CN204584250U - A kind of ladle for making steel - Google Patents
A kind of ladle for making steel Download PDFInfo
- Publication number
- CN204584250U CN204584250U CN201520316627.8U CN201520316627U CN204584250U CN 204584250 U CN204584250 U CN 204584250U CN 201520316627 U CN201520316627 U CN 201520316627U CN 204584250 U CN204584250 U CN 204584250U
- Authority
- CN
- China
- Prior art keywords
- indentured
- layer
- working lining
- bag
- permanent layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model relates to a kind of ladle for making steel, comprise box hat, box hat madial wall is coated with successively permanent layer in the outer permanent layer of bag wall and bag wall, in bag wall, permanent layer inwall is coated with indentured molten pool working layer and indentured slag line working lining, and indentured slag line working lining is arranged on indentured molten pool working layer top, box hat inner bottom part is provided with bag end permanent layer, bag end permanent layer is provided with Bao Di non-percussion district working lining, the sidewall of Bao Di non-percussion district working lining is close to indentured molten pool working layer and is arranged, bag end impact zone working lining is provided with in the middle part of Bao Di non-percussion district working lining, the outer permanent layer of bag wall is formed by micropore high temperature insulating brick masonry, in bag wall, permanent layer at the bottom of permanent layer and bag is formed by the cast of High-Alumina castable refractory, indentured molten pool working layer is built by laying bricks or stones by carbon free precast block and is formed, indentured slag line working lining is built by laying bricks or stones by magnesia carbon brick and is formed, bag end impact zone working lining is built by laying bricks or stones by carbon-free prefabricated component and is formed.Advantage: safety, life-span length, good heat insulating, steel quality are high, lightweight.
Description
Technical field
The present invention relates to a kind of steel-making equipment, particularly a kind of ladle for making steel.
Background technology
Ladle is as the important container piece of metallurgical industry, and ladle is not only storage, the transloading equipment of molten steel, simultaneously or the key equipment of external refining.Along with improving constantly of steel and iron industry smelting technique, iron and steel enterprise is in order to improve the level of production, reduce production cost, enhance the competitiveness, greatly develop the treatment technology of molten steel, external refining is than constantly increasing, smelting condition is day by day harsh, Tapping Temperature of Bof is high, and molten steel terminates from converter tapping to refining treatment, the transport of experience and the processing procedure time is long, operation is many, temperature drop is large.The condition of work of ladle in smelting process is day by day harsh, requirements at the higher level are proposed to ladle lining liner, in steel smelting procedure, ladle lining liner not only will meet safety, long-lived, stable operation, simultaneously to ladle heat preservation and insulation and be beneficial to Cleanliness of Molten Steel and propose requirement.
Ladle lining liner is made up of working lining, permanent layer, heat-insulation layer usually, and existing ladle lining inner liner work layer generally adopts carbonaceous article magnesia-alumina-carbon brick and magnesia carbon brick, and permanent layer adopts high alumina castable, and heat-insulation layer adopts flame-retardant fibre board, vermiculite board.Along with improving constantly of steel and iron industry smelting technique, molten steel is serious to the erosion of refractory lining, causes ladle lining fireproof material on the low side for service life, and change frequent, labor strength is high, and all transfer efficients of ladle are low; The raising of tapping temperature and refining ratio, such that ladle wall temperature is too high, molten steel temperature drop is large, cause heat loss excessive, be unfavorable for the energy-saving and cost-reducing of smelting iron and steel; Ladle lining liner adopts carbonaceous article in smelting process, can pollute, be unfavorable for the production of variety steel to molten steel; Insulation material flame-retardant fibre board, vermiculite board in use, there will be efflorescence, hollow phenomenon, cause liner to loosen, there is potential safety hazard in ladle running process.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of ladle for making steel, effectively solve molten steel in prior art serious to the erosion of ladle lining liner, cause ladle lining fireproof material on the low side for service life, change frequent, labor strength is high, and all transfer efficients of ladle are low; The raising of tapping temperature and refining ratio, such that ladle wall temperature is too high, molten steel temperature drop is large, cause heat loss excessive, be unfavorable for the energy-saving and cost-reducing of smelting iron and steel; Ladle lining liner adopts carbonaceous article in smelting process, can pollute, be unfavorable for the production of variety steel to molten steel; Insulation material flame-retardant fibre board, vermiculite board in use, there will be efflorescence, hollow phenomenon, cause liner to loosen, there is the defect of potential safety hazard in ladle running process.
The technical scheme that the present invention solves the problems of the technologies described above is as follows: a kind of ladle for making steel, comprise box hat, above-mentioned box hat madial wall covers successively and is provided with permanent layer in the outer permanent layer of bag wall and bag wall, permanent layer inwall is coated with respectively indentured molten pool working layer and indentured slag line working lining in above-mentioned bag wall, and above-mentioned indentured slag line working lining is arranged on indentured molten pool working layer top, above-mentioned box hat inner bottom part is provided with bag end permanent layer, permanent layer at the bottom of above-mentioned bag is provided with Bao Di non-percussion district working lining, the sidewall of above-mentioned Bao Di non-percussion district working lining is close to indentured molten pool working layer and is arranged, bag end impact zone working lining is provided with in the middle part of above-mentioned Bao Di non-percussion district working lining, the outer permanent layer of above-mentioned bag wall is formed by micropore high temperature insulating brick masonry, in above-mentioned bag wall, permanent layer at the bottom of permanent layer and bag is formed by the cast of High-Alumina castable refractory, above-mentioned indentured molten pool working layer is built by laying bricks or stones by carbon free precast block and is formed, above-mentioned indentured slag line working lining is built by laying bricks or stones by magnesia carbon brick and is formed, above-mentioned Bao Di non-percussion district working lining is poured into a mould by aluminum-spinel castable and is formed, impact zone working lining at the bottom of above-mentioned bag is built by laying bricks or stones by carbon-free prefabricated component and is formed.
The invention has the beneficial effects as follows:
Ladle for making steel of the present invention is safe and reliable, long service life, good heat insulating, be beneficial to Cleanliness of Molten Steel, improves molten steel purity and quality, reduces overall weight, make whole ladle safe and stable operation.
On the basis of technique scheme, the present invention can also do following improvement.
Further, above-mentioned indentured molten pool working layer lower end is provided with projection, and above-mentioned projection covers on Bao Di non-percussion district working lining.
The beneficial effect of above-mentioned further scheme is adopted to be prevent Bao Di non-percussion district working lining from coming off because using for a long time and then affect normal use.
Accompanying drawing explanation
Fig. 1 is the cross-sectional view of the ladle for making steel of the present invention;
In accompanying drawing, the list of parts representated by each label is as follows:
1, box hat, 2, the outer permanent layer of bag wall, 3, permanent layer in bag wall, 4, indentured molten pool working layer, 5, indentured slag line working lining, 6, bag end permanent layer, 7, Bao Di non-percussion district working lining, 8, bag end impact zone working lining, 41, projection.
Detailed description of the invention
Be described principle of the present invention and feature below in conjunction with accompanying drawing, example, only for explaining the present invention, is not intended to limit scope of the present invention.
Embodiment: as shown in Figure 1, ladle for making steel of the present invention, comprise box hat 1, above-mentioned box hat 1 madial wall covers successively and is provided with permanent layer 3 in the outer permanent layer 2 of bag wall and bag wall, permanent layer 3 inwall is coated with respectively indentured molten pool working layer 4 and indentured slag line working lining 5 in above-mentioned bag wall, and above-mentioned indentured slag line working lining 5 is arranged on indentured molten pool working layer 4 top, above-mentioned box hat 1 inner bottom part is provided with bag end permanent layer 6, permanent layer 6 at the bottom of above-mentioned bag is provided with Bao Di non-percussion district working lining 7, the sidewall of above-mentioned Bao Di non-percussion district working lining 7 is close to indentured molten pool working layer 4 and is arranged, bag end impact zone working lining 8 is provided with in the middle part of above-mentioned Bao Di non-percussion district working lining 7, the outer permanent layer 1 of above-mentioned bag wall is formed by micropore high temperature insulating brick masonry, in above-mentioned bag wall, permanent layer 3 and bag end permanent layer 6 are formed by the cast of High-Alumina castable refractory, above-mentioned indentured molten pool working layer 4 is built by laying bricks or stones by carbon free precast block and is formed, above-mentioned indentured slag line working lining 5 is built by laying bricks or stones by magnesia carbon brick and is formed, above-mentioned Bao Di non-percussion district working lining 7 is poured into a mould by aluminum-spinel castable and is formed, impact zone working lining 8 at the bottom of above-mentioned bag is built by laying bricks or stones by carbon-free prefabricated component and is formed.
Above-mentioned indentured molten pool working layer 4 lower end is provided with projection 41, and above-mentioned projection 41 covers on Bao Di non-percussion district working lining 7.
The performance parameter for each working lining of ladle of making steel of the present embodiment is specially: the outer permanent layer 2 of bag wall adopts micropore high temperature insulating brick masonry, and its Specifeca tion speeification is: bulk density is 1.0 ~ 1.2gcm
-3, cold crushing strength>=6MPa, heating permanent line rate of change 1350 DEG C × 12h be 0 ~ 1.5%, thermal conductivity factor 350 ± 25 DEG C≤0.55W/mK, thickness is set to 80 ~ 100mm; In bag wall, permanent layer 3 adopts High-Alumina castable refractory to pour into a mould, and its Specifeca tion speeification is: bulk density 110 DEG C × 24h>=2.5gcm
-3, compressive resistance 110 DEG C × 24h>=30MPa, compressive resistance 1450 DEG C × 3h>=40MPa, Linear change rate 1450 DEG C × 3h be ± 1%, Al
2o
3content is 50% ~ 90%, and thickness is set to 10 ~ 30mm;
Indentured molten pool working layer 4 is built by laying bricks or stones by carbon free precast block and is formed, and its Specifeca tion speeification is: bulk density>=2.9gcm
-3, compressive resistance 110 DEG C × 24h>=30MPa, Al
2o
3+ content of MgO is>=80%, and wherein, carbon free precast block is with high alumina corundum for aggregate, and fused magnesite, alumina powder and ultrafine silica powder are substrate material synthesis;
Bag end permanent layer 6 adopts High-Alumina castable refractory to pour into a mould, and its Specifeca tion speeification is: bulk density 110 DEG C × 24h>=2.5gcm
-3, compressive resistance 110 DEG C × 24h>=30MPa, compressive resistance 1450 DEG C × 3h>=40MPa, Linear change rate 1450 DEG C × 3h be ± 1%, Al
2o
3content is 50% ~ 90%;
Bao Di non-percussion district working lining 7 adopts aluminum-spinel castable to pour into a mould, bulk density 110 DEG C × 24h>=2.8gcm
-3, compressive resistance 110 DEG C × 24h>=30MPa, Al
2o
3+ content of MgO is>=80%;
Bag end impact zone working lining 8 adopts carbon-free prefabricated component to build by laying bricks or stones, and its Specifeca tion speeification is: bulk density>=2.9gcm
-3, compressive resistance 110 DEG C × 24h>=30MPa, Al
2o
3+ content of MgO is>=80%.
In above-mentioned, micropore high temperature insulating brick is fired by materials such as mullite powder, pore-forming material, normal temperature reinforcing agent, high-temperature expansion agent, high temperature reinforcing agents and is formed, the advantage such as it has, and unit weight is light, heat-proof quality good, heat resistance is strong, cold crushing strength is high, have stable high-temperature performance, low price, high-alumina refractory castable for aggregate and powder with High-Alumina raw material, adds bonding agent and makes, magnesia carbon brick is using high-melting-point alkalescence oxides magnesium (fusing point 2800 DEG C) and is difficult to be invaded the high-melting-point carbon materials of profit as raw material by slag, adds various non-oxidized substance additive and makes, carbon free precast block and carbon-free prefabricated component are all aggregate with corundum, fused magnesite, alumina powder and ultrafine silica powder are substrate material synthesis, in implementation process, in bag wall, permanent layer 3 adopts High-Alumina castable refractory to pour into a mould, and its thickness is lower, under the prerequisite of anti-molten steel penetrating power ensureing permanent layer 3 in bag wall, significantly reduce the weight of permanent layer 3 in ladle wall, and then reduce the production and application cost of ladle, the outer permanent layer 2 of bag wall adopts micropore high temperature insulating brick masonry, its thickness is higher, lightweight, have stable high-temperature performance, stop to occur efflorescence, hollow phenomenon, and low price, can play in conjunction with permanent layer 3 in bag wall and reduce ladle lining liner weight, improve the heat preservation and insulation of ladle, ensure the anti-molten steel penetrating power of ladle, guarantee the effect of ladle safe and stable operation.
Ladle for making steel of the present invention is safe and reliable, long service life, good heat insulating, be beneficial to Cleanliness of Molten Steel, improves molten steel purity and quality, reduces overall weight, make whole ladle safe and stable operation.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (2)
1. the ladle for making steel, it is characterized in that: comprise box hat (1), described box hat (1) madial wall covers successively and is provided with permanent layer (3) in the outer permanent layer (2) of bag wall and bag wall, permanent layer (3) inwall is coated with respectively indentured molten pool working layer (4) and indentured slag line working lining (5) in described bag wall, and described indentured slag line working lining (5) is arranged on indentured molten pool working layer (4) top, described box hat (1) inner bottom part is provided with bag end permanent layer (6), permanent layer (6) at the bottom of described bag is provided with Bao Di non-percussion district working lining (7), the sidewall of described Bao Di non-percussion district working lining (7) is close to indentured molten pool working layer (4) and is arranged, described Bao Di non-percussion district working lining (7) middle part is provided with bag end impact zone working lining (8), the outer permanent layer (1) of described bag wall is formed by micropore high temperature insulating brick masonry, in described bag wall, permanent layer (3) and bag end permanent layer (6) are formed by the cast of High-Alumina castable refractory, described indentured molten pool working layer (4) is built by laying bricks or stones by carbon free precast block and is formed, described indentured slag line working lining (5) is built by laying bricks or stones by magnesia carbon brick and is formed, described Bao Di non-percussion district working lining (7) is poured into a mould by aluminum-spinel castable and is formed, impact zone working lining (8) at the bottom of described bag is built by laying bricks or stones by carbon-free prefabricated component and is formed.
2. the ladle for making steel according to claim 1, it is characterized in that: described indentured molten pool working layer (4) lower end is provided with projection (41), and described projection (41) covers in Bao Di non-percussion district working lining (7).