CN106543876A - A kind of fire prevention nano-polyurethane floor paint - Google Patents
A kind of fire prevention nano-polyurethane floor paint Download PDFInfo
- Publication number
- CN106543876A CN106543876A CN201610933388.XA CN201610933388A CN106543876A CN 106543876 A CN106543876 A CN 106543876A CN 201610933388 A CN201610933388 A CN 201610933388A CN 106543876 A CN106543876 A CN 106543876A
- Authority
- CN
- China
- Prior art keywords
- parts
- nano
- floor paint
- fire prevention
- polyurethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The nano-polyurethane floor paint the invention discloses one kind is prevented fires, the floor paint include following parts by weight of component：70 90 parts of waterborne polyurethane resin, 5 11 parts of VTES, 4.5 6.5 parts of nano magnesia, 46 parts of actinolite powder, 37 parts of zinc naphthenate, 48 parts of divinyl dimethoxysilane, 59 parts of polyether Glycols, 7 10 parts of pure-acrylic emulsion, 49 parts of tetraethyl orthosilicate, 2.4 3.6 parts of DBSA, 14 parts of butyl titanate, 58 parts of lauryl magnesium sulfate, 59 parts of Nano titanium nitride.Present invention fire prevention nano-polyurethane floor paint is solvent-free, nontoxic, environmental protection, it is to avoid harm of the organic solvent to health, is capable of achieving construction and the complete feature of environmental protection applied.The characteristics of with preferable resistance to water, fire line, high coloring power, color inhibition.Layer surface brightness is higher, color and luster is vivider, physical property more preferably.
Description
Technical field
The present invention relates to a kind of floor paint, more particularly to a kind of fire prevention nano-polyurethane floor paint.
Background technology
Fire prevention floor paint has globality, and seamless, environmental protection, nontoxic non-stimulated peculiar smell, wear-resistant, anti-corrosion, waterproof are prevented
Dirt, the advantages of appearance is beautiful.Fire prevention floor paint is liquid form, in uniformly densely solid film-shaped after the completion of construction, can be extensive
Fabrication facility floor, residential building earth's surface or metope, institutional settings, warehouse are applied to, the vast field to fire protection requirement is waited.Wherein prevent
Fiery nano-polyurethane floor paint has preferable mechanical performance, and general hardness is all higher, but also with wear and shock-resistant
Ability, chemical resistance are good, good weatherability.And terrace paint coating is developed so far, because which has excellent Physical Mechanical
The performances such as energy, electrical insulation capability, resistance to chemical attack, are widely applied in the every field of national economy, and its yield is continuous
Increase, quality is improved constantly, new varieties are continued to bring out.With the continuous development of market economy, competition is also to grow in intensity, and that is just
Needs are developed in the technology and production capacity of enterprise, promote coating to update, and nano paint, with existing floor paint
Raw materials used to have compared unrivaled ultra-fine property and uniqueness, its product combination property and quality are significantly better than its similar product
Product, and cost is less than traditional product, has caused the great attention of countries in the world, and by leader's building coating industry new trend, into
For the new fashion of decoration industry, nanometer terrace paint coating has become the inexorable trend of terrace paint coating development.Accordingly, it would be desirable to develop
A kind of fire prevention nano-polyurethane floor paint that can overcome problem described above.
The content of the invention
It is an object of the invention to provide a kind of fire prevention nano-polyurethane floor paint.
To achieve these goals, the nano-polyurethane floor paint the invention provides one kind is prevented fires, comprising following weight portion
Component：Waterborne polyurethane resin 70-90 parts, VTES 5-11 parts, nano magnesia 4.5-6.5 parts, sun rise
Stone flour 4-6 parts, zinc naphthenate 3-7 parts, divinyl dimethoxysilane 4-8 parts, polyether Glycols 5-9 parts, pure-acrylic emulsion 7-
10 parts, tetraethyl orthosilicate 4-9 parts, DBSA 2.4-3.6 parts, butyl titanate 1-4 parts, lauryl magnesium sulfate 5-8 parts,
Nano titanium nitride 5-9 parts.
Which also includes HMDS 4-9 parts.
Which also includes nano-pearl rock 8-15 parts.
Which also includes carboxymethylcellulose calcium 10-15 parts.
Beneficial effect：Present invention fire prevention nano-polyurethane floor paint is solvent-free, nontoxic, environmental protection, it is to avoid have
Harm of the machine solvent to health, is capable of achieving construction and the complete feature of environmental protection applied.With preferable resistance to water, fire line,
The characteristics of high coloring power, color inhibition.Layer surface brightness is higher, color and luster is vivider, physical property more preferably.
Specific embodiment
Embodiment 1
The fire prevention nano-polyurethane floor paint of the present embodiment, comprising following parts by weight of component：70 parts of waterborne polyurethane resin, ethene
5 parts of ethyl triethoxy silicane alkane, 4.5 parts of nano magnesia, actinolite powder 4-6 parts, 3 parts of zinc naphthenate, divinyl dimethoxy
4 parts of silane, 5 parts of polyether Glycols, 7 parts of pure-acrylic emulsion, 4 parts of tetraethyl orthosilicate, 2.4 parts of DBSA, butyl titanate 1
Part, 5 parts of lauryl magnesium sulfate, 5 parts of Nano titanium nitride.Above-mentioned material is put in agitator tank, agitator tank temperature is 50 DEG C, stirring
Mix, be obtained after normal temperature is cooled to after mixing.
The performance that the present embodiment is obtained floor paint is measured, the performance test data for detecting are：Paint film is smooth, light
It is sliding, pencil hardness：1H, adhesive force：≤ 1 grade, pliability：≤ 2mm, resistance to impact：>=30mm, compression strength：80MPa, resistance to combustion
Time：>=30min, flame propagation ratio：≤ 20, burning quality loss：＜ 4g, char volume≤20cm3, resistance to water, immersion 7
After it：Unchanged, bubble-free is wrinkle resistant, do not fall off；Salt fog resistance 5 days：1 grade.
Embodiment 2
The fire prevention nano-polyurethane floor paint of the present embodiment, comprising following parts by weight of component：90 parts of waterborne polyurethane resin, ethene
11 parts of ethyl triethoxy silicane alkane, 6.5 parts of nano magnesia, 46 parts of actinolite powder, 7 parts of zinc naphthenate, divinyl dimethoxy
8 parts of silane, polyether Glycols 5-9 parts, 10 parts of pure-acrylic emulsion, 9 parts of tetraethyl orthosilicate, 3.6 parts of DBSA, metatitanic acid fourth
4 parts of ester, 8 parts of lauryl magnesium sulfate, 9 parts of Nano titanium nitride, 9 parts of HMDS.Above-mentioned material is put in agitator tank,
Agitator tank temperature is 80 DEG C, stirs and evenly mixs, is obtained after being cooled to normal temperature after mixing.
The performance that the present embodiment is obtained floor paint is measured, the performance test data for detecting are：Paint film is smooth, light
It is sliding, pencil hardness：1H, adhesive force：≤ 1 grade, pliability：≤ 2mm, resistance to impact：>=30mm, compression strength：82MPa, resistance to combustion
Time：>=30min, flame propagation ratio：≤ 20, burning quality loss：＜ 4g, char volume≤20cm3, resistance to water, immersion 7
After it：Unchanged, bubble-free is wrinkle resistant, do not fall off；Salt fog resistance 5 days：1 grade.
Embodiment 3
The fire prevention nano-polyurethane floor paint of the present embodiment, comprising following parts by weight of component：70 parts of waterborne polyurethane resin, ethene
5 parts of ethyl triethoxy silicane alkane, 4.5 parts of nano magnesia, actinolite powder 4-6 parts, 3 parts of zinc naphthenate, divinyl dimethoxy
4 parts of silane, 5 parts of polyether Glycols, 7 parts of pure-acrylic emulsion, 4 parts of tetraethyl orthosilicate, 2.4 parts of DBSA, butyl titanate 1
Part, 5 parts of lauryl magnesium sulfate, 5 parts of Nano titanium nitride, 4 parts of HMDS, 8 parts of nano-pearl rock.Above-mentioned material is put
Enter in agitator tank, agitator tank temperature is 50 DEG C, stirs and evenly mixs, is obtained after being cooled to normal temperature after mixing.
The performance that the present embodiment is obtained floor paint is measured, the performance test data for detecting are：Paint film is smooth, light
It is sliding, pencil hardness：1H, adhesive force：≤ 1 grade, pliability：≤ 2mm, resistance to impact：>=30mm, compression strength：85MPa, resistance to combustion
Time：>=30min, flame propagation ratio：≤ 20, burning quality loss：＜ 4g, char volume≤20cm3, resistance to water, immersion 7
After it：Unchanged, bubble-free is wrinkle resistant, do not fall off；Salt fog resistance 5 days：1 grade.
Embodiment 4
The fire prevention nano-polyurethane floor paint of the present embodiment, comprising following parts by weight of component：90 parts of waterborne polyurethane resin, ethene
11 parts of ethyl triethoxy silicane alkane, 6.5 parts of nano magnesia, 46 parts of actinolite powder, 7 parts of zinc naphthenate, divinyl dimethoxy
8 parts of silane, polyether Glycols 5-9 parts, 10 parts of pure-acrylic emulsion, 9 parts of tetraethyl orthosilicate, 3.6 parts of DBSA, metatitanic acid fourth
4 parts of ester, 8 parts of lauryl magnesium sulfate, 9 parts of Nano titanium nitride, 9 parts of HMDS, 15 parts of nano-pearl rock, carboxymethyl are fine
15 parts of dimension element.Above-mentioned material is put in agitator tank, agitator tank temperature is 80 DEG C, is stirred and evenly mixed, after being cooled to normal temperature after mixing
It is obtained.
The performance that the present embodiment is obtained floor paint is measured, the performance test data for detecting are：Paint film is smooth, light
It is sliding, pencil hardness：1H, adhesive force：≤ 1 grade, pliability：≤ 2mm, resistance to impact：>=30mm, compression strength：88MPa, resistance to combustion
Time：>=30min, flame propagation ratio：≤ 20, burning quality loss：＜ 4g, char volume≤20cm3, resistance to water, immersion 7
After it：Unchanged, bubble-free is wrinkle resistant, do not fall off；Salt fog resistance 5 days：1 grade.
The above, is only presently preferred embodiments of the present invention, not makees any pro forma restriction to the present invention, though
So the present invention is disclosed above with preferred embodiment, but is not limited to the present invention, any to be familiar with this professional technology people
Member, in the range of without departing from technical solution of the present invention, when making a little change or modification using the technology contents of the disclosure above
For the Equivalent embodiments of equivalent variations, as long as being the content without departing from technical solution of the present invention, the technical spirit of the foundation present invention
Any simple modification, equivalent variations and the modification made to above example, still falls within the scope of technical solution of the present invention
It is interior.
Claims (4)
1. a kind of fire prevention nano-polyurethane floor paint, it is characterised in that comprising following parts by weight of component：Waterborne polyurethane resin 70-
90 parts, VTES 5-11 parts, nano magnesia 4.5-6.5 parts, actinolite powder 4-6 parts, zinc naphthenate 3-7
Part, divinyl dimethoxysilane 4-8 parts, polyether Glycols 5-9 parts, pure-acrylic emulsion 7-10 parts, tetraethyl orthosilicate 4-9 parts,
DBSA 2.4-3.6 parts, butyl titanate 1-4 parts, lauryl magnesium sulfate 5-8 parts, Nano titanium nitride 5-9 parts.
2. the fire prevention nano-polyurethane floor paint according to claim 1, it is characterised in that：Which also includes two silicon of hexamethyl
Azane 4-9 parts.
3. the fire prevention nano-polyurethane floor paint according to claim 2, it is characterised in that：Which also includes nano-pearl rock
8-15 parts.
4. it is according to claim 3 fire prevention nano-polyurethane floor paint, it is characterised in that：Which also includes carboxymethyl cellulose
Plain 10-15 parts.