯M2的质量占所述高分子聚合物A的质量的30~80%；阳离子单体M3的质量占所述高分子聚合物A的质量的0.5~5%；所述复合表面活性剂B的质量为所述高分子聚合物A的质量的1~10%；所述有机溶液C的质量为所述高分子聚合物A的质量的30~60%；所述去离子水的质量为所述高分子聚合物A的质量的2~4倍；所述引发剂D的质量为所述高分子聚合物A的质量的0. 1~5%。
所述方法具体包括以下步骤：步骤S10. 制备预乳液：按各组分质量比称取后，（甲基）丙烯酸全氟烷基丙烯酸酯M1、丙烯酸烷基酯M2、阳离子单体M3、复合表面活性剂B、有机溶液C和去离子水在40~80℃下剪切分散形成预乳液；步骤S20. 制备引发剂D水溶液：将所述引发剂D制成质量分数为5~20%的引发剂水溶液；步骤S30. 在氮气气氛下，将所述步骤S10制得的所述预乳液的20～50%与所述步骤S20制得的所述引发剂D水溶液的20~50%混合，65~90℃下保温半小时，获得种子乳液；以及，步骤S40. 在氮气气氛下，向步骤S30获得的所述种子乳液中加入剩下的预乳液及剩下的引发剂D水溶液，在65~90℃下保温4~5小时，获得所述三防整理剂。
本发明所述的三防整理剂尤其适于高支高密涤纶面料的三防整理。
本领域技术人员可以理解的是，如无特殊说明，本发明所述实际均为市售产品。
在本发明所述的三防整理剂中，添加了阳离子单体M3。通过调整所述阳离子单体M3的具体种类和用量，可以调整本发明所述三防整理剂的电性及电量，达到增强所述三防整理剂在织物表面的吸附量的目的。由于高支高密涤纶面料本身带有负电荷，因此，本发明所述的三防整理剂由于增强了电量从而增强了其与面料之间的吸附量。因此，本发明所述的三防整理剂具有显著的三防效果，在同用量的前提下可以大幅提高三防效果，进而降低使用成本。
具体实施方式
以下，结合具体实施方式，对本发明的技术进行详细描述。应当知道的是，以下具体实施方式仅用于帮助本领域技术人员理解本发明，而非对本发明的限制。
实施例1
在本实施例中，提供一种三防整理剂，专用于高支高密涤纶面料。所述三防整理剂的制备方法具体如下。
将70份8碳全氟烷基丙烯酸酯、170份丙烯酸十八酯、5份丙烯酰氧乙基二甲基苄基氯化铵、3份SP-80、5份SE-10、5份十八烷基二甲基苄基氯化铵、80份丙二醇单丁基醚和1份正十二硫醇加入反应器中，在50℃下加入600份去离子水高速剪切分散乳化30分钟得到预乳液。将2份引发剂V50用去离子水溶解为质量分数为10%的引发剂水溶液，向安装有搅拌器、温度计、氮气导管和回流冷凝装置的反应器中通入氮气，向其中加入25%的预乳液和30%的引发剂水溶液，80℃保温反应30分钟，得到泛蓝光的种子乳液，最后向种子乳液中加入剩下的预乳液和引发剂水溶液，滴加完80℃保温4小时，即得到一种高支高密涤纶面料专用的三防整理剂。冷却至室温后过滤包装即可。
实施例2
在本实施例中，提供一种三防整理剂，专用于高支高密涤纶面料。所述三防整理剂的制备方法具体如下。
将70份8碳全氟烷基丙烯酸酯，100份丙烯酸十八酯，70份丙烯酸十六酯，5份丙烯酰氧乙基二甲基苄基氯化铵，3份SP-80，5份SE-10，5份十八烷基二甲基苄基氯化铵，80份丙二醇单丁基醚和1份正十二硫醇加入反应器中，在50℃加入600份去离子水高速剪切分散乳化30分钟得到预乳液。将2份引发剂V50用去离子水溶解为质量分数为10%的引发剂水溶液，向安装有搅拌器、温度计、氮气导管和回流冷凝装置的反应器中通入氮气，向其中加入25%的预乳液和30%的引发剂水溶液，80℃保温反应30分钟，得到泛蓝光的种子乳液，最后向种子乳液中加入剩下的预乳液和引发剂水溶液，滴加完80℃保温4小时，即得到一种高支高密涤纶面料专用三防整理剂。冷却至室温后过滤包装即可。
实施例3
在本实施例中，提供一种三防整理剂，专用于高支高密涤纶面料。所述三防整理剂的制备方法具体如下。
将70份8碳全氟烷基丙烯酸酯，170份丙烯酸十八酯，5份甲基丙烯酰氧乙基二甲基苄基氯化铵，3份SP-80，5份AEO-7，5份十八烷基二甲基苄基氯化铵，80份丙二醇单丁基醚和1份正十二硫醇加入反应器中，在50℃加入600份去离子水高速剪切分散乳化30分钟得到预乳液。将2份引发剂V50用去离子水溶解为质量分数为10%的引发剂水溶液，向安装有搅拌器、温度计、氮气导管和回流冷凝装置的反应器中通入氮气，向其中加入25%的预乳液和30%的引发剂水溶液，80℃保温反应30分钟，得到泛蓝光的种子乳液，最后向种子乳液中加入剩下的预乳液和引发剂水溶液，滴加完80℃保温4小时，即得到一种高支高密涤纶面料专用三防整理剂。冷却至室温后过滤包装即可。
实施例4
在本实施例中，提供一种三防整理剂，专用于高支高密涤纶面料。所述三防整理剂的制备方法具体如下。
将70份8碳全氟烷基丙烯酸酯，170份丙烯酸十八酯，10份二甲氨基丙基丙烯酰胺，10份冰醋酸3份SP-80，5份SE-10，5份十八烷基二甲基苄基氯化铵，80份丙二醇单丁基醚和1份正十二硫醇加入反应器中，在50℃加入590份去离子水高速剪切分散乳化30分钟得到预乳液。将2份引发剂V50用去离子水溶解为质量分数为10%的引发剂水溶液，向安装有搅拌器、温度计、氮气导管和回流冷凝装置的反应器中通入氮气，向其中加入25%的预乳液和30%的引发剂水溶液，80℃保温反应30分钟，得到泛蓝光的种子乳液，最后向种子乳液中加入剩下的预乳液和引发剂水溶液，滴加完80℃保温4小时，即得到一种高支高密涤纶面料专用三防整理剂。冷却至室温，过滤，包装。
在本发明所述的三防整理剂中，添加了阳离子单体M3。通过调整所述阳离子单体M3的具体种类和用量，可以调整本发明所述三防整理剂的电性及电量，达到增强所述三防整理剂在织物表面的吸附量的目的。由于高支高密涤纶面料本身带有负电荷，因此，本发明所述的三防整理剂由于增强了电量从而增强了其与面料之间的吸附量。因此，本发明所述的三防整理剂具有显著的三防效果，在同用量的前提下可以大幅提高三防效果，进而降低使用成本。
本发明已由上述相关实施例加以描述，然而上述实施例仅为实施本发明的范例。必需指出的是，已公开的实施例并未限制本发明的范围。相反地，包含于权利要求书的精神及范围的修改及均等设置均包括于本发明的范围内。
Claims (10)
1.一种三防整理剂，用于织物的三防整理，其特征在于，所述三防整理剂为有效成分包含高分子聚合物A的水包油型乳液；其中，
所述高分子聚合物A由（甲基）丙烯酸全氟烷基丙烯酸酯M1、丙烯酸烷基酯M2和阳离子单体M3在引发剂D引发的条件下聚合而成；并且，
所述（甲基）丙烯酸全氟烷基丙烯酸酯M1的质量占所述高分子聚合物A的质量的15~70%；
丙烯酸烷基酯M2的质量占所述高分子聚合物A的质量的30~80%；
阳离子单体M3的质量占所述高分子聚合物A的质量的0.5~5%；并且，
所述阳离子单体M3选自含有C=C双键的胺类或者含有C=C双键的季铵盐类中的一种或几种的混合物；
优选的，所述阳离子单体M3选自烯丙基胺、二烯丙基胺、三烯丙基胺、二甲基二烯丙基氯化铵、四烯丙基氯化铵、丙烯酸二甲氨基乙酯、丙烯酰氧乙基三甲基氯化铵、丙烯酰氧乙基二甲基苄基氯化铵、甲基丙烯酸二甲氨基乙酯、甲基丙烯酰氧乙基三甲基氯化铵、甲基丙烯酰氧乙基二甲基苄基氯化铵、二甲氨基丙基甲基丙烯酰胺、甲基丙烯酰丙基三甲基氯化铵、二甲氨基丙基丙烯酰胺、丙烯酰丙基三甲基氯化铵、N-羟甲基丙烯酰胺和二甲基丙烯酰胺中的一种或几种混合。
2.如权利要求1所述的三防整理剂，其特征在于，所述（甲基）丙烯酸全氟烷基丙烯酸酯M1选自含有4～14个全氟烷基碳的全氟丙烯酸酯单体中的一种或几种混合。
3.如权利要求1所述的三防整理剂，其特征在于，所述丙烯酸烷基酯M2选自1,6-己二醇二丙烯酸酯、丙烯酸-2-乙基己酯、丙烯酸丁酯、丙烯酸异辛酯、丙烯酸-2-乙氧基乙酯、丙烯酸十二酯、丙烯酸十六酯、丙烯酸十八酯、丙烯酸环己酯、甲基丙烯酸十八酯、丙烯酸甲酯、甲基丙基酸甲酯、丙烯酸-2-羟基乙酯、丙烯酸-2氰基乙酯、丙烯酸异冰片酯和甲基丙烯酸异冰片酯中的一种或几种混合。
4.如权利要求1所述的三防整理剂，其特征在于，所述引发剂D的质量为所述高分子聚合物A的质量的0. 1~5%；并且，所述引发剂D选自水溶性引发剂V50，过硫酸铵和过硫酸钾等中的一种。
5.如权利要求1所述的三防整理剂，其特征在于，所述三防整理剂还包含复合表面活性剂B、有机溶液C和去离子水；其中，
所述复合表面活性剂B的质量为所述高分子聚合物A的质量的1~10%；
所述有机溶液C的质量为所述高分子聚合物A的质量的30~60%；
所述去离子水的质量为所述高分子聚合物A的质量的2~4倍。
6.如权利要求5所述的三防整理剂，其特征在于，所述复合表面活性剂B由阳离子表面活性剂和非离子表面活性剂组成；其中，所述阳离子表面活性剂与所述非离子表面活性剂的质量比为1 : (0.2~2)，其特征在于，所述阳离子表面活性剂选自十八烷基三甲基氯化铵、十六烷基三甲基氯化铵、十六烷基溴化吡啶、十六烷基三甲基季溴化铵、十八烷基二甲基苄基季氯化铵或双十八烷基二甲基氯化铵中的一种或几种混合；所述非离子表面活性剂选自脂肪醇聚氧乙烯醚、烷基酚聚氧乙烯醚、脂肪酸聚氧乙烯酯、脂肪胺聚氧乙烯醚、烷基醇酰胺聚氧乙烯醚、嵌段聚氧乙烯-聚氧丙烯醚、失水山梨醇脂肪酸酯或聚氧乙烯失水山梨醇脂肪酸酯中的一种或几种混合。
7.如权利要求5所述的三防整理剂，其特征在于，所述有机溶液C选自丙二醇单丁基醚、乙二醇丙醚、丙二醇单丙基醚、丙二醇乙醚、二乙二醇乙醚乙酸酯和二异丁基甲酮中的一种或几种混合。
8.一种如权利要求1所述的三防整理剂的制备方法，其特征在于，所述方法是：将（甲基）丙烯酸全氟烷基丙烯酸酯M1、丙烯酸烷基酯M2、阳离子单体M3、复合表面活性剂B、有机溶液C和去离子水在40~80℃下剪切分散形成预乳液；取部分所述预乳液后加入部分质量分数为5~20%的引发剂D水溶液，65~90℃下保温半小时，获得种子乳液；最后，向所述种子乳液中加入剩下的预乳液及剩下的质量分数为5~20%的引发剂D水溶液，在65~90℃下保温4~5小时，获得所述三防整理剂；其中，
所述高分子聚合物A由（甲基）丙烯酸全氟烷基丙烯酸酯M1、丙烯酸烷基酯M2和阳离子单体M3在引发剂D引发的条件下聚合而成；并且，
所述（甲基）丙烯酸全氟烷基丙烯酸酯M1的质量占所述高分子聚合物A的质量的15~70%；
丙烯酸烷基酯M2的质量占所述高分子聚合物A的质量的30~80%；
阳离子单体M3的质量占所述高分子聚合物A的质量的0.5~5%；
所述复合表面活性剂B的质量为所述高分子聚合物A的质量的1~10%；
所述有机溶液C的质量为所述高分子聚合物A的质量的30~60%；
所述去离子水的质量为所述高分子聚合物A的质量的2~4倍；
所述引发剂D的质量为所述高分子聚合物A的质量的0. 1~5%。
9.如权利要求8所述的制备方法，其特征在于，所述方法具体包括以下步骤：
步骤S10. 制备预乳液：按各组分质量比称取后，将（甲基）丙烯酸全氟烷基丙烯酸酯M1、丙烯酸烷基酯M2、阳离子单体M3、复合表面活性剂B、有机溶液C和去离子水在40~80℃下剪切分散形成预乳液；
步骤S20. 制备引发剂D水溶液：将所述引发剂D制成质量分数为5~20%的引发剂水溶液；
步骤S30. 在氮气气氛下，将所述步骤S10制得的所述预乳液的20～50%与所述步骤S20制得的所述引发剂D水溶液的20~50%混合，65~90℃下保温半小时，获得种子乳液；以及，
步骤S40. 在氮气气氛下，向步骤S30获得的所述种子乳液中加入剩下的预乳液及剩下的引发剂D水溶液，在65~90℃下保温4~5小时，获得所述三防整理剂。
10.如权利要求1所述的三防整理剂在高支高密涤纶面料染整工艺中的应用。