CN106398843A - 一种润滑油组合物 - Google Patents

一种润滑油组合物 Download PDF

Info

Publication number
CN106398843A
CN106398843A CN201610831350.1A CN201610831350A CN106398843A CN 106398843 A CN106398843 A CN 106398843A CN 201610831350 A CN201610831350 A CN 201610831350A CN 106398843 A CN106398843 A CN 106398843A
Authority
CN
China
Prior art keywords
parts
oil
lubricating oil
oxidation
zinc oxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610831350.1A
Other languages
English (en)
Inventor
杨阳
张宇
刘明星
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Yuxi New Material Technology Co Ltd
Original Assignee
Suzhou Yuxi New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Yuxi New Material Technology Co Ltd filed Critical Suzhou Yuxi New Material Technology Co Ltd
Priority to CN201610831350.1A priority Critical patent/CN106398843A/zh
Publication of CN106398843A publication Critical patent/CN106398843A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种润滑油组合物，属于润滑油技术领域。该润滑油组合物，按质量份数计：蓖麻油70～80份、改性大豆油10～15份、甲基硅油5～10份、缓蚀剂2～5份、防锈复合油5～10份、抗氧化防腐剂0.5～2份、氨基甲酸锌4～8份、有机钼1.2～1.5份、乙烯‑丙烯共聚物2～5份、非离子型表面活性剂4～8份、油溶性纳米氧化锌1.2～2.4份。采用蓖麻油和改性大豆油作为基础油生物降解率高，粘度指数高，粘温性能好，优良的极压抗磨性能，低温流动性好，原料易得，成本低。

Description

一种润滑油组合物
技术领域
本发明涉及润滑油技术领域，尤其是一种润滑油组合物。
背景技术
润滑油通常会用于压缩机中来减少摩擦，增强密封和移除汽缸及曲轴箱组件中的热量。汽缸润滑油由一种或多种抑制剂配制来帮助避免压缩机内部和工艺管路中其它处的乙烯聚合。该油润滑汽缸组件，该汽缸组件可以具有抵着固定表面移动的密封圈或在移动表面上带有的固定密封圈。由于在高压下产生的负荷，这些组件通常是金属的。这些润滑油的典型基础流体包括矿物油和多种合成油。加入添加剂用于抗腐蚀，金属钝化，抗磨，氧化稳定性，粘度改进，润滑，及其他的目的。
润滑油由基础油和添加剂两部分组成，基础油是润滑油的主要成分，决定着润滑油的基本性质，添加剂则可弥补和改善基础油性能方面的不足，赋予某些新的性能，是润滑油的重要组成部分。
目前，在钢铁、汽车、一般器械、精密器械等各种产业领域中，大多使用以精制油或合成油为基油的润滑油。近年，为了满足器械装置的小型化、低电流化、长寿化，越来越要求提高润滑油的摩擦特性及耐磨耗性。另外，考虑到节能、成本、环境等观点，防止金属生锈显得越发重要，与之相伴，提高润滑油防锈性的要求也越来越高。
发明内容
本发明的目的是：本发明为了解决现有技术中的不足，提供一种环保、较好摩擦特性、耐磨耗性及防锈性能的润滑油组合物。
为了实现本发明目的，本发明采用的技术方案如下：
一种润滑油组合物，所述润滑油组合物，按质量份数计：蓖麻油70～80份、改性大豆油10～15份、甲基硅油5～10份、缓蚀剂2～5份、防锈复合油5～10份、抗氧化防腐剂0.5～2份、氨基甲酸锌4～8份、有机钼1.2～1.5份、乙烯-丙烯共聚物2～5份、非离子型表面活性剂4～8份、油溶性纳米氧化锌1.2～2.4份。
进一步地，所述防锈复合油为羊毛脂镁皂与石油磺酸钡的混合物，其质量比为1：2。
进一步地，所述抗氧化防腐剂选自二烷基二硫代氨基甲酸锑、二烷基二硫代氨基甲酸锌、二烷基二硫代氨基甲酸酯中的任意两种，其质量比为1：2。
进一步地，所述润滑油组合物，按质量份数计：蓖麻油72～78份、改性大豆油12～14份、甲基硅油6～9份、缓蚀剂2.5～4份、防锈复合油6～8份、抗氧化防腐剂0.8～1.5份、氨基甲酸锌5～7份、有机钼1.3～1.5份、乙烯-丙烯共聚物2.5～4份、非离子型表面活性剂5～7份、油溶性纳米氧化锌1.4～2份。
进一步地，所述润滑油组合物，按质量份数计：蓖麻油75份、改性大豆油12份、甲基硅油8份、缓蚀剂3份、防锈复合油7份、抗氧化防腐剂1.2份、氨基甲酸锌6份、有机钼1.5份、乙烯-丙烯共聚物3份、非离子型表面活性剂6份、油溶性纳米氧化锌1.5份。
进一步地，所述的油溶性纳米氧化锌通过将纳米氧化锌、钛酸丁酯和硬脂酸经超声分散处理制得，其中，所述的纳米氧化锌、钛酸丁酯和硬脂酸的质量比为1：(0.01～0.1)：(0.1～2)。
采用本发明的技术方案的有益技术效果是：
1、采用蓖麻油和改性大豆油作为基础油，植物油中的甘油酯易水解，生物降解率高。粘度指数高，粘温性能好。优良的极压抗磨性能，因为植物油极性分子在金属表面形成保护膜。低温流动性好，植物油的倾点较矿物油低，原料易得，成本低。
2、采用本发明的润滑油，更环保，防锈、抗磨减摩能力好，提高摩擦副承载能力，延长设备的使用寿命。
具体实施方式
下面结合具体实施例对本发明的防锈润滑剂做进一步说明。
本发明一种润滑油，该润滑油的质量份数组成如下：蓖麻油70～80份、改性大豆油10～15份、甲基硅油5～10份、缓蚀剂2～5份、防锈复合油5～10份、抗氧化防腐剂0.5～2份、氨基甲酸锌4～8份、有机钼1.2～1.5份、乙烯-丙烯共聚物2～5份、非离子型表面活性剂4～8份、油溶性纳米氧化锌1.2～2.4份。
所述防锈复合油为羊毛脂镁皂与石油磺酸钡的混合物，其质量比为1：2。
所述抗氧化防腐剂选自二烷基二硫代氨基甲酸锑、二烷基二硫代氨基甲酸锌、二烷基二硫代氨基甲酸酯中的任意两种，其质量比例为1：2。
实施例1
1)称取各原料：蓖麻油70份、改性大豆油10份、甲基硅油10份、缓蚀剂5份、防锈复合油5份、抗氧化防腐剂2份、氨基甲酸锌4份、有机钼1.5份、乙烯-丙烯共聚物2份、非离子型表面活性剂4份、油溶性纳米氧化锌2.4份。
2)在反应釜中加入所称取的蓖麻油、改性大豆油、甲基硅油，搅拌混合均匀，再依次加入缓蚀剂、抗氧化防腐剂、防锈复合油、氨基甲酸锌、有机钼、乙烯-丙烯共聚物，继续搅拌30min，最后加入非离子型表面活性剂、油溶性纳米氧化锌继续搅拌50min，得到所需润滑油。
实施例2
1)称取各原料：蓖麻油80份、改性大豆油15份、甲基硅油5份、缓蚀剂2份、防锈复合油10份、抗氧化防腐剂0.5份、氨基甲酸锌8份、有机钼1.2份、乙烯-丙烯共聚物5份、非离子型表面活性剂8份、油溶性纳米氧化锌1.2份。
2)在反应釜中加入所称取的蓖麻油、改性大豆油、甲基硅油，搅拌混合均匀，再依次加入缓蚀剂、抗氧化防腐剂、防锈复合油、氨基甲酸锌、有机钼、乙烯-丙烯共聚物，继续搅拌30min，最后加入非离子型表面活性剂、油溶性纳米氧化锌继续搅拌50min，得到所需润滑油。
实施例3
1)称取各原料：蓖麻油72份、改性大豆油14份、甲基硅油9份、缓蚀剂2.5份、防锈复合油6份、抗氧化防腐剂0.8份、氨基甲酸锌5份、有机钼1.3份、乙烯-丙烯共聚物4份、非离子型表面活性剂5份、油溶性纳米氧化锌2份。
2)在反应釜中加入所称取的蓖麻油、改性大豆油、甲基硅油，搅拌混合均匀，再依次加入缓蚀剂、抗氧化防腐剂、防锈复合油、氨基甲酸锌、有机钼、乙烯-丙烯共聚物，继续搅拌30min，最后加入非离子型表面活性剂、油溶性纳米氧化锌继续搅拌50min，得到所需润滑油。
实施例4
1)称取各原料：蓖麻油78份、改性大豆油12份、甲基硅油6份、缓蚀剂4份、防锈复合油8份、抗氧化防腐剂1.5份、氨基甲酸锌7份、有机钼1.5份、乙烯-丙烯共聚物2.5份、非离子型表面活性剂7份、油溶性纳米氧化锌1.4份。
2)在反应釜中加入所称取的蓖麻油、改性大豆油、甲基硅油，搅拌混合均匀，再依次加入缓蚀剂、抗氧化防腐剂、防锈复合油、氨基甲酸锌、有机钼、乙烯-丙烯共聚物，继续搅拌30min，最后加入非离子型表面活性剂、油溶性纳米氧化锌继续搅拌50min，得到所需润滑油。
实施例5
1)称取各原料：蓖麻油75份、改性大豆油12份、甲基硅油8份、缓蚀剂3份、防锈复合油7份、抗氧化防腐剂1.2份、氨基甲酸锌6份、有机钼1.5份、乙烯-丙烯共聚物3份、非离子型表面活性剂6份、油溶性纳米氧化锌1.5份。
2)在反应釜中加入所称取的蓖麻油、改性大豆油、甲基硅油，搅拌混合均匀，再依次加入缓蚀剂、抗氧化防腐剂、防锈复合油、氨基甲酸锌、有机钼、乙烯-丙烯共聚物，继续搅拌30min，最后加入非离子型表面活性剂、油溶性纳米氧化锌继续搅拌50min，得到所需润滑油。
以上所述的本发明实施方式，并不构成对本发明保护范围的限定。人何在本发明的精神和原则之内所作的修改、等同替换和改进等，均应包含在本发明的保护范围之内。

Claims (6)

1.一种润滑油，其特征在于：所述润滑油的质量份数组成如下：蓖麻油70～80份、改性大豆油10～15份、甲基硅油5～10份、缓蚀剂2～5份、防锈复合油5～10份、抗氧化防腐剂0.5～2份、氨基甲酸锌4～8份、有机钼1.2～1.5份、乙烯-丙烯共聚物2～5份、非离子型表面活性剂4～8份、油溶性纳米氧化锌1.2～2.4份。
2.根据权利要求1所述的一种润滑油，其特征在于：所述防锈复合油为羊毛脂镁皂与石油磺酸钡的混合物，其质量比为1：2。
3.根据权利要求1所述的一种润滑油，其特征在于：所述抗氧化防腐剂选自二烷基二硫代氨基甲酸锑、二烷基二硫代氨基甲酸锌、二烷基二硫代氨基甲酸酯中的任意两种，其质量比为1：2。
4.根据权利要求1所述的一种润滑油，其特征在于：所述润滑油的质量份数组成如下：蓖麻油72～78份、改性大豆油12～14份、甲基硅油6～9份、缓蚀剂2.5～4份、防锈复合油6～8份、抗氧化防腐剂0.8～1.5份、氨基甲酸锌5～7份、有机钼1.3～1.5份、乙烯-丙烯共聚物2.5～4份、非离子型表面活性剂5～7份、油溶性纳米氧化锌1.4～2份。
5.根据权利要求1所述的一种润滑油，其特征在于：所述润滑油的质量份数组成如下：蓖麻油75份、改性大豆油12份、甲基硅油8份、缓蚀剂3份、防锈复合油7份、抗氧化防腐剂1.2份、氨基甲酸锌6份、有机钼1.5份、乙烯-丙烯共聚物3份、非离子型表面活性剂6份、油溶性纳米氧化锌1.5份。
6.根据权利要求1所述的一种润滑油，其特征在于：所述的油溶性纳米氧化锌通过将纳米氧化锌、钛酸丁酯和硬脂酸经超声分散处理制得，其中，所述的纳米氧化锌、钛酸丁酯和硬脂酸的质量比为1：(0.01～0.1)：(0.1～2)。
CN201610831350.1A 2016-09-19 2016-09-19 一种润滑油组合物 Pending CN106398843A (zh)