CN1196369A - Silicon Acrylote paint and preparation method thereof - Google Patents
Silicon Acrylote paint and preparation method thereof Download PDFInfo
- Publication number
- CN1196369A CN1196369A CN 97105779 CN97105779A CN1196369A CN 1196369 A CN1196369 A CN 1196369A CN 97105779 CN97105779 CN 97105779 CN 97105779 A CN97105779 A CN 97105779A CN 1196369 A CN1196369 A CN 1196369A
- Authority
- CN
- China
- Prior art keywords
- paint
- water
- coating
- filler
- silicon acrylote
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A paint for building contains acrylic emulsion, silicon resin, filler (titanium dioxide powder, mica powder, talc powder or light calcium), filming assistant, thickening agent, water-proofing agent, disperser, defoaming agent, antiseptic and water, and features the function to resist water, acid, alkali, salt fog and ultraviolet ray, not cracking and dropping, high air permeability, flame-retarding and no poison.
Description
The invention belongs to a kind of coating that is used to whitewash building walls.
At present, the most frequently used building coating of China can be divided into oil paint and water-borne coatings two big series.For oil paint, because it contains objectionable constituent such as formaldehyde, organic solvent, benzene series thing and heavy metal, and organic appearance agent is inflammable, not only bring many constant to construction, and evaporate in the air, can cause environmental pollution and waste of material again, also easily efflorescence, variable color of product, come off, life cycle is short, thereby it can influence decorative effect and anti-guarantor property.In order to protect environment, save energy, to increase the benefit; people research and develop water-borne coatings; though water-borne coatings can overcome above-mentioned shortcoming; but the water-borne coatings of throwing on the domestic market belongs to low grade products more; poor product quality, class does not increase, and is difficult to adapt to the needs of the national economic development; its main shortcoming is: gloss is low, poor adhesive force, not water-fastly wash, self-cleaning is poor, fugitive color, can only be applicable to the decoration of common building thing.
The object of the present invention is to provide that a kind of color and luster is permanent, strong adhesion, good weatherability, and the preparation method of the building coating of antiacid alkali and this coating.
The present invention realizes like this.The coating that the present invention produced is to be main raw material with ACRYLIC EMULSION, silicone resin, filler and water, has added film coalescence aid, thickening material, water-resisting agent, dispersion agent, defoamer and sanitas therein again and has made.Proportioning in the coating of the present invention between each composition (by weight percentage) is: filler 40～50; ACRYLIC EMULSION 25～40; Silicone resin 7～10; Film coalescence aid 1～8; Thickening material 2.5～5.5; Water-resisting agent 2～4; Dispersion agent 2～8; Defoamer 0.1～0.5; Sanitas 0.1～0.3; Water 25～30.Filler described in the coating of the present invention is made up of titanium dioxide, mica powder and talcum powder or light weight calcium, and the best proportioning (by weight percentage) in the filler between the various compositions is: titanium dioxide 40～60; Mica powder 30～40; Talcum powder or light weight calcium 10～20.
Coating of the present invention both can be used as interior wall and had been coated with, has also can be used as exterior coating.Here need to prove this coating as exterior coating, used titanium dioxide is rutile-type preferably, because the titanium dioxide of rutile-type has uvioresistant and anti-effect of peeling off.And being used for interior wall coating, its titanium dioxide is preferably selected anatase titanium dioxide for use.
Coating of the present invention can be made white, also can make other colors.If this coating make white can directly select said ratio for use, in order to strengthen the white content of this coating, can in this coating, add ultramarine, the add-on of its ultramarine is preferably 0.1～0.3%, by weight.
Coating of the present invention also can be made chromatic, and its color is to decide according to user's needs, and the color of its adding can be that oxide tillandsia, red iron oxide, medium chrome yellow medium yellow etc. are multiple.It is best that the add-on of its pigment is controlled at 20～30% of coating weight.
The making method of this coating is: the used raw material of this coating is prepared burden according to the given ratio of said ratio, after will going up raw material and preparing, at first water, filler, dispersion agent, water-resisting agent and defoamer being added the material-compound tank high speed stirs, after it is mixed, send into sand mill and grind, after fineness to be ground reaches 30～60 microns, it is sent in the dispersion tank, add ACRYLIC EMULSION, silicone resin then, after waiting to stir, add thickening material, film coalescence aid, sanitas again.Stir, with ammoniacal liquor the pH value of the coating solution that stirs is adjusted to 7～10 at last, promptly obtain this coating finished product after filtering.
If it is lily that this coating is made, can not add ultramarine, and it is stirred.If this coating is made colo(u)r coating, can add required pigment again, it is stirred gets final product.
Because this coating produces with high molecular ACRYLIC EMULSION and silicone resin, it promptly is suitable for buildings and does interior wall coating, also is suitable for buildings and does exterior coating.It has waterproof, antiacid, alkali resistant, salt fog resistance, anti-an amount of ultraviolet ray and anti-ly peel off, function such as dry and cracked and dried wet abrasion, and ventilation property is strong, fire prevention, safety non-toxic.This coating color and luster is permanent, and the tinting strength of color and strong covering power, coating be shank color not for a long time.This coating can be deployed into different colors according to user's needs, make building walls reach luxurious, elegant decorative effect.But this coating can be brushed roller coating, can be sprayed in construction, and films to form and be exceedingly fast, and labor and material saving is applicable to painted, the decoration and the waterproofing protection on the inner, external wall of the concrete of all kinds of buildings and masonry face, ground, roofing, grid surface, top.
This coating is through the detection of national agent authorized, and every index all is up to state standards.This coating in container, deposit do not lump, do not condense, low-temperature stability is good, appearance of coat smooth smooth, color and luster is even; Washability can reach more than 10000 times, the coating no change; Water tolerance＞1000 are hour non-foaming; Acid resistance＞600 are hour non-foaming; Alkali resistance＞700 hour; 30 not efflorescence that circulate of freeze-thaw resistance; 1 grade of sticking power; Shock strength J=2; Gentle curved tough song mm=4.8; Viscosity=100～110k μ.
Claims (4)
1. silicon Acrylote paint, it is characterized in that: its composition (weight %) is: filler 40～50; ACRYLIC EMULSION 25～40; Silicone resin 7～10; Film coalescence aid 1～8; Thickening material 2.5～5.5; Water-resisting agent 2～4; Dispersion agent 2～8; Defoamer 0.1～0.5; Sanitas 01.～0.3; Wherein filler is made up of titanium dioxide, mica powder and talcum powder or light weight calcium, and the proportioning between them (weight %) is a titanium dioxide 40～60; Mica powder 30～40; Talcum powder or light weight calcium 10～20.
2. according to claim, described silicon Acrylote paint is characterized in that: its composition (weight %) is: ultramarine 0.1～0.3.
3. silicon Acrylote paint according to claim 1 is characterized in that: add 20～30% pigment in mentioned component, said pigment is oxide tillandsia or red iron oxide or medium chrome yellow medium yellow.
4. method for preparing silicon Acrylote paint as claimed in claim 1, it is characterized in that: at first with water, filler, dispersion agent, stir in water-resisting agent and the defoamer adding material-compound tank, to be mixed evenly after, sending into sand mill grinds, to be ground refine to 30～60 microns after, it is sent in the dispersion tank, add ACRYLIC EMULSION then, silicone resin, after waiting to stir, add thickening material again, film coalescence aid and sanitas stir, with ammoniacal liquor the pH value of the coating solution that stirs is adjusted to 7～10 at last, promptly obtain this coating finished product after filtering.