CN101311227A - Environment-protecting and high elasticity water-proof paint - Google Patents
Environment-protecting and high elasticity water-proof paint Download PDFInfo
- Publication number
- CN101311227A CN101311227A CNA2007100522637A CN200710052263A CN101311227A CN 101311227 A CN101311227 A CN 101311227A CN A2007100522637 A CNA2007100522637 A CN A2007100522637A CN 200710052263 A CN200710052263 A CN 200710052263A CN 101311227 A CN101311227 A CN 101311227A
- Authority
- CN
- China
- Prior art keywords
- water
- paint
- defoamer
- add
- stirring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environmental protection high-elasticity waterproof paint, which comprises emulsion, a dispersant, a wetting agent, an antifoamer, short glass fibers, water, coarse whiting, wollastonite powder, tailing and propanediol. The paint has the advantages of excellent aging resistant performance, stable performance under the action of ultraviolet radiation, heat, light and oxygen and long service life of the material. As the product is water-based nontoxic material, the construction is safe and simple without environment pollution; as the paint has undemanding requirement to foundation humidity content, the construction can be carried out when the water ratio is less than 15 percent; the binding power is strong, the binding strength between the material and cement foundation is up to over 0.3Mpa; the extensibility of the material is good, which can be up to over 300 percent. Therefore, the paint is characterized by excellent cracking resistant performance, excellent frost resistance performance, low-temperature flexibility, good construction performance, without foaming and good film-forming effect.
Description
Technical field
The present invention relates to environment-protecting and high elasticity water-proof paint, especially environment-protecting and high elasticity water-proof paint
Background technology
The water-proof material of Shi Yonging generally is the black water-proof material in the past, and this material is not only constructed loaded down with trivial details, and cold-resistant, resistance to elevated temperatures is poor, easily season cracking influences waterproof effect; Because it is a black, does not also have heat-blocking action, let alone beautification function.Also some waterproof coating on the market, but majority is thing from abroad, the price comparison height.The product innovation price is lower, is mainly used in waterproof, decoration, the impervious mending-leakage of buildings, as: the water-proof binding of aspects such as roofing, exterior wall, toilet, ground, vault, seam crossing and pipeline, ditch, pond, sealing, heat insulation, decoration and mending-leakage.
Summary of the invention
The object of the present invention is to provide an environment-protecting and high elasticity water-proof paint, this coating ageing-resistant performance is good, stable performance under ultraviolet ray, heat, light, the oxygen effect, material long service life.
Technical scheme of the present invention is: a kind of environment-protecting and high elasticity water-proof paint, and its described raw material in the component of weight part is:
Emulsion 320-360 dispersion agent 731A 2-3 dispersion agent P19 4-6 wetting agent 1-3
Defoamer 0.8-1.2 staple glass fibre 7-8 water 18-22 coarse whiting 300-400
Wollastonite powder 120-160 sand 120-160 defoamer 1-3 propylene glycol 8-12,
The preparation method of this coating is: a, emulsion is dropped in the scuffing of cylinder bore starting outfit, stirring at low speed; B, with dispersion agent, wetting agent, AMP-95, defoamer, etc. be sequentially added into successively; C, staple glass fibre and water are carried out wetting back in proportion add; D, fully disperse mixing to staple glass fibre after, slowly evenly add coarse whiting, wollastonite powder, tailings successively, fully disperse; E, adding defoamer, stirring and evenly mixing; F, adding propylene glycol, stirring and evenly mixing; G, apparent viscosity situation add ammoniacal liquor and adjust PH to the 8-9 value, add thickening material ASE-60 and adjust viscosity to 6000mPa.S; H, treat complete mixing after, discharging is canned.
The invention has the advantages that: ageing-resistant performance is good, stable performance under ultraviolet ray, heat, light, the oxygen effect, material long service life.Product is the aq. type non-toxic material, construction safety, simple, free from environmental pollution, and not tight to basic unit's water capacity requirement, water ratio＜15% all can be constructed.Cohesive force is strong, and material and cement basal plane cohesive strength can reach more than the 0.3MPa.Material good-extensibility, unit elongation can reach more than 300%, and therefore, the resistance to cleavage excellence also has good frost resistance and low temperature flexibility.Application property is good, and is non-foaming, film-formation result good.The scope of utilization is more extensive: the coagulation flat ground of roofing, gutter, awning and various irregular waterproof position; Exterior wall, base plate, elevator hole, subterranean tunnel, open caisson, pipeline etc. in the concrete of hypogee; The toilet of surface structures, bathroom, kitchen, flower bed, pond etc.At any rule or irregular basal plane top roll, brush this coating, can both form rubber waterproof layer continuously, this is that coiled material is beyond one's reach.Product is used for decoration of exterior wall, not only plays beautification function and also plays impervious, moistureproof, mildew-proof function.This coating single-component package, on-the-spot only need stirring is the available method construction of scraping or brushing that is coated with, and be easy to use.Waterproof paint also needn't be constructed again on a large scale just in case seepage occurs, only need carry out sectional repair, and both laborsaving, it is economical to save time again.
Embodiment
A kind of environment-protecting and high elasticity water-proof paint, the preparation method is: a, 340 kilograms of emulsions are dropped in the scuffings of cylinder bore starting outfit, stirring at low speed; B, with 2.4 kg.p.m. powder 731A, 5 kg.p.m. powder P19,2 kilograms of wetting agents, 1 kilogram of defoamer, etc. be sequentially added into successively; C, 7.5 kilograms of staple glass fibres and 20 kg water are carried out wetting back in proportion add; D, fully disperse mixing to staple glass fibre after, slowly evenly add 340 kilograms of coarse whitings, 140 kilograms of wollastonite powder, 140 kg sand successively, fully disperse; E, 2 kilograms of defoamers of adding, stirring and evenly mixing; F, 10 kilograms of propylene glycol of adding, stirring and evenly mixing; G, apparent viscosity situation add ammoniacal liquor and adjust PH to the 8-9 value, add thickening material ASE-60 and adjust viscosity to 6000mPa.S; H, treat complete mixing after, discharging is canned.
Claims (1)
1, a kind of environment-protecting and high elasticity water-proof paint, its described raw material with the weight part component is:
Emulsion 320-360 dispersion agent 731A 2-3 dispersion agent P19 4-6 wetting agent 1-3
Defoamer 0.8-1.2 staple glass fibre 7-8 water 18-22 coarse whiting 300-400
Wollastonite powder 120-160 sand 120-160 defoamer 1-3 propylene glycol 8-12
The preparation method of this coating is: a, with in the emulsion input cylinder, starting outfit, stirring at low speed; B, be sequentially added into dispersion agent 731A, dispersion agent P19, wetting agent, defoamer in the cylinder successively; C, staple glass fibre and water are carried out wetting back in proportion add; D, fully disperse mixing to staple glass fibre after, slowly evenly add coarse whiting, wollastonite powder, tailings successively, fully disperse; E, adding defoamer, stirring and evenly mixing; F, adding propylene glycol, stirring and evenly mixing; G, apparent viscosity situation add ammoniacal liquor and adjust PH to the 8-9 value, add thickening material ASE-60 and adjust viscosity to 6000mPa.S; H, treat complete mixing after, discharging is canned.