CN106554208A - A kind of new alumina silica refractory - Google Patents
A kind of new alumina silica refractory Download PDFInfo
- Publication number
- CN106554208A CN106554208A CN201510626119.4A CN201510626119A CN106554208A CN 106554208 A CN106554208 A CN 106554208A CN 201510626119 A CN201510626119 A CN 201510626119A CN 106554208 A CN106554208 A CN 106554208A
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- alumina silica
- silica refractory
- new alumina
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The mass fraction of a kind of new alumina silica refractory, its component and each component is pyrophyllite powder 30-35 parts, Kaolin 25-30 parts, titanium dioxide 5-8 parts, graphite 5-8 parts, carborundum 3-5 parts, ferrum oxide 3-5 parts, calcium oxide 3-5 parts.By above-mentioned technical proposal, a kind of new alumina silica refractory of the present invention has excellent fire resistance and long service life, is resistant to more than 2100 DEG C of high temperature using the refractory brick that the material is prepared from.
Description
Technical field
The invention belongs to technical field of refractory materials, more particularly to a kind of new alumina silica refractory.
Background technology
Refractory material refers to that refractoriness is not less than 1580 DEG C of a class Inorganic Non-metallic Materials.Refractoriness is
Refer to that refractory material bullet sample, in the case of no loading, is resisted high temperature action and do not soften and melt what is fallen
Celsius temperature.But define only with refractoriness, 1580 DEG C are not
It is absolute.Now being defined as all physicochemical properties allows its material for using in high temperature environments to be referred to as
Refractory material.Refractory material is widely used in metallurgy, chemical industry, oil, machine-building, silicate, dynamic
The industrial circles such as power, in metallurgical industry, consumption is maximum, accounts for the 50%~60% of total output.
Application to refractory in iron and steel, non-ferrous metal, glass, cement, ceramics, petrochemical industry, machinery,
The every field of the national economy such as boiler, light industry, electric power, military project, is to ensure above-mentioned industry production fortune
Row and technology develop requisite stock, play irreplaceable in hot industry production development
Important function.Wherein alumina silica refractory is a kind of high-quality refractory material, with various excellent
Performance, enjoys consumers.But existing alumina silica refractory service life is short, it would be highly desirable to
Improve.
The content of the invention
It is an object of the present invention to propose a kind of new aluminium silicate for being capable of high temperature resistant and long service life
Refractory material, thus more suitable for practicality.
The object of the invention to solve the technical problems is to employ the following technical solutions to realize.According to this
The mass fraction of a kind of new alumina silica refractory that invention is proposed, its component and each component is that leaf is cured
Stone powder 30-35 parts, Kaolin 25-30 parts, titanium dioxide 5-8 parts, graphite 5-8 parts, carborundum
3-5 parts, ferrum oxide 3-5 parts, calcium oxide 3-5 parts.
The object of the invention to solve the technical problems is further realized also using following technical measures.
The mass fraction of aforesaid new alumina silica refractory, its component and each component is pyrophyllite powder
30 parts, 25 parts of Kaolin, 5 parts of titanium dioxide, 5 parts of graphite, 3 parts of carborundum, 3 parts of ferrum oxide,
3 parts of calcium oxide.
The mass fraction of aforesaid new alumina silica refractory, its component and each component is pyrophyllite powder
32 parts, 26 parts of Kaolin, 6 parts of titanium dioxide, 6 parts of graphite, 4 parts of carborundum, 3 parts of ferrum oxide,
3 parts of calcium oxide.
The mass fraction of aforesaid new alumina silica refractory, its component and each component is pyrophyllite powder
33 parts, 27 parts of Kaolin, 7 parts of titanium dioxide, 7 parts of graphite, 4 parts of carborundum, 4 parts of ferrum oxide,
4 parts of calcium oxide.
The mass fraction of aforesaid new alumina silica refractory, its component and each component is pyrophyllite powder
34 parts, 29 parts of Kaolin, 8 parts of titanium dioxide, 8 parts of graphite, 4 parts of carborundum, 5 parts of ferrum oxide,
4 parts of calcium oxide.
By above-mentioned technical proposal, a kind of new alumina silica refractory of the present invention has excellent fire resisting
Performance and long service life, are resistant to more than 2100 DEG C of high temperature using the refractory brick that the material is prepared from.
Described above is only the general introduction of technical solution of the present invention, in order to better understand the present invention's
Technological means, and being practiced according to the content of description, and in order to allow the above-mentioned of the present invention and
Other purposes, feature and advantage can become apparent, and describe in detail especially exemplified by preferred embodiment below.
Specific embodiment
Further to illustrate the present invention to reach technological means and the work(taken by predetermined goal of the invention
Effect, below in conjunction with preferred embodiment, to according to a kind of new alumina silica refractory proposed by the present invention
Its specific embodiment, structure, feature and its effect, describe in detail as after.
Embodiment 1
The mass fraction of a kind of new alumina silica refractory of the present invention, its component and each component is that leaf is cured
30 parts of stone powder, 25 parts of Kaolin, 5 parts of titanium dioxide, 5 parts of graphite, 3 parts of carborundum, oxidation
3 parts of ferrum, 3 parts of calcium oxide.
Embodiment 2
The mass fraction of a kind of new alumina silica refractory of the present invention, its component and each component is that leaf is cured
32 parts of stone powder, 26 parts of Kaolin, 6 parts of titanium dioxide, 6 parts of graphite, 4 parts of carborundum, oxidation
3 parts of ferrum, 3 parts of calcium oxide.
Embodiment 3
The mass fraction of a kind of new alumina silica refractory of the present invention, its component and each component is that leaf is cured
33 parts of stone powder, 27 parts of Kaolin, 7 parts of titanium dioxide, 7 parts of graphite, 4 parts of carborundum, oxidation
4 parts of ferrum, 4 parts of calcium oxide.
Embodiment 4
The mass fraction of a kind of new alumina silica refractory of the present invention, its component and each component is that leaf is cured
34 parts of stone powder, 29 parts of Kaolin, 8 parts of titanium dioxide, 8 parts of graphite, 4 parts of carborundum, oxidation
5 parts of ferrum, 4 parts of calcium oxide.
The above, is only presently preferred embodiments of the present invention, and any form is not done to the present invention
On restriction, although the present invention is disclosed above with preferred embodiment, but is not limited to this
It is bright, any those skilled in the art, in the range of without departing from technical solution of the present invention, when can
A little change is made using the technology contents of the disclosure above or the Equivalent embodiments of equivalent variations are modified to,
In every case it is the content without departing from technical solution of the present invention, implements to more than according to the technical spirit of the present invention
Any simple modification, equivalent variations and modification that example is made, still fall within the model of technical solution of the present invention
In enclosing.
Claims (5)
1. a kind of new alumina silica refractory, it is characterised in that:The mass parts of its component and each component
Number for pyrophyllite powder 30-35 parts, Kaolin 25-30 parts, titanium dioxide 5-8 parts, graphite 5-8 parts,
Carborundum 3-5 parts, ferrum oxide 3-5 parts, calcium oxide 3-5 parts.
2. new alumina silica refractory according to claim 1, it is characterised in that:Its component
And the mass fraction of each component is 30 parts of pyrophyllite powder, 25 parts of Kaolin, 5 parts of titanium dioxide, stone
5 parts of ink, 3 parts of carborundum, 3 parts of ferrum oxide, 3 parts of calcium oxide.
3. new alumina silica refractory according to claim 1, it is characterised in that:Its component
And the mass fraction of each component is 32 parts of pyrophyllite powder, 26 parts of Kaolin, 6 parts of titanium dioxide, stone
6 parts of ink, 4 parts of carborundum, 3 parts of ferrum oxide, 3 parts of calcium oxide.
4. new alumina silica refractory according to claim 1, it is characterised in that:Its component
And the mass fraction of each component is 33 parts of pyrophyllite powder, 27 parts of Kaolin, 7 parts of titanium dioxide, stone
7 parts of ink, 4 parts of carborundum, 4 parts of ferrum oxide, 4 parts of calcium oxide.
5. new alumina silica refractory according to claim 1, it is characterised in that:Its component
And the mass fraction of each component is 34 parts of pyrophyllite powder, 29 parts of Kaolin, 8 parts of titanium dioxide, stone
8 parts of ink, 4 parts of carborundum, 5 parts of ferrum oxide, 4 parts of calcium oxide.