CN106479331A - A kind of special alkyd iron oxide red antirusting paint of quick-dry type environmental protection steel construction - Google Patents
A kind of special alkyd iron oxide red antirusting paint of quick-dry type environmental protection steel construction Download PDFInfo
- Publication number
- CN106479331A CN106479331A CN201510521210.XA CN201510521210A CN106479331A CN 106479331 A CN106479331 A CN 106479331A CN 201510521210 A CN201510521210 A CN 201510521210A CN 106479331 A CN106479331 A CN 106479331A
- Authority
- CN
- China
- Prior art keywords
- environmental protection
- iron oxide
- oxide red
- quick
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of special alkyd iron oxide red antirusting paint of quick-dry type environmental protection steel construction, and weight comprises following components：Plant oil modified antirust paint resin dedicated 15% ~ 50%, environmental protection 200# solvent 10% ~ 25%, dispersant 0.1% ~ 0.5%, iron oxide red 10% ~ 30%, zinc phosphate 5% ~ 30%, organobentonite 0.5% ~ 1%, methyl ethyl ketoxime 0.1% ~ 0.3%, efficient drier 0.5% ~ 1%.The present invention is applied to the metal surface of large-scale steel structure, uses generally as antirust paint.There is preferable adhesive force, moisture resistance, bottom surface paint communication property erosion that is good, especially adapting to anti-air.
Description
Technical field
The invention belongs to chemical technology field is and in particular to a kind of special alkyd iron oxide red antirusting paint of quick-dry type environmental protection steel construction.
Background technology
The anticorrosive paint of prior art is ground and add appropriate aluminum paste by long oil tetramethylolmethane, alkyd resin and iron oxide pigment, additive etc., and the drier such as cobalt, manganese, lead and organic solvent are formulated.There is drying time slowly (generally require and parch for 10 days about), difference of hardness (F level), the technical problem such as rustless property difference.
Content of the invention
The existing anticorrosive paint proposing for background technology is slow for drying time, difference of hardness, the technical problem such as rust-proof effect difference, it is an object of the invention to provide a kind of special alkyd iron oxide red antirusting paint of quick-dry type environmental protection steel construction.This coating is applied to the metal surface of large-scale steel structure, uses generally as priming paint.There is preferable adhesive force, moisture resistance, bottom surface paint communication property erosion that is good, especially adapting to anti-air.
Another object of the present invention is to providing a kind of special alkyd iron oxide red antirusting paint of quick-dry type environmental protection steel construction.
The purpose of the present invention can be achieved through the following technical solutions：
A kind of special alkyd iron oxide red antirusting paint of quick-dry type environmental protection steel construction, weight percentage comprises following components：
Plant oil modified antirust paint resin dedicated 15% ~ 50%
Environmental protection 200# solvent 10% ~ 25%
Dispersant 0.1% ~ 0.5%
Iron oxide red 10% ~ 30%
Zinc phosphate 5% ~ 30%
Organobentonite 0.5% ~ 1%
Methyl ethyl ketoxime 0.1% ~ 0.3%
Efficiently drier 0.5% ~ 1%.
Each component weight percentage sum of above-mentioned quick-drying type efficient anticorrosion alkyd iron red coating is 100%.
Preferably, the weight percentage of each component is：
Plant oil modified antirust paint resin dedicated 20% ~ 40%
Environmental protection 200# solvent 15% ~ 20%
Dispersant 0.1% ~ 0.5%
Iron oxide red 15% ~ 30%
Zinc phosphate 10% ~ 30%
Organobentonite 0.5% ~ 1%
Methyl ethyl ketoxime 0.1% ~ 0.3%
Efficiently drier 0.5% ~ 1%.
The preparation method of above-mentioned quick-drying type efficient anticorrosion alkyd iron red coating is：It is ground to fineness≤30 μm after first resin dedicated for plant oil modified antirust paint, environmental protection 200# solvent, dispersant, iron oxide red, zinc phosphate, organobentonite being mixed in proportion, be then proportionally added into methyl ethyl ketoxime and efficient drier mix homogeneously.
The present invention uses resin dedicated for refining vegetable oil modification antirust paint and iron oxide red（Rust resisting pigment）, extender pigment（Zinc phosphate）, dispersant, anti-settling agent（Organobentonite）And solvent（Environmental protection 200# solvent）After grinding, add efficient drier and anti-skinning auxiliary agent（Methyl ethyl ketoxime）It is formulated.
Beneficial effects of the present invention：
The quick-drying type efficient anticorrosion alkyd iron red coating of the present invention is applied to large-scale steel structure, the metal surface of the black such as bridge, uses generally as priming paint.There is preferable adhesive force, moisture resistance, bottom surface paint communication property erosion that is good, especially adapting to anti-air.This coating can be dried in 2 days and be delivered for use.At six months about, rustless property can be brought up to 2 years to the rust-proof effect of prior art by this product, and hardness reaches H level.
Specific embodiment
Using raw material：
Dispersant：2301
Efficiently drier：V-568,
Zinc phosphate：1250 mesh
Environmental protection 200# solvent, iron oxide red, organobentonite, methyl ethyl ketoxime are conventional commercial product.
Plant oil modified antirust paint is resin dedicated, model T-380, for the self-produced resin of my company.
Embodiment 1
A kind of special alkyd iron oxide red antirusting paint of quick-dry type environmental protection steel construction, weight percentage is composed of the following components：
Plant oil modified antirust paint resin dedicated 35%
Environmental protection 200# solvent 20%
Dispersant 0.3%
Iron oxide red 20%
Zinc phosphate 23%
Organobentonite 0.7%
Methyl ethyl ketoxime 0.2%
Efficiently drier 0.8%.
Preparation technology：
It is ground to fineness≤30 μm after first resin dedicated for plant oil modified antirust paint, environmental protection 200# solvent, dispersant, iron oxide red, zinc phosphate, organobentonite being mixed in proportion, be then proportionally added into methyl ethyl ketoxime and efficient drier mix homogeneously.
Embodiment 2
A kind of special alkyd iron oxide red antirusting paint of quick-dry type environmental protection steel construction, weight percentage is composed of the following components：
Plant oil modified antirust paint resin dedicated 40%
Environmental protection 200# solvent 15%
Dispersant 0.3%
Iron oxide red 23%
Zinc phosphate 20%
Organobentonite 0.8%
Methyl ethyl ketoxime 0.2%
Efficiently drier 0.7%.
Preparation technology is with embodiment 1.
Embodiment 3
A kind of special alkyd iron oxide red antirusting paint of quick-dry type environmental protection steel construction, weight percentage is composed of the following components：
Plant oil modified antirust paint resin dedicated 30%
Environmental protection 200# solvent 18%
Dispersant 0.5%
Iron oxide red 30%
Zinc phosphate 20%
Organobentonite 0.5%
Methyl ethyl ketoxime 0.3%
Efficiently drier 0.7%.
Preparation technology is with embodiment 1.
Embodiment 4
A kind of special alkyd iron oxide red antirusting paint of quick-dry type environmental protection steel construction, weight percentage is composed of the following components：
Plant oil modified antirust paint resin dedicated 20%
Environmental protection 200# solvent 20%
Dispersant 0.5%
Iron oxide red 28
Zinc phosphate 30%
Organobentonite 0.5%
Methyl ethyl ketoxime 0.2%
Efficiently drier 0.8%.
Preparation technology is with embodiment 1.
Embodiment 5
A kind of special alkyd iron oxide red antirusting paint of quick-dry type environmental protection steel construction, weight percentage is composed of the following components：
Plant oil modified antirust paint resin dedicated 50%
Environmental protection 200# solvent 25%
Dispersant 0.4%
Iron oxide red 10%
Zinc phosphate 13%
Organobentonite 0.6%
Methyl ethyl ketoxime 0.2%
Efficiently drier 0.8%.
Preparation technology is with embodiment 1.
Using method using the product of embodiment 1-5 preparation：Directly need adjustment viscosity can use with diluent according to construction, diluent is environmental protection rosin, and diluent consumption is 5 ~ 20%（I.e. in coating after every 1 part of dilution, weight percentage contains 5 ~ 20%
Environmental protection rosin）.
Quick-drying type efficient anticorrosion alkyd iron red coating of the present invention is applied to large-scale steel structure, the metal surface of the black such as bridge, uses generally as priming paint.There is preferable adhesive force, moisture resistance, bottom surface paint communication property erosion that is good, especially adapting to anti-air.This coating can be dried in 7 days and be delivered for use.At six months about, rustless property can be brought up to 2 years to the rust-proof effect of prior art by this product, and hardness reaches HB level.
Claims (4)
1. a kind of special alkyd iron oxide red antirusting paint of quick-dry type environmental protection steel construction is it is characterised in that weight percentage comprises following components：Plant oil modified antirust paint resin dedicated 15% ~ 50%, environmental protection 200# solvent 10% ~ 25%, dispersant 0.1% ~ 0.5%, iron oxide red 10% ~ 30%, zinc phosphate 5% ~ 30%, organobentonite 0.5% ~ 1%, methyl ethyl ketoxime 0.1% ~ 0.3%, efficient drier 0.5% ~ 1%.
2. the quick-drying type efficient anticorrosion alkyd iron red coating according to claim 1 is it is characterised in that the weight percentage of each component is：Plant oil modified antirust paint resin dedicated 20% ~ 40%, environmental protection 200# solvent 15% ~ 20%, dispersant 0.1% ~ 0.5%, iron oxide red 15% ~ 30%, zinc phosphate 10% ~ 30%, organobentonite 0.5% ~ 1%, methyl ethyl ketoxime 0.1% ~ 0.3%, efficient drier 0.5% ~ 1%.
3. the quick-drying type efficient anticorrosion alkyd iron red coating according to claim 1 is it is characterised in that its preparation method is：It is ground to fineness≤30 μm after first resin dedicated for plant oil modified antirust paint, environmental protection 200# solvent, dispersant, iron oxide red, zinc phosphate, organobentonite being mixed in proportion, be then proportionally added into methyl ethyl ketoxime and efficient drier mix homogeneously.
4. the quick-drying type efficient anticorrosion alkyd iron red coating described in claim 1, it is characterized in that being ground to fineness≤30 μm after first mixing in proportion resin dedicated for plant oil modified antirust paint, environmental protection 200# solvent, dispersant, iron oxide red, zinc phosphate, organobentonite, then it is proportionally added into methyl ethyl ketoxime and efficient drier mix homogeneously.