CN104291843A - Magnesia-alumina (MA) spinel - Google Patents
Magnesia-alumina (MA) spinel Download PDFInfo
- Publication number
- CN104291843A CN104291843A CN201410505133.4A CN201410505133A CN104291843A CN 104291843 A CN104291843 A CN 104291843A CN 201410505133 A CN201410505133 A CN 201410505133A CN 104291843 A CN104291843 A CN 104291843A
- Authority
- CN
- China
- Prior art keywords
- spinel
- good
- resistance
- magnesium
- magnesia
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an inorganic non-metallic material, and in particular relates to magnesia-alumina (MA) spinel. The MA spinel comprises the following minerals: Al2O3, MgO, SiO2, CaO and Fe2O3. The MA spinel disclosed by the invention has a relatively high melting point, has good erosion resistance and abrasion resistance, is good in thermal shock resistance, strong in anti-stripping capacity and good in slag resistance, also has a relatively stable chemical property, has relatively strong resistivity to basic molten slags, is a core point for applying an aluminum-magnesium refractory material, and is one of key matters for prolonging the service life. Therefore, the MA spinel is of an inorganic non-metallic material for producing a refractory material with excellent quality.
Description
Technical field
The present invention relates to a kind of ceramic, especially a kind of magnesium-aluminium spinel.
Background technology
Magnesium-aluminium spinel (being called for short MA) is widely used on refractory materials, smelting iron and steel, cement rotary kiln and glass industry kiln, is the desirable feedstock of producing the refractory productss such as the thermal zone Mg-Al spinel brick of cement rotary kiln, ladle brick, Refractory Carstables for Ladles.Itself and periclasite (being called for short M) are mixed in proportion the refractory magnesia-alumina material made, and substantially increase the corrosion resistance of steel plate lining, and have good resistance to flaking as ladle liner.
Summary of the invention
The present invention has aimed to provide a kind of magnesium-aluminium spinel, and its resistive connection structure spalling is good, and corrosion resistance is strong, good thermal shock stability, and its technical scheme adopted is as follows:
A kind of magnesium-aluminium spinel, is characterized in that: its mineral composition is Al
2o
3, MgO, SiO
2, CaO, Fe
2o
3, the weight percent of each composition is respectively Al
2o
382.5%, MgO15.5%, SiO
20.41%, CaO1.26%, Fe
2o
30.33%; The apparent porosity of described magnesium-aluminium spinel is 0.9%, and volume density is 3.48g/cm3, refractoriness 2130 DEG C.
Tool of the present invention has the following advantages: magnesium-aluminium spinel, through multistage homogenizing process, forms through more than 1800 DEG C high temperature sinterings in ultra-high-temperature tunnel kiln, and volume density is large, and mineral facies content is high, and grain development is good, even structure, steady quality.Magnesium-aluminium spinel has compared with high fusing point, thermal expansion is little, thermal stresses is low, heat shakes good stability, and simultaneously it has good anti-erosion, anticorrosive, peel-ability strong, the performance characteristics such as slag resistance is good, abrasion resistance, good thermal shock stability, high temperature resistant.Therefore, it is a kind of ceramic producing excellent quality refractory materials.
Embodiment
Below in conjunction with example, the invention will be further described:
A kind of magnesium-aluminium spinel, is characterized in that: its mineral composition is Al
2o
3, MgO, SiO
2, CaO, Fe
2o
3, the weight percent of each composition is respectively Al
2o
382.5%, MgO15.5%, SiO
20.41%, CaO1.26%, Fe
2o
30.33%; The apparent porosity of described magnesium-aluminium spinel is 0.9%, and volume density is 3.48g/cm3, refractoriness 2130 DEG C.
Describe the present invention by way of example above, but the invention is not restricted to above-mentioned specific embodiment, all any changes of doing based on the present invention or modification all belong to the scope of protection of present invention.
Claims (2)
1. a magnesium-aluminium spinel, is characterized in that: its mineral composition is Al
2o
3, MgO, SiO
2, CaO, Fe
2o
3, the weight percent of each composition is respectively Al
2o
382.5%, MgO15.5%, SiO
20.41%, CaO1.26%, Fe
2o
30.33%.
2. a kind of magnesium-aluminium spinel according to claim 1, is characterized in that: the apparent porosity of described magnesium-aluminium spinel is 0.9%, and volume density is 3.48g/cm3, refractoriness 2130 DEG C.